CN108660747A - 一种阻燃锦纶面料的制备方法 - Google Patents

一种阻燃锦纶面料的制备方法 Download PDF

Info

Publication number
CN108660747A
CN108660747A CN201810619581.5A CN201810619581A CN108660747A CN 108660747 A CN108660747 A CN 108660747A CN 201810619581 A CN201810619581 A CN 201810619581A CN 108660747 A CN108660747 A CN 108660747A
Authority
CN
China
Prior art keywords
fabric
flame
parts
preparation
retardant polyamide
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Withdrawn
Application number
CN201810619581.5A
Other languages
English (en)
Inventor
袁德梅
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Rugao Blueprint Knitting Garments Co Ltd
Original Assignee
Rugao Blueprint Knitting Garments Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Rugao Blueprint Knitting Garments Co Ltd filed Critical Rugao Blueprint Knitting Garments Co Ltd
Priority to CN201810619581.5A priority Critical patent/CN108660747A/zh
Publication of CN108660747A publication Critical patent/CN108660747A/zh
Withdrawn legal-status Critical Current

Abstract

本发明公开了一种阻燃锦纶面料的制备方法，其特征在于，包括步骤为：按重量分数计，在容器中顺序加入：乙醇10‑20份，十溴二苯乙烷25‑35份，二苯基磷酸酯15‑17份，充分搅拌一定时间；加入PH值调节剂将PH值调至7；将面料放入容器中充分浸泡一定时间；将浸泡好的面料取出自然晾干。通过上述方式，本发明阻燃锦纶面料的制备方法通过把锦纶面料浸泡到配置好的阻燃溶液中，使面料具备高效的阻燃性能，方法简单，效果明显。

Description

一种阻燃锦纶面料的制备方法
技术领域
本发明涉及纺织面料领域，特别是涉及一种阻燃锦纶面料的制备方法。
背景技术
随着人们生活水平的提高和以人为本的安防意识的增强，纺织品的阻燃性能越来越受到人们的关注，室内装饰织物、沙发、床上用品、电热毯、衣物等有些部位均是由锦纶面料制成，其本质上具备了严重的易燃性，一旦引发火灾，将会为人们带来极大的危害。
发明内容
本发明主要解决的技术问题是提供一种阻燃锦纶面料的制备方法，通过把锦纶面料浸泡到配置好的阻燃溶液中，使面料具备高效的阻燃性能，方法简单，效果明显。
为解决上述技术问题，本发明采用的一个技术方案是：提供一种阻燃锦纶面料的制备方法，包括步骤为：
(1)按重量分数计，在容器中顺序加入：乙醇10-20份，十溴二苯乙烷25-35份，二苯基磷酸酯15-17份，充分搅拌一定时间；
(2)加入PH值调节剂将PH值调至7；
(3)将面料放入容器中充分浸泡一定时间；
(4)将浸泡好的面料取出自然晾干。
在本发明一个较佳实施例中，所述搅拌时间为10-20分钟。
在本发明一个较佳实施例中，所述浸泡时间为20-30分钟。
本发明的有益效果是：本发明阻燃锦纶面料的制备方法通过把锦纶面料浸泡到配置好的阻燃溶液中，使面料具备高效的阻燃性能，方法简单，效果明显。
具体实施方式
下面将对本发明实施例中的技术方案进行清楚、完整地描述，显然，所描述的实施例仅是本发明的一部分实施例，而不是全部的实施例。基于本发明中的实施例，本领域普通技术人员在没有做出创造性劳动前提下所获得的所有其它实施例，都属于本发明保护的范围。
实施例一：
一种阻燃锦纶面料的制备方法，包括步骤为：
(1)按重量分数计，在容器中顺序加入：乙醇10份，十溴二苯乙烷25份，二苯基磷酸酯17份，充分搅拌10分钟；
(2)加入PH值调节剂将PH值调至7；
(3)将面料放入容器中充分浸泡30分钟；
(4)将浸泡好的面料取出自然晾干。
实施例二：
一种阻燃锦纶面料的制备方法，包括步骤为：
(1)按重量分数计，在容器中顺序加入：乙醇20份，十溴二苯乙烷35份，二苯基磷酸酯15份，充分搅拌20分钟；
(2)加入PH值调节剂将PH值调至7；
(3)将面料放入容器中充分浸泡20分钟；
(4)将浸泡好的面料取出自然晾干。
实施例三：
一种阻燃锦纶面料的制备方法，包括步骤为：
(1)按重量分数计，在容器中顺序加入：乙醇15份，十溴二苯乙烷30份，二苯基磷酸酯16份，充分搅拌15分钟；
(2)加入PH值调节剂将PH值调至7；
(3)将面料放入容器中充分浸泡25分钟；
(4)将浸泡好的面料取出自然晾干。
本发明阻燃锦纶面料的制备方法的有益效果是：
通过把锦纶面料浸泡到配置好的阻燃溶液中，使面料具备高效的阻燃性能，方法简单，效果明显。
以上所述仅为本发明的实施例，并非因此限制本发明的专利范围，凡是利用本发明说明书内容所作的等效结构或等效流程变换，或直接或间接运用在其它相关的技术领域，均同理包括在本发明的专利保护范围内。

Claims (3)

1.一种阻燃锦纶面料的制备方法，其特征在于，包括步骤为：
(1)按重量分数计，在容器中顺序加入：乙醇10-20份，十溴二苯乙烷25-35份，二苯基磷酸酯15-17份，充分搅拌一定时间；
(2)加入PH值调节剂将PH值调至7；
(3)将面料放入容器中充分浸泡一定时间；
(4)将浸泡好的面料取出自然晾干。
2.根据权利要求1所述的阻燃锦纶面料的制备方法，其特征在于，所述搅拌时间为10-20分钟。
3.根据权利要求1所述的阻燃锦纶面料的制备方法，其特征在于，所述浸泡时间为20-30分钟。
CN201810619581.5A 2018-06-13 2018-06-13 一种阻燃锦纶面料的制备方法 Withdrawn CN108660747A (zh)