CN108646528A - 金光红紫外荧光防伪激光打印机干式墨粉及其制备方法 - Google Patents
金光红紫外荧光防伪激光打印机干式墨粉及其制备方法 Download PDFInfo
- Publication number
- CN108646528A CN108646528A CN201810401070.6A CN201810401070A CN108646528A CN 108646528 A CN108646528 A CN 108646528A CN 201810401070 A CN201810401070 A CN 201810401070A CN 108646528 A CN108646528 A CN 108646528A
- Authority
- CN
- China
- Prior art keywords
- parts
- powder
- fake
- dry type
- ultraluminescence
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及一种金光红紫外荧光防伪激光打印机干式墨粉及其制备方法,属于激光打印耗材技术领域。其采用紫外荧光粉4~8份、金光红粉10~20份、含蜡苯丙树脂80~90份、聚丙烯蜡4~6份、电荷调节剂2~4份、氨基硅烷4~8份和六甲基硅氮烷13~18份,经混炼、挤塑、粉碎和过筛等步骤而制成。本发明专门为政府防伪红头文件研制,颜色亮丽,色彩纯正,满足政府行业防伪红头文件的印制要求,使打印图像过渡更加平滑,层次的再现也更加的真实。本发明激光打印机材质广泛,不仅可以打印普通复印纸张,同时可以适应卡片、胶片等各种介质、满足多种打印应用。同时在激光打印机金光红紫外荧光防伪干式墨粉中添加了紫外荧光粉,起到了防伪的效果。
Description
技术领域
本发明涉及一种金光红紫外荧光防伪激光打印机干式墨粉及其制备方法,属于激光打印耗材技术领域。
背景技术
印有“红头”、“红章”的政府公文通常被统称为“红头文件”,作为上情下达的正式官方文件,“红头文件”是各级党、政机关、企事业单位日常应用最广、打印量最多的文件类型。红头激光打印机解决方案不仅最大程度的优化了“红头文件”的印制流程更大幅提升了制作效率,更重要的是将传统繁琐的手工操作环节转化为电子化自动流程,自动完成红头、正文、公章、序号编注的一键打印输出,并直接自动装订成册,大大缩短了“红头文件”的印制时间这类政府公文的印制,但它缺少防伪功能,文件容易被复制。
发明内容
本发明的目的是克服上述不足之处,提供一种金光红紫外荧光防伪激光打印机干式墨粉及其制备方法,其满足政府行业防伪红头文件的印制要求,同时在激光打印机金光红紫外荧光防伪干式墨粉中添加了紫外荧光粉,在长波紫外灯照射下可看到红头文件、档案图文的防伪数码起到了防伪的效果。
本发明的技术方案,金光红紫外荧光防伪激光打印机干式墨粉,配方比例按重量份计如下:紫外荧光粉4~8份、金光红粉10~20份、含蜡苯丙树脂80~90份、聚丙烯蜡4~6份、电荷调节剂2~4份、氨基硅烷4~8份和六甲基硅氮烷13~18份。
所述紫外荧光粉:金光红粉质量比为2:5。
所述金光红紫外荧光防伪激光打印机干式墨粉的制备方法,按重量份计步骤如下:
(1)混合:首先将紫外荧光粉4~8份、金光红粉10~20份、含蜡苯丙树脂80~90份、聚丙烯蜡4~6份和电荷调节剂2~4份倒入混炼机中,经均匀混合800~1000r/min混合3~5min,制成混合料;
(2)出片:将步骤(1)所得混合料投入挤塑机中,在90~150℃的温度下将混合料挤出压制成片,厚度为8~12mm,然后将片状混合料冷却至40~45℃并粉碎成碎片;
(3)粉碎:用机械粉碎机将步骤(2)所得碎片粉碎成粒径为30~50μm的碎粉;
(4)球磨:用机械磨机对步骤(3)所得碎粉进行进一步机械磨粉碎,并依次进行分级、分离和收集,得到粒径为7~9μm的半成品颗粒;
(5)二次混合:加入氨基硅烷4~8份和六甲基硅氮烷13~18份,用1200~1300r/min的混炼机混合7~8min;
(6)过筛:对步骤(5)所得粉末用200~250目筛网过筛,即制备得到产品金光红紫外荧光防伪激光打印机干式墨粉。
本发明的有益效果:本发明制备所得产品专为政府防伪红头文件研制,颜色亮丽,色彩纯正,满足政府行业防伪红头文件的印制要求,使打印图像过渡更加平滑,层次的再现也更加的真实。其不仅可以打印普通复印纸张,同时可以适应卡片、胶片等各种介质、满足多种打印应用。
本发明在激光打印机金光红紫外荧光防伪干式墨粉中添加了紫外荧光粉,在长波紫外灯照射下可看到红头文件、档案图文的防伪数码起到了防伪的效果。
具体实施方式
以下实施例中电荷调节剂购自保土谷化学工业株式会社生产的E-84S,所述含蜡苯丙树脂的制备过程如申请号201410178938.2所述。
实施例1
选取4份紫外荧光粉、10份金光红粉、85份的含蜡苯丙树脂、3份的聚丙烯蜡、4份的电荷调节剂、4份的氨基硅烷和18份的六甲基硅氮烷,待用。
所述金光红紫外荧光防伪激光打印机干式墨粉的制备方法,按重量份计步骤如下:
(1)混合:首先将紫外荧光粉、金光红粉、含蜡苯丙树脂、聚丙烯蜡和电荷调节剂倒入混炼机中,经均匀混合800r/min混合5min,制成混合料;
(2)出片:将步骤(1)所得混合料投入挤塑机中,在90℃的温度下将混合料挤出压制成片,厚度为8mm,然后将片状混合料冷却至40℃并粉碎成碎片;
(3)粉碎:用机械粉碎机将步骤(2)所得碎片粉碎成粒径为30~50μm的碎粉;
(4)球磨:用机械磨机对步骤(3)所得碎粉进行进一步机械磨粉碎,并依次进行分级、分离和收集,得到粒径为7~9μm的半成品颗粒;
(5)二次混合:加入氨基硅烷和六甲基硅氮烷,用1200r/min的混炼机混合8min;
(6)过筛:对步骤(5)所得粉末用200目筛网过筛,即制备得到产品金光红紫外荧光防伪激光打印机干式墨粉。
实施例2
选取5份紫外荧光粉、15份金光红粉、90份的含蜡苯丙树脂、5份的聚丙烯蜡、3份的电荷调节剂、8份的氨基硅烷和13份的六甲基硅氮烷,待用。
所述金光红紫外荧光防伪激光打印机干式墨粉的制备方法,按重量份计步骤如下:
(1)混合:首先将紫外荧光粉、金光红粉、含蜡苯丙树脂、聚丙烯蜡和电荷调节剂倒入混炼机中,经均匀混合1000r/min混合3min,制成混合料;
(2)出片:将步骤(1)所得混合料投入挤塑机中,在150℃的温度下将混合料挤出压制成片,厚度为12mm,然后将片状混合料冷却至45℃并粉碎成碎片;
(3)粉碎:用机械粉碎机将步骤(2)所得碎片粉碎成粒径为30~50μm的碎粉;
(4)球磨:用机械磨机对步骤(3)所得碎粉进行进一步机械磨粉碎,并依次进行分级、分离和收集,得到粒径为7~9μm的半成品颗粒;
(5)二次混合:加入氨基硅烷和六甲基硅氮烷,用1300r/min的混炼机混合8min;
(6)过筛:对步骤(5)所得粉末用250目筛网过筛,即制备得到产品金光红紫外荧光防伪激光打印机干式墨粉。
实施例3
选取8份紫外荧光粉、20份金光红粉、80份的含蜡苯丙树脂、4份的聚丙烯蜡、2份的电荷调节剂、6份的氨基硅烷和15份的六甲基硅氮烷,待用。
所述金光红紫外荧光防伪激光打印机干式墨粉的制备方法,按重量份计步骤如下:
(1)混合:首先将紫外荧光粉、金光红粉、含蜡苯丙树脂、聚丙烯蜡和电荷调节剂倒入混炼机中,经均匀混合900r/min混合4min,制成混合料;
(2)出片:将步骤(1)所得混合料投入挤塑机中,在120℃的温度下将混合料挤出压制成片,厚度为10mm,然后将片状混合料冷却至43℃并粉碎成碎片;
(3)粉碎:用机械粉碎机将步骤(2)所得碎片粉碎成粒径为30~50μm的碎粉;
(4)球磨:用机械磨机对步骤(3)所得碎粉进行进一步机械磨粉碎,并依次进行分级、分离和收集,得到粒径为7~9μm的半成品颗粒;
(5)二次混合:加入氨基硅烷和六甲基硅氮烷,用1250r/min的混炼机混合8min;
(6)过筛:对步骤(5)所得粉末用230目筛网过筛,即制备得到产品金光红紫外荧光防伪激光打印机干式墨粉。
Claims (4)
1.金光红紫外荧光防伪激光打印机干式墨粉,其特征是配方比例按重量份计如下:紫外荧光粉4~8份、金光红粉10~20份、含蜡苯丙树脂80~90份、聚丙烯蜡4~6份、电荷调节剂2~4份、氨基硅烷4~8份和六甲基硅氮烷13~18份。
2.如权利要求1所述金光红紫外荧光防伪激光打印机干式墨粉,其特征是:紫外荧光粉:金光红粉质量比为2:4~6。
3.如权利要求1所述金光红紫外荧光防伪激光打印机干式墨粉,其特征是:所述紫外荧光粉:金光红粉质量比为2:5。
4.权利要求1所述金光红紫外荧光防伪激光打印机干式墨粉的制备方法,其特征是按重量份计步骤如下:
(1)混合:首先将紫外荧光粉4~8份、金光红粉10~20份、含蜡苯丙树脂80~90份、聚丙烯蜡4~6份和电荷调节剂2~4份倒入混炼机中,经均匀混合800~1000r/min混合3~5min,制成混合料;
(2)出片:将步骤(1)所得混合料投入挤塑机中,在90~150℃的温度下将混合料挤出压制成片,厚度为8~12mm,然后将片状混合料冷却至40~45℃并粉碎成碎片;
(3)粉碎:用机械粉碎机将步骤(2)所得碎片粉碎成粒径为30~50μm的碎粉;
(4)球磨:用机械磨机对步骤(3)所得碎粉进行进一步机械磨粉碎,并依次进行分级、分离和收集,得到粒径为7~9μm的半成品颗粒;
(5)二次混合:加入氨基硅烷4~8份和六甲基硅氮烷13~18份,用1200~1300r/min的混炼机混合7~8min;
(6)过筛:对步骤(5)所得粉末用200~250目筛网过筛,即制备得到产品金光红紫外荧光防伪激光打印机干式墨粉。