CN103676518A - 一种彩色磁性激光打印机碳粉及其制备方法 - Google Patents

一种彩色磁性激光打印机碳粉及其制备方法 Download PDF

Info

Publication number
CN103676518A
CN103676518A CN201210353029.9A CN201210353029A CN103676518A CN 103676518 A CN103676518 A CN 103676518A CN 201210353029 A CN201210353029 A CN 201210353029A CN 103676518 A CN103676518 A CN 103676518A
Authority
CN
China
Prior art keywords
laser printer
parts
magnetic laser
colorful
carbon powder
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201210353029.9A
Other languages
English (en)
Inventor
刘同波
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CN201210353029.9A priority Critical patent/CN103676518A/zh
Publication of CN103676518A publication Critical patent/CN103676518A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种彩色磁性激光打印机碳粉，它包括以下重量份配比的组分：树脂50-60份；铁磁粉末20-30份；电荷调节剂10-20份；流动剂1-3份；彩色色母2-5份；表面改性剂5-15份；将上述配比组分通过混料、分散、混炼、粉碎、分级、表面改性处理等得到最终产品。其有益效果在于：本发明的彩色磁性激光打印机碳粉，利用彩色色母作为颜色色调，制备的蓝色碳粉可直接用于施工图纸的打印，而不再采用打印硫酸纸、进行晒图等传统打印方式，因此，利用本发明的彩色磁性激光打印机碳粉打印施工图等彩色图纸，可节约大量的打印时间，节约成本，节约人力，真正做到低碳出图。

Description

一种彩色磁性激光打印机碳粉及其制备方法
【技术领域】
本发明涉及碳粉及其制备方法，尤其涉及一种彩色磁性打印机碳粉及其制备方法。
【背景技术】
墨粉主要指硒鼓中用来进行打印、成像的物质，虽然主要的成份是碳，但是和我们日常生活中的一些墨粉相比，硒鼓中的墨粉的颗粒更加的细小，化学稳定性更好；目前国内及国外黑白激光打印机当前使用黑色磁性或非磁性碳粉，直接使带有磁辊上粉机构的黑白激光打印机可以选择任何单一颜色碳粉，但是市场上还没有彩色磁性碳粉，因此，所有带有磁辊上粉机构的黑白激光打印机只能用黑色碳粉；由于不能打印其他单一颜色（黑色除外），所以，在打印施工图纸时，要先将图打印到硫酸纸上，然后使用晒图机晒图获得施工图纸，如此，在设计图纸打印方面，其时间长，效率低、浪费资源，周期长，人力成本高。
【发明内容】
本发明的目的在于有效克服上述技术的不足，提供一种彩色磁性激光打印机碳粉及其制备方法，该彩色碳粉可直接用于打印施工图纸，其效率高，成本低，节约时间。
本发明的技术方案是这样实现的：一种彩色磁性激光打印机碳粉，其特征在于，它包括以下重量份配比的组分：树脂50-60份；铁磁粉末20-30份；电荷调节剂10-20份；流动剂1-3份；彩色色母2-5份；表面改性剂5-15份；
优选地，所述树脂为苯丙树脂；
优选地，所述流动剂为石蜡；
优选地，所述彩色色母为蓝色颜料；
优选地，所述表面改性剂为改性二氧化硅。
本发明还提供了一种彩色磁性激光打印机碳粉的制备方法，它包括以下步骤：
A、混料，将上述配比组分一次加入原料混合机，在常温下搅拌混合，得到混合原料；
B、分散，将上述混合原料加入到高速分散机进行搅拌分散；
C、混炼，将分散好的材料使用同向双螺杆挤出机进行熔接混炼，挤出片状材料；
D、粉碎，将上述片状材料进行初级粉碎，经过筛选机获得0.5mm-2mm颗粒，再使用气流粉碎机获得1-25um的细微颗粒；
E、分级，使用风力多机分级机分选出合格产品；
F、后处理，将分选出的合格产品加入到混合机并添加表面改性剂混合10分钟以上，得到最终产品。
本发明的有益效果在于：本发明的彩色磁性激光打印机碳粉，利用彩色色母作为颜色色调，不同的色母配置出不同颜色的碳粉，当采用蓝色颜料作为色母时，制备的蓝色碳粉可直接用于施工图纸的打印，而不再采用打印硫酸纸、进行晒图等传统打印方式，因此，利用本发明的彩色磁性激光打印机碳粉打印施工图等彩色图纸，可节约大量的打印时间，节约成本，节约人力，真正做到低碳出图。
【具体实施方式】
实施例一：
选择树脂50份；铁磁粉末20份；电荷调节剂10份；流动剂1份；彩色色母2份；表面改性剂5份；
先将上述配比的树脂、铁磁粉末、电荷调节剂、流动剂、彩色色母及表面改性剂一次加入原料混合机，在常温下搅拌混合，得到混合原料；
再将上述混合原料加入到高速分散机进行搅拌分散；
之后，将分散好的材料使用同向双螺杆挤出机进行熔接混炼，挤出片状材料；
之后，将上述片状材料进行初级粉碎，经过筛选机获得0.5mm-2mm颗粒，再使用气流粉碎机获得1-25um的细微颗粒；
再之后，使用风力多机分级机分选出合格产品；
最后，将分选出的合格产品加入到混合机并添加表面改性剂混合10分钟以上，得到最终产品。
其中，树脂是苯丙树脂，流动剂是石蜡，彩色色母是蓝色颜料，表面改性剂是改性二氧化硅。
实施例二：
选择树脂55份；铁磁粉末25份；电荷调节剂15份；流动剂2份；彩色色母3份；表面改性剂10份；
先将上述配比的树脂、铁磁粉末、电荷调节剂、流动剂、彩色色母及表面改性剂一次加入原料混合机，在常温下搅拌混合，得到混合原料；
再将上述混合原料加入到高速分散机进行搅拌分散；
之后，将分散好的材料使用同向双螺杆挤出机进行熔接混炼，挤出片状材料；
之后，将上述片状材料进行初级粉碎，经过筛选机获得0.5mm--2mm颗粒，再使用气流粉碎机获得1-25um的细微颗粒；
再之后，使用风力多机分级机分选出合格产品；
最后，将分选出的合格产品加入到混合机并添加表面改性剂混合10分钟以上，得到最终产品。
其中，树脂是苯丙树脂，流动剂是石蜡，彩色色母是蓝色颜料，表面改性剂是改性二氧化硅。
实施例三：
选择树脂60份；铁磁粉末30份；电荷调节剂20份；流动剂3份；彩色色母5份；表面改性剂15份；
先将上述配比的树脂、铁磁粉末、电荷调节剂、流动剂、彩色色母及表面改性剂一次加入原料混合机，在常温下搅拌混合，得到混合原料；
再将上述混合原料加入到高速分散机进行搅拌分散；
之后，将分散好的材料使用同向双螺杆挤出机进行熔接混炼，挤出片状材料；
之后，将上述片状材料进行初级粉碎，经过筛选机获得0.5mm-2mm颗粒，再使用气流粉碎机获得1-25um的细微颗粒；
再之后，使用风力多机分级机分选出合格产品；
最后，将分选出的合格产品加入到混合机并添加表面改性剂混合10分钟以上，得到最终产品。
其中，树脂是苯丙树脂，流动剂是石蜡，彩色色母是蓝色颜料，表面改性剂是改性二氧化硅。
以上所描述的仅为本发明的较佳实施例，上述具体实施例不是对本发明的限制。在本发明的技术思想范畴内，可以出现各种变形及修改，凡本领域的普通技术人员根据以上描述所做的润饰、修改或等同替换，均属于本发明所保护的范围。

Claims (6)

1.一种彩色磁性激光打印机碳粉，其特征在于，它包括以下重量份配比的组分：树脂50-60份；铁磁粉末20-30份；电荷调节剂10-20份；流动剂1-3份；彩色色母2-5份；表面改性剂5-15份。
2.根据权利要求1所述的彩色磁性激光打印机碳粉，其特征在于：所述树脂为苯丙树脂。
3.根据权利要求1所述的彩色磁性激光打印机碳粉，其特征在于：所述流动剂为石蜡。
4.根据权利要求1所述的彩色磁性激光打印机碳粉，其特征在于：所述彩色色母为蓝色颜料。
5.根据权利要求1所述的彩色磁性激光打印机碳粉，其特征在于：所述表面改性剂为改性二氧化硅。
6.一种如权利要求1所述的彩色磁性激光打印机碳粉的制备方法，其特征在于，它包括以下步骤：
A、混料，将上述配比组分一次加入原料混合机，在常温下搅拌混合，得到混合原料；
B、分散，将上述混合原料加入到高速分散机进行搅拌分散；
C、混炼，将分散好的材料使用同向双螺杆挤出机进行熔接混炼，挤出片状材料；
D、粉碎，将上述片状材料进行初级粉碎，经过筛选机获得0.5mm-2mm颗粒，再使用气流粉碎机获得1-25um的细微颗粒；
E、分级，使用风力多机分级机分选出合格产品；
F、后处理，将分选出的合格产品加入到混合机并添加表面改性剂混合10分钟以上，得到最终产品。
CN201210353029.9A 2012-09-21 2012-09-21 一种彩色磁性激光打印机碳粉及其制备方法 Pending CN103676518A (zh)