CN108585487A - A kind of production method of glass device for sobering drunken people - Google Patents
A kind of production method of glass device for sobering drunken people Download PDFInfo
- Publication number
- CN108585487A CN108585487A CN201810685928.6A CN201810685928A CN108585487A CN 108585487 A CN108585487 A CN 108585487A CN 201810685928 A CN201810685928 A CN 201810685928A CN 108585487 A CN108585487 A CN 108585487A
- Authority
- CN
- China
- Prior art keywords
- parts
- glass
- drunken people
- sobering drunken
- glass metal
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to the vessel fields of dress wine, particularly disclose a kind of production method of glass device for sobering drunken people.1）60~80 parts, 5~10 parts feldspar powders of silica flour, 0~5 part of oyster shell whiting, 10~15 parts of boraxs, 0~5 part of sodium carbonate and 5~10 parts of nanometer curing materials are uniformly mixed, glass metal is melt at 1,300 1400 DEG C；2）1450~1600 DEG C are continuously heating to, bubble in glass metal is discharged；3）Glass metal is naturally cooled to 1000~1100 DEG C；4）Blow molding is pressed using press-and-blow process moulding process, oral area and blank first is made with the method for compacting, moves into and blows out mold in shaping mould.5）Finished products：Mold is annealed at 550~600 DEG C.Using device for sobering drunken people made of the present invention, moist, penetrating, product qualification rate can reach 95% or more, hold white wine 5 20 minutes using device for sobering drunken people made of the present invention, taste is obviously improved.
Description
Technical field
The present invention relates to the vessel field of dress wine, more particularly to a kind of production methods of glass device for sobering drunken people.
Background technology
Device for sobering drunken people also wakes bottle, pot of sobering up, be it is a kind of drink vessel used when new hair grape wine, effect is to allow wine
It is contacted with air, the fragrance of wine is allowed fully to volatilize, and the sediment in wine is allowed to separate, that is to say, that current device for sobering drunken people is only
It is to work to grape wine, does not work but for white wine；And pure grain brewing white spirit all uses traditional fermentation process, but ferment class
It will produce the strong stimulations substance such as a small amount of furfural, acetaldehyde, glyceraldehyde in substance, mouthfeel is pungent, bitter, and traditional handicraft can not arrange
It removes, the method for solution quality mouthfeel of sobering up there is presently no white wine.
Invention content
In order to compensate for the shortcomings of the prior art, the present invention provides a kind of glass that can solve white wine quality and mouthfeel to wake up
The production method of drinking vessel.
The present invention is achieved through the following technical solutions：
A kind of production method of glass device for sobering drunken people, characterized in that
1）The formation of glass metal（In parts by weight）：By 60~80 parts, 5~10 parts feldspar powders of silica flour, 0~5 part of oyster shell whiting,
10~15 parts of boraxs, 0~5 part of sodium carbonate and 5~10 parts of nanometer curing materials are uniformly mixed, and glass is melt at 1300-1400 DEG C
Glass liquid；
2）The clarification of glass metal and homogenizing：1450~1600 DEG C are continuously heating to, bubble in glass metal is discharged；
3）The cooling of glass metal：Glass metal is naturally cooled to 1000~1100 DEG C；
4）Press-and-blow process is molded：Blow molding is pressed using press-and-blow process moulding process, the mouth of glass device for sobering drunken people is first made of the method for compacting
Then portion and blank move into and blow out glass device for sobering drunken people mold in shaping mould again；
5）Finished products：Glass device for sobering drunken people mold after molding is annealed at 550~600 DEG C, eliminates internal stress.
The nanometer cures material by oyster shell whiting, inorganic antibacterial material and cerium oxide according to parts by weight 95~110:95~
110:5~10（Weight ratio）It mixes.
The nanometer cures material by oyster shell whiting, inorganic antibacterial material and cerium oxide according to parts by weight 100:100:5~10
（Weight ratio）It mixes.
The inorganic antibacterial material is inorganic complex antimicrobials or inorganic silver-series antibacterial agent.
The oyster shell whiting crushes processing by the shell sand or natural seashell of weathering and is made.
The beneficial effects of the invention are as follows：
Using device for sobering drunken people made of the present invention, moist, penetrating, product qualification rate can reach 95% or more, is made using the present invention
Device for sobering drunken people hold white wine 5-20 minutes, taste is obviously improved.
Specific implementation mode
" parts by weight " that " part " discussed below all refers to.Inorganic complex antimicrobials or inorganic silver system discussed below
Antiseptic is all known products, can be made by known method or market is bought；Such as：Silver-zeolite, silver-dissolubility glass
Glass, silver-activated carbon, silver-silica gel, silver-cupric phosphate, silver-calcium phosphate, silver-porous metals etc..
One, the making of oyster shell whiting：
1, oyster shell whiting is made in the crushing of the shell sand of weathering.
2, oyster shell whiting is made in natural seashell crushing.
Two, the preparation of nanometer curing material：
1,5 parts of any of the above-described kind of 95 parts of oyster shell whiting, 95 parts of inorganic complex antimicrobials and cerium oxide are subjected to compound obtained nanometer material
Material, complex method is known technology.
2,10 parts of any of the above-described kind of 110 parts of oyster shell whiting, 110 parts of inorganic complex antimicrobials and cerium oxide are subjected to compound be made
Nano material, complex method are known technology.
3,8 parts of any of the above-described kind of 100 parts of oyster shell whiting, 100 parts of inorganic complex antimicrobials and cerium oxide are subjected to compound be made
Nano material, complex method are known technology.
4,5 parts of any of the above-described kind of 95 parts of oyster shell whiting, 110 parts of inorganic silver-series antibacterial agent and cerium oxide compound be made is carried out to receive
Rice material, complex method is known technology.
5,10 parts of any of the above-described kind of 100 parts of oyster shell whiting, 95 parts of inorganic silver-series antibacterial agent and cerium oxide are subjected to compound be made
Nano material, complex method are known technology.
6,8 parts of any of the above-described kind of 110 parts of oyster shell whiting, 100 parts of inorganic silver-series antibacterial agent and cerium oxide are subjected to compound be made
Nano material, complex method are known technology.
Embodiment one：
1）The formation of glass metal：60 parts, 5 parts feldspar powders of silica flour, 10 parts of boraxs and 5 parts of any of the above-described kind of nanometers are cured into material
It is uniformly mixed, glass metal is melt at 1300 DEG C；
2）The clarification of glass metal and homogenizing：1450 DEG C are continuously heating to, bubble in glass metal is discharged；
3）The cooling of glass metal：Glass metal is naturally cooled to 1000 DEG C；
4）Press-and-blow process is molded：Blow molding is pressed using press-and-blow process moulding process, the mouth of glass device for sobering drunken people is first made of the method for compacting
Then portion and blank move into and blow out glass device for sobering drunken people mold in shaping mould again；
5）Finished products：Glass device for sobering drunken people mold after molding is annealed at 550 DEG C, eliminates internal stress.
Embodiment two：
1）The formation of glass metal：By 80 parts, 10 parts feldspar powders of silica flour, 5 parts of oyster shell whitings, 15 parts of boraxs, 5 parts of sodium carbonate and 10 parts
Any of the above-described kind of nanometer curing material is uniformly mixed, and glass metal is melt at 1400 DEG C；
2）The clarification of glass metal and homogenizing：1600 DEG C are continuously heating to, bubble in glass metal is discharged；
3）The cooling of glass metal：Glass metal is naturally cooled to 1100 DEG C；
4）Press-and-blow process is molded：Blow molding is pressed using press-and-blow process moulding process, the mouth of glass device for sobering drunken people is first made of the method for compacting
Then portion and blank move into and blow out glass device for sobering drunken people mold in shaping mould again；
5）Finished products：Glass device for sobering drunken people mold after molding is annealed at 600 DEG C, eliminates internal stress.
Embodiment three：
1）The formation of glass metal：It will be on 80 parts, 5 parts feldspar powders of silica flour, 5 parts of oyster shell whitings, 10 parts of boraxs, 5 parts of sodium carbonate and 5 parts
It states any nanometer of curing material to be uniformly mixed, glass metal is melt at 1400 DEG C；
2）The clarification of glass metal and homogenizing：1450 DEG C are continuously heating to, bubble in glass metal is discharged；
3）The cooling of glass metal：Glass metal is naturally cooled to 1100 DEG C；
4）Press-and-blow process is molded：Blow molding is pressed using press-and-blow process moulding process, the mouth of glass device for sobering drunken people is first made of the method for compacting
Then portion and blank move into and blow out glass device for sobering drunken people mold in shaping mould again；
5）Finished products：Glass device for sobering drunken people mold after molding is annealed at 550 DEG C, eliminates internal stress.
Example IV：
1）The formation of glass metal：60 parts, 10 parts feldspar powders of silica flour, 15 parts of boraxs, 10 parts of any of the above-described vertical nanometers are cured into material
Material is uniformly mixed, and glass metal is melt at 1300 DEG C；
2）The clarification of glass metal and homogenizing：1600 DEG C are continuously heating to, bubble in glass metal is discharged；
3）The cooling of glass metal：Glass metal is naturally cooled to 1000 DEG C；
4）Press-and-blow process is molded：Blow molding is pressed using press-and-blow process moulding process, the mouth of glass device for sobering drunken people is first made of the method for compacting
Then portion and blank move into and blow out glass device for sobering drunken people mold in shaping mould again；
5）Finished products：Glass device for sobering drunken people mold after molding is annealed at 600 DEG C, eliminates internal stress.
Embodiment five：
1）The formation of glass metal：It will be on 70 parts, 8 parts feldspar powders of silica flour, 3 parts of oyster shell whitings, 12 parts of boraxs, 2 parts of sodium carbonate and 7 parts
It states any nanometer of curing material to be uniformly mixed, glass metal is melt at 1350 DEG C；
2）The clarification of glass metal and homogenizing：1500 DEG C are continuously heating to, bubble in glass metal is discharged；
3）The cooling of glass metal：Glass metal is naturally cooled to 1050 DEG C；
4）Press-and-blow process is molded：Blow molding is pressed using press-and-blow process moulding process, the mouth of glass device for sobering drunken people is first made of the method for compacting
Then portion and blank move into and blow out glass device for sobering drunken people mold in shaping mould again；
5）Finished products：Glass device for sobering drunken people mold after molding is annealed at 580 DEG C, eliminates internal stress.
Embodiment six：
1）The formation of glass metal：By 60 parts, 7 parts feldspar powders of silica flour, 5 parts of oyster shell whitings, 10 parts of boraxs, 3 parts of sodium carbonate and 10 parts
Any of the above-described kind of nanometer curing material is uniformly mixed, and glass metal is melt at 1300 DEG C；
2）The clarification of glass metal and homogenizing：1550 DEG C are continuously heating to, bubble in glass metal is discharged；
3）The cooling of glass metal：Glass metal is naturally cooled to 1100 DEG C；
4）Press-and-blow process is molded：Blow molding is pressed using press-and-blow process moulding process, the mouth of glass device for sobering drunken people is first made of the method for compacting
Then portion and blank move into and blow out glass device for sobering drunken people mold in shaping mould again；
5）Finished products：Glass device for sobering drunken people mold after molding is annealed at 570 DEG C, eliminates internal stress.
Embodiment seven：
1）The formation of glass metal：75 parts, 5 parts feldspar powders of silica flour, 15 parts of boraxs, 1 part of sodium carbonate and 7 parts of nanometers are cured into material
It is uniformly mixed, glass metal is melt at 1400 DEG C；
2）The clarification of glass metal and homogenizing：1550 DEG C are continuously heating to, bubble in glass metal is discharged；
3）The cooling of glass metal：Glass metal is naturally cooled to 1100 DEG C；
4）Press-and-blow process is molded：Blow molding is pressed using press-and-blow process moulding process, the mouth of glass device for sobering drunken people is first made of the method for compacting
Then portion and blank move into and blow out glass device for sobering drunken people mold in shaping mould again；
5）Finished products：Glass device for sobering drunken people mold after molding is annealed at 550 DEG C, eliminates internal stress.
In addition to technical characteristic described in specification, remaining technical characteristic is technology known to those skilled in the art.
Claims (5)
1. a kind of production method of glass device for sobering drunken people, characterized in that
1）The formation of glass metal（In parts by weight）：By 60~80 parts, 5~10 parts feldspar powders of silica flour, 0~5 part of oyster shell whiting,
10~15 parts of boraxs, 0~5 part of sodium carbonate and 5~10 parts of nanometer curing materials are uniformly mixed, and glass is melt at 1300-1400 DEG C
Glass liquid；
2）The clarification of glass metal and homogenizing：1450~1600 DEG C are continuously heating to, bubble in glass metal is discharged；
3）The cooling of glass metal：Glass metal is naturally cooled to 1000~1100 DEG C；
4）Press-and-blow process is molded：Blow molding is pressed using press-and-blow process moulding process, the mouth of glass device for sobering drunken people is first made of the method for compacting
Then portion and blank move into and blow out glass device for sobering drunken people mold in shaping mould again；
5）Finished products：Glass device for sobering drunken people mold after molding is annealed at 550~600 DEG C, eliminates internal stress.
2. the production method of glass device for sobering drunken people according to claim 1, characterized in that the nanometer cures material by shell
Powder, inorganic antibacterial material and cerium oxide are according to parts by weight 95~110:95~110:5~10（Weight ratio）It mixes.
3. the production method for wanting the glass device for sobering drunken people described in 2 according to right, characterized in that the nanometer cures material by shell
Powder, inorganic antibacterial material and cerium oxide are according to parts by weight 100:100:5~10（Weight ratio）It mixes.
4. the production method of glass device for sobering drunken people according to claim 2 or 3, characterized in that the inorganic antibacterial material is
Inorganic complex antimicrobials or inorganic silver-series antibacterial agent.
5. according to the production method of Claims 2 or 3 any one of them glass device for sobering drunken people, characterized in that the oyster shell whiting by
The shell sand or natural seashell of weathering crush processing and are made.