CN108774046A - A kind of production method of ceramics device for sobering drunken people - Google Patents
A kind of production method of ceramics device for sobering drunken people Download PDFInfo
- Publication number
- CN108774046A CN108774046A CN201810686237.8A CN201810686237A CN108774046A CN 108774046 A CN108774046 A CN 108774046A CN 201810686237 A CN201810686237 A CN 201810686237A CN 108774046 A CN108774046 A CN 108774046A
- Authority
- CN
- China
- Prior art keywords
- parts
- glaze
- drunken people
- sobering drunken
- production method
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to the vessel fields of dress wine, particularly disclose a kind of production method of ceramic device for sobering drunken people.1)Conventional ceramic raw material and nano material are mixed into ball mill wet-milling 20-24 hour, then except iron, sieving, dehydration, pugging, aging pug is made;2)Particle by frit, kaolin and nano material mixed grinding to granularity less than 10 μm accounts for 90% or more;3)Pug is made to molding unpainted clay idol in a mold, molding unpainted clay idol is fired 30-50 minutes at a temperature of 1200-1250 DEG C then, porcelain body is made;4)By the porcelain body after biscuiting, above-mentioned glaze is applied with glaze spraying or glaze method, glazed thickness is controlled in 0.2-0.3 ㎜.5)Porcelain body after glazing is fired by glaze 20-30 minutes at a temperature of 1100-1150 DEG C, is burnt into finished product.It is sobered up to white wine using this kind of device for sobering drunken people, it is only necessary to 5~20 minutes, white wine rapid aging can be made, achieve the effect that promote white wine quality and mouthfeel.
Description
Technical field
The present invention relates to the vessel field of dress wine, more particularly to a kind of production method of ceramic device for sobering drunken people.
Background technology
Device for sobering drunken people also wakes bottle, pot of sobering up, be it is a kind of drink vessel used when new hair grape wine, effect is to allow wine
It is contacted with air, the fragrance of wine is allowed fully to volatilize, and the sediment in wine is allowed to separate, that is to say, that current device for sobering drunken people is only
It is to work to grape wine, does not work but for white wine;And pure grain brewing white spirit all uses traditional fermentation process, but ferment class
It will produce the strong stimulations substance such as a small amount of furfural, acetaldehyde, glyceraldehyde in substance, mouthfeel is pungent, bitter, and traditional handicraft can not arrange
It removes, the method for solution quality mouthfeel of sobering up there is presently no white wine.
Invention content
In order to compensate for the shortcomings of the prior art, the present invention provides a kind of ceramics that can solve white wine quality and mouthfeel to wake up
The production method of drinking vessel.
The present invention is achieved through the following technical solutions:
A kind of production method of ceramics device for sobering drunken people, characterized in that
1)Pug:Various conventional ceramic raw materials are mixed in proportion with nano material and directly enter ball mill wet-milling, grinding 20-24 is small
When, then remove that iron, sieving, dehydration, pugging, aging that pug is made is spare;
2)Glaze:By frit, kaolin and nano material in proportion mixed grinding to granularity less than 10 μm of particle account for 90% with
On;
3)Biscuiting porcelain body:Pug is made to molding unpainted clay idol in a mold, then the temperature by molding unpainted clay idol at 1200-1250 DEG C
Degree is lower to be fired 30-50 minutes, and porcelain body is made;
4)Glazing:By the porcelain body after biscuiting, above-mentioned glaze is applied with glaze spraying or glaze method, glazed thickness is controlled in 0.2-0.3 ㎜;
5)Firing:Porcelain body after glazing is fired by glaze 20-30 minutes at a temperature of 1100-1150 DEG C, is burnt into finished product.
The group in parts by weight of the glaze becomes:80-90 parts of frit, 5-10 parts of nano material, 5-10 parts of kaolin.
The group of the frit in parts by weight becomes:15-20 parts of oyster shell whiting, 15-20 parts of feldspar powder, 30-35 parts of silica flour,
0-5 parts of clay, 10-15 parts of borax, 0-5 parts of zinc oxide, 0-5 parts of lithium carbonate, 0-5 parts of talcum.
The group in parts by weight of the pug becomes:30-50 parts of oyster shell whiting, 10-15 parts of feldspar powder, silica flour 10-15
Part, 20-30 parts of clay, 5-10 parts of nano material.
The parts by weight group of the nano material becomes:Oyster shell whiting:Inorganic antibacterial material:Cerium oxide=0.95~1.1:
0.95~1.1:0.05~0.1.
The parts by weight group of the nano material becomes:Oyster shell whiting:Inorganic antibacterial material:Cerium oxide=1:1:0.05~0.1.
The inorganic antibacterial material is inorganic complex antimicrobials or inorganic silver-series antibacterial agent.
The oyster shell whiting crushes processing by the shell sand or natural seashell of weathering and is made.
The method sobered up using above-mentioned device for sobering drunken people, characterized in that before white wine is drunk, white wine is poured into the device for sobering drunken people
It is interior, it sobers up 5~20 minutes, makes white wine rapid aging, reach purpose of sobering up.
The beneficial effects of the invention are as follows:
The present invention provides a kind of device for sobering drunken people for white wine, are sobered up to white wine using this kind of device for sobering drunken people, it is only necessary to 5~20 points
Clock, you can make white wine rapid aging, achieve the effect that promote white wine quality and mouthfeel.
Specific implementation mode
" parts by weight " that " part " discussed below all refers to.Inorganic complex antimicrobials or inorganic silver system discussed below
Antiseptic is all known products, can be made by known method or market is bought;Such as:Silver-zeolite, silver-dissolubility glass
Glass, silver-activated carbon, silver-silica gel, silver-cupric phosphate, silver-calcium phosphate, silver-porous metals etc..
One, the making of oyster shell whiting:
1, oyster shell whiting is made in the crushing of the shell sand of weathering.
2, oyster shell whiting is made in natural seashell crushing.
Two, the preparation of nano material:
1,5 parts of any of the above-described kind of 95 parts of oyster shell whiting, 95 parts of inorganic complex antimicrobials and cerium oxide are subjected to compound obtained nanometer material
Material, complex method is known technology.
2,10 parts of any of the above-described kind of 110 parts of oyster shell whiting, 110 parts of inorganic complex antimicrobials and cerium oxide are subjected to compound be made
Nano material, complex method are known technology.
3,8 parts of any of the above-described kind of 100 parts of oyster shell whiting, 100 parts of inorganic complex antimicrobials and cerium oxide are subjected to compound be made
Nano material, complex method are known technology.
4,5 parts of any of the above-described kind of 95 parts of oyster shell whiting, 110 parts of inorganic silver-series antibacterial agent and cerium oxide compound be made is carried out to receive
Rice material, complex method is known technology.
5,10 parts of any of the above-described kind of 100 parts of oyster shell whiting, 95 parts of inorganic silver-series antibacterial agent and cerium oxide are subjected to compound be made
Nano material, complex method are known technology.
6,8 parts of any of the above-described kind of 110 parts of oyster shell whiting, 100 parts of inorganic silver-series antibacterial agent and cerium oxide are subjected to compound be made
Nano material, complex method are known technology.
Three, the preparation of frit:
1, by any of the above-described kind of 15 parts of oyster shell whiting, 15 parts of feldspar powder, 30 parts of silica flour, frit, preparation method is made in 10 parts of borax
For known technology.
2, by any of the above-described kind of 20 parts of oyster shell whiting, 20 parts of feldspar powder, 35 parts of silica flour, 5 parts of clay, 15 parts of borax, oxidation
Frit is made in 5 parts of zinc, 5 parts of lithium carbonate, 5 parts of talcum, and preparation method is known technology.
3, by any of the above-described kind of 18 parts of oyster shell whiting, 17 parts of feldspar powder, 32 parts of silica flour, 3 parts of clay, 12 parts of borax, oxidation
Frit is made in 2.5 parts of zinc, 4 parts of lithium carbonate, 3 parts of talcum, and preparation method is known technology.
4, by any of the above-described kind of 15 parts of oyster shell whiting, 20 parts of feldspar powder, 30 parts of silica flour, 5 parts of clay, 5 parts of zinc oxide, talcum
5 parts are made frit, and preparation method is known technology.
5, by any of the above-described kind of 20 parts of oyster shell whiting, 15 parts of feldspar powder, 35 parts of silica flour, 15 parts of borax, 5 parts of lithium carbonate is made
Frit, preparation method are known technology.
6, by any of the above-described kind of 15 parts of oyster shell whiting, 18 parts of feldspar powder, 35 parts of silica flour, 1 part of clay, 15 parts of borax, oxidation
Frit is made in 5 parts of zinc, 4 parts of lithium carbonate, and preparation method is known technology.
7, by any of the above-described kind of 20 parts of oyster shell whiting, 15 parts of feldspar powder, 32 parts of silica flour, 5 parts of clay, 10 parts of borax, oxidation
Frit is made in 3 parts of zinc, 3 parts of lithium carbonate, 2.5 parts of talcum, and preparation method is known technology.
Embodiment one:
1)Pug:Any of the above-described kind of 30 parts of oyster shell whiting, 10 parts of feldspar powder, 10 parts of silica flour, 20 parts of clay, any of the above-described kind of nanometer
The mixing of 5 parts of material directly enters ball mill wet-milling, grinds 20 hours, then except iron, sieving, dehydration, pugging, aging that pug is made is standby
With;
2)Glaze:By any of the above-described kind of 80 parts of frit, 5 parts of any nano material, 5 parts of mixed grinding to granularities of kaolin are less than
10 μm of particle accounts for 90% or more;
3)Biscuiting porcelain body:Pug is made to molding unpainted clay idol in a mold, then by molding unpainted clay idol at a temperature of 1200 DEG C
It fires 30 minutes, porcelain body is made;
4)Glazing:By the porcelain body after biscuiting, above-mentioned glaze is applied with glaze spraying or glaze method, glazed thickness is controlled in 0.2-0.3 ㎜.
5)Firing:Porcelain body after glazing is fired by glaze 20 minutes at a temperature of 1100 DEG C, is burnt into finished product.
Embodiment two:
1)Pug:By any of the above-described kind of 50 parts of oyster shell whiting, 15 parts of feldspar powder, 15 parts of silica flour, 30 parts of clay, any of the above-described kind is received
Rice 10 parts of material mixing directly enters ball mill wet-milling, grinds 24 hours, then except iron, sieving, dehydration, pugging, aging mud is made
Expect spare;
2)Glaze:By any of the above-described kind of 90 parts of frit, 10 parts of any nano material, 10 parts of mixed grindings of kaolin are small to granularity
90% or more is accounted in 10 μm of particles;
3)Biscuiting porcelain body:Pug is made to molding unpainted clay idol in a mold, then by molding unpainted clay idol at a temperature of 1250 DEG C
It fires 50 minutes, porcelain body is made;
4)Glazing:By the porcelain body after biscuiting, above-mentioned glaze is applied with glaze spraying or glaze method, glazed thickness is controlled in 0.2-0.3 ㎜.
5)Firing:Porcelain body after glazing is fired by glaze 30 minutes at a temperature of 1150 DEG C, is burnt into finished product.
Embodiment three:
1)Pug:Any of the above-described kind of 30 parts of oyster shell whiting, 15 parts of feldspar powder, 10 parts of silica flour, 30 parts of clay, any of the above-described kind of nanometer
The mixing of 5 parts of material directly enters ball mill wet-milling, grinds 24 hours, then except iron, sieving, dehydration, pugging, aging that pug is made is standby
With;
2)Glaze:By any of the above-described kind of 80 parts of frit, any of the above-described kind of 10 parts of nano material, 5 parts of kaolin, mixed grinding to grain
Particle of the degree less than 10 μm accounts for 90% or more;
3)Biscuiting porcelain body:Pug is made to molding unpainted clay idol in a mold, then by molding unpainted clay idol at a temperature of 1250 DEG C
It fires 30 minutes, porcelain body is made;
4)Glazing:By the porcelain body after biscuiting, above-mentioned glaze is applied with glaze spraying or glaze method, glazed thickness is controlled in 0.2-0.3 ㎜.
5)Firing:Porcelain body after glazing is fired by glaze 20 minutes at a temperature of 1150 DEG C, is burnt into finished product.
Example IV:
1)Pug:By any of the above-described kind of 50 parts of oyster shell whiting, 10 parts of feldspar powder, 15 parts of silica flour, 20 parts of clay, any of the above-described kind is received
Rice 10 parts of material mixing directly enters ball mill wet-milling, grinds 20 hours, then except iron, sieving, dehydration, pugging, aging mud is made
Expect spare;
2)Glaze:By any of the above-described kind of 90 parts of frit, any of the above-described kind of 5 parts of nano material, 10 parts of kaolin, mixed grinding to grain
Particle of the degree less than 10 μm accounts for 90% or more;
3)Biscuiting porcelain body:Pug is made to molding unpainted clay idol in a mold, then by molding unpainted clay idol at a temperature of 1200 DEG C
It fires 50 minutes, porcelain body is made;
4)Glazing:By the porcelain body after biscuiting, above-mentioned glaze is applied with glaze spraying or glaze method, glazed thickness is controlled in 0.2-0.3 ㎜.
5)Firing:Porcelain body after glazing is fired by glaze 30 minutes at a temperature of 1100 DEG C, is burnt into finished product.
Embodiment five:
1)Pug:By any of the above-described kind of 40 parts of oyster shell whiting, 12 parts of feldspar powder, 13 parts of silica flour, 25 parts of clay, any of the above-described kind is received
Rice 8 parts of material mixing directly enters ball mill wet-milling, grinds 22 hours, then except iron, sieving, dehydration, pugging, aging pug is made
It is spare;
2)Glaze:By 2 any of the above-described kinds of 85 parts of frits, any of the above-described kind of 8 parts of nano material, 7 parts of mixed grindings of kaolin to grain
Particle of the degree less than 10 μm accounts for 90% or more;
3)Biscuiting porcelain body:Pug is made to molding unpainted clay idol in a mold, then by molding unpainted clay idol at a temperature of 1230 DEG C
It fires 40 minutes, porcelain body is made;
4)Glazing:By the porcelain body after biscuiting, above-mentioned glaze is applied with glaze spraying or glaze method, glazed thickness is controlled in 0.2-0.3 ㎜.
5)Firing:Porcelain body after glazing is fired by glaze 25 minutes at a temperature of 1130 DEG C, is burnt into finished product.
Embodiment six:
1)Pug:By any of the above-described kind of 30 parts of oyster shell whiting, 13 parts of feldspar powder, 15 parts of silica flour, 20 parts of clay, any of the above-described kind is received
Rice 7 parts of material mixing directly enters ball mill wet-milling, grinds 20-24 hours, then except iron, sieving, dehydration, pugging, aging be made
Pug is spare;
2)Glaze:By any of the above-described kind of 80 parts of frit, any of the above-described kind of 6 parts of nano material, 7 parts of mixed grindings of kaolin to granularity
Particle less than 10 μm accounts for 90% or more;
3)Biscuiting porcelain body:Pug is made to molding unpainted clay idol in a mold, then by molding unpainted clay idol at a temperature of 1200 DEG C
It fires 50 minutes, porcelain body is made;
4)Glazing:By the porcelain body after biscuiting, above-mentioned glaze is applied with glaze spraying or glaze method, glazed thickness is controlled in 0.2-0.3 ㎜.
5)Firing:Porcelain body after glazing is fired by glaze 25 minutes at a temperature of 1150 DEG C, is burnt into finished product.
The method sobered up using above-mentioned device for sobering drunken people:Before drinking white spirit, white wine is poured into device for sobering drunken people, is sobered up 5~20 points
Clock makes white wine rapid aging, reaches purpose of sobering up, and can promote white wine quality and mouthfeel.
In addition to technical characteristic described in specification, remaining technical characteristic is technology known to those skilled in the art.
Claims (9)
1. a kind of production method of ceramics device for sobering drunken people, characterized in that
1)Pug:Various conventional ceramic raw materials are mixed in proportion with nano material and directly enter ball mill wet-milling, grinding 20-24 is small
When, then remove that iron, sieving, dehydration, pugging, aging that pug is made is spare;
2)Glaze:By frit, kaolin and nano material in proportion mixed grinding to granularity less than 10 μm of particle account for 90% with
On;
3)Biscuiting porcelain body:Pug is made to molding unpainted clay idol in a mold, then the temperature by molding unpainted clay idol at 1200-1250 DEG C
Degree is lower to be fired 30-50 minutes, and porcelain body is made;
4)Glazing:By the porcelain body after biscuiting, above-mentioned glaze is applied with glaze spraying or glaze method, glazed thickness is controlled in 0.2-0.3 ㎜;
5)Firing:Porcelain body after glazing is fired by glaze 20-30 minutes at a temperature of 1100-1150 DEG C, is burnt into finished product.
2. the production method of ceramics device for sobering drunken people according to claim 1, characterized in that the glaze in parts by weight
Group becomes:80-90 parts of frit, 5-10 parts of nano material, 5-10 parts of kaolin.
3. the production method of ceramics device for sobering drunken people according to claim 2, characterized in that the group of the frit in parts by weight
Become:15-20 parts of oyster shell whiting, 15-20 parts of feldspar powder, 30-35 parts of silica flour, 0-5 parts of clay, 10-15 parts of borax, zinc oxide 0-
5 parts, 0-5 parts of lithium carbonate, 0-5 parts of talcum.
4. it is according to any one of claims 1 to 3 ceramics device for sobering drunken people production method, characterized in that the pug with
The group of parts by weight meter becomes:30-50 parts of oyster shell whiting, 10-15 parts of feldspar powder, 10-15 parts of silica flour, 20-30 parts of clay, nanometer material
5-10 parts of material.
5. the production method of ceramics device for sobering drunken people according to claim 4, characterized in that the parts by weight group of the nano material
Become:Oyster shell whiting:Inorganic antibacterial material:Cerium oxide=0.95~1.1:0.95~1.1:0.05~0.1.
6. the production method of ceramics device for sobering drunken people according to claim 5, characterized in that the parts by weight group of the nano material
Become:Oyster shell whiting:Inorganic antibacterial material:Cerium oxide=1:1:0.05~0.1.
7. the production method of ceramics device for sobering drunken people according to claim 6, characterized in that the inorganic antibacterial material is inorganic
Complex antimicrobials or inorganic silver-series antibacterial agent.
8. the production method of ceramics device for sobering drunken people according to claim 7, characterized in that the oyster shell whiting is by weathering
Shell sand or natural seashell crush processing and are made.
9. the method sobered up using device for sobering drunken people according to any one of claims 8, characterized in that before white wine is drunk, white wine is poured into institute
It states in device for sobering drunken people, sobers up 5~20 minutes, make white wine rapid aging, reach purpose of sobering up.