CN102670031B - Water glass with far infrared ceramic inner container - Google Patents
Water glass with far infrared ceramic inner container Download PDFInfo
- Publication number
- CN102670031B CN102670031B CN201210162536.4A CN201210162536A CN102670031B CN 102670031 B CN102670031 B CN 102670031B CN 201210162536 A CN201210162536 A CN 201210162536A CN 102670031 B CN102670031 B CN 102670031B
- Authority
- CN
- China
- Prior art keywords
- inner bag
- water tumbler
- water
- glaze layer
- surface glaze
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The invention relates to a health care water glass, in particular to a water glass with a far infrared ceramic inner container, comprising an inner container (1) of the water glass, wherein the inner sides of the bottom surface and the side wall of the inner container (1) are provided with inner container surface glaze layers (2); the inner container (1) of the water glass is an inner ceramic container; and the inner container surface glaze layers (2) contain far infrared materials. The water contact part (the inner container surface glaze layers) of the water glass with the far infrared inner container contains health care materials, and the contact area of the health care materials and water is shown as follows: pir2+2pir*h, (r is the inner radius of each inner container surface glaze layer, and h is the height of each inner container surface glaze layer); the contact area of the health care materials and the water is greatly increased; and the health care effect is more ideal. In addition, the inner ceramic container does not have the problem that a metal water glass rusts, so that the service life of the water glass is greatly prolonged.
Description
Technical field
The present invention relates to Health-care drinking cup, is a kind of far-infrared ceramic inner bag water tumbler specifically.
Background technology
The existing health-care material of common Health-care drinking cup on the market and the contact area of water are generally: cup inner bottom surface is long-pending, i.e. π * r2 (inside radius that r is inner bag).Its contact area is limited, so health-care effect is undesirable.
Summary of the invention
For the defect existing in prior art, the object of the present invention is to provide a kind of far-infrared ceramic inner bag water tumbler, the part contacting with water (cup courage surface glaze layer) all contains health-care material, the contact area of health-care material and water is: π r2+2 π r * h, (r is the inside radius of cup courage surface glaze layer, h is a height for cup courage surface glaze layer), increased considerably the contact area of health-care material and water, health-care effect is better.And the problem that ceramic liner does not exist metal water tumbler to get rusty, has extended service life of water tumbler greatly.
For reaching above object, the technical scheme that the present invention takes is:
A far-infrared ceramic inner bag water tumbler, is characterized in that, comprising: water tumbler inner bag 1, on the medial surface of its bottom surface and sidewall, be equipped with a glass courage surface glaze layer 2,
Described water tumbler inner bag 1 is ceramic liner,
Described cup courage surface glaze layer 2 contains far-infrared material.
On the basis of technique scheme, the component of described water tumbler inner bag 1 is by mass percentage:
The exquisite natural bovine bone powder 40%~55% of 500 objects,
Kaolin 25%~37%,
Feldspar 5%~15%,
Quartz 3%~8%,
Hydroxymethyl cellulose sodium CMC 0.3%,
The component of described cup courage surface glaze layer 2 is by mass percentage:
Lithium carbonate 5%,
Strontium carbonate 6%,
Feldspar 48%,
Quartz 24%,
3000 object tourmaline powders 5%,
Talcum powder 8%.
On the basis of technique scheme, the preparation process of water tumbler inner bag finished product is as follows:
step 1, water tumbler inner bag material is processed:
Step 1.1, by carrying out mist projection granulating processing after the natural bovine bone powder of exquisiteness, feldspar and quartzy mixing, makes powder body material possess mobility, facilitates moulding,
When mist projection granulating, add 10% polyvinyl alcohol of dry powder body material gross weight as adhesive, in same time, carry the mass ratio U of powder and air
sfor 1-4, air velocity 18-25m/s;
Step 1.2, after the products therefrom after step 1.1 is processed is mixed with kaolin, carries out ball-milling treatment as blank, ball milling 14 hours,
During ball milling, the mass ratio of blank, ball, water, hydroxymethyl cellulose sodium CMC is: blank: ball: water: hydroxymethyl cellulose sodium CMC=1:1.5:0.6:0.003,
Ballstone grating during ball milling is: large: in: little=15:25:60, large ballstone diameter is 80mm, and middle ballstone diameter is 60mm, and bead stone diameter is 40mm;
Step 1.3, sends products therefrom after ball milling into filter press and dewaters to water content below 5%;
Step 1.4, carries out vacuum pugging by products therefrom after dehydration, and more than the vacuum 720mmHg of vacuum deairing machine, rotating speed 20r/min, makes the moisture in blank even, blank structure even compact, pore-free, and plasticity improves, and dry tenacity improves;
After lithium carbonate, strontium carbonate, zinc oxide, feldspar, quartz, boric acid, tourmaline powder and talcum powder are mixed, as cup courage surface glaze layer material, carry out ball-milling treatment, ball milling 42 hours,
During ball milling, the mass ratio of cup courage surface glaze layer material, ball, water is: cup courage surface glaze layer material: ball: water=1:2:0.55,
Ballstone grating during ball milling is: large: in: little=2:3:5, large ballstone diameter is 50mm, and middle ballstone diameter is 40mm, and bead stone diameter is 30mm;
step 3, the mixing of water tumbler inner bag blank, moulding, dry, biscuiting:
Step 3.1, by the water tumbler inner bag blank after step 1 is processed, cold rolling moulding, is used the desk-top roller head machine of steady job to carry out former roll extrusion, and roller-head is 0.6 with speed of mainshaft ratio, obtains water tumbler inner bag idiosome,
Step 3.2, the water tumbler inner bag idiosome after cold rolling moulding is dried 3 hours under the condition of 150 ℃,
Step 3.3, dried water tumbler inner bag idiosome, under the condition of 800 ℃, biscuiting is 5 minutes,
step 4, glazing:
Water tumbler inner bag idiosome after biscuiting, swings glaze method by the employing of cup courage surface glaze layer material and carries out glazing, swings glaze twice,
step 5, kiln-firing:
Water tumbler inner bag idiosome after glazing is entered to kiln, and the mode by 300 ℃/h of intensifications, is warming up to 1200 ℃, fires 8 hours, obtains water tumbler inner bag finished product.
Far-infrared ceramic inner bag water tumbler of the present invention, the part contacting with water (cup courage surface glaze layer) all contains health-care material, the contact area of health-care material and water is: π r2+2 π r * h, (r is the inside radius of cup courage surface glaze layer, h is the height of cup courage surface glaze layer), the contact area that has increased considerably health-care material and water, health-care effect is better.And the problem that ceramic liner does not exist metal water tumbler to get rusty, has extended service life of water tumbler greatly.
Accompanying drawing explanation
The present invention has following accompanying drawing:
The structural representation of Fig. 1 far-infrared ceramic inner bag water tumbler.
The specific embodiment
Below in conjunction with accompanying drawing, the present invention is described in further detail.
As shown in Figure 1, far-infrared ceramic inner bag water tumbler of the present invention, comprising:
Water tumbler inner bag 1 is equipped with a glass courage surface glaze layer 2 on the medial surface of its bottom surface and sidewall,
Described water tumbler inner bag 1 is ceramic liner,
Described cup courage surface glaze layer 2 contains far-infrared material.
On the basis of technique scheme, the component of described water tumbler inner bag 1 is by mass percentage:
The exquisite natural bovine bone powder 40%~55% of 500 objects,
Kaolin 25%~37%,
Feldspar 5%~15%,
Quartz 3%~8%,
Hydroxymethyl cellulose sodium CMC 0.3%,
Also 10% of the dry powder body material gross weight of interpolation polyvinyl alcohol is as adhesive in the preparation, and dry powder body material refers to the natural bovine bone powder of aforesaid exquisiteness, kaolin, feldspar, quartz and hydroxymethyl cellulose sodium CMC,
The component of described cup courage surface glaze layer 2 is by mass percentage:
Lithium carbonate 5%,
Strontium carbonate 6%,
Feldspar 48%,
Quartz 24%,
3000 object tourmaline powders 5%,
Talcum powder 8%.
Be below the embodiment of the component of some water tumbler inner bags 1:
Embodiment 1:
The exquisite natural bovine bone powder 55% of 500 objects,
Kaolin 31.7%,
Feldspar 10%,
Quartz 3%,
Hydroxymethyl cellulose sodium CMC 0.3%,
Embodiment 2:
The exquisite natural bovine bone powder 49.7% of 500 objects,
Kaolin 37%,
Feldspar 10%,
Quartz 3%,
Hydroxymethyl cellulose sodium CMC 0.3%,
Embodiment 3:
The exquisite natural bovine bone powder 49.7% of 500 objects,
Kaolin 32%,
Feldspar 15%,
Quartz 3%,
Hydroxymethyl cellulose sodium CMC 0.3%,
Embodiment 4:
The exquisite natural bovine bone powder 49.7% of 500 objects,
Kaolin 32%,
Feldspar 10%,
Quartz 8%,
Hydroxymethyl cellulose sodium CMC 0.3%,
Embodiment 5:
The exquisite natural bovine bone powder 40% of 500 objects,
Kaolin 36.7%,
Feldspar 15%,
Quartz 8%,
Hydroxymethyl cellulose sodium CMC 0.3%,
Embodiment 6:
The exquisite natural bovine bone powder 51.7% of 500 objects,
Kaolin 25%,
Feldspar 15%,
Quartz 8%,
Hydroxymethyl cellulose sodium CMC 0.3%,
Embodiment 7:
The exquisite natural bovine bone powder 52% of 500 objects,
Kaolin 32%,
Feldspar 11%,
Quartz 4.7%,
Hydroxymethyl cellulose sodium CMC 0.3%,
Embodiment 8:
The exquisite natural bovine bone powder 48% of 500 objects,
Kaolin 35%,
Feldspar 12.7%,
Quartz 4%,
Hydroxymethyl cellulose sodium CMC 0.3%,
On the basis of technique scheme, the preparation process of water tumbler inner bag finished product following (water tumbler inner bag finished product refers to water tumbler inner bag 1 and cup courage surface glaze layer 2):
step 1, water tumbler inner bag material is processed (water tumbler inner bag 1 raw material is processed):
Step 1.1, by carrying out mist projection granulating processing after the natural bovine bone powder of exquisiteness, feldspar and quartzy mixing, makes powder body material possess mobility, facilitates moulding,
When mist projection granulating, add 10% polyvinyl alcohol of dry powder body material gross weight as adhesive, in same time, carry the mass ratio U of powder and air
sfor 1-4, air velocity 18-25m/s;
In described same time, carry the mass ratio U of powder and air
scan be 1,2,3 or 4,
Described air velocity can be 18 m/s, 19 m/s, 20 m/s, 21 m/s, 22 m/s, 23 m/s, 24 m/s or 25 m/s,
Step 1.2, after the products therefrom after step 1.1 is processed is mixed with kaolin, carries out ball-milling treatment (adding hydroxymethyl cellulose sodium CMC during ball-milling treatment) as blank (water tumbler inner bag blank), ball milling 14 hours,
During ball milling, the mass ratio of blank, ball, water, hydroxymethyl cellulose sodium CMC is: blank: ball: water: hydroxymethyl cellulose sodium CMC=1:1.5:0.6:0.003, and the CMC CMC wherein adding plays bonding, emulsification,
Ballstone grating during ball milling is: large: in: little=15:25:60, large ballstone diameter is 80mm, and middle ballstone diameter is 60mm, and bead stone diameter is 40mm;
Step 1.3, will be after step 1.2 ball-milling treatment products therefrom send into filter press and dewater to water content below 5%;
Described water content can be 5%, 4.9%, 4.8%, 4.7%, 4.6%, 4.5%, 4.0%, 3.8% or lower,
Step 1.4 will be carried out vacuum pugging by products therefrom after step 1.3 dehydration, and more than the vacuum 720mmHg of vacuum deairing machine, rotating speed 20r/min, makes the moisture in blank even, blank structure even compact, pore-free, and plasticity improves, and dry tenacity improves;
After lithium carbonate, strontium carbonate, zinc oxide, feldspar, quartz, boric acid, tourmaline powder and talcum powder are mixed, as cup courage surface glaze layer material, carry out ball-milling treatment, ball milling 42 hours,
During ball milling, the mass ratio of cup courage surface glaze layer material, ball, water is: cup courage surface glaze layer material: ball: water=1:2:0.55,
Ballstone grating during ball milling (ballstone number of stages proportioning) is: large: in: little=2:3:5, large ballstone diameter is 50mm, and middle ballstone diameter is 40mm, and bead stone diameter is 30mm;
step 3, the mixing of water tumbler inner bag blank, moulding, dry, biscuiting:
Step 3.1, by the water tumbler inner bag blank after step 1 is processed, cold rolling moulding, is used the desk-top roller head machine of steady job to carry out former roll extrusion, and roller-head is 0.6 with speed of mainshaft ratio, obtains water tumbler inner bag idiosome,
Step 3.2, the water tumbler inner bag idiosome after cold rolling moulding is dried 3 hours under the condition of 150 ℃,
Step 3.3, dried water tumbler inner bag idiosome, under the condition of 800 ℃, biscuiting is 5 minutes,
step 4, glazing:
Water tumbler inner bag idiosome after biscuiting, swings glaze method by the employing of cup courage surface glaze layer material and carries out glazing, swings glaze twice,
step 5, kiln-firing:
Water tumbler inner bag idiosome after glazing is entered to kiln, and the mode by 300 ℃/h of intensifications, is warming up to 1200 ℃, fires 8 hours, obtains water tumbler inner bag finished product.
The glaze layer of the water tumbler inner bag finished product of making (cup courage surface glaze layer 2) can be launched the far infrared wave of 8~14 micron wave lengths, and (tourmaline is the special polarity crystalline solid of a kind of structure, self can produce far ir ray), cause the resonance of water clusters, cause in water clusters hydrogen bond rupture between molecule and molecule, thereby an individual ponding group is decomposed into a plurality of small size water bodies, thereby realizes the effect of activated water.
Far-infrared ceramic inner bag water tumbler of the present invention, the part contacting with water (cup courage surface glaze layer) all contains health-care material, the contact area of health-care material and water is: π r2+2 π r * h, (r is the inside radius of cup courage surface glaze layer, h is the height of cup courage surface glaze layer), the contact area that has increased considerably health-care material and water, health-care effect is better.And the problem that ceramic liner does not exist metal water tumbler to get rusty, has extended service life of water tumbler greatly.
The content not being described in detail in this description belongs to the known prior art of professional and technical personnel in the field.
Claims (2)
1. a far-infrared ceramic inner bag water tumbler, is characterized in that, comprising: water tumbler inner bag (1), on the medial surface of its bottom surface and sidewall, be equipped with a glass courage surface glaze layer (2),
Described water tumbler inner bag (1) is ceramic liner,
Described cup courage surface glaze layer (2) contains far-infrared material;
The component of described water tumbler inner bag (1) is by mass percentage:
The exquisite natural bovine bone powder 40%~55% of 500 objects,
Kaolin 25%~37%,
Feldspar 5%~15%,
Quartz 3%~8%,
Hydroxymethyl cellulose sodium CMC 0.3%,
The component of described cup courage surface glaze layer (2) is by mass percentage:
Lithium carbonate 5%,
Strontium carbonate 6%,
Zinc oxide 2%,
Feldspar 48%,
Quartz 24%,
Boric acid 2%,
3000 object tourmaline powders 5%,
Talcum powder 8%.
2. far-infrared ceramic inner bag water tumbler as claimed in claim 1, is characterized in that, the preparation process of water tumbler inner bag finished product is as follows:
Step 1, water tumbler inner bag material is processed:
Step 1.1, by carrying out mist projection granulating processing after the natural bovine bone powder of exquisiteness, feldspar and quartzy mixing, makes powder body material possess mobility, facilitates moulding,
When mist projection granulating, add 10% polyvinyl alcohol of dry powder body material gross weight as adhesive, in same time, carry the mass ratio U of powder and air
sfor 1-4, air velocity 18-25m/s;
Step 1.2, after the products therefrom after step 1.1 is processed is mixed with kaolin, carries out ball-milling treatment as blank, ball milling 14 hours,
During ball milling, the mass ratio of blank, ball, water, hydroxymethyl cellulose sodium CMC is: blank: ball: water: hydroxymethyl cellulose sodium CMC=1:1.5:0.6:0.003,
Ballstone grating during ball milling is: large: in: little=15:25:60, large ballstone diameter is 80mm, and middle ballstone diameter is 60mm, and bead stone diameter is 40mm;
Step 1.3, sends products therefrom after ball milling into filter press and dewaters to water content below 5%;
Step 1.4, carries out vacuum pugging by products therefrom after dehydration, and more than the vacuum 720mmHg of vacuum deairing machine, rotating speed 20r/min, makes the moisture in blank even, blank structure even compact, pore-free, and plasticity improves, and dry tenacity improves;
Step 2, cup courage surface glaze layer material is processed:
After lithium carbonate, strontium carbonate, zinc oxide, feldspar, quartz, boric acid, tourmaline powder and talcum powder are mixed, as cup courage surface glaze layer material, carry out ball-milling treatment, ball milling 42 hours,
During ball milling, the mass ratio of cup courage surface glaze layer material, ball, water is: cup courage surface glaze layer material: ball: water=1:2:0.55,
Ballstone grating during ball milling is: large: in: little=2:3:5, large ballstone diameter is 50mm, and middle ballstone diameter is 40mm, and bead stone diameter is 30mm;
Step 3, the mixing of water tumbler inner bag blank, moulding, dry, biscuiting:
Step 3.1, by the water tumbler inner bag blank after step 1 is processed, cold rolling moulding, is used the desk-top roller head machine of steady job to carry out former roll extrusion, and roller-head is 0.6 with speed of mainshaft ratio, obtains water tumbler inner bag idiosome,
Step 3.2, the water tumbler inner bag idiosome after cold rolling moulding is dried 3 hours under the condition of 150 ℃,
Step 3.3, dried water tumbler inner bag idiosome, under the condition of 800 ℃, biscuiting is 5 minutes,
Step 4, glazing:
Water tumbler inner bag idiosome after biscuiting, swings glaze method by the employing of cup courage surface glaze layer material and carries out glazing, swings glaze twice,
Step 5, kiln-firing:
Water tumbler inner bag idiosome after glazing is entered to kiln, and the mode by 300 ℃/h of intensifications, is warming up to 1200 ℃, fires 8 hours, obtains water tumbler inner bag finished product.