CN106477891A - A kind of active ceramic and preparation method thereof - Google Patents
A kind of active ceramic and preparation method thereof Download PDFInfo
- Publication number
- CN106477891A CN106477891A CN201610919097.5A CN201610919097A CN106477891A CN 106477891 A CN106477891 A CN 106477891A CN 201610919097 A CN201610919097 A CN 201610919097A CN 106477891 A CN106477891 A CN 106477891A
- Authority
- CN
- China
- Prior art keywords
- parts
- glaze
- mesh
- energy
- ground
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
A kind of active ceramic and preparation method thereof, belongs to consumer goods industries.It is characterized in that：Including bottom base layer, ground glaze layer and cover coat, the parts by weight of raw materials of described ground glaze layer and/or cover coat consists of：Energy powder is added, wherein energy powder adds a certain amount of calcium gluconate, the adjuvant of stone needle, zinc glutamate and Os Draconis composition under the collocation of multi mineral raw material in raw glaze raw material and/or cullet of glaze.The activity of each energy powder can preferably be excited so as to energy field forms the complex energy field of the phase coordinating and unifying.Preparation method is characterised by the process of lapping of energy powder adding keeping 520 DEG C ~ 580 DEG C this specified temps, grind at this temperature and enable to the energy field of each material and be ground mixing under specific excited state, thus showing higher field effect in final ceramic.
Description
Technical field
A kind of active ceramic and preparation method thereof, belongs to consumer goods industries.
Background technology
The energy to biological physiological function with certain role and influence can be produced in currently known many Ores
, this energy field includes magnetic field, infrared ray that mineral itself send etc., and its specific mechanism of action is still not clear.But it is right
By objective reality for a certainty again for the actively impact of human body.This material can be to the effect of biological physiological function generation effect
It is referred to as energy field effect or referred to as field effect in the present invention.Now with more product utilization this energy field effect system
Standby medical health care products.
Ceramic material is widely used as traditional sintered material, is used not only for building decoration, more applies to
Sphere of life, such as water tumbler, water tumbler inner bag, pan, massager etc..The glaze paint of the densification of ceramic material surfaces is main function
Part.Also have at present and be added with the material with magnetic effect in some ceramic materials as magnetic health-care articles for use.However, current city
There are ceramic-like magnetic health-care articles for use, field effect is weaker on, this is because the various raw materials with field effect of pulverulence
Each does what he thinks is right in magnetic field, do not form unified energy field like that to bulk starting material, lead to interfere, reduce physiotheraping effect,
Lead to overall curative effect little.And in ceramic field because powder or slurry can only be used during becoming base and glazing, and need
Want high-temperature firing, lead to not the raw material using monoblock with field effect.
Content of the invention
The technical problem to be solved in the present invention is：Overcome the deficiencies in the prior art, provide a kind of effect to mutually promote, field is imitated
Active ceramic that should be stronger and preparation method thereof.
The technical solution adopted for the present invention to solve the technical problems is：This active ceramic it is characterised in that：Including bottom base
Layer, ground glaze layer and cover coat, the parts by weight of raw materials of described ground glaze layer and/or cover coat consists of：Raw glaze raw material and/or glaze
710 ~ 890 parts of frit, 22.2 ~ 22.75 parts of energy powder, the weight portion of wherein energy powder consists of：5 ~ 5.5 parts of Buddha's warrior attendant YAOSHI, green
2.4 ~ 2.7 parts of imperial or royal seal, 1.1 ~ 1.5 parts of lazurite, 3.3 ~ 3.7 parts of corallite, 1.6 ~ 1.8 parts of obsidian, yellow quartz 0.03 ~ 0.07
Part, 3.3 ~ 3.7 parts of Maifanitum, adjuvant；Described adjuvant is 3.8 ~ 4.1 parts of calcium gluconate, 0.3 ~ 0.6 part of stone needle, glutamic acid
0.01 ~ 0.015 part of zinc, 0.2 ~ 0.3 part of Os Draconis.
A kind of energy active energy powder is with the addition of, this energy powder is particularly suitable in ceramic glaze in the glaze of the present invention
Middle interpolation uses, and can adapt to the preparation technology of ceramic glaze.Need in the energy powder that the present invention adds to add the pass of the present invention
Key auxiliary material combination, the inventors found that the calcium gluconate described in adding, stone needle, zinc glutamate, Os Draconis form auxiliary
Material, can preferably excite the activity of each energy powder, make the energy field of each material of energy powder form the synthesis of the phase coordinating and unifying
Energy field, each magnetic field adding component or the infrared field of line are in mutual excited state, and field effect is higher.Adjuvant described in energy powder
Other materials in addition can discharge different energy field, keeps higher field effect in the ceramic made, and keeps each
Add the magnetic field of component or the infrared field of line is in mutual excited state.
Described Os Draconis, another name：Lu Hu lose life, that gal bone, Os Draconis, Os Draconis (calcined), five OS DRACONISs, green grass or young cropsization Os Draconis, OS DRACONIS,
Os Draconis.For ancient times mammal as if class, rhinoceros class, Hippocampal cortex etc. skeleton fossil.
Preferably, the mass ratio of described calcium gluconate and stone needle is 3.8 ~ 3.9：0.5.When above-mentioned adjuvant is using above-mentioned
During quality ratio, the amount of enable that powder shows highest field effect in ceramic material.
Preferably, described tourmaline is aphrizite, and the weight portion of interpolation is 2.4 ~ 2.5 parts.Aphrizite is tourmaline（Electrically
Stone）A kind of middle raw material adapting to present invention allocation most, contains indispensable trace element in a lot of human bodies, such as in aphrizite
Copper, zinc, ferrum etc., aphrizite has functions that uniqueness for anti-ageing, the reparation of human body skin, and aphrizite can help people body
Adsorbed with the soil in skin, skin can also be repaired simultaneously, really play the effect of looks improving and the skin nourishing.Aphrizite can
Strong kidney, the vitality of lifting people, aphrizite can also absorb and weaken the internal negative energy of the person, help people slow down pressure and
Fatigue, the pathogenic QI in the body in exclusion body, person health is played the role of positive.In addition, aphrizite can also adjust blood following
Ring, helps for sleep, and plays the effect of enhancing immunity.Make when holding the container of water or food in being added to ceramic glaze,
The loss of nutritional labeling, the trace element of supplements and water can preferably be reduced.
Preferably, the weight portion that the weight portion that described cullet of glaze adds is 710 ~ 750 parts, energy powder adds is 22.6
~ 22.7 parts.Cullet of glaze, as fritted glaze, because oil plant frit has been carried out once firing, leads to and energy powder in the present invention
Combination there is certain particularity.When using above-mentioned preferred proportioning, can more fully ensure energy powder in ceramic glaze
The abundance of material, makes the field effect of each material reach optimal mutual excited state.
Preferably, the weight portion composition of described raw glaze raw material includes 350 ~ 450 parts of Kaolin, clay 100 ~ 150
Part, 50 ~ 80 parts of Talcum, 50 ~ 80 parts of Anhydrite, 40 ~ 60 parts of dolomite, 10 ~ 30 parts of zinc oxide.The present invention provides a kind of energy
The raw glaze raw material composition of powder adaptation, can more fully ensure energy powder in ceramic glaze when raw glaze is used alone
Distribution is it is ensured that the abundant effect of secondary effect.
A kind of preparation method of above-mentioned active ceramic is it is characterised in that preparation process is：
1）Weighed material and be sufficiently mixed by the weight portion composition of energy powder；First use grinder in 520 DEG C ~ 580 DEG C of temperature
It is ground under degree obtaining the energy powder of 2000 mesh ~ 6000 mesh；
2）The energy powder of 2000 mesh ~ 6000 mesh and raw glaze raw material and/or cullet of glaze form by weight to weigh and jointly exist afterwards
Glaze is ground to obtain in grinder；
3）Step 2 is applied on the bottom base pressing）Prepared glaze, then is fired obtaining final product at 1050 DEG C ~ 1130 DEG C.
The energy powder that the present invention uses can form more preferably activity through particular abrasive technique after preparing, and energy powder exists
520 DEG C ~ 580 DEG C this specified temps are kept, inventor finds to grind at this temperature and enables to each thing in process of lapping
The energy field of material is ground mixing under specific excited state, thus showing higher field effect in final energy powder
Should.Only need co-ground when mixing with other Glaze Composition, both can guarantee that and kept respectively adding in the ceramic being eventually fabricated
Plus the magnetic field of component or the infrared field of line are in mutual excited state.
Preferably, the advanced premixing before the energy powder with 2000 mesh ~ 6000 mesh mixes of described raw glaze raw material.Energy
Ensure raw material mix homogeneously it is ensured that the glaze layer quality made.
Preferably, described cullet of glaze first puts into step 2）Grinder in be ground to 2000 mesh ~ 6000 mesh, then will
The energy powder of 2000 mesh ~ 6000 mesh puts into and carries out co-ground.Cullet of glaze first grinds and is that energy powder mixes, and can guarantee that raw material
Mix homogeneously is it is ensured that the glaze layer quality made.
Preferably, 540 DEG C ~ 555 DEG C of the temperature in described grinder.Field effect can be obtained the strongest under identical proportioning
Final ceramic.
Zn, Fe, Mn, Cu, Co, A1, Se, Cr, Ag, Sr, Ga, Ge, Li is contained in the Buddha's warrior attendant YAOSHI adopting in the present invention,
The various trace elements such as Ti, Mo, V, the Fe in Buddha's warrior attendant YAOSHI, the trace element such as Zn, Mn, Cu, Co promotes organic
Grow up and develop, and blood circulation promoting, the function Buddha's warrior attendant of the element such as Cu, Zn, Mo, I reinforcement resistance and immunocompetence
YAOSHI has adsorption and bactericidal action because of special tectonic in structure and chemically.Learn Buddha's warrior attendant YAOSHI to unit by experiment
The absorption affinity of element is Pb（Lead）：63~95%,Cd（Cadmium）：35~68%,As（Arsenic）：37.2%,Hg（Hydrargyrum）：80%, F（Fluorine）：64~69%.
Put into Buddha's warrior attendant YAOSHI solution in coliform culture vessel, have 97.55% adsorbed death.The ability specific activity charcoal of absorption abnormal flavour
High several times, in addition with anticancer, prevent radiation, Auto-regulator metabolism and blood circulation, extend the life-span, supplement the work such as energy
With being generally used for arteriosclerosis, leg ulcer that hypertension, diabetes, nephritis, vein occlusion cause, burn, depilation, wet
Rash, tinea pedis, neurodermatitiss, miliaria, increase, anticancer, prevent radiation etc..
The corallite adopting in the present invention can prevent the women's physiologicals such as dysmenorrhoea disease, and the effect that protection skeleton is grown up, to blood
The disease of aspect has detecting function, it is likely that there being anemia if more wearing color and be lighter, the problems such as poor circulation, the heart
Disease of ZANG-organs and nervous system disease are well suited for wearing from patient, and substantially corallite has side to the growth such as skin, fingernail, hair
Help.
The obsidian adopting in the present invention is among all spar, a kind of property received spar the strongest.Can just will quickly
Neighbouring miscellaneous QI or negativity energy, inspiration in it invisible space in.Can draw the energy contained is crossed on human body, releive
Uncomfortable.
The yellow quartz adopting in the present invention is also effective in cure for pancreas and endocrine nervous system, and to glycosuria, patient less may be used
Or lack, also can treat swelling stomach function regulating and knot, main gastrointestinal function, dyspepsia or the unbalance person of diet suitably use.Also clear up tight
Open emotion, help the function of the digestive system such as the intestines and stomach.
The Maifanitum adopting in the present invention is made up of 25000 Multiple components, can discharge several mineral materials.Maifanitum is acceptable
Ionize noxious substance using the method that self component passes through to absorb, decompose.Released mineral matter simultaneously balances mineral quantity, Maifanitum
The requisite various mineral of human body can be given out in water.Supplemented by absorbing unnecessary mineral or released mineral matter
It is not enough, and Maifanitum can balance the quantity of mineral.The various trace element of Maifanitum release are such as：Potassium, phosphorus, ferrum, sulphur, manganese,
Magnesium etc., these materials play an important role to enzyme and hormonal synthesis.Maifanitum can also be treated " dermatosiss, swelling, skin scabies,
Traumatic injury of skin etc. ".And Maifanitum is especially effective to removing various chemical toxicants.Also have attention, Maifanitum energy in the present invention
Discharge the infrared ray beneficial to human body.
The stone needle adopting in the present invention can send many far ir rays beneficial to human body and ultrasonic pulse, promotes
Blood microcirculation, conditioning metabolism, its effect is equivalent to far infrared therapeutic apparatus+ultrasonic therapeutic apparatus dual function.Stone needle
The energy that can contain by its own carry out the potential of exciting human, have calm the nerves, QI and blood regulating, dredging the meridian, to purify Liver and kidney etc. dirty
Device, excludes unnecessary toxin, strengthens the effect of the immunocompetence of people comprehensively.
Compared with prior art, the present invention is had an advantageous effect in that：The above-mentioned active ceramic of the present invention, glaze used
Material and energy active energy powder can adapt to ceramic process environments, keep higher field effect, keep each magnetic adding component
Field or the infrared field of line are in mutual excited state.In the energy active energy powder that the technique scheme of the present invention is added simultaneously
Need the crucial auxiliary material combination using the present invention, the inventors found that a certain amount of calcium gluconate of interpolation, stone needle, paddy
Propylhomoserin zinc, the adjuvant of Os Draconis composition, can preferably excite the activity of each energy powder so as to energy field forms the phase coordinating and unifying
Complex energy field, each magnetic field adding component or the infrared field of line are in mutual excited state, and field effect is higher.Described in energy powder
Other materials beyond adjuvant can discharge different energy field, and the present invention provides the glaze side of above-mentioned adaptation ceramic process environment
Case.More preferably activity can be formed again after the particular abrasive technique preparation of the present invention, the energy powder that the present invention adds is grinding
520 DEG C ~ 580 DEG C this specified temps are kept, inventor finds to grind at this temperature and enables to each material during mill
Energy field be ground mixing under specific excited state, thus showing higher field effect in final ceramic
Should.
Specific embodiment
With reference to specific embodiment, the present invention will be further described.
Embodiment 1
1）Cover-coat enamel raw material forms by weight：400 parts of Kaolin, 125 parts of clay, 65 parts of Talcum, 65 parts of Anhydrite, white clouds
50 parts of stone, 20 parts of zinc oxide, 10 parts of colorant weigh mixing for standby use after material；
2）Weight portion composition by energy powder：5.3 parts of Buddha's warrior attendant YAOSHI, 2.5 parts of aphrizite, 1.3 parts of lazurite, 3.5 parts of corallite,
1.7 parts of obsidian, 0.05 part of yellow quartz, 3.6 parts of Maifanitum, 3.8 parts of calcium gluconate, 0.5 part of stone needle, zinc glutamate 0.013
Part, 0.25 part of Os Draconis weigh material and are sufficiently mixed；Then it is ground obtaining at a temperature of 550 DEG C with grinder
The energy powder of 2000 mesh ~ 6000 mesh；
3）The step 1 of the energy powder of 22.6 part of 2000 mesh ~ 6000 mesh and 745 parts）After prepared cover-coat enamel raw material weighs by weight
Common grinding in grinder obtains final product cover-coat enamel glaze；
4）After applying traditional ground-coat enamel on the pot shape of molding, water tumbler type, the hemispheric bottom base of diameter 0.3cm ~ 1cm respectively
Applying the thick step 3 of 2mm）Prepared cover-coat enamel glaze, then is fired obtaining final product at 1050 DEG C ~ 1130 DEG C.
Embodiment 2
1）The weight portion composition of cover-coat enamel raw material includes 350 parts of Kaolin, 150 parts of clay, 50 parts of Talcum, 80 parts of Anhydrite, oxygen
Change 30 parts of zinc, 10 parts of colorant weighs mixing for standby use after material；
2）The weight portion of energy powder consists of：5.2 parts of Buddha's warrior attendant YAOSHI, 2.4 parts of aphrizite, 1.5 parts of lazurite, 3.5 parts of corallite,
1.7 parts of obsidian, 0.04 part of yellow quartz, 3.6 parts of Maifanitum, 3.9 parts of calcium gluconate, 0.5 part of stone needle, zinc glutamate 0.013
Part, 0.27 part of Os Draconis weigh material and are sufficiently mixed；Then it is ground obtaining at a temperature of 545 DEG C with grinder
The energy powder of 2000 mesh ~ 6000 mesh；
3）Traditional ground-coat enamel raw material of the energy powder of 22.7 part of 2000 mesh ~ 6000 mesh and 710 parts exists after weighing by weight jointly
Grind in grinder and obtain final product ground-coat enamel glaze；
4）Step 3 is applied respectively on the pot shape of molding, water tumbler type, the hemispheric bottom base of diameter 0.3cm ~ 1cm）Prepared
Ground-coat enamel glaze, then drenches the thick step 1 of 1.5mm again）Prepared cover-coat enamel, is fired obtaining final product through under the conditions of 1050 DEG C ~ 1130 DEG C.
Embodiment 3
1）The weight portion of cover-coat enamel raw material forms and includes 450 parts of Kaolin, 100 parts of clay, 80 parts of Talcum, 50 parts of Anhydrite,
60 parts of dolomite, 10 parts of zinc oxide, 10 parts of colorant weigh mixing for standby use after material；
2）The weight portion of energy powder consists of：10.6 parts of Buddha's warrior attendant YAOSHI, 5.0 parts of aphrizite, 2.4 parts of lazurite, corallite 6.8
Part, 3.4 parts of obsidian, 0.10 part of yellow quartz, 6.8 parts of Maifanitum, 7.6 parts of calcium gluconate, 1.0 parts of stone needle, zinc glutamate
0.022 part, 0.46 part of Os Draconis weigh material and are sufficiently mixed；Then it is ground at a temperature of 540 DEG C with grinder
Obtain the energy powder of 2000 mesh ~ 6000 mesh；
3）The energy powder of 22.2 part of 2000 mesh ~ 6000 mesh and 800 parts of traditional ground-coat enamel raw material are grinding after weighing by weight jointly
Grind in grinding machine and obtain final product ground-coat enamel glaze；The step 1 of the energy powder of 22.2 part of 2000 mesh ~ 6000 mesh and 760 parts）Prepared cover-coat enamel is former
Material jointly grinds in grinder after weighing by weight and obtains final product cover-coat enamel glaze；
4）First after-applied step 3 on the pot shape of molding, water tumbler type, the hemispheric bottom base of diameter 0.3cm ~ 1cm respectively）System
Glaze glaze after the ground-coat enamel glaze obtaining and 1mm, then is fired obtaining final product at 1050 DEG C ~ 1130 DEG C.
Embodiment 4
1）Be ground to after 2000 mesh ~ 6000 mesh by putting into 450 parts of cullet of glazes in grinders, with 200 parts of Kaolin, 100 parts
Clay, 40 parts of Talcums, 40 parts of Anhydrites, 25 parts of dolomites, 5 parts of zinc oxide, 10 parts of colorant composition raw glazes mix to obtain standby cover-coat enamel
Raw material；
2）The weight portion of energy powder consists of：5.3 parts of Buddha's warrior attendant YAOSHI, blue 2.6 parts of tourmaline, 1.3 parts of lazurite, 3.5 parts of corallite,
1.7 parts of obsidian, 0.05 part of yellow quartz, 3.5 parts of Maifanitum, 3.9 parts of calcium gluconate, 0.5 part of stone needle, zinc glutamate 0.012
Part, 0.25 part of Os Draconis weigh material and are sufficiently mixed；First it is ground obtaining 2000 at a temperature of 555 DEG C with grinder
The energy powder of mesh ~ 6000 mesh；
3）The step 1 of the energy powder of 22.7 part of 2000 mesh ~ 6000 mesh and 870 parts）Prepared standby cover-coat enamel raw material claims by weight
After taking, common grinding in grinder obtains final product cover-coat enamel glaze；
4）After applying traditional ground-coat enamel on the pot shape of molding, water tumbler type, the hemispheric bottom base of diameter 0.3cm ~ 1cm respectively,
Drench the thick step 3 of 2.5mm again）Prepared cover-coat enamel glaze, then apply polish glaze after be fired at 1050 DEG C ~ 1130 DEG C be
?.
Embodiment 5
1）Obtain fritted glaze powder using being ground to 2000 mesh ~ 6000 mesh in 890 parts of cullet of glazes input grinders as cover-coat enamel raw material；
2）The weight portion of energy powder consists of：5 parts of Buddha's warrior attendant YAOSHI, 2.7 parts of Watermelon tourmalin, 1.5 parts of lazurite, 3.3 parts of corallite,
1.8 parts of obsidian, 0.03 part of yellow quartz, 3.7 parts of Maifanitum, 3.8 parts of calcium gluconate, 0.6 part of stone needle, zinc glutamate 0.015
Part, 0.2 part of Os Draconis weigh material and are sufficiently mixed；First it is ground obtaining 2000 at a temperature of 520 DEG C with grinder
The energy powder of mesh ~ 6000 mesh；
3）The energy powder of 22.75 part of 2000 mesh ~ 6000 mesh and 890 parts of steps 1）The cover-coat enamel raw material of preparation is common after weighing by weight
Obtain final product cover-coat enamel glaze with grinding in grinder；
4）Step 3 is applied respectively on the pot shape of molding, water tumbler type, the hemispheric bottom base of diameter 0.3cm ~ 1cm）Prepared
Cover-coat enamel glaze, then is fired obtaining final product at 1050 DEG C ~ 1130 DEG C.
Embodiment 6
1）Obtain fritted glaze powder using being ground to 2000 mesh ~ 6000 mesh in 750 parts of cullet of glazes input grinders as cover-coat enamel raw material；
2）The weight portion of energy powder consists of：5.5 parts of Buddha's warrior attendant YAOSHI, 2.4 parts of rubellite, 1.1 parts of lazurite, 3.7 parts of corallite,
1.6 parts of obsidian, 0.07 part of yellow quartz, 3.3 parts of Maifanitum, 4.1 parts of calcium gluconate, 0.3 part of stone needle, zinc glutamate 0.01
Part, 0.3 part of Os Draconis weigh material and are sufficiently mixed；First it is ground obtaining 2000 at a temperature of 580 DEG C with grinder
The energy powder of mesh ~ 6000 mesh；
3）The energy powder of 22.53 part of 2000 mesh ~ 6000 mesh is being ground afterwards jointly with weighing by weight of 750 parts of traditional ground-coat enamel raw materials
Grind in grinding machine and obtain final product ground-coat enamel glaze；
4）Step 3 is applied respectively on the pot shape of molding, water tumbler type, the hemispheric bottom base of diameter 0.3cm ~ 1cm）Prepared
Ground-coat enamel glaze, then drenches the thick step 1 of 1.5mm）Prepared cover-coat enamel raw material, then apply polish glaze after through 1050 DEG C ~ 1130 DEG C bars
It is fired obtaining final product under part.
Comparative example 1
1）The weight portion composition of raw glaze raw material pressed by cover-coat enamel raw material：400 parts of Kaolin, 125 parts of clay, 65 parts of Talcum, long
65 parts of stone, 50 parts of dolomite, 20 parts of zinc oxide, 10 parts of colorant weigh mixing for standby use after material；
2）Weight portion composition by energy powder：5.3 parts of Buddha's warrior attendant YAOSHI, 2.5 parts of aphrizite, 1.3 parts of lazurite, 3.5 parts of corallite,
1.7 parts of obsidian, 0.05 part of yellow quartz, 3.6 parts of Maifanitum weigh material and are sufficiently mixed；Then use grinder 550
It is ground at a temperature of DEG C obtaining the energy powder of 2000 mesh ~ 6000 mesh；
3）The step 1 of the energy powder of 22.6 part of 2000 mesh ~ 6000 mesh and 745 parts）After prepared cover-coat enamel raw material weighs by weight
Common grinding in grinder obtains final product cover-coat enamel glaze；
4）After applying traditional ground-coat enamel on the pot shape of molding, water tumbler type, the hemispheric bottom base of diameter 0.3cm ~ 1cm respectively,
Apply step 3 again）Prepared cover-coat enamel glaze, then is fired obtaining final product through subsequent handling at 1050 DEG C ~ 1130 DEG C.
Comparative example 2
1）Cover-coat enamel raw material forms by weight：400 parts of Kaolin, 125 parts of clay, 65 parts of Talcum, 65 parts of Anhydrite, white clouds
50 parts of stone, 20 parts of zinc oxide, 10 parts of colorant weigh mixing for standby use after material；
2）Weight portion composition by energy powder：5.3 parts of Buddha's warrior attendant YAOSHI, 2.5 parts of aphrizite, 1.3 parts of lazurite, 3.5 parts of corallite,
1.7 parts of obsidian, 0.05 part of yellow quartz, 3.6 parts of Maifanitum, 3.8 parts of calcium gluconate, 0.5 part of stone needle, zinc glutamate 0.013
Part, 0.25 part of Os Draconis weigh material and are sufficiently mixed；Then with grinder be ground at normal temperatures obtaining 2000 mesh ~
The energy powder of 6000 mesh；
3）The cover-coat enamel raw material of the energy powder of 22.6 part of 2000 mesh ~ 6000 mesh and 745 parts of step 1 preparations is common after weighing by weight
Grind in grinder and obtain final product；
4）After applying traditional ground-coat enamel on the pot shape of molding, water tumbler type, the hemispheric bottom base of diameter 0.3cm ~ 1cm respectively,
Apply step 3 again）Prepared cover-coat enamel glaze, then is fired obtaining final product through subsequent handling at 1050 DEG C ~ 1130 DEG C.
Comparative example 3
1）Obtain fritted glaze powder by being ground to 2000 mesh ~ 6000 mesh in 500 parts of cullet of glazes input grinders；
2）Weight portion composition by energy powder：5.3 parts of Buddha's warrior attendant YAOSHI, 2.5 parts of aphrizite, 1.3 parts of lazurite, 3.5 parts of corallite,
1.7 parts of obsidian, 0.05 part of yellow quartz, 3.6 parts of Maifanitum, 3.8 parts of calcium gluconate, 0.5 part of stone needle, zinc glutamate 0.013
Part, 0.25 part of Os Draconis weigh material and are sufficiently mixed；Then it is ground obtaining at a temperature of 550 DEG C with grinder
The energy powder of 2000 mesh ~ 6000 mesh；
3）The fritted glaze powder of the energy powder of 22.6 part of 2000 mesh ~ 6000 mesh and 500 parts of step 1 preparations is common after weighing by weight
Obtain final product with grinding in grinder；
4）After applying traditional ground-coat enamel on the pot shape of molding, water tumbler type, the hemispheric bottom base of diameter 0.3cm ~ 1cm respectively,
Apply step 3 again）Prepared cover-coat enamel glaze, is then fired at 1050 DEG C ~ 1130 DEG C, cracking in sintering procedure, becomes
Product fragility is big it is impossible to normal use.
The ceramic cooker with glaze paint that each embodiment and comparative example are obtained, can be close to outside ceramic cooker be coated with metal
Surrounding layer, it is also possible to directly use, respectively puts into 100 Fructus Fragariae Ananssaes of same time period harvesting in each pan.Each pan opens lid and protects
Fructus Fragariae Ananssae in embodiment 1, embodiment 4 and the corresponding pan of embodiment 6 after depositing 24h has no addles, in the corresponding pan of embodiment 2
Fructus Fragariae Ananssae have 1 to addle in the middle part of pan, the Fructus Fragariae Ananssae in embodiment 3 and the corresponding pan of embodiment 5 has 2 corruption in the middle part of pan
Bad, the corresponding pan of comparative example 1 has 16 can addle in zones of different, and the corresponding pan of comparative example 2 has 8 in zones of different
Can addle；Embodiment and documents 1 are compared it can be seen that the adjuvant adding in the present invention has to the activity of each material
There is excitation, the energy field phase of each material can be made to unify, so that ceramic cooker keeps higher comprehensive field effect, can make
Food therein preferably keeps nutrition.Compare it can be seen that the present invention is in a heated state to energy powder with comparative example 2
It is ground, the bigger field effect remaining each material.
The ceramic cup with glaze paint that each embodiment and comparative example are obtained, adds the distilled water of equivalent in ceramic cup,
The plant section of the identical number of sheets is taken on same strain Epipremnum aureum (Linde et Andre) (Bunting.), each ceramic cup is inserted into five sections of such plant section samples.Real after one day
The Epipremnum aureum (Linde et Andre) (Bunting.) plant section applying example 1, embodiment 4 and the corresponding ceramic cup of embodiment 6 bears the root system of 1cm ~ 2cm length, and embodiment 2 is corresponding
The Epipremnum aureum (Linde et Andre) (Bunting.) plant section of ceramic cup bear the root system of 0.5cm ~ 1.5cm length, embodiment 3 and the corresponding ceramic cup of embodiment 5 green
Trailing plants plant section bears the root system of 0.5cm ~ 1cm length, and comparative example 1, the Epipremnum aureum (Linde et Andre) (Bunting.) plant section of the corresponding ceramic cup of comparative example 2 have no root system
Bear.Embodiment and documents 1,2 are compared it can be seen that the adjuvant adding in the present invention has to the activity of each material and excites
Effect, can make the energy field phase of each material unify, so that ceramic cup keeps higher comprehensive field effect, can supplement distilled water
In mineral element, stimulate cell potential, increase cytoactive, promote plant growing.
The hemispherical ceramic granule with glaze paint that each embodiment and comparative example are obtained, this ceramic particle is pressed 1/dm3
Density be embedded in electric blanket, give 100 old peoples, 100 subhealth states, the middle age of 100 body overdraws respectively
Use, carry out practical test after using one week, the health of the user of each embodiment is significantly better than the use of comparative example
The health of person.Test event is：（1）, heavy burden aptitude tests, the user of embodiment 1 bear ability compared with comparative example 1
User mean height 9%, compared with comparative example 2 user mean height 4%；（2）Equilibrant（Stand with one foot to the knee and stretch single armed）Test, real
Apply example 1 user equilibration time compared with comparative example 1 user mean height 17%, compared with comparative example 2 user mean height
8.6%；（3）Pliability is tested（Feet station is stood and is fixed, and straight-arm turns round body, uses front hook Amax, with rear corner A " max, then A "
Max ＞ Amax and（A” max—Amax）Corresponding arc length about 10 ~ 30cm（The heavier effect of body more obvious it is meant that situation to
Good）, the pliability of the user of embodiment 1 compared with the user mean height 13% of comparative example 1, compared with the user mean height of comparative example 2
5%.Embodiment 1 and comparative example 1,2 are compared it can be seen that the adjuvant that adds in the present invention has to the activity of each material and excites work
With the energy field phase of each material being made to unify, so that fibrous material keeps higher comprehensive field effect, using rear activation people
Somatic activity, blood circulation promoting, to the health of human body, there is higher positive role.
The above, be only presently preferred embodiments of the present invention, is not the restriction that the present invention is made with other forms, appoints
What those skilled in the art possibly also with the disclosure above technology contents changed or be modified as equivalent variations etc.
Effect embodiment.But every without departing from technical solution of the present invention content, according to the present invention technical spirit to above example institute
Any simple modification, equivalent variations and the remodeling made, still falls within the protection domain of technical solution of the present invention.
Claims (9)
1. a kind of active ceramic it is characterised in that：Including bottom base layer, ground glaze layer and cover coat, described ground glaze layer and/or cover coat
Parts by weight of raw materials consist of：Raw glaze raw material and/or 710 ~ 890 parts of cullet of glaze, 22.2 ~ 22.75 parts of energy powder, wherein can
The weight portion of amount powder consists of：5 ~ 5.5 parts of Buddha's warrior attendant YAOSHI, 2.4 ~ 2.7 parts of tourmaline, 1.1 ~ 1.5 parts of lazurite, corallite 3.3 ~
3.7 parts, 1.6 ~ 1.8 parts of obsidian, 0.03 ~ 0.07 part of yellow quartz, 3.3 ~ 3.7 parts of Maifanitum, adjuvant；Described adjuvant is Fructus Vitis viniferae
3.8 ~ 4.1 parts of Calciofon, 0.3 ~ 0.6 part of stone needle, 0.01 ~ 0.015 part of zinc glutamate, 0.2 ~ 0.3 part of Os Draconis.
2. a kind of active ceramic according to claim 1 it is characterised in that：Described calcium gluconate and the quality of stone needle
Than for 3.8 ~ 3.9：0.5.
3. a kind of active ceramic according to claim 1 it is characterised in that：Described tourmaline is aphrizite, the weight of interpolation
Amount part is 2.4 ~ 2.5 parts.
4. a kind of active ceramic according to claim 1 it is characterised in that：The weight portion that described cullet of glaze adds is
710 ~ 750 parts, energy powder add weight portion be 22.6 ~ 22.7 parts.
5. a kind of active ceramic according to claim 1 it is characterised in that：The weight portion composition of described raw glaze raw material
Including 350 ~ 450 parts of Kaolin, 100 ~ 150 parts of clay, 50 ~ 80 parts of Talcum, 50 ~ 80 parts of Anhydrite, dolomite 40 ~ 60
Part, 10 ~ 30 parts of zinc oxide.
6. a kind of preparation method of the active ceramic described in any one of claim 1 ~ 5 is it is characterised in that preparation process is：
1）Weighed material and be sufficiently mixed by the weight portion composition of energy powder；First use grinder in 520 DEG C ~ 580 DEG C of temperature
It is ground under degree obtaining the energy powder of 2000 mesh ~ 6000 mesh；
2）The energy powder of 2000 mesh ~ 6000 mesh and raw glaze raw material and/or cullet of glaze form by weight to weigh and jointly exist afterwards
Glaze is ground to obtain in grinder；
3）Step 2 is applied on the bottom base pressing）Prepared glaze, then is fired obtaining final product at 1050 DEG C ~ 1130 DEG C.
7. a kind of active ceramic according to claim 6 preparation method it is characterised in that：Described raw glaze raw material exists
Advanced premixing before mixing with the energy powder of 2000 mesh ~ 6000 mesh.
8. a kind of active ceramic according to claim 6 preparation method it is characterised in that：Described cullet of glaze is first thrown
Enter step 2）Grinder in be ground to 2000 mesh ~ 6000 mesh, then the energy powder of 2000 mesh ~ 6000 mesh put into jointly ground
Mill.
9. a kind of active ceramic according to claim 6 preparation method it is characterised in that：Temperature in described grinder
540 DEG C ~ 555 DEG C of degree.