CN108505178A - A kind of high-strength vortex spinning yarn and its production method - Google Patents
A kind of high-strength vortex spinning yarn and its production method Download PDFInfo
- Publication number
- CN108505178A CN108505178A CN201810616875.2A CN201810616875A CN108505178A CN 108505178 A CN108505178 A CN 108505178A CN 201810616875 A CN201810616875 A CN 201810616875A CN 108505178 A CN108505178 A CN 108505178A
- Authority
- CN
- China
- Prior art keywords
- yarn
- strength
- control
- fiber
- fasciated
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of high-strength vortex spinning yarn and its production methods.The high-strength vortex spinning yarn, including heart yarn and control of two-dimensional braided fasciated yarn；Heart yarn includes centred beam and outer wrapping fiber；Heart yarn is made of vortex blended weave, and outer wrapping fiber spiral winding is coated on outside centred beam；Centred beam is made of parallel without twisting harness the short fibre of carbon fiber；Outer wrapping fiber is made of aramid fiber；16 ingot fasciated yarns of the reticular structure that control of two-dimensional braided fasciated yarn is formed by high-strength polyethylene strand outside heart yarn by control of two-dimensional braided machine.Present invention process advantages of simple, the high-strength vortex spinning yarn of production, using covering yarn structure, heart yarn is made up of Technology of Air Vortex Spinning, has fibre compact degree good, uniform force, and tensile strength is high, and shock resistance is good；Control of two-dimensional braided fasciated yarn can further promote the intensity of the present invention, while aramid fiber prevents occurring sliding wriggling between control of two-dimensional braided fasciated yarn and heart yarn, improves bond strength, promotes anti-cutting performance.
Description
Technical field
The present invention relates to vortex field of textiles, more particularly to a kind of high-strength vortex spinning yarn and its production method.
Background technology
With the change of people's consumption idea and the continuous improvement of quality of the life, function of the people to textiles such as clothings
It is required that paying attention to increasingly, people increasingly pursue same textile and are provided simultaneously with a variety of utility functions as much as possible, to adapt to and improve
Living environment, working environment and the health of itself.And yarn is the basic material of various textiles, the structure and function of yarn are straight
Connecing influences the quality and performance of textile.
Yarn is generally manufactured using single natural fiber or single chemical fibre at present.Natural fiber by
It is right in flexibility, durability, gas permeability, pure property and biodegradable and preferable hygroscopicity and gas permeability
The advantages that body is non-hazardous, but there is also the insufficient problems of strength.Especially taking place frequently now with terrorist incident, the peace of people
Full protection consciousness constantly enhancing, wherein anti-stab, anti-cutting product exploitation is increasingly subject to the attention of researcher with research.Yarn conduct
Anti-stab, anti-cutting product raw material, the intensity of yarn directly determine the performance of anti-stab anti-cutting product.Therefore, demand one kind is high-strength
The new type yarn that degree, anti-cutting are had excellent performance.
Invention content
In order to solve the above technical problems, the present invention provides a kind of high-strength vortex spinning yarn and its production methods, using whirlpool
It flows outer wrapping fiber made of core wire and control of two-dimensional braided machine made of spinning process to coordinate, it is weak to solve existing yarn texture intensity, prevents
The problem of cutting poor performance.
In order to achieve the above objectives, technical scheme is as follows：A kind of high-strength vortex spinning yarn, including heart yarn and two dimension
Weave fasciated yarn；The heart yarn includes centred beam and outer wrapping fiber；The heart yarn is made of vortex blended weave, the outsourcing
Fiber spiral is wrapped around outside the centred beam；The parallel no twisted lines that the centred beam is made of the short fibre of carbon fiber
Beam；The outer wrapping fiber is made of aramid fiber；The control of two-dimensional braided fasciated yarn passes through high-strength polyethylene stock by control of two-dimensional braided machine
16 ingot fasciated yarns of the reticular structure that line is formed outside the heart yarn.
As a preferred embodiment of the present invention, the high-strength polyethylene strand by high-strength polyethylene long filament twist Split Down and
At.
As a preferred embodiment of the present invention, carbon fiber described in the heart yarn is short fine blended with the aramid fiber
Than being 1：2.
As a preferred embodiment of the present invention, the carbon fiber staple length is 35-50mm.
As a preferred embodiment of the present invention, the aramid fiber length is 80-100mm.
A kind of production method of high-strength vortex spinning yarn, includes the following steps：
The short fine and aramid fiber of carbon fiber after cutting is passed through griping cotton machine, cotton blender machine, opener, double cottons by step 1 successively
After case cotton feeder, lapper, carding machine, drawing frame and vortex flow spinner processing, heart yarn is made；
Step 2, twisting Split Down is carried out to high-strength polyethylene long filament and high-strength polyethylene strand is made, then by the heart yarn and
High-strength polyethylene strand forms 16 ingot fasciated yarns outside the heart yarn, yarn finished product is made by control of two-dimensional braided machine.
Through the above technical solutions, the advantageous effect of technical solution of the present invention is：Present invention process advantages of simple, is manufactured into
This low, high-strength vortex spinning yarn of production, the covering yarn structure coordinated using heart yarn and control of two-dimensional braided fasciated yarn, heart yarn pass through whirlpool
Stream spinning process is made, and has fibre compact degree good, uniform force, and tensile strength is high, and shock resistance is good；Control of two-dimensional braided fasciated yarn
It can play the role of structural strengthening, further promote the intensity of the present invention, while aramid fiber prevents control of two-dimensional braided fasciated yarn
Occur sliding between heart yarn to wriggle, improves bond strength, promote anti-cutting performance.
Description of the drawings
In order to more clearly explain the embodiment of the invention or the technical proposal in the existing technology, to embodiment or will show below
There is attached drawing needed in technology description to be briefly described, it should be apparent that, the accompanying drawings in the following description is only this
Some embodiments of invention for those of ordinary skill in the art without creative efforts, can be with
Obtain other attached drawings according to these attached drawings.
Fig. 1 is the structural diagram of the present invention.
Number and the corresponding component title represented by letter in figure：
1. 2. outer wrapping fiber of centred beam, 3. control of two-dimensional braided fasciated yarn.
Specific implementation mode
Following will be combined with the drawings in the embodiments of the present invention, and technical solution in the embodiment of the present invention carries out clear, complete
Site preparation describes, it is clear that described embodiments are only a part of the embodiments of the present invention, instead of all the embodiments.It is based on
Embodiment in the present invention, those of ordinary skill in the art are obtained every other without creative efforts
Embodiment shall fall within the protection scope of the present invention.
Embodiment
In conjunction with Fig. 1, the invention discloses a kind of high-strength vortex spinning yarns, including heart yarn and control of two-dimensional braided fasciated yarn 3.Heart yarn
Including centred beam 1 and outer wrapping fiber 2.Heart yarn is made of vortex blended weave, and 2 spiral winding of outer wrapping fiber is coated on center line
Outside beam 1.Centred beam 1 is made of parallel without twisting harness the short fibre of carbon fiber.Outer wrapping fiber 2 is made of aramid fiber.It is preferred that
, the short fine blending ratio with aramid fiber of carbon fiber is 1 in heart yarn：2.Carbon fiber staple length is 35-50mm.Aramid fiber is long
Degree is 80-100mm.The net that control of two-dimensional braided fasciated yarn 3 is formed by high-strength polyethylene strand outside heart yarn by control of two-dimensional braided machine
16 ingot fasciated yarns of shape structure.
In order to ensure that the intensity of control of two-dimensional braided fasciated yarn 3, high-strength polyethylene strand twist Split Down by high-strength polyethylene long filament
It forms.
The production method of above-mentioned high-strength vortex spinning yarn, includes the following steps：
The short fine and aramid fiber of carbon fiber after cutting is passed through griping cotton machine, cotton blender machine, opener, double cottons by step 1 successively
After case cotton feeder, lapper, carding machine, drawing frame and vortex flow spinner processing, heart yarn is made, mainly by opener process, clear
Cotton process, carding step, mixing in doubling step and air vortex spinning process.
Step 2, twisting Split Down is carried out to high-strength polyethylene long filament and high-strength polyethylene strand is made, then by heart yarn and high-strength
Polyethylene strand forms 16 ingot fasciated yarns outside heart yarn, yarn finished product is made by control of two-dimensional braided machine.
By above-mentioned specific embodiment, the beneficial effects of the invention are as follows：Present invention process advantages of simple, manufacturing cost is low,
The high-strength vortex spinning yarn of production, the covering yarn structure coordinated using heart yarn and control of two-dimensional braided fasciated yarn 3, heart yarn pass through vortex spinning
Technique is made, and has fibre compact degree good, uniform force, and tensile strength is high, and shock resistance is good；3 energy of control of two-dimensional braided fasciated yarn
Enough play the role of structural strengthening, further promoted the present invention intensity, while aramid fiber prevent control of two-dimensional braided fasciated yarn 3 with
Occur sliding between heart yarn to wriggle, improves bond strength, promote anti-cutting performance.
The foregoing description of the disclosed embodiments enables those skilled in the art to implement or use the present invention.
Various modifications to these embodiments will be apparent to those skilled in the art, as defined herein
General Principle can be realized in other embodiments without departing from the spirit or scope of the present invention.Therefore, of the invention
It is not intended to be limited to the embodiments shown herein, and is to fit to and the principles and novel features disclosed herein phase one
The widest range caused.
Claims (6)
1. a kind of high-strength vortex spinning yarn, which is characterized in that including heart yarn and control of two-dimensional braided fasciated yarn；The heart yarn includes center
Harness and outer wrapping fiber；The heart yarn is made of vortex blended weave, and the outer wrapping fiber spiral winding is coated on the center
Outside harness；The centred beam is made of parallel without twisting harness the short fibre of carbon fiber；The outer wrapping fiber is by aramid fiber structure
At；The netted knot that the control of two-dimensional braided fasciated yarn is formed by high-strength polyethylene strand outside the heart yarn by control of two-dimensional braided machine
16 ingot fasciated yarns of structure.
2. high-strength vortex spinning yarn according to claim 1, which is characterized in that the high-strength polyethylene strand is by high-strength poly-
The twisting Split Down of ethylene long filament forms.
3. high-strength vortex spinning yarn according to claim 2, which is characterized in that carbon fiber described in the heart yarn it is short it is fine with
The blending ratio of the aramid fiber is 1：2.
4. high-strength vortex spinning yarn according to claim 3, which is characterized in that the carbon fiber staple length is 35-
50mm。
5. high-strength vortex spinning yarn according to claim 4, which is characterized in that the aramid fiber length is 80-
100mm。
6. a kind of production method of high-strength vortex spinning yarn, which is characterized in that include the following steps：
Step 1, by the carbon fiber after cutting is short fine and aramid fiber pass through successively griping cotton machine, cotton blender machine, opener, double hopper to
After cotton machine, lapper, carding machine, drawing frame and vortex flow spinner processing, heart yarn is made；
Step 2, twisting Split Down is carried out to high-strength polyethylene long filament and high-strength polyethylene strand is made, then by the heart yarn and high-strength
Polyethylene strand forms 16 ingot fasciated yarns outside the heart yarn, yarn finished product is made by control of two-dimensional braided machine.