CN203007533U

CN203007533U - Flax blending composite fasciated yarn used for knitting

Info

Publication number: CN203007533U
Application number: CN 201220718329
Authority: CN
Inventors: 吴凌; 陈慰来; 易定红
Original assignee: ZHEJIANG DUNNU UNITED INDUSTRIAL Co Ltd
Current assignee: ZHEJIANG DUNNU UNITED INDUSTRIAL Co Ltd
Priority date: 2012-12-24
Filing date: 2012-12-24
Publication date: 2013-06-19
Anticipated expiration: 2022-12-24

Abstract

The utility model discloses a flax blending composite fasciated yarn used for knitting. The flax blending composite fasciated yarn comprises a core yarn (1) and two fasciated yarns(2,3), the two fasciated yarns are respectively and spirally wound on the core yarn (1) in S and Z twisting directions, the fasciated yarns (2,3) are dyeable filaments, and the fineness ratio of the core yarn (1) and the fasciated yarns (2,3) is 3:1-4:1. The flax blending composite fasciated yarn used for knitting is stable in twist, less in yarn hair, fine in color and high in strength, and has proper elasticity.

Description

Knitting with the compound wrapped yarn of flax blending

Technical field

The utility model relates to a kind of compound wrapped yarn, and concrete relating to is a kind of knitting with the compound wrapped yarn of flax blending.

Background technology

Flax has the characteristics such as natural gas permeability, hygroscopicity, salubrious property, hydrofuge and antibacterial bacteriostatic, is the at first textile raw material of environmental protection, and particularly summer, product was liked by consumers in general deeply its series of products.At present, conventional linen yarn is when braiding, and end breakage rate is high, generally is only applicable to woven braiding, has had a strong impact on its scope of application and purposes.The CN200710066826.8 patent discloses a kind of manufacture craft of flax blended spinning, and it is mainly set about from blended weave, though can improve the bar evenness of yarn, can not reduce the surface hairiness of linen yarn.The CN201010269608.6 patent discloses a kind of production method of flax blended knitting yarns, and the twist of the flax blended spinning that the method is produced can not be firm, and can not improve the brute force of yarn, and yarn color is more dull, and the gained appearance of fabrics is abundant not.

The utility model content

In order to solve the above-mentioned technical problem that exists in prior art, the purpose of this utility model is on the basis of flax blended spinning, provides that a kind of twist is stable, filoplume is few, and color and luster is good, and is powerful high, has suitably flexible knitting with the compound wrapped yarn of flax.

This knitting compound wrapped yarn of flax blending of using is comprised of heart yarn and two wrapped yarns, and described wrapped yarn helical form is wrapped on described heart yarn, and is wrapped on described heart yarn according to s and z sth. made by twisting direction respectively.

Further, described wrapped yarn is for dyeing long filament.

Further, the fineness ratio of described heart yarn and wrapped yarn is 3:1-4:1.

knitting heart yarn with the compound wrapped yarn of flax of the present utility model is flax blending staple fibre yarn, its flax content is between 40% ~ 80%, this blending heart yarn is added with certain twist, then at two less long filaments of fineness of basic upper outside looping of blended yarn, when the compound wrapped yarn of flax that obtains has kept the characteristic of flax, yarn twist has obtained firmly, whole brute force increases, filoplume significantly reduces, reduced the end breakage rate of yarn in the knitting machine weaving process, adopt the outsourcing long filament of different color, can improve sodolin color unicity and gloss, improved the whole wearability of linen fabrics.

Description of drawings

Fig. 1 is knitting structural representation with the compound wrapped yarn of flax blending of the present utility model;

Fig. 2 is that this is knitting with the compound wrapped yarn manufacturing process flow diagram of flax blending.

The specific embodiment

The utility model is described in further detail below in conjunction with accompanying drawing.

As shown in Figure 1, of the present utility model knitting with the compound wrapped yarn of flax blending, formed by heart yarn 1 and wrapped yarn 2,3, wrapped yarn 2,3 helical forms are wrapped on heart yarn 1, above-mentioned wrapped yarn 2,3 is comprised of two stainable long filaments, two threads are twisted with the fingers direction according to s and z respectively and are wrapped on heart yarn 1, flax blending staple fibre yarn that heart yarn 1 is formed by flax and other fiber blends.

As shown in Figure 2, of the present utility modelly knittingly at first obtain flax blending short fiber heart yarn 1 with the compound wrapped yarn of flax blending, flax content remains in 40% ~ 80% scope, and namely yarn has the characteristic of flax, has again the shortcoming of having improved pure flax simultaneously; Then wrapped yarn 2,3 is carried out on looping heart yarn 1 in opposite direction according to sequencing, sth. made by twisting is twisted with the fingers to being respectively s and z, what the looping mode adopted is spiral looping method, requirement is looping fully, namely require heart yarn 1 and wrapped yarn 2,3 fineness ratio to be about 3:1-4:1, wrapped yarn 2,3 the looping twist are identical and less, and the looping speed of controlling two wrapped yarns is consistent, can obtain the compound wrapped yarn of flax as shown in Figure 1.Above-mentioned looping can be carried out on coating machine, wherein wrapped yarn 2,3 its raw materials can be selected the long filaments such as terylene, polyamide fibre polypropylene fibre, but terylene thread is better, and the sequencing of looping can be changed, the color of two threads can be the same or different, and obtains like this yarn color and luster various.

Shown in the above and figure is only preferred embodiment of the present utility model.Should be pointed out that for the person of ordinary skill of the art, under the prerequisite that does not break away from the utility model principle, can also make some modification and improvement, these also should be considered as belonging to protection domain of the present utility model.

Claims

One kind knitting with flax blending compound wrapped yarn, formed by heart yarn (1) and two wrapped yarns (2,3), it is characterized in that: described wrapped yarn (2,3) helical form is wrapped on described heart yarn (1), and is wrapped on described heart yarn (1) according to s and z sth. made by twisting direction respectively.
2. as claimed in claim 1 knitting with the compound wrapped yarn of flax blending, it is characterized in that: described wrapped yarn (2,3) is the long filament that can dye.
3. as claimed in claim 1 knitting with the compound wrapped yarn of flax blending, it is characterized in that: the fineness ratio of described heart yarn (1) and wrapped yarn (2,3) is 3:1-4:1.