CN101724944B - Wool acrylic composite yarn and spinning method thereof - Google Patents
Wool acrylic composite yarn and spinning method thereof Download PDFInfo
- Publication number
- CN101724944B CN101724944B CN200810225620XA CN200810225620A CN101724944B CN 101724944 B CN101724944 B CN 101724944B CN 200810225620X A CN200810225620X A CN 200810225620XA CN 200810225620 A CN200810225620 A CN 200810225620A CN 101724944 B CN101724944 B CN 101724944B
- Authority
- CN
- China
- Prior art keywords
- composite yarn
- acrylic fibers
- yarn
- twist
- nitrile
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The invention relates to a wool acrylic composite yarn and a spinning method thereof. The wool acrylic composite yarn contains the following components in percentage by weight: 50 percent of bright semi-bulky acrylic strips, 20 to 30 percent of woolen strips and 20 to 30 percent of acidic bulky acrylic strips. The invention also provides a spinning method of the wool acrylic composite yarn, comprising the following steps of: spinning the bright semi-bulky acrylic strips into an all-acrylic single yarn, spinning the woolen strips and the acidic bulky acrylic strips into a wool acrylic single yarn, and twisting the all-acrylic single yarn and the wool acrylic single yarn together into the wool acrylic composite yarn. Clothing spun by the wool acrylic composite yarn has good elasticity, rich color, good glossiness, softness and rich elasticity, and can generate an AB bright effect after being dyed.
Description
Technical field
The present invention relates to spinning technique, particularly a kind of mao of nitrile composite yarn and spinning method for genuine thereof.
Background technology
Hair nitrile blended yarn is the yarn product that at home and abroad sells well on the yarn consumption market in recent years.Hair nitrile blending product has kept soft, the elasticity foot of wool, the good characteristic that warmth retention property is good, the TENSILE STRENGTH of having brought into play acrylic fibers is good, ABRASION RESISTANCE is strong, anti-pilling, feltability, and the taking and the characteristics bright-colored, that cost is low that are better than wool fibre, be a kind of cheap and good-quality yarn product, liked by consumers in general.
Along with increasing substantially of development of market economy and living standards of the people, the consumer is also more and more higher to the requirement of dress ornament and textile product, particularly to the color and luster of product and the higher variation that also more becomes of requirement of texture.Develop new hair nitrile blended yarn kind and positive impetus is arranged satisfying consumer demand, adapt to market development and improving the business economic benefit.
Summary of the invention
The purpose of this invention is to provide the hair nitrile composite yarn that a kind of elasticity is strong, Color is good.
The invention provides a kind of mao of nitrile composite yarn, its contain following percentage by weight component: 50% has light half swollen acrylic fibers bar, 20～30% fertile wool top and 20～30% acid varicosity acrylic fibers bars.
Preferably, the present invention use shrinkage be 5～18% light half swollen acrylic fibers bar arranged.
Preferably, the present invention uses fiber number as 1.5D～3D light half swollen acrylic fibers bar to be arranged.
Preferably, to use number be 56 in the present invention
S～66
SFertile wool top.
Preferably, the present invention uses the acid varicosity acrylic fibers bar of fiber number as 2D～3D.
The AB yarn of hair nitrile composite yarn of the present invention for forming, one full nitrile single thread that light half swollen acrylic fibers bar spinning forms of serving as reasons wherein, another strand hair nitrile single thread that fertile wool top and acid varicosity acrylic fibers bar spinning form of serving as reasons by two strands of yarns spinning.
The present invention also provides a kind of method that spins above-mentioned hair nitrile composite yarn, and the technological process of this method is as follows:
(1) light half swollen acrylic fibers bar is arranged by following flow process by formula rate: silver mixing, scalp acupuncture, two pins, three pins, four pins, rove, spun yarn and twisting are spun into number and are 1/30N, the twist and be 350T/m and sth. made by twisting to being the full nitrile single thread of Z;
(2) by the fertile wool top of formula rate and acid varicosity acrylic fibers bar by following flow process: silver mixing, scalp acupuncture, two pins, three pins, four pins, rove, spun yarn and twisting, being spun into number is that 1/30.5N, the twist are 410T/m and twist with the fingers to the hair nitrile single thread for Z;
(3) with the hair nitrile single thread of the full nitrile single thread of step (1) gained and step (2) gained and close and twist, to be spun into the twist be 225T/m, twist with the fingers to being the hair nitrile composite yarn of 2/29N for S and number.
Hair nitrile composite yarn of the present invention is formed by two or more raw material blending, and be the AB yarn, so after the dyed processing, can produce bright effect of AB, the light half swollen acrylic fibers that have wherein make the glossiness of this yarn very desirable simultaneously, can make this yarn have better Color and add acid varicosity acrylic fibers.In addition and since adopted the shrinkage of proper proportion be 5～18% light half swollen acrylic fibers bar arranged, make hair nitrile composite yarn of the present invention have better elastic.Therefore, good by ready-made clothes rich color, the glossiness of hair nitrile composite yarn of the present invention spinning, and soft and high resilience.
The specific embodiment
Following examples are used to illustrate the present invention, but are not used for limiting the scope of the invention.
Embodiment 1
Raw material: 50% shrinkage is that 5% 2D has light half swollen acrylic fibers bar, 25% 60
SFertile wool top, the acid varicosity acrylic bar (aforementioned proportion is weight percentage) of 50% 3D.
Manufacture flow process:
(1) 2D of formula rate is had light half swollen acrylic fibers by following flow process: B412 gilling machine, B423 pin are dredged machine, B432 pin and are dredged that machine, B442 pin are dredged machine, the B452 pin is dredged machine, FB441 Speed frames, B583 fine spining machine and VTS-08 two-for-one twister, are spun into number and are 1/30N, the twist and be 350T/m and sth. made by twisting to being the full nitrile single thread of Z.
(2) with 60 of formula rate
SThe acid varicosity acrylic fibers of fertile hair and 3D are by following flow process: B412 gilling machine, B423 pin are dredged machine, B432 pin and are dredged that machine, B442 pin are dredged machine, the B452 pin is dredged machine, FB441 Speed frames, B583 fine spining machine and VTS-08 two-for-one twister, and being spun into number is that 1/30.5N, the twist are 410T/m and twist with the fingers to mao nitrile single thread that is Z.
(3) full nitrile single thread that will obtain through above-mentioned steps and hair nitrile single thread be by the AC238 bobbin winder and close and twist, and to be spun into the twist be 225T/m, twist with the fingers to being the hair nitrile composite yarn of 2/29N for S and number.
After testing, the size variation of this mao nitrile composite yarn is 1.2～1.8%, and fracture strength is 300～380N/10m, and the twist irregularity rate is 6～8%.
After this mao nitrile composite yarn spinning ready-made clothes and dyed processing, the ready-made clothes color is abundant and glossiness is good, softness and high resilience.
Embodiment 2
Raw material: 50% shrinkage is that 10% 1.5D has light half swollen acrylic fibers bar, 20% 56
SFertile wool top, the acid varicosity acrylic bar (aforementioned proportion is weight percentage) of 30% 2D.
Manufacture flow process with embodiment 1.
After testing, the size variation of this mao nitrile composite yarn is 1.2～1.8%, and fracture strength is 350～400N/10m, and the twist irregularity rate is 6～8%.
After this mao nitrile composite yarn spinning ready-made clothes and dyed processing, the ready-made clothes color is abundant and glossiness is good, softness and high resilience.
Embodiment 3
Raw material: 50% shrinkage is that 18% 3D has light half swollen acrylic fibers bar, 30% 66
SFertile wool top, the acid varicosity acrylic bar (aforementioned proportion is weight percentage) of 20% 3D.
Manufacture flow process with embodiment 1.
After testing, the size variation of this mao nitrile composite yarn is 1.2～1.8%, and fracture strength is 280～350N/10m, and the twist irregularity rate is 6～8%.
After this mao nitrile composite yarn spinning ready-made clothes and dyed processing, the ready-made clothes color is abundant and glossiness is good, softness and high resilience.
Claims (5)
1. hair nitrile composite yarn, its contain following percentage by weight component: 50% has light half swollen acrylic fibers bar, 20～30% fertile wool top and 20～30% acid varicosity acrylic fibers bars; The described shrinkage that light half swollen acrylic fibers bar arranged is 5～18%, fiber number is 1.5D～3D.
2. hair nitrile composite yarn as claimed in claim 1 is characterized in that described fertile wool top is that number is 56
S～66
SFertile wool top.
3. hair nitrile composite yarn as claimed in claim 1 is characterized in that described acid varicosity acrylic fibers bar is that fiber number is the acid varicosity acrylic fibers bar of 2D～3D.
4. as each described hair nitrile composite yarn of claim 1～3, it is two strands of AB yarns that the yarn spinning forms, one full nitrile single thread that light half swollen acrylic fibers bar spinning forms of serving as reasons wherein, another strand hair nitrile single thread that fertile wool top and acid varicosity acrylic fibers bar spinning form of serving as reasons.
5. the method for each described hair nitrile composite yarn of spinning such as claim 1～4, its step is as follows:
(1) light half swollen acrylic fibers bar is arranged by following flow process by formula rate: silver mixing, scalp acupuncture, two pins, three pins, four pins, rove, spun yarn and twisting are spun into number and are 1/30N, the twist and be 350T/m and sth. made by twisting to being the full nitrile single thread of Z;
(2) by the fertile wool top of formula rate and acid varicosity acrylic fibers bar by following flow process: silver mixing, scalp acupuncture, two pins, three pins, four pins, rove, spun yarn and twisting, being spun into number is that 1/30.5N, the twist are 410T/m and twist with the fingers to the hair nitrile single thread for Z;
(3) with the hair nitrile single thread of the full nitrile single thread of step (1) gained and step (2) gained and close and twist, to be spun into the twist be 225T/m, twist with the fingers to being the hair nitrile composite yarn of 2/29N for S and number.