CN107881615A - A kind of vortex spinning compound core-spun yarn and its production method - Google Patents
A kind of vortex spinning compound core-spun yarn and its production method Download PDFInfo
- Publication number
- CN107881615A CN107881615A CN201711395759.4A CN201711395759A CN107881615A CN 107881615 A CN107881615 A CN 107881615A CN 201711395759 A CN201711395759 A CN 201711395759A CN 107881615 A CN107881615 A CN 107881615A
- Authority
- CN
- China
- Prior art keywords
- core
- fibre
- wire
- spun yarn
- tencel
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses vortex spinning compound core-spun yarn and its production method.The composite yarn, including yarn body；Yarn body includes core and clad；Core includes wire arranged in parallel；Clad spiral surrounding is coated on outside core；Clad includes wrapper fibre and parallel non-twist core fibre；Parallel non-twist core fibre is located at the inner side of wrapper fibre；Wrapper fibre is mixed with parallel non-twist core fibre by tencel and ultra-fine denier modal.Simple production process of the present invention, the compound core-spun yarn of manufacture has conductive effect good, resistivity is low, the characteristics of intensity is high, not easy to break is drawn high, tencel can improve the smooth and gloss of yarn, make wire surface not easy to wear, fabric, which is made, has silk texture, and fine denier modal can increase the pliability of fabric and excellent personal wearability, while tencel and fine denier modal can play good insulating effect.
Description
Technical field
The present invention relates to vortex field of textiles, more particularly to a kind of vortex spinning compound core-spun yarn and its production method.
Background technology
Vortex spinning grows up on the basis of Air-Jet Spinning, using fixed vortex spinning spool, to replace height
A kind of spinning method that the rotor of speed revolution is spinned.Air injection air vortex spinning using the rotation of air make long fibre to
The center of yarn is gathered, and short-term dimension is scattered to be coated on outer layer.This unique production method can not only produce covering yarn, and
The yarn of the production dual structure such as different fibre length, degree of shrinkage can be utilized, colourful outstanding yarn can be spun, there is hair
The characteristics of plumage is few, and density is high, refreshing perception is good, and washing fastness is good, moisture retention and bulkiness are good.
Intelligent clothing is by among electronic product involvement clothes, and the function of set electron device and the comfortableness of textile are in one
Body, it is wearable device " ultimate form ", in physiological characteristic detection, health control, life auxiliary, physical culture, amusement and military affairs
There is extensive and important application prospect Deng field.Fabric conducting wire connects each primary electron function element, is intelligence
The important component of energy clothes.Fabric conducting wire need to possess electrical conductivity height, mechanical property is good, reliability is high, light, man-machine
The features such as friendly.At present, the method for preparing fabric conducting wire mainly has 2 kinds：First, utilize sputtering, chemical vapor deposition, electricity
The methods of plating, silk-screen printing, inkjet printing, deposits conductive material, the conductor wire Louis obtained using this kind of method in fabric face
Peel off, brittleness is high, it usually needs road encapsulation makes manufactured conductive fabric gas permeability and extension to improve its mechanical property after progress
Property decline；Second, by conductive yarn using embroidery, loop bonding, it is woven, knitting the methods of be implanted into fabric in form conducting wire, this
Conductive fabric made from kind method has the advantages that gas permeability is good with durability.By wire (such as stainless steel wire, copper wire) profit
It is implanted into aforementioned manners in fabric, obtained conducting wire has higher electrical conductivity and excellent mechanical property, but shortcoming is
The conductive fabric of formation has a hard sense, and comfortableness is poor.
The content of the invention
In order to solve the above technical problems, the invention provides a kind of vortex spinning compound core-spun yarn and its production method, with
Wire using Technology of Air Vortex Spinning, is made composite yarn, solves existing conductive fabric and hard sense be present, relax as core
The problem of adaptive is poor.
To reach above-mentioned purpose, technical scheme is as follows：A kind of vortex spinning compound core-spun yarn, including yarn sheet
Body；The yarn body includes core and clad；The core includes wire arranged in parallel；The clad spiral shell
Rotation surround and is coated on outside the core；The clad includes wrapper fibre and parallel non-twist core fibre；It is described parallel non-twist
Core fibre is located at the inner side of the wrapper fibre；The wrapper fibre is with parallel non-twist core fibre by tencel and ultra-fine denier modal
Mix.
As a preferred embodiment of the present invention, the wire is filamentary silver, a diameter of 25-40 μm of the wire.
As a preferred embodiment of the present invention, polyurethane coating, the polyurethane are externally coated with the wire
The thickness of coating is 1-2 μm.
As a preferred embodiment of the present invention, the clad is by 50%A100 tencels and 50% ultra-fine denier modal system
Into.
As a preferred embodiment of the present invention, a diameter of 150-200 μm of the yarn body.
A kind of production method of vortex spinning compound core-spun yarn, comprises the following steps：
Step 1, pre-treatment is carried out to tencel and ultra-fine denier modal；Opening or cleaning is carried out successively to tencel and ultra-fine denier modal
Cotton process, carding step and mixing in doubling step processing；
Step 2, pre-treatment is carried out to wire；Polyurethane adhesive is heated to 60-80 DEG C, is then in wire and stretches
State, by cool drying under normal temperature, making polyurethane adhesive be evenly coated at wire surface from polyurethane adhesive；
Step 3, the guide body center at nozzle entrance is passed through using DHU-P02 types spray painting vortex spinning machine, wire
Core filaments guiding through hole enter in vortex tube, and tencel and super fine denier Modal fibre beam enter nozzle by nozzle entrance, press
Contracting air is injected in vortex tube at a high speed along spray orifice, and high speed swirling eddy is formed in vortex tube, envionmental humidity 65%, is spun
Yarn speed 300m/min, 262 times of total draft, 35 times of dominant draft, spindle diameter 1.1mm, tension force 120mN.
Pass through above-mentioned technical proposal, the beneficial effect of technical solution of the present invention are：Simple production process of the present invention, manufacture
Compound core-spun yarn has conductive effect good, and resistivity is low, draw high intensity height, it is not easy to break the characteristics of, tencel can improve yarn
Smooth and gloss, make wire surface not easy to wear, fabric, which is made, has silk texture, and fine denier modal can increase fabric
Pliability and excellent personal wearability, while tencel and fine denier modal can play good insulating effect.
Brief description of the drawings
In order to illustrate more clearly about the embodiment of the present invention or technical scheme of the prior art, below will be to embodiment or existing
There is the required accompanying drawing used in technology description to be briefly described, it should be apparent that, drawings in the following description are only this
Some embodiments of invention, for those of ordinary skill in the art, on the premise of not paying creative work, can be with
Other accompanying drawings are obtained according to these accompanying drawings.
Fig. 1 is the structural representation of the present invention.
Corresponding component title of the numeral represented by with letter in figure：
1. the parallel non-twist wrapper fibre of core fibre 3. of core 2..
Embodiment
Below in conjunction with the accompanying drawing in the embodiment of the present invention, the technical scheme in the embodiment of the present invention is carried out clear, complete
Site preparation describes, it is clear that described embodiment is only part of the embodiment of the present invention, rather than whole embodiments.It is based on
Embodiment in the present invention, those of ordinary skill in the art are obtained every other under the premise of creative work is not made
Embodiment, belong to the scope of protection of the invention.
Embodiment
With reference to Fig. 1, the invention discloses a kind of vortex spinning compound core-spun yarn, including yarn body；The yarn body
Including core and clad；The core includes wire arranged in parallel；The clad spiral surrounding is coated on institute
State outside core；The clad includes wrapper fibre and parallel non-twist core fibre；The parallel non-twist core fibre is positioned at described
The inner side of wrapper fibre；The wrapper fibre is mixed with parallel non-twist core fibre by tencel and ultra-fine denier modal.
A diameter of 150-200 μm of the yarn body.The wire is filamentary silver, a diameter of 25- of the wire
40μm.Polyurethane coating is externally coated with the wire, the thickness of the polyurethane coating is 1-2 μm.
In order to optimize the structure of clad, the clad is made up of 50%A100 tencels and 50% ultra-fine denier modal.
A kind of production method of vortex spinning compound core-spun yarn, comprises the following steps：
Step 1, pre-treatment is carried out to tencel and ultra-fine denier modal；Opening or cleaning is carried out successively to tencel and ultra-fine denier modal
Cotton process, carding step and mixing in doubling step processing；
Step 2, pre-treatment is carried out to wire；Polyurethane adhesive is heated to 60-80 DEG C, is then in wire and stretches
State, by cool drying under normal temperature, making polyurethane adhesive be evenly coated at wire surface from polyurethane adhesive；
Step 3, the guide body center at nozzle entrance is passed through using DHU-P02 types spray painting vortex spinning machine, wire
Core filaments guiding through hole enter in vortex tube, and tencel and super fine denier Modal fibre beam enter nozzle by nozzle entrance, press
Contracting air is injected in vortex tube at a high speed along spray orifice, and high speed swirling eddy is formed in vortex tube, envionmental humidity 65%, is spun
Yarn speed 300m/min, 262 times of total draft, 35 times of dominant draft, spindle diameter 1.1mm, tension force 120mN.
By above-mentioned specific embodiment, the beneficial effects of the invention are as follows：Simple production process of the present invention, the compound bag of manufacture
Heart yarn line has conductive effect good, and resistivity is low, draw high intensity height, it is not easy to break the characteristics of, tencel can improve the smooth of yarn
With gloss, make wire surface not easy to wear, fabric, which is made, has silk texture, and fine denier modal can increase the pliability of fabric
With excellent personal wearability, while tencel and fine denier modal can play good insulating effect.
The foregoing description of the disclosed embodiments, professional and technical personnel in the field are enable to realize or using the present invention.
A variety of modifications to these embodiments will be apparent for those skilled in the art, as defined herein
General Principle can be realized in other embodiments without departing from the spirit or scope of the present invention.Therefore, it is of the invention
The embodiments shown herein is not intended to be limited to, and is to fit to and principles disclosed herein and features of novelty phase one
The most wide scope caused.
Claims (6)
1. a kind of vortex spinning compound core-spun yarn, it is characterised in that including yarn body；The yarn body includes core and bag
Coating；The core includes wire arranged in parallel；The clad spiral surrounding is coated on outside the core；Institute
Stating clad includes wrapper fibre and parallel non-twist core fibre；The parallel non-twist core fibre is located at the interior of the wrapper fibre
Side；The wrapper fibre is mixed with parallel non-twist core fibre by tencel and ultra-fine denier modal.
2. vortex spinning compound core-spun yarn according to claim 1, it is characterised in that the wire is filamentary silver, described
A diameter of 25-40 μm of wire.
3. vortex spinning compound core-spun yarn according to claim 2, it is characterised in that be externally coated with the wire
Polyurethane coating, the thickness of the polyurethane coating is 1-2 μm.
4. vortex spinning compound core-spun yarn according to claim 3, it is characterised in that the clad was by 50%A100 days
Silk and 50% ultra-fine denier modal are made.
5. vortex spinning compound core-spun yarn according to claim 3, it is characterised in that the yarn body it is a diameter of
150-200μm。
6. a kind of production method of vortex spinning compound core-spun yarn, it is characterised in that comprise the following steps：
Step 1, pre-treatment is carried out to tencel and ultra-fine denier modal；Opening picking work is carried out successively to tencel and ultra-fine denier modal
Sequence, carding step and mixing in doubling step processing；
Step 2, pre-treatment is carried out to wire；Polyurethane adhesive is heated to 60-80 DEG C, is then in wire and stretches shape
State, by cool drying under normal temperature, making polyurethane adhesive be evenly coated at wire surface from polyurethane adhesive；
Step 3, using DHU-P02 types spray painting vortex spinning machine, the core that wire passes through the guide body center at nozzle entrance
Silk guiding through hole enters in vortex tube, and tencel and super fine denier Modal fibre beam enter nozzle by nozzle entrance, and compression is empty
Gas is injected in vortex tube at a high speed along spray orifice, and high speed swirling eddy, envionmental humidity 65%, spinning speed are formed in vortex tube
Spend 300m/min, 262 times of total draft, 35 times of dominant draft, spindle diameter 1.1mm, tension force 120mN.