CN108485348A - 一种建筑内墙用强力乳胶漆及其制备方法 - Google Patents

一种建筑内墙用强力乳胶漆及其制备方法 Download PDF

Info

Publication number
CN108485348A
CN108485348A CN201810290063.3A CN201810290063A CN108485348A CN 108485348 A CN108485348 A CN 108485348A CN 201810290063 A CN201810290063 A CN 201810290063A CN 108485348 A CN108485348 A CN 108485348A
Authority
CN
China
Prior art keywords
parts
emulsion paint
wall
agent
emulsion
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201810290063.3A
Other languages
English (en)
Inventor
不公告发明人
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CN201810290063.3A priority Critical patent/CN108485348A/zh
Publication of CN108485348A publication Critical patent/CN108485348A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种建筑内墙用强力乳胶漆，所述建筑内墙用强力乳胶漆的配方如下：钛白粉30‑40份、增粘树脂乳液10‑20份、超细二氧化硅2‑7份、杀菌剂1‑5份、润湿分散剂1‑3份、消泡剂2‑4份、增稠剂3‑5份、稳定剂4‑8份、触变剂2‑5份、防腐剂6‑8份、颜料1‑5份，本发明以钛白粉为原料，不仅成本低廉而且防水性好，在加入增粘树脂乳液可以保证该乳胶漆的粘贴强度，具有良好的耐高温性和耐侵蚀性能，增强乳胶漆的粘结强度以及提高乳胶漆的抗热震性能，颜料可以形成遮光层，有效的降低基料用量，保证涂膜的光泽，防腐剂和杀菌剂配合可以抑制微生物的生长和繁殖，以延长乳胶漆的保存时间，适合推广和普及。

Description

一种建筑内墙用强力乳胶漆及其制备方法
技术领域
本发明属于建筑技术领域，更具体地说，尤其涉及一种建筑内墙用强力乳胶漆。同时，本发明还涉及一种建筑内墙用强力乳胶漆的制备方法。
背景技术
乳胶漆，乳胶涂料的俗称，是以丙烯酸酯共聚乳液为代表的一大类合成树脂乳液涂料。乳胶漆是水分散性涂料，它是以合成树脂乳液为基料，填料经过研磨分散后加入各种助剂精制而成的涂料。
乳胶漆具备了与传统墙面涂料不同的众多优点，如易于涂刷、干燥迅速、漆膜耐水、耐擦洗性好等。在我国，人们习惯上把合成树脂乳液为基料，以水为分散介质，加入颜料、填料(亦称体质颜料)和助剂，经一定工艺过程制成的涂料；但是传统的乳胶漆不具有抑菌、低温远红外和防静电性能。如当其用在室内装饰时，易在潮湿区域滋生细菌且无低温远红外功能。并且传统乳胶漆的耐冻融性、耐天候老化性和粘结性较差，为此，现有的乳胶漆还有待提高。
发明内容
本发明的目的是为了解决现有技术中存在的缺点，结构设计简单合理，制造成本低，节能环保，防火防水性好，杀菌抗腐蚀抗老化能力强，使用方便粘结性高，适用范围广，有利于推广和普及，而提出的一种建筑内墙用强力乳胶漆。
为实现上述目的，本发明提供如下技术方案：一种建筑内墙用强力乳胶漆，所述建筑内墙用强力乳胶漆的配方如下：钛白粉30-40份、增粘树脂乳液10-20份、超细二氧化硅2-7份、杀菌剂1-5份、润湿分散剂1-3份、消泡剂2-4份、增稠剂3-5份、稳定剂4-8份、触变剂2-5份、防腐剂6-8份、颜料1-5份。
优选的，所述增粘树脂乳液为改性松香树脂乳液、萜稀树脂乳液、乙烯醋酸乙烯酯乳液、氯乙烯偏二氯乙烯乳液、醋酸乙烯酯叔碳酸酯乳液、丙烯酸酯乳液和丙烯酸树脂共聚物乳液中的一种或几种的混合物。
优选的，所述所述颜料为碳酸钙、硅酸铝或者硫酸钡中的一种或多种。
优选的，所述所述润湿剂为包括乙醇、乙二醇剂、有机硅润湿剂、大豆软磷脂润湿剂、硫醇类润湿剂、酰肼类润湿剂或聚氧化乙烯烷化醚类润湿剂中的任意一种或至少二种的混合物，消泡剂为消泡剂包括乳化硅油、高碳醇脂肪酸酯复合物、聚氧乙烯聚氧丙烯季戊四醇醚、聚氧乙烯聚氧丙醇胺醚、聚氧丙烯甘油醚、聚氧丙烯聚氧乙烯甘油醚或聚二甲基硅氧烷中的任意一种或至少二种的混合物，增稠剂包括碱溶胀型增稠剂、缔合型增稠剂或纤维素类增稠剂中的任意一种或至少二种的混合物。
优选的，所述所述稳定剂为氧化锌或者氧化镁，触变剂为膨润土或者硅酸铝，防腐剂为亚硝酸盐或者二氧化硫。
本发明还提供一种建筑内墙用强力乳胶漆的制备方法，包括如下步骤：
S1、把钛白粉单体混合放入反应釜内，然后加入增粘树脂乳液在85℃～95℃的条件下搅拌3-4h然后自然冷却；
S2、当反应釜内温度冷却到25℃～35℃的时候取样检测乳化反应是否充分，合格之后在往反应釜内添加增稠剂、稳定剂和防腐剂加热至80℃～100℃并搅拌15-25min；
S3、用高速分散研磨机内分别把颜料和超细二氧化硅依次充分研磨，然后把研磨后的颜料和超细二氧化硅与润湿分散剂一起加入反应釜内搅拌，并控制反应釜的温度在30℃～50℃；
S4、最后在反应釜内加入杀菌剂、触变剂和消泡剂搅拌2-3min，然后冷却至10℃～20℃抽样检测；
S5、检测合格用过滤器过滤然后包装入库，在成品外售之前在进行最后一步的出厂检测。
优选的，所述反应釜内搅拌机的转速为6000-8000rpm/min。
优选的，所述过滤器的过滤方式为压滤，且过滤器的进料端设有加料罐。
本发明的技术效果和优点：本发明提供的一种建筑内墙用强力乳胶漆，与传统的乳胶漆相比，本发明以钛白粉为原料，不仅成本低廉而且防水性好，在加入增粘树脂乳液可以保证该乳胶漆的粘贴强度，具有良好的耐高温性和耐侵蚀性能，增强乳胶漆的粘结强度以及提高乳胶漆的抗热震性能，颜料可以形成遮光层，有效的降低基料用量，保证涂膜的光泽，防腐剂和杀菌剂配合可以抑制微生物的生长和繁殖，以延长乳胶漆的保存时间；本发明提供的一种建筑内墙用强力乳胶漆的制备方法，通过反应釜把各种原料之间进行混合，不仅省时省力，而且便于控制，提高制备的准确度，同时两次抽样检测可以保证乳胶漆的质量，该发明操作方便，制备周期短，省时省力，便于调节，精确度高，保证产品质量，适用范围广，有利于推广和普及。
具体实施方式
为了使本发明的目的、技术方案及优点更加清楚明白，以下结合具体实施例，对本发明进行进一步详细说明。应当理解，此处所描述的具体实施例仅仅用以解释本发明，并不用于限定本发明。基于本发明中的实施例，本领域普通技术人员在没有做出创造性劳动前提下所获得的所有其他实施例，都属于本发明保护的范围。
实施例1
一种建筑内墙用强力乳胶漆，所述建筑内墙用强力乳胶漆的配方如下：钛白粉30份、改性松香树脂乳液10份、碳酸钙2份、二氧化硅1份、乙醇1份、醋酸丁酯2份、羟乙基纤维素3份、氧化锌4份、膨润土2份、亚硝酸盐6份。
本发明还提供一种建筑内墙用强力乳胶漆的制备方法，包括如下步骤：
S1、把钛白粉单体混合放入反应釜内，然后加入改性松香树脂乳液在85℃的条件下搅拌3h然后自然冷却，反应釜内搅拌机的转速为6000rpm/min；
S2、当反应釜内温度冷却到25℃的时候取样检测乳化反应是否充分，合格之后在往反应釜内添加羟乙基纤维素、氧化锌和亚硝酸盐加热至80℃并搅拌15min；
S3、用高速分散研磨机内分别把碳酸钙和超细二氧化硅依次充分研磨，然后把研磨后的碳酸钙和超细二氧化硅与乙醇一起加入反应釜内搅拌，并控制反应釜的温度在30℃；
S4、最后在反应釜内加入膨润土、杀菌剂和醋酸丁酯搅拌2min，然后冷却至10℃抽样检测；
S5、检测合格用过滤器过滤然后包装入库，在成品外售之前在进行最后一步的出厂检测，过滤器的过滤方式为压滤，且过滤器的进料端设有加料罐。
实施例2
一种建筑内墙用强力乳胶漆，所述建筑内墙用强力乳胶漆的配方如下：钛白粉35份、乙烯醋酸乙烯酯乳液15份、硅酸铝4份、二氧化硅3份、乙醇2份、醋酸丁酯3份、羟乙基纤维素4份、氧化锌6份、膨润土3份、亚硝酸盐7份。
本发明还提供一种建筑内墙用强力乳胶漆的制备方法，包括如下步骤：
S1、钛白粉单体混合放入反应釜内，然后加入乙烯醋酸乙烯酯乳液在90℃的条件下搅拌3.5h然后自然冷却，反应釜内搅拌机的转速为7000rpm/min；
S2、当反应釜内温度冷却到30℃的时候取样检测乳化反应是否充分，合格之后在往反应釜内添加羟乙基纤维素、氧化锌和亚硝酸盐加热至90℃并搅拌20min；
S3、用高速分散研磨机内分别把硅酸铝和超细二氧化硅依次充分研磨，然后把研磨后的硅酸铝和超细二氧化硅与乙醇一起加入反应釜内搅拌，并控制反应釜的温度在40℃；
S4、最后在反应釜内加入膨润土、杀菌剂和醋酸丁酯搅拌2.5min，然后冷却至15℃抽样检测；
S5、检测合格用过滤器过滤然后包装入库，在成品外售之前在进行最后一步的出厂检测，过滤器的过滤方式为压滤，且过滤器的进料端设有加料罐。
实施例3
一种建筑内墙用强力乳胶漆，所述建筑内墙用强力乳胶漆的配方如下：钛白粉40份、萜稀树脂乳液20份、硫酸钡7份、钛白粉5份、乙二醇3份、玉米油4份、水溶性的聚丙烯酸盐5份、氧化镁8份、硅酸铝5份、二氧化硫8份。
本发明还提供一种建筑内墙用强力乳胶漆的制备方法，包括如下步骤：
S1、把钛白粉单体混合放入反应釜内，然后加入萜稀树脂乳液在895℃的条件下搅拌4h然后自然冷却，反应釜内搅拌机的转速为8000rpm/min；
S2、当反应釜内温度冷却到35℃的时候取样检测乳化反应是否充分，合格之后在往反应釜内添加水溶性的聚丙烯酸盐、氧化镁和二氧化硫加热至100℃并搅拌25min；
S3、用高速分散研磨机内分别把硫酸钡和超细二氧化硅依次充分研磨，然后把研磨后的硫酸钡与乙二醇一起加入反应釜内搅拌，并控制反应釜的温度在50℃；
S4、最后在反应釜内加入硅酸铝、杀菌剂和玉米油搅拌3min，然后冷却至20℃抽样检测；
S5、检测合格用过滤器过滤然后包装入库，在成品外售之前在进行最后一步的出厂检测，过滤器的过滤方式为压滤，且过滤器的进料端设有加料罐。
综上所述：本发明提供的一种建筑内墙用强力乳胶漆，与传统的乳胶漆相比，本发明以钛白粉为原料，不仅成本低廉而且防水性好，在加入增粘树脂乳液可以保证该乳胶漆的粘贴强度，具有良好的耐高温性和耐侵蚀性能，增强乳胶漆的粘结强度以及提高乳胶漆的抗热震性能，颜料可以形成遮光层，有效的降低基料用量，保证涂膜的光泽，防腐剂和杀菌剂配合可以抑制微生物的生长和繁殖，以延长乳胶漆的保存时间；本发明提供的一种建筑内墙用强力乳胶漆的制备方法，通过反应釜把各种原料之间进行混合，不仅省时省力，而且便于控制，提高制备的准确度，同时两次抽样检测可以保证乳胶漆的质量，该发明操作方便，制备周期短，省时省力，便于调节，精确度高，保证产品质量，适用范围广，有利于推广和普及。
最后应说明的是：以上所述仅为本发明的优选实施例而已，并不用于限制本发明，尽管参照前述实施例对本发明进行了详细的说明，对于本领域的技术人员来说，其依然可以对前述各实施例所记载的技术方案进行修改，或者对其中部分技术特征进行等同替换,凡在本发明的精神和原则之内，所作的任何修改、等同替换、改进等，均应包含在本发明的保护范围之内。

Claims (8)

1.一种建筑内墙用强力乳胶漆，其特征在于：所述建筑内墙用强力乳胶漆的配方如下：钛白粉30-40份、增粘树脂乳液10-20份、超细二氧化硅2-7份、杀菌剂1-5份、润湿分散剂1-3份、消泡剂2-4份、增稠剂3-5份、稳定剂4-8份、触变剂2-5份、防腐剂6-8份、颜料1-5份。
2.根据权利要求1所述的一种建筑内墙用强力乳胶漆，其特征在于：所述增粘树脂乳液为改性松香树脂乳液、萜稀树脂乳液、乙烯醋酸乙烯酯乳液、氯乙烯偏二氯乙烯乳液、醋酸乙烯酯叔碳酸酯乳液、丙烯酸酯乳液和丙烯酸树脂共聚物乳液中的一种或几种的混合物。
3.根据权利要求1所述的一种建筑内墙用强力乳胶漆，其特征在于：所述颜料为碳酸钙、硅酸铝或者硫酸钡中的一种或多种。
4.根据权利要求1所述的一种建筑内墙用强力乳胶漆，其特征在于：所述润湿剂为包括乙醇、乙二醇剂、有机硅润湿剂、大豆软磷脂润湿剂、硫醇类润湿剂、酰肼类润湿剂或聚氧化乙烯烷化醚类润湿剂中的任意一种或至少二种的混合物，消泡剂为消泡剂包括乳化硅油、高碳醇脂肪酸酯复合物、聚氧乙烯聚氧丙烯季戊四醇醚、聚氧乙烯聚氧丙醇胺醚、聚氧丙烯甘油醚、聚氧丙烯聚氧乙烯甘油醚或聚二甲基硅氧烷中的任意一种或至少二种的混合物，增稠剂包括碱溶胀型增稠剂、缔合型增稠剂或纤维素类增稠剂中的任意一种或至少二种的混合物。
5.根据权利要求1所述的一种建筑内墙用强力乳胶漆，其特征在于：所述稳定剂为氧化锌或者氧化镁，触变剂为膨润土或者硅酸铝，防腐剂为亚硝酸盐或者二氧化硫。
6.一种权利要求1所述的建筑内墙用强力乳胶漆的制备方法，其特征在于：包括如下步骤：
S1、把钛白粉单体混合放入反应釜内，然后加入增粘树脂乳液在85℃～95℃的条件下搅拌3-4h然后自然冷却；
S2、当反应釜内温度冷却到25℃～35℃的时候取样检测乳化反应是否充分，合格之后在往反应釜内添加增稠剂、稳定剂和防腐剂加热至80℃～100℃并搅拌15-25min；
S3、用高速分散研磨机内分别把颜料和超细二氧化硅依次充分研磨，然后把研磨后的颜料和超细二氧化硅与润湿分散剂一起加入反应釜内搅拌，并控制反应釜的温度在30℃～50℃；
S4、最后在反应釜内加入杀菌剂、触变剂和消泡剂搅拌2-3min，然后冷却至10℃～20℃抽样检测；
S5、检测合格用过滤器过滤然后包装入库，在成品外售之前在进行最后一步的出厂检测。
7.根据权利要求6所述的一种建筑内墙用强力乳胶漆的制备方法，其特征在于：所述反应釜内搅拌机的转速为6000-8000rpm/min。
8.根据权利要求6所述的一种建筑内墙用强力乳胶漆的制备方法，其特征在于：所述过滤器的过滤方式为压滤，且过滤器的进料端设有加料罐。
CN201810290063.3A 2018-04-03 2018-04-03 一种建筑内墙用强力乳胶漆及其制备方法 Pending CN108485348A (zh)