CN108411625A - Terahertz accumulation of heat health care fabric and preparation method thereof - Google Patents
Terahertz accumulation of heat health care fabric and preparation method thereof Download PDFInfo
- Publication number
- CN108411625A CN108411625A CN201810087554.8A CN201810087554A CN108411625A CN 108411625 A CN108411625 A CN 108411625A CN 201810087554 A CN201810087554 A CN 201810087554A CN 108411625 A CN108411625 A CN 108411625A
- Authority
- CN
- China
- Prior art keywords
- fabric
- accumulation
- heat
- heat health
- terahertz
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
A kind of Terahertz accumulation of heat health care fabric of present invention offer and preparation method thereof, the method includes：(i) accumulation of heat health-care solution is prepared；(ii) pending fabric is immersed in the accumulation of heat health-care solution；(iii) by step (ii), treated, and fabric is carried out dehydrating, to obtain the Terahertz accumulation of heat health care fabric；Wherein, the accumulation of heat health-care solution includes：The trihydroxy ethane that weight percent is 23 35%, the ten water Boratexes that weight percent is 13 18%, the washing soda that weight percent is 8 16%, the distilled water that the THz wave active water and weight percent that weight percent is 2 10% are 35 50%.The present invention also provides the products by the prepared Terahertz accumulation of heat health care fabric manufacture of the above method.The Terahertz accumulation of heat health care fabric of the present invention, also with human body peripheral vasodilation is promoted, promotes the healthcare functions such as tissue functional recovery other than with conventional heat accumulation function.
Description
The application be the applying date be August in 2016 30, entitled " Terahertz accumulation of heat health care fabric and its making side
The divisional application of the application for a patent for invention of method ".
Technical field
Present invention relates in general to a kind of fabrics with accumulation of heat healthcare function, specifically, the present invention relates to it is a kind of too
Hertz accumulation of heat health care fabric and preparation method thereof.
Background technology
THz wave is middle and later periods the last century 80's just by definite designation, refers to frequency in 0.1THz to 10THz models
It encloses, the sunlight wave that wavelength arrives 3mm ranges 0.03.The research hotspot of many developed countries of the world is had become in recent years.2004
U.S. government is chosen as THz wave technology the four of " changing ten big technologies of future world "；Japan was classified as in 2005
First of " ten big key strategy target of national pillar ".
There are many warming fabric at present on the market, main useful far infrared or the processed fabric of heat-storage agent, this to knit
Object has the function of enhancing warming effect, but there is also some disadvantages for this fabric, and the fabric such as handled with heat-storage agent is mainly
By solid-solid phase-change accumulation of heat, the shortcomings of it is unstable that there are phase-transition heat-preservings, and conductibility is poor；The fabric handled with far infrared is because making
Its snugness of fit is set to be affected with electrode assembly or equipped with infra-red material.In addition, it is existing using far infrared or
The processed fabric of heat-storage agent does not have healthcare function.In order to overcome in the prior art poor thermal conductivity, wear the shortcomings of uncomfortable,
There is an urgent need for a kind of accumulation of heat function well, warming fabrics comfortable and easy to wear and with healthcare function for this field.
Invention content
On the one hand, the present invention provides a kind of production method of Terahertz accumulation of heat health care fabric, the method includes：
(i) accumulation of heat health-care solution is prepared；
(ii) pending fabric is immersed in the accumulation of heat health-care solution；
(iii) by step (ii), treated, and fabric is carried out dehydrating, and is knitted to obtain the Terahertz accumulation of heat health care
Object；
Wherein, the accumulation of heat health-care solution includes：
Weight percent is the trihydroxy ethane of 23-35%,
Weight percent is the ten water Boratexes of 13-18%,
Weight percent is the washing soda of 8-16%,
Weight percent is the THz wave active water of 2-10%, and
Weight percent is the distilled water of 35-50%.
In certain embodiments of the present invention, the weight of THz wave active water included in the accumulation of heat health-care solution
Amount percentage is 2-8% or 2-6% or 2-4%.
In the Terahertz accumulation of heat health-care solution of the present invention, the THz wave active water is preferably Japan
The human body active water that the A-2OA-CA of SantaMineral companies production is handled through THz wave.
In the method for the making Terahertz accumulation of heat health care fabric of the present invention, in step (ii), with bath raio for 1：20 to
1：35 immerse the pending fabric in the accumulation of heat health-care solution；Also, the fabric of the method processing of the present invention can be used
Including animal origin fabric, vegetable fibre fabric, science fabric and/or mixed goods, the animal origin fabric is selected from：
Fleece fabrics, wool fabric, rabbit hair fabric, camel wool fabric, yak pile fabric, silk fabric and its mixture；The plant
Fabric is selected from：Cotton fabric and hemp fabric；The science fabric is selected from：Acrylic fiber fabric, terylene are fine
Dimensional fabric and spandex fibre fabric；The mixed goods is selected from：The mixing of Mao Yurong, the mixing of Mao Yumian, the mixing of silk and cotton,
Silk and the mixing of chemical fibre, the mixed goods of silk and fiber crops.
In the preferred embodiment of the present invention, method of the invention further includes being carried out to the pending fabric
Pretreatment, the pretreatment includes boiling, cleaning and drying；And the Terahertz accumulation of heat obtained later to step (iii) processing
Health care fabric sprays THz wave active water, wherein the dosage of the THz wave active water is 2-10ml/m2Or 2-8ml/
m2Or 2-6ml/m2Or 2-4ml/m2。
On the other hand, the present invention is provided by the prepared Terahertz accumulation of heat health care fabric of the above method.The THz wave
Accumulation of heat health care fabric can give off wavelength as 4-16 microns, the THz wave of frequency 0.8-2.5THz.
Another aspect, the present invention also provides the systems by the prepared Terahertz accumulation of heat health care fabric manufacture of the above method
Product, wherein the product includes dress ornament and bedding.
The present invention has the following advantages that in terms of existing technologies：The Terahertz accumulation of heat health care fabric of the present invention is due to adopting
It is handled with the accumulation of heat health-care solution of the active water containing THz wave, accumulation of heat effect is better than conventional accumulation of heat fabric, phase alternating temperature
Degree is stablized, and shell temperature can be made to rise up to 6 degree after dress, while improving blood flow velocity 8-13%, increase blood flow 5-
8%, therefore, accumulation of heat health care fabric of the invention is other than with conventional heat accumulation function also with promotion human body peripheral vessel
Expansion promotes tissue functional recovery, improves blood microcirculation, improves metabolism, and the fatigue substances such as removal lactic acid alleviate muscle
Pain, relaxation nervous system, especially improves the motion function of self-disciplining nerve cell, mitigates the positions such as body joints, waist
The healthcare function of pain etc..
Specific implementation mode
To make the object, technical solutions and advantages of the present invention clearer, it is illustrated with further below to this hair
The specific implementation mode of bright the to be described in detail but described below present invention is used only for for example, not to this hair
Bright protection domain constitutes any restriction.
Embodiment 1.
The present embodiment makes Terahertz accumulation of heat using wool fabric as illustrative pending fabric, by following methods and protects
Strong fabric：
(1) to the pretreatment of wool fabric：With 95 DEG C~100 DEG C of distilled water boiling wool fabric 0.5 hour, after boiling
It is cleaned with distilled water, drying and processing is then carried out at 70 DEG C~75 DEG C.
(2) accumulation of heat health-care solution is prepared：The trihydroxy ethane that weight percent is 23%, which is dissolved in weight percent, is
In 50% distilled water, the ten water Boratexes and again that weight percent is 15% are gradually added into after trihydroxy ethane is completely dissolved
The washing soda that percentage is 10% is measured, waits for standing 30 minutes after ten water Boratexes and washing soda are completely dissolved, with
After be stirred continuously mixed solution and be slowly added dropwise with weight percent be 2% THz wave active water, at 20 DEG C after being added dropwise
It is persistently stirred at~45 DEG C 15-30 minutes, it is spare to obtain accumulation of heat health-care solution, THz wave active water used in the present embodiment
It is the active water that the A-2OA-CA of Japanese SantaMineral companies production is handled through THz wave.
(3) Terahertz accumulation of heat health care fabric is made：The pretreated wool fabric of step (1) is put into step (2) to prepare
Accumulation of heat health-care solution in, bath raio 1:25~1:30, dip time 1 hour；It then takes out and is dehydrated, at 70 DEG C~75 DEG C
Under the conditions of carry out drying and processing 0.5 hour, dosage 10ml/ cool to being sprayed 3-5 times with THz wave active water after room temperature after fabric
m2, dry, finally carry out it is whole scald, obtain Terahertz accumulation of heat health care fabric #1 samples.
Embodiment 2.
The present embodiment makes Terahertz accumulation of heat using fleece fabrics as illustrative pending fabric, by following methods and protects
Strong fabric：
(1) to the pretreatment of fleece fabrics：With 75 DEG C~105 DEG C of distilled water boiling fleece fabrics at least 0.5 hour, steam
It is cleaned with distilled water after boiling, drying and processing is then carried out at 45 DEG C~65 DEG C.
(2) accumulation of heat health-care solution is prepared：The trihydroxy ethane that weight percent is 25%, which is dissolved in weight percent, is
In 45% distilled water, the ten water Boratexes and again that weight percent is 18% are gradually added into after trihydroxy ethane is completely dissolved
The washing soda that percentage is 8% is measured, waits for standing 30 minutes after ten water Boratexes and washing soda are completely dissolved, then
Be stirred continuously mixed solution and be slowly added dropwise with weight percent be 4% THz wave active water, after being added dropwise 20 DEG C~
It is persistently stirred at 25 DEG C 15-30 minutes, obtains that accumulation of heat health-care solution is spare, and THz wave active water used in the present embodiment is
The human body active water that the A-2OA-CA of Japanese SantaMineral companies production is handled through THz wave.
(3) Terahertz accumulation of heat health care fabric is made：The pretreated fleece fabrics of step (1) is put into step (2) to prepare
Accumulation of heat health-care solution in, bath raio 1:25~1:35, dip time at least 1 hour；Then take out and be dehydrated, 45 DEG C~
Drying and processing 0.5 hour is carried out under the conditions of 75 DEG C, dosage cool to being sprayed 3 times with THz wave active water after room temperature after fabric
8ml/m2, dry, finally carry out it is whole scald, obtain Terahertz accumulation of heat health care fabric #2 samples.
Embodiment 3.
The present embodiment makes Terahertz accumulation of heat using rabbit hair fabric as illustrative pending fabric, by following methods and protects
Strong fabric：
(1) to the pretreatment of rabbit hair fabric：With 65 DEG C~70 DEG C of distilled water boiling rabbit hair fabric 0.5 hour, after boiling
It is cleaned with distilled water, drying and processing is then carried out at 60 DEG C~65 DEG C.
(2) accumulation of heat health-care solution is prepared：The trihydroxy ethane that weight percent is 31%, which is dissolved in weight percent, is
In 40% distilled water, the ten water Boratexes and again that weight percent is 16% are gradually added into after trihydroxy ethane is completely dissolved
The washing soda that percentage is 13% is measured, waits for standing 30 minutes after ten water Boratexes and washing soda are completely dissolved, with
After be stirred continuously mixed solution and be slowly added dropwise with weight percent be 6% THz wave active water, at 20 DEG C after being added dropwise
It is persistently stirred at~45 DEG C 15-30 minutes, it is spare to obtain accumulation of heat health-care solution, THz wave active water used in the present embodiment
It is the human body active water that the A-2OA-CA of Japanese SantaMineral companies production is handled through THz wave.
(3) Terahertz accumulation of heat health care fabric is made：The pretreated rabbit hair fabric of step (1) is put into step (2) to prepare
Accumulation of heat health-care solution in, bath raio 1:25~1:30, dip time 0.5 hour；It then takes out and is dehydrated, 65 DEG C~70
Drying and processing 0.5 hour is carried out under the conditions of DEG C, dosage 6ml/ cool to being sprayed 5 times with THz wave active water after room temperature after fabric
m2, dry, finally carry out it is whole scald, obtain Terahertz accumulation of heat health care fabric #3 samples.
Embodiment 4.
The present embodiment makes terahertz using woollen and cashmere blended fabric as illustrative pending fabric by following methods
Hereby accumulation of heat health care fabric：
(1) to the pretreatment of woollen and cashmere blended fabric (wherein, wool 70%, cashmere 30%)：With 75 DEG C~80
DEG C distilled water boiling woollen and cashmere blended fabric 0.5 hour, cleaned with distilled water after boiling, then carried out at 65 DEG C~70 DEG C
Drying and processing.
(2) accumulation of heat health-care solution is prepared：The trihydroxy ethane that weight percent is 30%, which is dissolved in weight percent, is
In 35% distilled water, the ten water Boratexes and again that weight percent is 15% are gradually added into after trihydroxy ethane is completely dissolved
The washing soda that percentage is 12% is measured, waits for standing 30 minutes after ten water Boratexes and washing soda are completely dissolved, with
After be stirred continuously mixed solution and be slowly added dropwise with weight percent be 8% THz wave active water, at 20 DEG C after being added dropwise
It is persistently stirred at~45 DEG C 15-30 minutes, it is spare to obtain accumulation of heat health-care solution, THz wave active water used in the present embodiment
It is the human body active water that the A-2OA-CA of Japanese SantaMineral companies production is handled through THz wave.
(3) Terahertz accumulation of heat health care fabric is made：The pretreated woollen and cashmere blended fabric of step (1) is put into step
(2) in the accumulation of heat health-care solution prepared, bath raio 1:25~1:30, dip time 0.5 hour；It then takes out and is dehydrated,
Drying and processing 0.5 hour is carried out under the conditions of 70 DEG C~75 DEG C, after fabric it is cool to carry out after room temperature it is whole scald, obtain Terahertz accumulation of heat guarantor
Strong fabric #4 samples.
Embodiment 5.
The present embodiment makes Terahertz accumulation of heat using silk fabric as illustrative pending fabric, by following methods and protects
Strong fabric：
(1) to the pretreatment of silk fabric：With 55 DEG C~65 DEG C of distilled water boiling silk fabric 0.5 hour, after boiling
It is cleaned with distilled water, drying and processing is then carried out at 50 DEG C~55 DEG C.
(2) accumulation of heat health-care solution is prepared：The trihydroxy ethane that weight percent is 26%, which is dissolved in weight percent, is
In 35% distilled water, the ten water Boratexes and again that weight percent is 16% are gradually added into after trihydroxy ethane is completely dissolved
The washing soda that percentage is 13% is measured, waits for standing 30 minutes after ten water Boratexes and washing soda are completely dissolved, with
After be stirred continuously mixed solution and be slowly added dropwise with weight percent be 10% THz wave active water, at 20 DEG C after being added dropwise
It is persistently stirred at~45 DEG C 15-30 minutes, it is spare to obtain accumulation of heat health-care solution, THz wave active water used in the present embodiment
It is the human body active water that the A-2OA-CA of Japanese SantaMineral companies production is handled through THz wave.
(3) Terahertz accumulation of heat health care fabric is made：The pretreated silk fabric of step (1) is put into step (2) to prepare
Accumulation of heat health-care solution in, bath raio 1:25~1:30, dip time 0.5 hour；It then takes out and is dehydrated, 55 DEG C~60
Drying and processing 0.5 hour is carried out under the conditions of DEG C, dosage 2ml/ cool to being sprayed 2 times with THz wave active water after room temperature after fabric
m2, dry, progress is whole to scald, and obtains Terahertz accumulation of heat health care fabric #5 samples.
The radiation wavelength and normal emittance for the Terahertz accumulation of heat health care fabric sample that above-mentioned five embodiments make according to
Standard GB/T/TT287-2008 (heating by infrared radiation test method) is detected, and testing result is as listed by the following table 1.
The testing result for the Terahertz accumulation of heat health care fabric sample that 1. above-mentioned five embodiments of table make
Comparative example
In comparative example, equally use wool fabric, fleece fabrics, rabbit hair fabric, woollen and cashmere blended fabric with
And silk fabric is respectively as pending fabric, using the accumulation of heat agent solution without THz wave active water, by with above-mentioned reality
It applies the identical technological parameter of the technological parameter described in example respectively to handle this five kinds of pending fabrics, making obtains routine
Accumulation of heat fabric.
Five kinds of Terahertz accumulation of heat health cares that human body wears above-described embodiment making are detected according to national FZ/T 73036-2010
Shell temperature of the fabric after 30 minutes and wear body surface of the five kinds of conventional accumulation of heat fabrics of comparative example making after 30 minutes
Temperature, and the operation instructions detection human body provided according to manufacturer using doppler flow inaging detector wears above-described embodiment making
Five kinds of Terahertz accumulation of heat health care fabrics after blood flow velocity and blood flow and wear five kinds made in comparative example
The blood flow velocity and blood flow of conventional accumulation of heat fabric, the following table 2, which is listed, to be used relative to dress without THz wave active water
Shell temperature, blood flow velocity and blood flow of the fabric after 30 minutes after conventional heat-storage agent solution treatment wears the present invention too
The hertz accumulation of heat health care fabric percentage that shell temperature, blood flow velocity and blood flow improve after 30 minutes.
The accumulation of heat health properties of 2. 5 kinds of Terahertz accumulation of heat health care fabrics of table
From upper Tables 1 and 2 as can be seen that by the prepared Terahertz accumulation of heat health care fabric of method of the present invention red
Under UV radiation can generation wavelength be 4-16 micron, the THz wave of 0.8-2.5THz, human body dress Terahertz of the invention
Shell temperature increases by 1 DEG C -6 DEG C, and blood flow velocity and blood after human body wears the accumulation of heat health care fabric after accumulation of heat health care fabric
Flow can be improved, this just plays the expansion for promoting human body peripheral vessel, improves the health-care effect of blood microcirculation, to
Alleviate myalgia, so that nervous system is relaxed, the motion function of especially self-disciplining nerve cell is improved, according to three
250 clinical reports of first hospital are shown, prove that the prepared Terahertz accumulation of heat health care of method by the present invention is knitted by Blind Test
Object has apparent curative effect, effective percentage to reach 86% or more the pain at the positions such as joint, waist caused by gout etc..
Above in association with specific implementation mode, the present invention is described, these specific implementation modes are merely exemplary
, protection scope of the present invention cannot be limited with this, it will be understood by those skilled in the art that before not departing from essence of the invention
Put that various modifications can be carried out, change or replacement.Therefore, according to various equivalent variations made by the present invention, this hair is still fallen within
Bright covered range.
Claims (3)
1. the production method of Terahertz accumulation of heat health care fabric, the method includes：
(i) accumulation of heat health-care solution is prepared comprising：Trihydroxy ethane is dissolved in distilled water, waits for that trihydroxy ethane is completely molten
It is gradually added into ten water Boratexes and washing soda after solution, waits for standing 30 after ten water Boratexes and washing soda are completely dissolved
Minute, it is then stirred continuously mixed solution and THz wave active water is slowly added dropwise, held at 20 DEG C~45 DEG C after being added dropwise
Continuous stirring 15-30 minutes, obtains the accumulation of heat health-care solution；
(ii) by 75 DEG C~105 DEG C of the distilled water boiling at least 0.5 hour of pending fabric, with distillation washing after boiling
Only, drying and processing is then carried out at 45 DEG C~65 DEG C；
(iii) step (ii) treated fabric is immersed in the accumulation of heat health-care solution, bath raio 1:25~1:35, when dipping
Between at least 1 hour；
(iv) step (iii) treated fabric is taken out, drying and processing is carried out under the conditions of 45 DEG C~75 DEG C 0.5 hour, waited for
Fabric is cool to be sprayed 3 times to after room temperature with THz wave active water, dosage 2-10ml/m2, dry, stored to obtain the Terahertz
Hot health care fabric；
Wherein, the accumulation of heat health-care solution includes：
Weight percent is the trihydroxy ethane of 23-35%,
Weight percent is the ten water Boratexes of 13-18%,
Weight percent is the washing soda of 8-16%,
Weight percent is the THz wave active water of 2-10%, and
Weight percent is the distilled water of 35-50%,
Wherein, the fabric is selected from：Wool fabric, fleece fabrics, rabbit hair fabric, woollen and cashmere blended fabric and silk fabric；
It is 4-16 microns that the Terahertz accumulation of heat health care fabric, which can give off wavelength, the THz wave of frequency 0.8-2.5THz.
2. the method for claim 1, wherein weight of THz wave active water included in the accumulation of heat health-care solution
Amount percentage is 2-8% or 2-6% or 2-4%.
3. the method for claim 1, wherein the dosage of the THz wave active water is 2-8ml/m2Or 2-6ml/
m2Or 2-4ml/m2。