CN103668660A - Method for manufacturing far-infrared health care fabric cloth - Google Patents
Method for manufacturing far-infrared health care fabric cloth Download PDFInfo
- Publication number
- CN103668660A CN103668660A CN201310504816.3A CN201310504816A CN103668660A CN 103668660 A CN103668660 A CN 103668660A CN 201310504816 A CN201310504816 A CN 201310504816A CN 103668660 A CN103668660 A CN 103668660A
- Authority
- CN
- China
- Prior art keywords
- preparation
- fabric cloth
- organizine
- care material
- health
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a method for manufacturing a far-infrared health care fabric cloth. The method comprises the following steps that a) warp yarn raw materials are manufactured; b) warp yarns are manufactured; c) weft yarns are selected; d) the fabric cloth is woven through a machine; e) aftertreatment is carried out on the fabric cloth. The method for manufacturing the far-infrared health care fabric cloth is reasonable in process arrangement, the process is easy and convenient to implement, cost is proper, far-infrared micro powder in the fabric cloth can release quantitative far-infrared rays, the blood circulation of a human body is effectively improved, and metabolism is promoted. Meanwhile, the fabric cloth is high in washing fastness and lasting in physiotherapy effect and has no toxic and side effect on the human body. Based on the advantages, the fabric cloth can be made into underwear, bed sheets, bedding, waistcoats, shorts and the like, and is wide in application.
Description
Technical field
The present invention relates to a kind of preparation method of fabric cloth, relate in particular to a kind of preparation method with the fabric cloth of far infrared health care effect, belong to fabric technical field.
Background technology
The various clothes clothes that clothes general reference is worn with it, its Main Function is warming, as the medium of flak jacket; And in modern society, clothes on the constant basis of basic function, is more and more focused on functional exploitation keeping, people, by techniques such as blending, dipping, coatings, add function material in clothing fabric to, to give clothes multiple different function.
Along with the quickening of people's rhythm of life, the continuous increase of operating pressure, the energy that people drop into aspect improving the health is very limited, has caused a lot of people all in a kind of sub-health state, and fitness go fromes bad to worse.People nurse one's health by medicine or food mostly, but the former tends to bring very large side effect to human body, and the latter's curative effect is limited, once occur eating and drinking immoderately, also can work the mischief to health.For this reason, people constantly increase the R&D intensity, particularly underclothes fabric to functional fabric, and people wish only to need wearing functions type clothing, just can in working at ordinary times, learn, living, nurse one's health function, improve physique.
Far infrared is the deep enough skin of a kind of energy and hypodermic ray, because the vibration frequency of far infrared and human inner cell's molecule is approaching, can cause the resonance of atom and the molecule of human body cell, see through sympathetic response and absorb, between molecule, friction forms thermal response, impels subcutaneous deep temperature to rise, and make Marjoram Extract, accelerate blood circulation, be conducive to remove blood vessel and hoard harmful substance in thing and body, reach activation histocyte, prevent object aging, strengthening immune system.But because fabric cloth is in the deficiency aspect selection and preparation technology, to such an extent as to the physical therapy efficacy of far infrared in fabric cloth can't bring into play completely, ageing too low, complicated process of preparation, can not meet the requirement that people produce and use.
Summary of the invention
For the demand, the invention provides a kind of preparation method of farinfrared health-care material cloth, this preparation method's procedure arrangement is reasonable, it is convenient to implement, methodological science, and the physical therapy efficacy of the far infrared micro mist in the fabric cloth making is remarkable, can effectively promote blood circulation of human body, strengthen human immunological competence; Meanwhile, fabric cloth fastness to washing is high, and physical therapy efficacy is lasting, and without any side effects to human body.
The present invention is a kind of preparation method of farinfrared health-care material cloth, and this preparation method comprises the steps: a) preparation organizine raw material, b) prepares organizine, c) the standby tram of choosing, d) woven fabric cloth, e) fabric cloth post processing.
In a preferred embodiment of the present invention, in described step a), the main component of organizine raw material and percentage composition proportioning thereof are: far infrared powder 5%-8%, polyethylene terephthalate particle 85%-90%, and all the other are relevant auxiliary agent; The particle diameter of far infrared powder is about 40-50nm; The granularity of polyethylene terephthalate particle is about 50 orders; Flexibilizer in auxiliary agent selects phthalic acid ester, defoamer to select dimethicone or polyether-modified silicon, heat stabilizer to select triethyl phosphate or phosphite.
In a preferred embodiment of the present invention, in described step b), organizine adopts melt spinning technique to be prepared, and comprises batch mixing and during Primary Processing.
In a preferred embodiment of the present invention, described batch mixing process is as follows: first, in polyethylene terephthalate particle reaction still, temperature of reaction kettle rises to 230 ℃-240 ℃ and constantly stirring, and mixing time is about 10-12 minute; Then, add far infrared powder, temperature of reaction kettle promotes 10 ℃-15 ℃, fully stirs 20-25 minute; Finally, add auxiliary agent, temperature of reaction kettle maintains 230 ℃ of left and right, stirs 2-3 minute.
In a preferred embodiment of the present invention, described during Primary Processing is as follows: first, compound is imported to spray silk equipment, spinning head aperture is 0.02mm, and the expulsion pressure of spinning head is controlled at 15-16MPa, and injection temperation is controlled at more than 230 ℃; Then, carry out slow cooling in hot air chamber, hot air chamber temperature is controlled at 80 ℃; Then, filament is imported in cold water and carries out cooling and curing processing, be about 10 minutes cool time; Finally, adopt dry, oil, the technique such as curling, drafting, twisting processes; Organizine is multi cord, and number of share of stock is 3, and number is 16S, and the twist is 360.
In a preferred embodiment of the present invention, in described step c), tram is selected natural sliver, and sliver is doublet cord, and number is 32S, and the twist is 300.
In a preferred embodiment of the present invention, in described step d), fabric cloth adopts longitude and latitude weaving to be prepared, and woven density is 168*196, and woven thickness is about 0.28-0.32mm.
The present invention has disclosed a kind of preparation method of farinfrared health-care material cloth, and this preparation method's procedure arrangement is reasonable, and process implementing is easy, cost is moderate, far infrared micro mist in fabric cloth can discharge quantitative far ir ray, effectively improves blood circulation of human body, enhances metabolism; Meanwhile, fabric cloth fastness to washing is high, and physical therapy efficacy is lasting, without any side effects to human body; Based on above advantage, this fabric cloth can be made into the goods such as underwear, sheet, bed clothes, vest pants, is widely used.
Accompanying drawing explanation
Below in conjunction with the drawings and specific embodiments, the present invention is further detailed explanation:
Fig. 1 is the preparation method's of embodiment of the present invention farinfrared health-care material cloth process figure;
The specific embodiment
Below in conjunction with accompanying drawing, preferred embodiment of the present invention is described in detail, thereby so that advantages and features of the invention can be easier to be it will be appreciated by those skilled in the art that, protection scope of the present invention is made to more explicit defining.
Fig. 1 is the preparation method's of embodiment of the present invention farinfrared health-care material cloth process figure; This preparation method comprises the steps: a) preparation organizine raw material, b) prepares organizine, c) the standby tram of choosing, d) woven fabric cloth, e) fabric cloth post processing.
Embodiment 1
The preparation method's of the farinfrared health-care material cloth that the present invention mentions specific implementation process is as follows:
A) preparation organizine raw material, the main component of organizine raw material and percentage composition proportioning thereof are: far infrared powder 5%-6%, polyethylene terephthalate particle 88%-90%, all the other are relevant auxiliary agent; Wherein, the particle diameter of far infrared powder is about 40-45nm; The granularity of polyethylene terephthalate particle is about 50 orders; Flexibilizer in auxiliary agent selects phthalic acid ester, defoamer to select dimethicone or polyether-modified silicon, heat stabilizer to select triethyl phosphate or phosphite.
B) prepare organizine, organizine adopts melt spinning technique to be prepared, and comprises batch mixing and during Primary Processing;
Batch mixing process is as follows: first, in polyethylene terephthalate particle reaction still, temperature of reaction kettle rises to 230 ℃-235 ℃ and constantly stirring, and mixing time is about 12 minutes; Then, add far infrared powder, temperature of reaction kettle promotes 10 ℃-12 ℃, fully stirs 22 minutes; Finally, add auxiliary agent, temperature of reaction kettle maintains 230 ℃ of left and right, stirs 2 minutes, makes compound;
During Primary Processing is as follows: first, compound is imported to spray silk equipment, spinning head aperture is 0.02mm, and the expulsion pressure of spinning head is controlled at 15MPa, and injection temperation is controlled at more than 230 ℃; Then, carry out slow cooling in hot air chamber, hot air chamber temperature is controlled at 80 ℃; Then, filament is imported in cold water and carries out cooling and curing processing, be about 10 minutes cool time; Finally, adopt dry, oil, the technique such as curling, drafting, twisting processes; Organizine is multi cord, and number of share of stock is 3, and number is 16S, and the twist is 360, and string diameter is about 0.015-0.018mm;
C) the standby tram of choosing, tram is selected natural sliver, and sliver is doublet cord, and number is 32S, and the twist is 300, string diameter is about 0.02-0.022mm;
D) woven fabric cloth, fabric cloth adopts longitude and latitude weaving to be prepared, and woven density is 168*196, and woven thickness is about 0.32-0.35mm;
E) fabric cloth post processing, aftertreatment technology comprises: dyeing, destarch, washing, oven dry, thermocompression forming, singe, cutting edge etc.
Embodiment 2
The preparation method's of the farinfrared health-care material cloth that the present invention mentions specific implementation process is as follows:
A) preparation organizine raw material, the main component of organizine raw material and percentage composition proportioning thereof are: far infrared powder 6%-8%, polyethylene terephthalate particle 85%-88%, all the other are relevant auxiliary agent; Wherein, the particle diameter of far infrared powder is about 45nm; The granularity of polyethylene terephthalate particle is about 50 orders; Flexibilizer in auxiliary agent selects phthalic acid ester, defoamer to select dimethicone or polyether-modified silicon, heat stabilizer to select triethyl phosphate or phosphite.
B) prepare organizine, organizine adopts melt spinning technique to be prepared, and comprises batch mixing and during Primary Processing;
Batch mixing process is as follows: first, in polyethylene terephthalate particle reaction still, temperature of reaction kettle rises to 235 ℃-240 ℃ and constantly stirring, and mixing time is about 10 minutes; Then, add far infrared powder, temperature of reaction kettle promotes 12 ℃-15 ℃, fully stirs 20 minutes; Finally, add auxiliary agent, temperature of reaction kettle maintains 230 ℃ of left and right, stirs 2.5 minutes, makes compound;
During Primary Processing is as follows: first, compound is imported to spray silk equipment, spinning head aperture is 0.02mm, and the expulsion pressure of spinning head is controlled at 16MPa, and injection temperation is controlled at more than 230 ℃; Then, carry out slow cooling in hot air chamber, hot air chamber temperature is controlled at 80 ℃; Then, filament is imported in cold water and carries out cooling and curing processing, be about 10 minutes cool time; Finally, adopt dry, oil, the technique such as curling, drafting, twisting processes; Organizine is multi cord, and number of share of stock is 3, and number is 16S, and the twist is 360, and string diameter is about 0.015-0.018mm;
C) the standby tram of choosing, tram is selected natural sliver, and sliver is doublet cord, and number is 32S, and the twist is 300, string diameter is about 0.02-0.022mm;
D) woven fabric cloth, fabric cloth adopts longitude and latitude weaving to be prepared, and woven density is 168*196, and woven thickness is about 0.32-0.35mm;
E) fabric cloth post processing, aftertreatment technology comprises: dyeing, destarch, washing, oven dry, thermocompression forming, singe, cutting edge etc.
The present invention has disclosed a kind of preparation method of farinfrared health-care material cloth, is characterized in: this preparation method's procedure arrangement is reasonable, and process implementing is easy, cost is moderate, far infrared micro mist in fabric cloth can discharge quantitative far ir ray, effectively improves blood circulation of human body, enhances metabolism; Meanwhile, fabric cloth fastness to washing is high, and physical therapy efficacy is lasting, without any side effects to human body; Based on above advantage, this fabric cloth can be made into the goods such as underwear, sheet, bed clothes, vest pants, is widely used.
The above; it is only the specific embodiment of the present invention; but protection scope of the present invention is not limited to this; any those of ordinary skill in the art are in the disclosed technical scope of the present invention; the variation that can expect without creative work or replacement, within all should being encompassed in protection scope of the present invention.Therefore, protection scope of the present invention should be as the criterion with the protection domain that claims were limited.
Claims (7)
1. a preparation method for farinfrared health-care material cloth, is characterized in that, this preparation method comprises the steps: a) preparation organizine raw material, b) prepares organizine, c) the standby tram of choosing, d) woven fabric cloth, e) fabric cloth post processing.
2. the preparation method of farinfrared health-care material cloth according to claim 1, it is characterized in that, in described step a), the main component of organizine raw material and percentage composition proportioning thereof are: far infrared powder 5%-8%, polyethylene terephthalate particle 85%-90%, and all the other are relevant auxiliary agent; The particle diameter of far infrared powder is about 40-50nm; The granularity of polyethylene terephthalate particle is about 50 orders; Flexibilizer in auxiliary agent selects phthalic acid ester, defoamer to select dimethicone or polyether-modified silicon, heat stabilizer to select triethyl phosphate or phosphite.
3. the preparation method of farinfrared health-care material cloth according to claim 1, is characterized in that, in described step b), organizine adopts melt spinning technique to be prepared, and comprises batch mixing and during Primary Processing.
4. the preparation method of farinfrared health-care material cloth according to claim 3, it is characterized in that, described batch mixing process is as follows: first, and in polyethylene terephthalate particle reaction still, temperature of reaction kettle rises to 230 ℃-240 ℃ and constantly stirring, and mixing time is about 10-12 minute; Then, add far infrared powder, temperature of reaction kettle promotes 10 ℃-15 ℃, fully stirs 20-25 minute; Finally, add auxiliary agent, temperature of reaction kettle maintains 230 ℃ of left and right, stirs 2-3 minute.
5. the preparation method of farinfrared health-care material cloth according to claim 3, it is characterized in that, described during Primary Processing is as follows: first, compound is imported to spray silk equipment, spinning head aperture is 0.02mm, the expulsion pressure of spinning head is controlled at 15-16MPa, and injection temperation is controlled at more than 230 ℃; Then, carry out slow cooling in hot air chamber, hot air chamber temperature is controlled at 80 ℃; Then, filament is imported in cold water and carries out cooling and curing processing, be about 10 minutes cool time; Finally, adopt dry, oil, the technique such as curling, drafting, twisting processes; Organizine is multi cord, and number of share of stock is 3, and number is 16S, and the twist is 360.
6. the preparation method of farinfrared health-care material cloth according to claim 1, is characterized in that, in described step c), tram is selected natural sliver, and sliver is doublet cord, and number is 32S, and the twist is 300.
7. the preparation method of farinfrared health-care material cloth according to claim 1, is characterized in that, in described step d), fabric cloth adopts longitude and latitude weaving to be prepared, and woven density is 168*196, and woven thickness is about 0.28-0.32mm.