CN101215778A - Anion far infrared post finishing method for silk wadding quilt - Google Patents
Anion far infrared post finishing method for silk wadding quilt Download PDFInfo
- Publication number
- CN101215778A CN101215778A CNA2008100190284A CN200810019028A CN101215778A CN 101215778 A CN101215778 A CN 101215778A CN A2008100190284 A CNA2008100190284 A CN A2008100190284A CN 200810019028 A CN200810019028 A CN 200810019028A CN 101215778 A CN101215778 A CN 101215778A
- Authority
- CN
- China
- Prior art keywords
- silk floss
- maceration extract
- arrangement
- finishing
- far infrared
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a far infrared finishing method of negative ions of silk floss quilts, which is characterized in that the method comprises respectively preparing finishing maceration extract A and B, and finishing maceration extract A comprises nanometer negative-ions far-infrared radiating body and dispersing agent and water, and finishing maceration extract B comprises low temperature cementing compound and silk cotton softening agent, placing finishing maceration extract A in dry silk cotton after heating, dipping for at least 40 minutes, dewatering, and drying to the wet containing rate which is 8-12%, utilizing finishing maceration extract B to dip and handle for 30-40 minutes, producing a silk floss quilt with a conventional method after centrifugally dewatering and drying. The silk floss quilt of the invention can effectively release negative ions, omnidirectional emission rate of the far infrared method can reach 88%, and the invention can effectively improve qi-blood circulation of human bodies, which plays an excellent health care effect, meanwhile, the invention is soft, whose bulkiness property is excellent, and has excellent performance property.
Description
Technical field
The present invention relates to a kind of postfinishing process of bondedfibre fabric, be specifically related to a kind of afterfinish method of silk floss quilt, so that possess health-care effect through the silk floss quilt of arrangement.
Background technology
Silk floss quilt is that raw material is made with the natural silk fiber, owing to human body skin and cardiovascular health-care effect arranged, more be subjected to domestic and international consumer's welcome deeply with the characteristics light and soft, comfortable, that warmth retention property is good.Traditional manufacture method is, is raw material with the dupion, places it in to release to heat in the soda ash to boil, and degumming silkworm cocoons adopts the last garnetting of the manual collar to be processed into silk floss quilt until the very easily garnetting of cocoon layer silk.Yet, traditional silk floss quilt preparation method, kind is very single, can not meeting the market requirement.
Raising day by day along with people's living standard, health care consciousness strengthens, increasing consumer favor use integrating of natural fabric warming with articles for use health care, thereby, silk floss quilt is carried out post processing, make it not only have softness, comfortable, good wearability such as warmth retention property is good, possess health care simultaneously, can increase the new varieties of silk floss quilt, further improve the class and the added value of product.
To improve air quality and to promote that the blood of human body microcirculation is a purpose, carry out anion and far-infrared finishing, can make product obtain new health care function.Anion is commonly called as " air vitamin " or " long-lived plain ", very important to health, the occurring in nature anion concentration is different because of the region, forest, waterfall are the profuse regions of anion concentration, and the people is in and wherein can feels relaxed and joyful, and in the bedroom, especially winter, the room air circulation was less, and the carbon dioxide that spues during sleep quality can make the room air muddiness, sharply descends and be directed at indoor negative ion concentration, and the people is not felt well.Fabric is carried out anion finishing, can make it constantly to discharge anion, keep room air fresh.Simultaneously, microcirculation has confidential relation in health and the body, and far infrared has ferocious penetrability, can be penetrated into subcutis, from warm to whole body in the body, thereby causes that resonance cell makes generation thermogenetic effect in the body.Silk floss quilt is carried out the arrangement of anion and far infrared dual-use function simultaneously, will obtain comparatively desirable health-care effect.
In the prior art, Shang Weiyou carries out the report of anion and far infrared health care arrangement to silk floss quilt.To the method that fabric carries out anion and far infrared processing, a kind of is to sneak into functional material in fiber, and by spraying the long filament that silk obtains to have functional effect, another kind is that fabric is carried out the back arrangement, obviously can only carry out a kind of processing in back to silk floss quilt.Yet, when at present silk fabrics being carried out functional topical finishing, all need to adopt high temperature adhesive, if when this class afterfinish method is used for the back arrangement of silk floss quilt, the softness of silk floss quilt, bulkiness are decreased, influence the wearability of silk floss quilt.How when making silk floss quilt obtain anion, far infrared performance, keeping its good wearability, is to need the problem that solves at present.
Summary of the invention
The object of the invention provides a kind of anion far infrared post finishing method of silk floss quilt, when the silk floss quilt of arrangement is obtaining anion, far infrared performance, keeps its softness, bulkiness, possesses good wearability.
For achieving the above object, the technical solution used in the present invention is: a kind of anion far infrared post finishing method of silk floss quilt,
(1) preparation arrangement maceration extract A, described arrangement maceration extract A comprises that percentage by weight is the nano-negative ion far-infrared radiator that has active group of 2-6%, the dispersant of 0.3-1%, surplus is a water, described dispersant is selected from the polyoxyethylene alcohol alkyl ether;
(2) preparation arrangement maceration extract B, described arrangement maceration extract B comprises that percentage by weight is the low temperature adhesive of 2-6%, the silk floss softener of 2-5%;
(3) will put maceration extract A in order and be heated to 60～80 ℃, put into the shredded dried bean curd silk floss, the bath raio of solution is 1: 15～25, after silk floss all impregnated in arrangement maceration extract A, regulating dipping temperature is 65～75 ℃, dip time at least 40 minutes, then, with the silk floss dehydration behind the dipping, dry to moisture percentage be 8～12%;
(4) silk floss after will drying is with arrangement maceration extract B impregnation process, 40～45 ℃ of dipping temperatures, and dip time 30～40 minutes after centrifugal dehydration, the oven dry, is made into silk floss quilt with conventional method.
In the technique scheme, the dehydration in the described step (3) is centrifugal dehydration 1～2 minute, and bake out temperature is 70～80 ℃, drying time 20～30 minutes.
Dehydration in the described step (4) is centrifugal dehydration 1～2 minute, and bake out temperature is 70～80 ℃.
In the technique scheme, the nanometer grade powder of described nano-negative ion far-infrared radiator for adopting micropowder processing method to obtain mixed by tourmaline and far-infrared ceramic powder.Described low temperature adhesive can be selected the polypropylene ester adhesive for use.Described silk floss softener is a hydrophilic organic silicon.
Because the technique scheme utilization, the present invention compared with prior art has following advantage:
1. because the present invention has adopted nano level anion far-infrared radiator, it possesses more active group, can combine effectively with silk floss quilt, the product that obtains can effectively discharge anion, simultaneously, the outer normal direction total emissivity value of its far ultraviolet reaches 88%, can effectively improve the QI-blood circulation of human body, plays the good health care effect;
2. the present invention adopts dipping method twice, when flooding for the second time, add low temperature adhesive and silk floss softener, thereby avoided because the flexible decline problem of the silk floss that the adhesive in the arrangement of back causes, silk floss quilt softness, bulkiness after arrangement are good, have good wearability.
Description of drawings
Fig. 1 is the relative radiant-energy spectrum curve map of anion far infrared silk floss quilt infrared ray that the embodiment of the invention one arrangement obtains.
The specific embodiment
Below in conjunction with drawings and Examples the present invention is further described:
Embodiment one: a kind of anion far infrared post finishing method of silk floss quilt
(1) preparation arrangement maceration extract A, described arrangement maceration extract A comprises that percentage by weight is the nano-negative ion far-infrared radiator that has active group of 2-6%, the dispersant of 0.3-1%, surplus is a water, described dispersant is selected from the polyoxyethylene alcohol alkyl ether;
(2) preparation arrangement maceration extract B, described arrangement maceration extract B comprises that percentage by weight is the low temperature adhesive of 2-6%, the silk floss softener of 2-5%;
(3) will put maceration extract A in order and be heated to 60～80 ℃, put into the shredded dried bean curd silk floss, the bath raio of solution is 1: 15～25, after silk floss all impregnated in arrangement maceration extract A, regulating dipping temperature is 65～75 ℃, dip time at least 40 minutes, then, with the silk floss dehydration behind the dipping, dry to moisture percentage be 8～12%;
(4) silk floss after will drying is with arrangement maceration extract B impregnation process, 40～45 ℃ of dipping temperatures, and dip time 30～40 minutes after centrifugal dehydration, the oven dry, is made into silk floss quilt with conventional method.
In the present embodiment, the nanometer grade powder of nano-negative ion far-infrared radiator for adopting micropowder processing method to obtain mixed by tourmaline and far-infrared ceramic powder.
It is 1 centimetre sample that the silk floss quilt that present embodiment is obtained is made into thickness, carries out anion and detects, and its testing result is as shown in the table:
The anion testing result of table 1 anion far infrared silk floss quilt
| Anion several/centimetre 3 | |||||||||
| Sample | 730 280 | 400 300 | 560 320 | 360 650 | 540 920 | 460 1080 | 600 860 | 500 | Mean value 570 |
Silk floss quilt is according to varying in weight, and its thickness is also different, and its thickness of 1 kilogram silk floss quilt is about 4-5 centimetre, and therefore, the d/d anion number of the silk floss after the arrangement is than big several times of above-mentioned testing result.
After testing, the silk floss quilt far infrared normal direction total emissivity value that present embodiment obtains reaches 88%, according to research, the far infrared radiation rate of general far-infrared fabric reaches the QI-blood circulation that just can improve human body more than 80%, strengthen blood microcirculation, enhance metabolism, play the good health care effect.
Referring to accompanying drawing 1, for the anion far infrared rays silk floss by the relative radiant-energy spectrum curve of infrared ray, its infra-red radiation frequency band is based on 8～14 micron wave length scopes, this is very consistent with the absorption of human body wavelength, and human body can absorb a large amount of infra-red radiations, thereby improves the QI-blood circulation of human body, increase blood microcirculation, enhance metabolism, improve the immune disease-resistance ability, thereby have and significantly heat the health-care physical therapy effect.
Claims (4)
1. the anion far infrared post finishing method of a silk floss quilt is characterized in that:
(1) preparation arrangement maceration extract A, described arrangement maceration extract A comprises that percentage by weight is the nano-negative ion far-infrared radiator that has active group of 2-6%, the dispersant of 0.3-1%, surplus is a water, described dispersant is selected from the polyoxyethylene alcohol alkyl ether;
(2) preparation arrangement maceration extract B, described arrangement maceration extract B comprises that percentage by weight is the low temperature adhesive of 2-6%, the silk floss softener of 2-5%;
(3) will put maceration extract A in order and be heated to 60～80 ℃, put into the shredded dried bean curd silk floss, the bath raio of solution is 1: 15～25, after silk floss all impregnated in arrangement maceration extract A, regulating dipping temperature is 65～75 ℃, dip time at least 40 minutes, then, with the silk floss dehydration behind the dipping, dry to moisture percentage be 8～12%;
(4) silk floss after will drying is with arrangement maceration extract B impregnation process, 40～45 ℃ of dipping temperatures, and dip time 30～40 minutes after centrifugal dehydration, the oven dry, is made into silk floss quilt with conventional method.
2. the anion far infrared post finishing method of silk floss quilt according to claim 1, it is characterized in that: the dehydration in the described step (3) is centrifugal dehydration 1～2 minute, and bake out temperature is 70～80 ℃, drying time 20～30 minutes.
3. the anion far infrared post finishing method of silk floss quilt according to claim 1, it is characterized in that: the dehydration in the described step (4) is centrifugal dehydration 1～2 minute, and bake out temperature is 70～80 ℃.
4. the anion far infrared post finishing method of silk floss quilt according to claim 1, it is characterized in that: the nanometer grade powder of described nano-negative ion far-infrared radiator for adopting micropowder processing method to obtain mixed by tourmaline and far-infrared ceramic powder.