CN106351014A - Red bean velvet far infrared heating and warm keeping functional fabric - Google Patents
Red bean velvet far infrared heating and warm keeping functional fabric Download PDFInfo
- Publication number
- CN106351014A CN106351014A CN201610730748.6A CN201610730748A CN106351014A CN 106351014 A CN106351014 A CN 106351014A CN 201610730748 A CN201610730748 A CN 201610730748A CN 106351014 A CN106351014 A CN 106351014A
- Authority
- CN
- China
- Prior art keywords
- fabric
- nano
- semen phaseoli
- powder
- far infrared
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to a red bean velvet far infrared heating and warm keeping functional fabric. During preparation, firstly, one or more of cotton fibers, polyester fibers and viscose fibers are adopted, mixed and woven into a fabric, and after refining, bleaching and dyeing are carried out, two-sided napping processing is carried out on a sanding machine, so that a red bean velvet fabric is obtained; then, the red bean velvet fabric is placed into a finishing agent prepared from one or mixture of more of nano titanium dioxide, nano aluminum oxide and nano zinc oxide powder to be subjected to finishing; and finally, tendering, sizing and finishing are carried out, so that the red bean velvet far infrared heating and warm keeping functional fabric is obtained. The preparation method of the fabric is simple, steps are easy to operate, the obtained fabric is subjected to napping treatment, the cloth surface is soft and comfortable, the washing fastness is high, no color change is caused, the cloth surface is fluffy and soft, and the fabric has three functions, namely a far infrared function, a moisture absorption heating function and a thermal insulation property.
Description
Technical field
The present invention relates to a kind of Semen Phaseoli floss far infrared heating heat-preserving function fabric, belong to knitting fabric preparing technical field.
Background technology
With the progress and development of science, clothing demand in addition to the primary demand to clothing, to tool New function for the people
Increasingly increasing.As underwear fabric, there is far infrared performance and the fabric of moisture absorption heating function, heat-preserving function triple functions
By moisture absorption heating function and far infrared function, the deep layer of skin can be penetrated, accelerate blood circulation, improve microcirculation shape
State, lifts human metabolism, has health care and the effect of auxiliary insulation.
Content of the invention
The invention aims to solving textile and its carrying out far infrared, moisture absorption heating with the fabric of chemical fibre blending
Functionalization arranges problem easy to change, washing fastness is low, fabric hardens, there is provided a kind of Semen Phaseoli floss far infrared heating heat-preserving function
Fabric, preparation process is simple, step is easily operated.
The present invention adopt the following technical scheme that a kind of Semen Phaseoli floss far infrared heating heat-preserving function fabric it is characterised in that: system
Standby technique comprises the steps:
(1) preparation of Semen Phaseoli velvet fabric
A, raw material adopt one or more of cotton fiber, polyster fibre, viscose fiber fiber blend, and fineness of yarn is 21～50
English props up or adopts polyester filament, and the fineness of long filament is 100 ~ 200d；
B, knitting: yarn is woven into from the two-sided knitting weft machine through 30 ~ 38 inches, pin number 18 ~ 36 pins/inch for the cylinder
Fabric；
C, refine, bleaching: the fabric that step (b) is obtained carries out refine and bleaching；
The condition of described refine is: refine bath raio be 15～30:1, refining temperature be 90～100 DEG C, refining time be 15～
50min；
The condition of described bleaching is: bleaching liquid is the hydrogen peroxide of concentration 1～40%, and bleaching bath ratio is for 5～20:1, the temperature of bleaching
For 15～55 DEG C, bleaching time is 5～35min；
D, dyeing: the fabric after processing through step (c) is dyeed；
E, dyeing post processing: processed using weak cation softening agent, the addition of weak cation softening agent is fabric weight
1.5～2.5%, bath raio is 5～30:1, is rolled after normal temperature dipping 1～5min, and pick-up is 25～80%, then 80～
105 DEG C of drying；
F, open width dry finishing: the fabric after step (e) is processed is 25～35% through dehydration to moisture content, it is fixed to dry in open width
Arranged in type machine, temperature is 150～165 DEG C, speed is 15～16m/min；
Pretreatment before g, napping: fabric is successively through overboard, decatize, drying and processing；
H, napping are processed: Semen Phaseoli velvet fabric is carried out on roughing-up machine double-edged napping processing, the speed of fabric is 16～
18m/min, the rotating speed of carbon brush hair roller are 1800～2000 turns/min；
(2) finishing functions of Semen Phaseoli velvet fabric: nano modification far-infrared magnetic functional finishing agent is stirred 5～30min at normal temperatures,
Mixing speed is 150～300 rad/min, by nano-far-infrared magnetic functional finishing agent homogeneous impregnation Semen Phaseoli velvet fabric, Ran Hou
Semen Phaseoli velvet fabric is padded, treatment temperature is 120～190 DEG C under pressure 0.5mpa ~ 10mpa pressure, process time 0.5min ~
3min；
(3) stentering forming arranges: the Semen Phaseoli velvet fabric after step (2) is processed carries out stentering forming arrangement, and temperature is 140 ~ 195
DEG C, the speed of fabric is 25 ~ 45m/min, and upper overfeed ratio is 15 ~ 35%, obtains Semen Phaseoli floss far infrared heating heat-preserving function fabric.
Further, the group of the nano-far-infrared magnetic functional finishing agent in described step (2) is divided into: nano modification titanium dioxide
Titanium valve body, nano aluminium oxide, one or more: 1.5 ~ 5g/l of nanometer Zinc oxide powder, penetrating agent: 2 ~ 5g/l, dispersant: 1 ~
3 g/l.
Further, described penetrating agent is fatty alcohol-polyoxyethylene ether, alkylphenol polyoxyethylene, aliphatic acid polyethenoxy
One or more of ether.
Further, described dispersant is sodium tripolyphosphate, sodium hexameta phosphate, sodium lauryl sulphate, fatty acid polyglycol second
One or more of diol ester.
Further, the preparation method of described nano-far-infrared magnetic functional finishing agent is: (1) nano-powder preparation method:
By titanium dioxide powder, zinc oxide, one or more of alumina powder jointed be that 1.5 ~ 5g/l adds distilled water to enter according to concentration
Row mix and blend, and prepare mass concentration for 2 ~ 3g/l cationic softener, add 2 ~ 5 g/l successively in cationic softener
Penetrating agent, mechanical ball grinding machine is ground, is ground rotating speed in 500 ~ 50000 rad/min, milling time is 0.5 ~ 2h,
Obtain nano-powder, through filtering, 30-150 DEG C of drying obtains nano-powder, and the particle diameter of nano-powder is in 0.5 ~ 100nm；
(2) by above-mentioned ground nano-powder through filtering, the nanometer powder of 1.5 ~ 5g/l and the dispersant of 1 ~ 3 g/l are configured
Solution, be uniformly mixed, be warming up to 50 ~ 55 DEG C, continue stirring 40 ~ 45min, cooling obtain finishing agent.
Further, described refining liquid component is: the knitting refining agent of 0.5～5g/l 729,1～5g/l soda, balance of
Water.
Further, the alkaline aqueous solution that described step (1) decline aqueous solution is 0.01～1mol/l for concentration, bath raio is
50～100:1, fabric soaks 1～50min in overboard solution, and the temperature of drying and processing is 60～90 DEG C, and drying time is 3～
10min；Then carry out decatize, steam temperature is 50～105 DEG C, steam pressure during decatize is 2～10mpa, steaming time is 5
～60min.
Preparation method of the present invention is simple, and step is easily operated, environmental friendly, and the Semen Phaseoli floss far infrared heating preparing is protected
Good stability washed by heating function fabric, and cloth pale face becomes, and far infrared performance, moisture absorption heating performance, heat-insulating property all reach state
Family's standard requires, as the underwear good application prospect of fabric performance.
Specific embodiment
Below in conjunction with specific embodiment, the present invention is further illustrated.
Embodiment one:
A kind of Semen Phaseoli floss far infrared heating heat-preserving function fabric, preparation technology comprises the steps:
(1) a kind of preparation of Semen Phaseoli velvet fabric
A, raw material adopt cotton fiber and viscose fiber blending, and fineness of yarn props up for 40 English, and adopts polyester filament, the fineness of long filament
For 150d；
B, knitting: yarn is woven into fabric from the two-sided knitting weft machine through 34 inches, 24 pins/inch for the cylinder；
C, refine, bleaching: the fabric that step (b) is obtained carries out refine and bleaching；
The condition of described refine is: refining liquid component is: the knitting refining agent of 0.5g/l 729,1g/l soda, balance of water；Refine
Bath raio is 15:1, and refining temperature is 90 DEG C, and refining time is 15min；
The condition of described bleaching is: bleaching liquid is the hydrogen peroxide of concentration 1.5%, and for 5:1, the temperature of bleaching is 55 DEG C to bleaching bath ratio,
Bleaching time is 35min；
D, dyeing: the fabric after processing through step (c) is dyeed；
E, dyeing post processing: using weak cation softening agent s200 process, the addition of weak cation softening agent s200 is
The 1.5% of fabric weight, bath raio is 5:1, is rolled after normal temperature dipping 1min, and pick-up is 25%, then dries at 80 DEG C；
F, open width dry finishing: the fabric after step (e) is processed is 25% through dehydration to moisture content, in open width drying and setting machine
In arranged, temperature be 150 DEG C, speed be 16m/min；
Pretreatment before g, napping: successively through overboard, decatize, drying and processing, overboard solution is the alkali of 0.01mol/l for concentration to fabric
Property aqueous solution, bath raio is 50:1, and fabric soaks 1min in overboard solution, and the temperature of drying and processing is 60 DEG C, and drying time is
3min；Then carry out decatize, steam temperature is 105 DEG C, steam pressure during decatize is mpa, steaming time is 5min；
H, napping are processed: the fabric after step (f) is processed carries out double-edged napping processing, the car of fabric on roughing-up machine
Speed is 16m/min, the rotating speed of carbon brush hair roller is 1800 turns/min；
(2) far-infrared functional, moisture absorption heating function, heat-preserving function arrange: by nano modification far-infrared magnetic functional finishing agent normal
Temperature is lower to stir 5min, and mixing speed is 300 rad/min, by nano-far-infrared magnetic functional finishing agent homogeneous impregnation Semen Phaseoli matte
Material, then pads Semen Phaseoli velvet fabric under pressure 0.5mpa pressure, and treatment temperature is 120 DEG C, process time 3min；
The group of nano-far-infrared magnetic functional finishing agent is divided into: nano modification titanium dioxide powder, nano aluminium oxide, nano zine oxide
One or more: 1.5g/l of powder body, penetrating agent: 2g/l, dispersant: 1 g/l；
Penetrating agent is one or more of fatty alcohol-polyoxyethylene ether, alkylphenol polyoxyethylene, aliphatic acid polyethenoxy ether；
Dispersant is one of sodium tripolyphosphate, sodium hexameta phosphate, sodium lauryl sulphate, fatty acid polyethylene glycol ester or many
Kind；
The preparation method of nano-far-infrared magnetic functional finishing agent is: nano-powder preparation method: by titanium dioxide powder, oxidation
Zinc, one or more of alumina powder jointed add distilled water to carry out mix and blend according to concentration for 1.5g/l, and prepare quality
Concentration is 2g/l cationic softener, adds the penetrating agent of 2 g/l successively in cationic softener, enterprising in mechanical ball grinding machine
Row grinds, and grinds rotating speed in 500rad/min, milling time is 2h, obtains nano-powder, through filtering, 30 DEG C of drying obtain nanometer
Powder body, the particle diameter of nano-powder is in 100nm；By above-mentioned ground nano-powder through filtering, the nanometer powder of configuration 1.5g/l
With the solution of the dispersant of 2g/l, it is uniformly mixed, is warming up to 50 DEG C, continue stirring 40min, cooling obtains finishing agent；
(3) stentering forming arranges: the Semen Phaseoli velvet fabric after step (2) is processed carries out stentering forming arrangement, and temperature is 140 DEG C,
The speed of fabric is 25m/min, and upper overfeed ratio is 15%.
Embodiment two:
A kind of Semen Phaseoli floss far infrared heating heat-preserving function fabric, preparation technology comprises the steps:
(1) a kind of preparation of Semen Phaseoli velvet fabric
A, raw material adopt cotton fiber and viscose fiber blending, and fineness of yarn props up for 40 English, and adopts polyester filament, the fineness of long filament
For 150 Denier；
B, knitting: yarn is woven into fabric from the two-sided knitting weft machine through 30 inches, 18 pins/inch for the cylinder；
C, refine, bleaching: the fabric that step (b) is obtained carries out refine and bleaching；
The condition of described refine is: refining liquid component is: the knitting refining agent of 0.8g/l 729,2g/l soda, balance of water；Refine
Bath raio is 25:1, and refining temperature is 100 DEG C, and refining time is 25min；
The condition of described bleaching is: bleaching liquid is the hydrogen peroxide of concentration 3%, and for 15:1, the temperature of bleaching is 35 DEG C to bleaching bath ratio,
Bleaching time is 15min；
D, dyeing: the fabric after processing through step (c) is dyeed；
E, dyeing post processing: using weak cation softening agent s200 process, the addition of weak cation softening agent s200 is
The 0.5% of fabric weight, bath raio is 25:1, is rolled after normal temperature dipping 1min, and pick-up is 35%, then dries at 80 DEG C；
F, open width dry finishing: the fabric after step (e) is processed is 35% through dehydration to moisture content, in open width drying and setting machine
In arranged, temperature be 165 DEG C, speed be 16m/min；
Pretreatment before g, napping: successively through overboard, decatize, drying and processing, overboard solution is the alkali of 0.1mol/l for concentration to fabric
Property aqueous solution, bath raio is 50:1, and fabric soaks 3min in overboard solution, and the temperature of drying and processing is 70 DEG C, and drying time is
3min；Then carry out decatize, steam temperature is 105 DEG C, steam pressure during decatize is 2mpa, steaming time is 5min；
H, napping are processed: the fabric after step (f) is processed carries out double-edged napping processing, the car of fabric on roughing-up machine
Speed is 16m/min, the rotating speed of carbon brush hair roller is 2000 turns/min；
(2) far-infrared functional, moisture absorption heating function, heat-preserving function arrange: by nano modification far-infrared magnetic functional finishing agent normal
Temperature is lower to stir 20min, and mixing speed is 200 rad/min, by nano-far-infrared magnetic functional finishing agent homogeneous impregnation Semen Phaseoli matte
Material, then pads Semen Phaseoli velvet fabric under pressure 8mpa pressure, and treatment temperature is 150 DEG C, process time 2min；
The group of nano-far-infrared magnetic functional finishing agent is divided into: nano modification titanium dioxide powder, nano aluminium oxide, nano zine oxide
One or more: 3g/l of powder body, penetrating agent: 3g/l, dispersant: 2 g/l；
Penetrating agent is one or more of fatty alcohol-polyoxyethylene ether, alkylphenol polyoxyethylene, aliphatic acid polyethenoxy ether；
Dispersant is one of sodium tripolyphosphate, sodium hexameta phosphate, sodium lauryl sulphate, fatty acid polyethylene glycol ester or many
Kind；
The preparation method of nano-far-infrared magnetic functional finishing agent is: nano-powder preparation method: by titanium dioxide powder, oxidation
Zinc, one or more of alumina powder jointed add distilled water to carry out mix and blend according to concentration for 3g/l, and it is dense to prepare quality
Spend for 2g/l cationic softener, add the penetrating agent of 3g/l successively in cationic softener, mechanical ball grinding machine is carried out
Grind, grind rotating speed in 5000 rad/min, milling time is 1h, obtains nano-powder, through filtering, 100 DEG C of drying are received
Rice flour body, the particle diameter of nano-powder is in 80nm；By above-mentioned ground nano-powder through filtering, the nanometer powder of configuration 3g/l
With the solution of the dispersant of 2 g/l, it is uniformly mixed, is warming up to 50 DEG C, continue stirring 42min, cooling obtains finishing agent；
(3) stentering forming arranges: the Semen Phaseoli velvet fabric after step (2) is processed carries out stentering forming arrangement, and temperature is 160 DEG C,
The speed of fabric is 15m/min, and upper overfeed ratio is 25%.
Embodiment three:
A kind of Semen Phaseoli floss far infrared heating heat-preserving function fabric, preparation technology comprises the steps:
(1) a kind of preparation of Semen Phaseoli velvet fabric
A, raw material adopt cotton fiber and viscose fiber blending, and fineness of yarn props up for 50 English, and adopts polyester filament, the fineness of long filament
For 200d；
B, knitting: yarn is woven into fabric from the two-sided knitting weft machine through 38 inches, 36 pins/inch for the cylinder；
C, refine, bleaching: the fabric that step (b) is obtained carries out refine and bleaching；
The condition of described refine is: refining liquid component is: the knitting refining agent of 0.8g/l 729,2g/l soda, balance of water；Refine
Bath raio is 30:1, and refining temperature is 100 DEG C, and refining time is 50min；
The condition of described bleaching is: bleaching liquid is the hydrogen peroxide of concentration 3%, and for 20:1, the temperature of bleaching is 15 DEG C to bleaching bath ratio,
Bleaching time is 5min；
D, dyeing: the fabric after processing through step (c) is dyeed；
E, dyeing post processing: using weak cation softening agent s200 process, the addition of weak cation softening agent s200 is
The 2.5% of fabric weight, bath raio is 30:1, is rolled after normal temperature dipping 5min, and pick-up is 80%, then dries at 105 DEG C；
F, open width dry finishing: the fabric after step (e) is processed is 35% through dehydration to moisture content, in open width drying and setting machine
In arranged, temperature be 150 DEG C, speed be 15m/min；
Pretreatment before g, napping: successively through overboard, decatize, drying and processing, overboard solution is the alkalescence of 1mol/l for concentration to fabric
Aqueous solution, bath raio is 100:1, and fabric soaks 50min in overboard solution, and the temperature of drying and processing is 90 DEG C, and drying time is
10min；Then carry out decatize, steam temperature is 50 DEG C, steam pressure during decatize is 10mpa, steaming time is 60min；
H, napping are processed: the fabric after step (f) is processed carries out double-edged napping processing, the car of fabric on roughing-up machine
Speed is 16m/min, the rotating speed of carbon brush hair roller is 2000 turns/min；
(2) far-infrared functional, moisture absorption heating function, heat-preserving function arrange: by nano modification far-infrared magnetic functional finishing agent normal
Temperature is lower to stir 30min, and mixing speed is 150 rad/min, by nano-far-infrared magnetic functional finishing agent homogeneous impregnation Semen Phaseoli matte
Material, then pads Semen Phaseoli velvet fabric under pressure 10mpa pressure, and treatment temperature is 190 DEG C, process time 0.5min；
The group of nano-far-infrared magnetic functional finishing agent is divided into: nano modification titanium dioxide powder, nano aluminium oxide, nano zine oxide
One or more: 5g/l of powder body, penetrating agent: 5g/l, dispersant: 3 g/l；
Penetrating agent is one or more of fatty alcohol-polyoxyethylene ether, alkylphenol polyoxyethylene, aliphatic acid polyethenoxy ether；
Dispersant is one of sodium tripolyphosphate, sodium hexameta phosphate, sodium lauryl sulphate, fatty acid polyethylene glycol ester or many
Kind；
The preparation method of nano-far-infrared magnetic functional finishing agent is: nano-powder preparation method: by titanium dioxide powder, oxidation
Zinc, one or more of alumina powder jointed add distilled water to carry out mix and blend according to concentration for 5g/l, and it is dense to prepare quality
Spend for 3g/l cationic softener, add the penetrating agent of 5 g/l successively in cationic softener, mechanical ball grinding machine is carried out
Grind, grind rotating speed in 50000 rad/min, milling time is 0.5h, obtains nano-powder, through filtering, 150 DEG C of drying obtain
Nano-powder, the particle diameter of nano-powder is in 0.5nm；By above-mentioned ground nano-powder through filtering, the nano powder of configuration 5g/l
The solution of the dispersant of end and 3 g/l, is uniformly mixed, is warming up to 55 DEG C, continues stirring 45min, and cooling obtains finishing agent；
(3) stentering forming arranges: the Semen Phaseoli velvet fabric after step (2) is processed carries out stentering forming arrangement, and temperature is 195 DEG C,
The speed of fabric is 45m/min, and upper overfeed ratio is 35%.
Claims (7)
1. a kind of Semen Phaseoli floss far infrared heating heat-preserving function fabric it is characterised in that: preparation technology comprises the steps:
(1) preparation of Semen Phaseoli velvet fabric
A, raw material adopt one or more of cotton fiber, polyster fibre, viscose fiber fiber blend, and fineness of yarn is 21～50
English props up or adopts polyester filament, and the fineness of long filament is 100 ~ 200d；
B, knitting: yarn is woven into from the two-sided knitting weft machine through 30 ~ 38 inches, pin number 18 ~ 36 pins/inch for the cylinder
Fabric；
C, refine, bleaching: the fabric that step (b) is obtained carries out refine and bleaching；
The condition of described refine is: refine bath raio be 15～30:1, refining temperature be 90～100 DEG C, refining time be 15～
50min；
The condition of described bleaching is: bleaching liquid is the hydrogen peroxide of concentration 1～40%, and bleaching bath ratio is for 5～20:1, the temperature of bleaching
For 15～55 DEG C, bleaching time is 5～35min；
D, dyeing: the fabric after processing through step (c) is dyeed；
E, dyeing post processing: processed using weak cation softening agent, the addition of weak cation softening agent is fabric weight
1.5～2.5%, bath raio is 5～30:1, is rolled after normal temperature dipping 1～5min, and pick-up is 25～80%, then 80～
105 DEG C of drying；
F, open width dry finishing: the fabric after step (e) is processed is 25～35% through dehydration to moisture content, it is fixed to dry in open width
Arranged in type machine, temperature is 150～165 DEG C, speed is 15～16m/min；
Pretreatment before g, napping: fabric is successively through overboard, decatize, drying and processing；
H, napping are processed: Semen Phaseoli velvet fabric is carried out on roughing-up machine double-edged napping processing, the speed of fabric is 16～
18m/min, the rotating speed of carbon brush hair roller are 1800～2000 turns/min；
(2) finishing functions of Semen Phaseoli velvet fabric: nano modification far-infrared magnetic functional finishing agent is stirred 5～30min at normal temperatures,
Mixing speed is 150～300 rad/min, by nano-far-infrared magnetic functional finishing agent homogeneous impregnation Semen Phaseoli velvet fabric, Ran Hou
Semen Phaseoli velvet fabric is padded, treatment temperature is 120～190 DEG C, process time 0.5 ~ 3min under pressure 0.5 ~ 10mpa pressure；
(3) stentering forming arranges: the Semen Phaseoli velvet fabric after step (2) is processed carries out stentering forming arrangement, and temperature is 140 ~ 195
DEG C, the speed of fabric is 25 ~ 45m/min, and upper overfeed ratio is 15 ~ 35%, obtains Semen Phaseoli floss far infrared heating heat-preserving function fabric.
2. Semen Phaseoli floss far infrared heating heat-preserving function fabric as claimed in claim 1 it is characterised in that: in described step (2)
The group of nano-far-infrared magnetic functional finishing agent be divided into: nano modification titanium dioxide powder, nano aluminium oxide, nano zinc oxide powder
One or more: 1.5 ~ 5g/l of body, penetrating agent: 2 ~ 5g/l, dispersant: 1 ~ 3 g/l.
3. Semen Phaseoli floss far infrared heating heat-preserving function fabric as claimed in claim 2 it is characterised in that: described penetrating agent be fat
One or more of fat polyoxyethylenated alcohol, alkylphenol polyoxyethylene, aliphatic acid polyethenoxy ether.
4. Semen Phaseoli floss far infrared heating heat-preserving function fabric as claimed in claim 2 it is characterised in that: described dispersant be three
One or more of polyphosphate sodium, sodium hexameta phosphate, sodium lauryl sulphate, fatty acid polyethylene glycol ester.
5. Semen Phaseoli floss far infrared heating heat-preserving function fabric as claimed in claim 2 it is characterised in that: described nano-far-infrared
The preparation method of magnetic functional finishing agent is: (1) nano-powder preparation method: by titanium dioxide powder, zinc oxide, alumina powder jointed
One or more of according to concentration be 1.5 ~ 5g/l add distilled water carry out mix and blend, and prepare mass concentration be 2 ~ 3g/l
Cationic softener, adds the penetrating agent of 2 ~ 5 g/l successively in cationic softener, is ground on mechanical ball grinding machine,
Grind rotating speed in 500-50000 rad/min, milling time is 0.5-2h, obtains nano-powder, through filtration, 30-150 DEG C of drying
Obtain nano-powder, the particle diameter of nano-powder is in 0.5-100nm；
(2) by above-mentioned ground nano-powder through filtering, the nanometer powder of 1.5 ~ 5g/l and the dispersant of 1 ~ 3 g/l are configured
Solution, be uniformly mixed, be warming up to 50 ~ 55 DEG C, continue stirring 40 ~ 45min, cooling obtain finishing agent.
6. Semen Phaseoli floss far infrared heating heat-preserving function fabric as claimed in claim 1 it is characterised in that: described refining liquid component
For: the knitting refining agent of 0.5～5g/l 729,1～5g/l soda, balance of water.
7. Semen Phaseoli floss far infrared heating heat-preserving function fabric as claimed in claim 1 it is characterised in that: in described step (1)
The alkaline aqueous solution that overboard solution is 0.01～1mol/l for concentration, bath raio is 50～100:1, and fabric soaks in overboard solution
1～50min, the temperature of drying and processing is 60～90 DEG C, and drying time is 3～10min；Then carry out decatize, steam temperature is
50～105 DEG C, steam pressure during decatize is 2～10mpa, and steaming time is 5～60min.