CN108374124A - 一种合金钢 - Google Patents

一种合金钢 Download PDF

Info

Publication number
CN108374124A
CN108374124A CN201810272611.XA CN201810272611A CN108374124A CN 108374124 A CN108374124 A CN 108374124A CN 201810272611 A CN201810272611 A CN 201810272611A CN 108374124 A CN108374124 A CN 108374124A
Authority
CN
China
Prior art keywords
steel alloy
alloy
steel
present
less
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201810272611.XA
Other languages
English (en)
Inventor
冯满
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CN201810272611.XA priority Critical patent/CN108374124A/zh
Publication of CN108374124A publication Critical patent/CN108374124A/zh
Pending legal-status Critical Current

Abstract

本发明涉及一种合金钢，机电设备使用的一种合金钢。

Description

一种合金钢
技术领域
本发明涉及一种合金钢，机电设备使用的一种合金钢。
背景技术
目前机电设备制造使用的合金钢20Cr2Ni4，对于有高等级要求的机电设备生产厂家其力学性能的抗拉强度、屈服强度、伸长率、冲击功不能达到高等级产品的设计要求，易疲劳、开裂，不能满足特殊行业的要求。因此需要一种新的方案解决上述技术问题。
发明内容
本发明所要解决的是克服现有技术存在的问题。提供一种合金钢，使其力学性能提高，能够用于制造高等级技术要求的机电设备。
本发明解决上述技术所采用的技术方案为一种合金钢，其质量百分比(％)组成如下：
本发明有针对性的优化合金钢元素的配比，提高合金钢(82A)的综合力学性能。
具体实施方式
为了加深对本发明的理解和认识，以下结合实施例对本发明做进一步描述。
为了得到符合性能要求合金钢材料，保证机电设备高强度部件性能要求。本发明通过改变合金钢中的微量元素的比例，得到实施例1-6个合金钢产品，其具体组成比见表1。
表1
化学成分(质量元素)％
序号 牌号 C Si Mn Cr Ni Mo
1 20Cr2Ni4 0.17-0.23 0.17-0.37 0.30-0.60 1.25-1.65 3.25-3.65
2 实施例1 0.16 0.2 0.4 1.2 3.9 0.2
3 实施例2 0.18 0.25 0.45 1.4 4.0 0.22
4 实施例3 0.20 0.30 0.5 1.4 4.2 0.26
5 实施例4 0.20 0.25 0.55 1.4 4.0 0.28
6 实施例5 0.18 0.25 0.4 1.4 4.0 0.25
7 实施例6 0.16 0.25 0.35 1.2 4.0 0.2
将表1得到的合金钢(82A)制成钢棒得到的性能见表2及与现有材料性能的对比。
表2
现有材料及本发明实施例合金材料的性能对比
从表2中可以看到，本发明的实施例1-6得到的合金钢(82A)其抗拉强度、屈服强度、断后伸长率、冲击功有了大幅提高，满足特种钢设备的使用。

Claims (5)

1.一种合金钢，其特征在于，所述合金钢包括：碳、硅、锰、磷、硫、铬、镍、钼、铜、铝、氧和铁；
上述元素的质量百分比为：碳0.14％-0.20％、硅0.15％-0.40％、锰0.30％-0.60％、磷不大于0.030％、硫不大于0.025、铬1.00％-1.40％、镍3.80％-4.30％、钼0.20％-0.30％、铜小于0.30％、铝小于0.05％、氧小于0.02％，其余为铁。
2.如权利要求1所述的合金钢，其特征在于，所述合金钢的抗拉强度为1350-1600Mpa。
3.如权利要求1所述的合金钢，其特征在于，所述合金钢的屈服强度为1250-1500Mpa。
4.如权利要求1所述的合金钢，其特征在于，所述合金钢的断后伸长率δ5为13-18％。
5.如权利要求1所述的合金钢，其特征在于，所述合金钢的冲击功ak为80-100J。
CN201810272611.XA 2018-03-29 2018-03-29 一种合金钢 Pending CN108374124A (zh)