CN108342650A - 一种合金钢 - Google Patents

一种合金钢 Download PDF

Info

Publication number
CN108342650A
CN108342650A CN201810272233.5A CN201810272233A CN108342650A CN 108342650 A CN108342650 A CN 108342650A CN 201810272233 A CN201810272233 A CN 201810272233A CN 108342650 A CN108342650 A CN 108342650A
Authority
CN
China
Prior art keywords
steel alloy
steel
present
sulphur
molybdenum
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201810272233.5A
Other languages
English (en)
Inventor
冯满
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CN201810272233.5A priority Critical patent/CN108342650A/zh
Publication of CN108342650A publication Critical patent/CN108342650A/zh
Pending legal-status Critical Current

Abstract

本发明涉及一种合金钢，提高了合金钢106A的综合力学性能，所述合金钢包括：碳、硅、锰、磷、硫、铬、钼、镍和铁；上述元素的质量百分比为：碳0.20％‑0.28％、硅0.10％‑0.35％、锰0.40％‑0.70％、磷不大于0.025％、硫不大于0.025％、铬3.00％‑3.50％、钼0.50％‑0.70％、镍不大于0.30％，其余为铁。

Description

一种合金钢
技术领域
本发明涉及一种合金钢。
背景技术
目前机电设备制造使用的合金钢1Cr5Mo对于有高等级要求的机电设备生产厂家，其力学性能的抗拉强度、屈服强度、伸长率不能达到高等级产品的设计要求。易疲劳、开裂不能满足特殊行业的要求，因此需要一种新的技术方案解决上述技术问题。
发明内容
本发明所要解决的技术问题是克服现有技术存在的缺陷问题，提供一种合金钢，使其力学性能得以提高，能够用于制造高等级技术要求的机电设备。
发明解决上述技术问题所采用的技术方案为：一种合金钢(106A)
其质量百分比的组成如下：
本发明有针对性的优化合金钢的配比，提高了合金钢106A的综合力学性能。
具体实施方式
为了加深对本发明的理解与认识，以下结合实施例对本发明做进一步描述：为了得到符合性能要求的合金钢材料，保证机电设备高强度部件的性能要求，本发明通过改变合金钢中的微量元素的比例，得到实施例1-6个合金钢产品，其具体组成见表1
表1
化学成分(质量分数)％
序号 牌号 C Si Mn Cr Mo Ni
1 1Cr5Mo ≤0.15 ≤0.50 ≤0.60 4-6 0.45-0.60 ≤0.6
2 实施例1 0.2 0.1 0.4 3.5 0.5 0.2
3 实施例2 0.24 0.2 0.5 3.5 0.5 0.2
4 实施例3 0.28 0.33 0.68 3.5 0.5 0.2
5 实施例4 0.2 0.1 0.4 3.0 0.7 0.3
6 实施例5 0.24 0.2 0.5 3.0 0.7 0.3
7 实施例6 0.28 0.33 0.68 3.0 0.7 0.3
将表1得到的合金钢(106A)制成钢棒得到的性能与现有材料性能的对比见表2
表2
现有材料与本发明实施例合金材料的性能对比
从表2中可以看到，本发明的实施例1-6得到的合金钢(106A)，其抗拉强度、屈服强度、断后伸长率都有了大幅提高，满足了高标准特种设备的使用要求。

Claims (4)

1.一种合金钢，其特征在于，所述合金钢包括：碳、硅、锰、磷、硫、铬、钼、镍和铁；
上述元素的质量百分比为：碳0.20％-0.28％、硅0.10％-0.35％、锰0.40％-0.70％、磷不大于0.025％、硫不大于0.025％、铬3.00％-3.50％、钼0.50％-0.70％、镍不大于0.30％，其余为铁。
2.如权利要求1所述的合金钢，其特征在于，所述合金钢的抗拉强度为800-1200Mpa。
3.如权利要求1所述的合金钢，其特征在于，所述合金钢的屈服强度为700-900Mpa。
4.如权利要求1所述的合金钢，其特征在于，所述合金钢的断后伸长率为20％-25％。
CN201810272233.5A 2018-03-29 2018-03-29 一种合金钢 Pending CN108342650A (zh)