CN1718830A - 一种制造芯棒用合金钢材料 - Google Patents

一种制造芯棒用合金钢材料 Download PDF

Info

Publication number
CN1718830A
CN1718830A CN 200510085632 CN200510085632A CN1718830A CN 1718830 A CN1718830 A CN 1718830A CN 200510085632 CN200510085632 CN 200510085632 CN 200510085632 A CN200510085632 A CN 200510085632A CN 1718830 A CN1718830 A CN 1718830A
Authority
CN
China
Prior art keywords
alloy steel
steel material
core rod
mpa
manufacturing core
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN 200510085632
Other languages
English (en)
Inventor
刘鹏程
秦宜传
吕文海
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Gangwei Hydraulic Part Co Ltd Baotou Iron And Steel Corp
Original Assignee
Gangwei Hydraulic Part Co Ltd Baotou Iron And Steel Corp
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Gangwei Hydraulic Part Co Ltd Baotou Iron And Steel Corp filed Critical Gangwei Hydraulic Part Co Ltd Baotou Iron And Steel Corp
Priority to CN 200510085632 priority Critical patent/CN1718830A/zh
Publication of CN1718830A publication Critical patent/CN1718830A/zh
Pending legal-status Critical Current

Abstract

本发明涉及一种制造芯棒用合金钢材料，其特征是：合金钢材料是由碳、硅、锰、铬、镍、钼、钒、磷、硫、铁元素组成，各元素的含量按重量百分比计：碳0.30～0.50％、硅0.20～0.80％、锰0.50～1.50％、铬1.20～2.50％、镍0.70～1.50％、钼0.25～0.80％、钒0.20～0.50％、磷≤0.02、硫≤0.008、余量为铁。其优点是：第一、具有良好的锻造性能，在制造芯棒的过程中经过六次加热六次锤锻，压缩比超过10，没有发现裂纹缺陷；第二、在高温状态下力学性能好，可提高芯棒的使用寿命，降低钢管的生产成本。

Description

一种制造芯棒用合金钢材料
                           技术领域
本发明涉及一种制造芯棒用合金钢材料。
                           背景技术
芯棒是生产无缝钢管的专用工具，为细长杆结构，最长可达17.5米。在负荷大、频率高、急冷、急热的恶劣条件下工作，消耗大，在生产无缝钢管的成本中占较大比重。目前，国内外制造芯棒用的材料均为H13。H13材料在加工中只能一次加热一次锻造成型，否则会产生严重的裂纹，因此要求有大加热炉、四锤头或六锤头的先进快锻锤加工毛坯，使毛坯成本较高。
                           发明内容
本发明的目的是提供一种具有良好的锻造性能，在高温状态下力学性能好，可提高芯棒使用寿命，降低无缝钢管生产成本的制造芯棒用合金钢材料。
本发明的合金钢材料是由碳、硅、锰、铬、镍、钼、钒、磷、硫、铁元素组成，各元素的含量按重量百分比计：碳0.30～0.50％、硅0.20～0.80％、锰0.50～1.50％、铬1.20～2.50％、镍0.70～1.50％、钼0.25～0.80％、钒0.20～0.50％、磷≤0.02、硫≤0.008、余量为铁。
本发明的优点是：第一、具有良好的锻造性能，在制造芯棒的过程中经过六次加热六次锤锻，截面积压缩比超过20，没有发现裂纹缺陷；而使用H13材料只能一次加热一次锻造成型，否则产生严重的裂纹；第二、在高温状态下力学性能好，可提高芯棒的使用寿命，降低钢管的生产成本。
                         具体实施方式
本发明的合金钢材料是由碳、硅、锰、铬、镍、钼、钒、磷、硫、铁元素组成，各元素的含量按重量百分比计：碳0.30～0.50％、硅0.20～0.80％、锰0.50～1.50％、铬1.20～2.50％、镍0.70～1.50％、钼0.25～0.80％、钒0.20～0.50％、磷≤0.02、硫≤0.008、余量为铁。
本发明的制造工艺流程为：电炉炼钢-→炉外精炼真空脱气-→铸锭-→调质。
下面是本发明的合金钢材料在力学性能方面的检验结果：
(1)横向常温力学性能
    σbMPa   σ0.2MPa     δ％     ψ％   AkvJ HRC
合金钢     111010601090 -     14.015.014.0     59.064.563.0   10397112      37.034.0     36.535.0     36.034.5
H13     11901200   10201020     16.011.5     57.052.0   8978      32.030.0     31.031.5     33.532.5
  1190   1020   15.5   52.5     79     34.0     34.5     35.0
(2)纵向常温力学性能
  σbMPa   σ0.2MPa     δ％    ψ％     AkvJ HRC
合金钢   106010701040 -     17.016.518.0    66.570.068.5     124123123     29.530.5     33.031.0     31.529.0
H13   119011901190   103010101010     17.015.012.5    55.553.059.5     312826     38.034.538.5     39.033.039.0     38.035.039.0
(3)向高温力学性能
                        550℃                         650℃
  σbMPa   σsMPa   δ％   ψ％   σbMPa   σsMPa   δ％     ψ％
合金钢 9951030   895890915   14.514.014.0   74.568.568.0   975980955   865855890   14.513.014.5     74.575.076.5
H13   101010101030 -   13.514.013.0   63.061.562.5   980975955 -   13.012.013.0     62.560.064.0
(4)重新热处理后合金钢材料与H13的纵向常温力学性能比较
    σbMPa    σ0.2MPa   δ％   ψ％   AkvJ HRC
  重新热处理后的合金钢     1230     1140   17.5   58.5   88   41.0   41.0   40.0
    1250     1170   16.5   57.0   87   42.5   42.5   41.0
    1240     1140   16.5   60.5   80   41.0   40.5   42.0
H13     1190     1030   17.0   55.5   31   38.0   39.0   38.0
    1190     1010   15.0   53.0   28   34.5   33.0   35.0
    1190     1010   12.5   59.5   26   38.5   39.0   39.0
  国外所给H13数据 1029-1176 ≥882 ≥8 ≥25 ≥15 34-39
实例一：
化学成份(重量百分比，余量为铁)：
  C   Si   Mn   P   S     Cr   Ni   Mo   V
  0.324   0.30   0.610   0.0119   0.002     1.41   0.916   0.307   0.25
力学性能：
  σb   σ0.2   δ   ψ  Akv(J)     HRC
  1240   1150   16.5   58.5  85     40.5-42.5
实例二：
化学成份(重量百分比，余量为铁)：
    C     Si     Mn     P     S     Cr     Ni     Mo     V
    0.35     0.34     0.60     0.015     0.002     1.54     0.85     0.31     0.30
力学性能：
  σb   σ0.2   δ    ψ  Akv(J)     HRC
  1250   1170   17.0     57  87     41-43

Claims (1)

1.一种制造芯棒用合金钢材料，其特征是：合金钢材料是由碳、硅、锰、铬、镍、钼、钒、磷、硫、铁元素组成，各元素的含量按重量百分比计：碳0.30～0.50％、硅0.20～0.80％、锰0.50～1.50％、铬1.20～2.50％、镍0.70～1.50％、钼0.25～0.80％、钒0.20～0.50％、磷≤0.02、硫≤0.008、余量为铁。
CN 200510085632 2005-07-20 2005-07-20 一种制造芯棒用合金钢材料 Pending CN1718830A (zh)