CN108358449A - The application method of lightweight porcelain low temperature transmutation erythema glaze - Google Patents
The application method of lightweight porcelain low temperature transmutation erythema glaze Download PDFInfo
- Publication number
- CN108358449A CN108358449A CN201810317933.1A CN201810317933A CN108358449A CN 108358449 A CN108358449 A CN 108358449A CN 201810317933 A CN201810317933 A CN 201810317933A CN 108358449 A CN108358449 A CN 108358449A
- Authority
- CN
- China
- Prior art keywords
- glaze
- transmutation
- parts
- erythema
- low temperature
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention belongs to ceramic manufacturing fields, and in particular to a kind of furnace transmutation glaze, preparation method and application method fired for light china.This kind of lightweight porcelain low temperature transmutation erythema glaze, including glass powder, clear frit glaze, red stain, nepheline powder, boric acid, kaolin, zinc oxide.This kind of transmutation erythema glaze glaze is at low cost, and easy to use, firing temperature is low, has unique artistic feeling.The glazing effect that this kind of transmutation erythema glaze is burnt out has red or copper red color background color, it uniformly distributed irregular black splotch on background color, the size of black splotch and respectively density change according to ceramic type and glazing thickness, have unique artistic effect.The porcelain made using this kind of glaze improves product specification and selling price, has higher economic value；In addition this kind of glaze can be produced with bulk industrial, can Rapid Popularization, using simple, there is stronger competitiveness on the market.
Description
The application is the divisional application of " lightweight porcelain low temperature transmutation erythema glaze formula, method of preparation and use ", original application
The applying date be on 08 27th, 2015, application No. is：CN201510534705.6.
Technical field
The invention belongs to ceramic manufacturing fields, and in particular to a kind of furnace transmutation glaze, preparation method for light china firing
And application method.
Background technology
When furnace transmutation glaze, that is, implements are burnt into kiln, due to containing in kiln there are many pigmentation element, oxidized or reduction,
Unexpected glaze colours effect is presented after kiln discharge.Traditional furnace transmutation glaze be high temperature firing, firing temperature at 1200 DEG C or more,
Firing time is mostly at 12 more than hour, and firing temperature is high, the time is long, and energy loss is big, leads to of high cost and not ring
It protects；And the glazing effect of existing lightweight white clouds pottery furnace transmutation glaze is single, kind is dull, and the consumer that can not cater to different individual characteies needs
It asks.
To solve the above problems, the patent of invention of Patent No. 201110133469.9 discloses a kind of furnace transmutation glaze white clouds
Pottery and its manufacture craft, this kind of Transmutation glaze white cloud ceramics, including white clouds greenwave body and impose on white clouds pottery billet surface on glaze
Layer, the glaze layer include directly apply white clouds make pottery billet surface ground-coat enamel and impose on the overglaze on ground-coat enamel face；The each group subpackage of ground-coat enamel
Include low-temperature lead-free frit, coloring oxide, calcium carbonate, alkaline earth metal compound, part kaolin；The each component of the overglaze is pressed
Weight proportion is low-temperature lead-free frit, part zinc oxide, part titanium oxide, coloring oxide, part kaolin.The burning of this kind of furnace transmutation glaze
Appointing at temperature need to be between 1080-1100 DEG C, and the glazed surface burnt out forms naturally crystallization flower.As people live
Horizontal continuous improvement, also constantly changes aesthetic diversified demand, if it is low to develop a kind of firing temperature, with area
Not in the glaze of traditional transmutation effect, can meet aesthetic diversified demand has positive meaning again.
Invention content
In order to solve deficiency in the prior art, the present invention provides a kind of lightweight porcelain low temperature transmutation erythema glaze, prepare
And application method.
Lightweight porcelain low temperature transmutation erythema glaze, which is characterized in that the glaze is as follows in parts by weight：Glass powder 30-
45 parts, 25-35 parts of clear frit glaze, 5-20 parts of red stain, 5-10 parts of nepheline powder, 5-10 parts of boric acid, 3-8 parts of kaolin, oxidation
2-5 parts of zinc.
Optimization, glaze is as follows in parts by weight：40 parts of glass powder, 30 parts of clear frit glaze, 10 parts of red stain, rosy clouds
5 parts of mountain flour, 5 parts of boric acid, 8 parts of kaolin, 2 parts of zinc oxide.
Optimization, glaze is as follows in parts by weight：42 parts of glass powder, 28 parts of clear frit glaze, 6 parts of red stain, nepheline
8 parts of powder, 6 parts of boric acid, 5 parts of kaolin, 5 parts of zinc oxide.
The preparation method of lightweight porcelain low temperature transmutation erythema glaze, which is characterized in that include the following steps：
Step 1, according to glaze weighing and proportioning, by glass powder, clear frit glaze, nepheline powder, boric acid, kaolin, oxidation
Zinc is put into ball grinder, and the water of 50-60% is added；
Step 2, ball milling are put into red stain and are added in ball grinder ball milling 20-40 minutes together after 10-15 hours；
Step 3, the glaze that step 2 is obtained are sieved for use, and transmutation erythema glaze is made.
Further, the glaze in step 3 crosses 200 mesh sieve.
The application method of lightweight porcelain low temperature transmutation erythema glaze, which is characterized in that include the following steps：
Step 1, light ceramics green body is prepared；
Step 2, transmutation erythema glaze is warming up to 35-40 DEG C, imposed on light ceramics green body, placed 5-10 hours；
Step 3, there is the ceramic body of transmutation erythema glaze to be put into oxidizing flame in kiln by to fire, firing temperature is 980
Between DEG C -1060 DEG C.
Further, the enameling method in step 2 is leaching glaze or glaze spraying.
Further, in step 3, after ceramic body enters kiln, kiln is brought rapidly up to firing temperature, naturally cold after firing
But.
Seen from the above description, lightweight porcelain low temperature transmutation erythema glaze provided by the invention, method of preparation and use, tool
It has the advantages that：First, glaze is at low cost, used raw material is all easy to get, and manufacture craft is simple；Second is that
It is easy to use, it only need to be in billet surface last layer glaze without ground-coat enamel using this kind of low temperature transmutation erythema glaze；Third, firing
Temperature is low, and transmutation effect can be realized between only needing 980 DEG C -1060 DEG C in the firing temperature of this kind of transmutation erythema glaze, saves
The energy；Fourth, having unique artistic feeling, the glazing effect that this kind of transmutation erythema glaze is burnt out has red or copper red color
Background color, uniformly distributed irregular black splotch on background color, the size of black splotch and respectively density are according to ceramics
Type and glazing thickness and change, have unique artistic effect；The porcelain made using this kind of glaze improves product specification
And selling price, there is higher economic value；In addition this kind of glaze can be produced with bulk industrial, can Rapid Popularization, use
Simply, there is stronger competitiveness on the market.
Specific implementation mode
For a better understanding of the technical solution of the present invention, embodiment provided by the invention is described below in detail.
Lightweight porcelain low temperature transmutation erythema glaze, it is as follows in parts by weight：30-45 parts of glass powder, clear frit glaze 25-
35 parts, 5-20 parts of red stain, 5-10 parts of nepheline powder, 5-10 parts of boric acid, 3-8 parts of kaolin, 2-5 parts of zinc oxide.
Specific embodiment one：
Glaze is as follows in parts by weight：40 parts of glass powder, 30 parts of clear frit glaze, 10 parts of red stain, 5 parts of nepheline powder,
5 parts of boric acid, 8 parts of kaolin, 2 parts of zinc oxide.
The preparation method of above-mentioned lightweight porcelain low temperature transmutation erythema glaze, includes the following steps：
Step 1, according to glaze weighing and proportioning, by glass powder, clear frit glaze, nepheline powder, boric acid, kaolin, oxidation
Zinc is put into ball grinder, and 60% water is added；
Step 2, ball milling are put into red stain and ball milling 30 minutes together are added in ball grinder after 12 hours；
The glaze that step 2 obtains is crossed 200 mesh sieve for use, transmutation erythema glaze is made by step 3.
The application method of lightweight porcelain low temperature transmutation erythema glaze, includes the following steps：
Step 1, light ceramics green body is prepared；
Step 2, transmutation erythema glaze is warming up to 38 DEG C, imposed on light ceramics green body, placed 8 hours, enameling method
For leaching glaze or glaze spraying；
Step 3, there is the ceramic body of transmutation erythema glaze to be put into oxidizing flame in kiln by to fire, firing temperature exists
1050 DEG C, after ceramic body enters kiln, kiln is brought rapidly up to firing temperature, natural cooling after firing.
Specific embodiment two：
Glaze is as follows in parts by weight：42 parts of glass powder, 28 parts of clear frit glaze, 6 parts of red stain, 8 parts of nepheline powder,
6 parts of boric acid, 5 parts of kaolin, 5 parts of zinc oxide.
The preparation method of the lightweight porcelain low temperature transmutation erythema glaze of specific embodiment two to four, includes the following steps：
Step 1, according to glaze weighing and proportioning, by glass powder, clear frit glaze, nepheline powder, boric acid, kaolin, oxidation
Zinc is put into ball grinder, and the water of 50-60% is added；
Step 2, ball milling are put into red stain and are added in ball grinder ball milling 20-40 minutes together after 10-15 hours；
The glaze that step 2 obtains is crossed 200 mesh sieve for use, transmutation erythema glaze is made by step 3.
The application method of lightweight porcelain low temperature transmutation erythema glaze, includes the following steps described in specific embodiment two：
Step 1, light ceramics green body is prepared；
Step 2, transmutation erythema glaze is warming up to 35-40 DEG C, imposed on light ceramics green body, placed 5-10 hours, apply
Glaze method is leaching glaze or glaze spraying；
Step 3, there is the ceramic body of transmutation erythema glaze to be put into oxidizing flame in kiln by to fire, firing temperature is 980
Between DEG C -1060 DEG C, after ceramic body enters kiln, kiln is brought rapidly up to firing temperature, natural cooling after firing.
Above-mentioned lightweight porcelain low temperature transmutation erythema glaze, method of preparation and use, glaze is at low cost, used raw material all
It is easy to get, and manufacture craft is simple；It is easy to use, it only need to be in base without ground-coat enamel using this kind of low temperature transmutation erythema glaze
Body surface face last layer glaze；Firing temperature is low, and the firing temperature of this kind of transmutation erythema glaze only needs 980 DEG C -1060 DEG C
Between transmutation effect can be realized, it is energy saving；With unique artistic feeling, glaze that this kind of transmutation erythema glaze is burnt out
Face effect has red or copper red color background color, and irregular black splotch is uniformly distributed on background color, black splotch
Size and respectively density change according to ceramic type and glazing thickness, have unique artistic effect；Use this kind of glaze system
The porcelain of work improves product specification and selling price, has higher economic value；In addition this kind of glaze can be with volume industrial
Metaplasia production, can Rapid Popularization, using simple, there is stronger competitiveness on the market.
The above, only present pre-ferred embodiments, therefore cannot be limited the scope of implementation of the present invention with this, i.e.,
According to equivalent changes and modifications made by scope of the present invention patent and description, it all should still belong to patent of the present invention and cover
In the range of.
Claims (3)
1. the application method of lightweight porcelain low temperature transmutation erythema glaze, which is characterized in that
The raw material of the glaze is as follows in parts by weight：30-45 parts of glass powder, 25-35 parts of clear frit glaze, red stain 5-20
Part, 5-10 parts of nepheline powder, 5-10 parts of boric acid, 3-8 parts of kaolin, 2-5 parts of zinc oxide；
Include the following steps：
Step 1, light ceramics green body is prepared；
Step 2, transmutation erythema glaze is warming up to 35-40 DEG C, imposed on light ceramics green body, placed 5-10 hours；
Step 3, there is the ceramic body of transmutation erythema glaze to be put into kiln oxidizing flame by to fire, firing temperature 980 DEG C-
Between 1060 DEG C.
2. the application method of lightweight porcelain low temperature transmutation erythema glaze according to claim 1, it is characterised in that：The step 2
In enameling method be leaching glaze or glaze spraying.
3. the application method of lightweight porcelain low temperature transmutation erythema glaze according to claim 1, it is characterised in that：The step 3
In, after ceramic body enters kiln, kiln is brought rapidly up to firing temperature, natural cooling after firing.