CN108329826A - 双组份无溶剂聚氨酯涂料 - Google Patents
双组份无溶剂聚氨酯涂料 Download PDFInfo
- Publication number
- CN108329826A CN108329826A CN201810027241.3A CN201810027241A CN108329826A CN 108329826 A CN108329826 A CN 108329826A CN 201810027241 A CN201810027241 A CN 201810027241A CN 108329826 A CN108329826 A CN 108329826A
- Authority
- CN
- China
- Prior art keywords
- component
- polyurethane coating
- antioxidant
- polyester polyol
- antifoaming agent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明涉及双组分无溶剂型聚氨酯涂料。具体而言，本发明通过各种原料的合理配比，使得所制备的聚氨酯涂料环保、无污染，易施工、操作简单，较市场上的其他聚氨酯材料，有极好的重涂性能，材料与材料间有极强的附着力，不会脱层，涂膜厚度可以调节，既可制成厚膜，也可制成薄涂层。具体而言，本发明提供一种聚氨酯涂料材料，其是通过包含活泼氢化合物和多异氰酸酯类的原料制备的，其中，活泼氢化合物选自聚酯多元醇。
Description
技术领域
本发明涉及双组份无溶剂聚氨酯涂料的合成领域，所述合成的聚氨酯涂料材料可用于路面涂料，属于有机高分子合成领域。
技术背景
聚氨酯也称为聚氨基甲酸酯，是主链上含有重复氨基甲酸酯基团的大分子化合物的统称。其通常是由有机二异氰酸酯或多异氰酸酯与二羟基或多羟基化合物聚合而成。聚氨酯的用途非常广泛，例如其可以代替橡胶、塑料和尼龙等，用于学校、机场、酒店、住宅小区、公交车专用道、自行车道、过路天桥、人行道、中央隔离线、高速公路隧道、高速公路危险段、急转弯公路、隧道进出口、室外停车场、坡道、购物中心停车场、机场、码头以及园林美化等。
通常聚氨酯是通过异氰酸酯与多元醇化合物发生加聚反应制得。反应原理大致如下：
(1)当-NCO/-OH>1，即-NCO基团过量时，生成的聚合物端基为异氰酸酯基：
(2)当-NCO/-OH＝1时，聚合物分子量无穷大；
(3)当-NCO/-OH<1，即-OH基团过量，生成的聚合物端基为羟基
聚氨酯涂料用做地面材料的时候，需要其材料强度大、环保、无污染，易施工、操作简单，且具有固化速度快、施工速度快捷、防腐防水性能好、耐温范围宽、工艺简单等特点。如果聚氨酯涂料材料色彩多样，装饰性能优良，耐老化，而且不加催化剂，则是更加优选的。
发明内容
为解决上述问题，本发明提供了一种双组份无溶剂聚氨酯地坪材料，环保、无污染，易施工、操作简单，较市场上的其他聚氨酯材料，有极好的重涂性能，材料与材料间有极强的附着力，不会脱层，涂膜厚度可以调节，既可制成厚膜，也可制成薄涂层。色彩多样，装饰性能优良，耐老化，而且不加催化剂，节约成本。
具体而言，本发明的聚氨酯涂料包含组分A和/或组分B。对于组分A，其包含或者由聚酯多元醇、蓖麻油、消泡剂、分散剂、紫外吸收剂、抗氧化剂、填料组成。对于组分B，其包含或者由多亚甲基多苯基异氰酸酯组成。任选地，组分A或组分B中含有颜料，例如氧化铁绿或氧化铁红。
在本发明中，任选地：
所述聚酯多元醇选自：聚己内酯多元醇、芳香族聚酯多元醇、特种多元醇、支化聚醚、聚酯多元醇、支链型聚酯多元醇，例如750；
所述蓖麻油选自：植物油多元醇、大豆油多元醇、松香酯多元醇、工业合成蓖麻油等；
所述消泡剂选自分子筛、氧化钙、有机硅类、聚合物型消泡剂，例如BYK-057；
所述分散剂选自：聚氨酯改性丙烯酸类或分散剂BYK-163；
所述紫外吸收剂例如可以为紫外线吸收剂UV-531；
所述抗氧化剂例如可以为抗氧剂1010；和/或
所述填料选自滑石粉、碳酸钙、高岭土、炭黑等。
进一步地，本发明中聚酯多元醇中的-OH与异氰酸酯中的-NCO的摩尔比为1:1。
优选地，本发明中聚酯多元醇、蓖麻油、消泡剂、分散剂、紫外吸收剂、抗氧化剂、碳酸钙粉末的质量比为72-88：85-105:1.0-1.3:1.0-1.3:0.9-1.1:0.9-1.1：144-176。优选地，本发明中聚酯多元醇、蓖麻油、消泡剂、分散剂、紫外吸收剂、抗氧化剂、碳酸钙粉末的质量比为76-84：90-100:1.1-1.3:1.1-1.3:0.95-1.05:0.95-1.05：150-165。最优选地，本发明中聚酯多元醇、蓖麻油、消泡剂、分散剂、紫外吸收剂、抗氧化剂、碳酸钙粉末的质量比为80：95:1.2:1.2:1：1：160。
本发明另一方面还提供了一种制备防滑的聚氨酯涂料的方法，其包括将包含或者由聚酯多元醇、蓖麻油、消泡剂、分散剂、紫外吸收剂、抗氧化剂、填料组成的原料制成组分A；和/或将包含或者由多亚甲基多苯基异氰酸酯WANNATE PM-200组成的原料制成组分B。任选地，组分A或组分B中含有颜料，例如氧化铁绿或氧化铁红。
在本发明的制备聚氨酯涂料的方法中，任选地：
所述聚酯多元醇选自：聚己内酯多元醇、芳香族聚酯多元醇、特种多元醇、支化聚醚、支链型聚酯多元醇，例如750；
所述蓖麻油选自大豆油多元醇、松香酯多元醇和工业合成蓖麻油等；
所述消泡剂选自分子筛、氧化钙、有机硅类、聚合物型消泡剂，例如BYK-057；
所述分散剂选自：聚氨酯改性丙烯酸类或分散剂BYK-163；
所述紫外吸收剂例如可以为紫外线吸收剂UV-531；
所述抗氧化剂例如可以为抗氧剂1010；和/或
所述填料选自滑石粉、碳酸钙、高岭土、炭黑等。
优选地，在本发明的制备聚氨酯涂料的方法中，组分A中聚酯多元醇中的-OH与组分B中异氰酸酯中的-NCO的摩尔比为1:1。
进一步优选地，在本发明的制备聚氨酯涂料的方法中，聚酯多元醇、蓖麻油、消泡剂、分散剂、紫外吸收剂、抗氧化剂、碳酸钙粉末的质量比为72-88：85-105:1.0-1.3:1.0-1.3:0.9-1.1:0.9-1.1：144-176。优选地，在本发明的制备聚氨酯涂料的方法中，聚酯多元醇、蓖麻油、消泡剂、紫外吸收剂、抗氧化剂、碳酸钙粉末的质量比为76-84：90-100:1.1-1.3:1.1-1.3:0.95-1.05:0.95-1.05：150-165。最优选地，在本发明的制备聚氨酯涂料的方法中，聚酯多元醇、蓖麻油、消泡剂、紫外吸收剂、抗氧化剂、碳酸钙粉末的质量比为80：95:1.2:1.2:1：1：160。
本发明的再一方面提供了本发明的聚氨酯涂料在用于铺设路面或墙面中的用途，其包括将本发明中组分A和组分B混匀后涂覆在路面或者墙面。
本发明还提供了上述组分A和/或组分B单独或者组合在制备用于防滑的聚氨酯涂料中的用途。进一步优选地，本发明中所述的防滑的聚氨酯涂料进一步具有耐水、耐碱和/或抗裂的特性。
最优选地，本发明中组分A含有无水硫酸钠和无水硫酸镁的混合物，其中无水硫酸钠和无水硫酸镁的质量比为2:1-1:2，优选为1:1.2，且该混合物占组分A和B总质量的0.8％-1.2％，优选1％。
本发明还提供了无水硫酸钠和无水硫酸镁的混合物在制备增强聚氨涂料的防滑功能中的用途。
本发明还提供了一种制备防滑的聚氨酯涂料的方法，其包括将无水硫酸钠和无水硫酸镁的混合物加入其中。任选地，无水硫酸钠和硫酸镁的质量比为2:1-1:2，优选为1:1.2，且该混合物占聚氨酯材料总质量的0.5％-1.0％，优选1％
通过本发明制备的聚氨酯涂料是一种无溶剂型双组份高强度聚氨酯材料，与环氧彩砂胶相比较，具有极佳的耐候性能，不受环境限制，能够长期暴露在太阳光线下不起粉起砂，与基材具有很好的粘接性；同时由于其不含溶剂的特性，因此能够在各种环境下轻松施工，且不会造成环境污染。
下面将通过借助以下实施例来更详细地说明本发明。以下实施例仅是说明性的，应该明白，本发明并不受下述实施例的限制。
下面将通过借助以下实施例来更详细地说明本发明。以下实施例仅是说明性的，应该明白，本发明并不受下述实施例的限制。
实施例1
本发明原料及配方，
A组分
B组分
| 品名 | 质量(KG) |
| 多亚甲基多苯基异氰酸酯(WANNATE PM-200) | 100 |
产品工艺：
1、将750、蓖麻油依次加入反应釜中，并搅拌；
2、将分散剂、消泡剂、抗氧剂、紫外线吸收剂依次加入反应釜，升温至90℃，并搅拌30分钟；
3、加入微细碳酸钙和氧化铁红；
4、升温至110℃，保温在110-115℃。
5、抽真空3小时；
6、降温至60℃，放料。
将由上述A组分配方制备的组分A与组分B混匀得到聚氨酯涂料，并对其进行理化指标检验。
物理性能：
化学性能
地坪涂装材料有害物质含量
实施例2
本发明原料及配方，
A组分
B组分
| 品名 | 质量(KG) |
| 多亚甲基多苯基异氰酸酯(WANNATE PM-200) | 100 |
产品工艺：
1、将750、蓖麻油依次加入反应釜中，并搅拌；
2、将分散剂、消泡剂、抗氧剂、紫外线吸收剂依次加入反应釜，升温至90℃，并搅拌30分钟；
3、加入微细碳酸钙、无水硫酸钠和硫酸镁的混合物以及氧化铁红；
4、升温至110℃，保温在110-115℃。
5、抽真空3小时；
6、降温至60℃，放料。
将由上述A组分配方制备的组分A与组分B混匀得到聚氨酯涂料，并对其进行理化指标检验。
物理性能：
化学性能
地坪涂装材料有害物质含量
实施例3
原料及配方，
A组分
B组分
| 品名 | 质量(KG) |
| 多亚甲基多苯基异氰酸酯(WANNATE PM-200) | 90 |
产品工艺：
1、将750、蓖麻油依次加入反应釜中，并搅拌；
2、将分散剂、消泡剂、抗氧剂、紫外线吸收剂依次加入反应釜，升温至90℃，并搅拌30分钟；
3、加入微细碳酸钙和氧化铁红；
4、升温至110℃，保温在110-115℃。
5、抽真空3小时；
6、降温至60℃，放料。
将由上述A组分配方制备的组分A与组分B混匀得到聚氨酯涂料，并对其进行理化指标检验。结果与实施例1类似，效果均满足相关国家标准的要求。
实施例4
原料及配方，
A组分
B组分
| 品名 | 质量(KG) |
| 多亚甲基多苯基异氰酸酯(WANNATE PM-200) | 112 |
产品工艺：
1、将750、蓖麻油依次加入反应釜中，并搅拌；
2、将分散剂、消泡剂、抗氧剂、紫外线吸收剂依次加入反应釜，升温至90℃，并搅拌30分钟；
3、加入微细碳酸钙和氧化铁红；
4、升温至110℃，保温在110-115℃。
5、抽真空3小时；
6、降温至60℃，放料。
将由上述A组分配方制备的组分A与组分B混匀得到聚氨酯涂料，并对其进行理化指标检验。结果与实施例1类似，效果均满足相关国家标准的要求。
虽然用上述实施方式描述了本发明，应当理解的是，在不背离本发明的精神的前提下，本发明可进行进一步的修饰和变动，且这些修饰和变动均属于本发明的保护范围之内。
Claims (10)
1.一种聚氨酯涂料，其包含或由组分A和/或组分B组成或制成，其中组分A包含或者由聚酯多元醇、蓖麻油、消泡剂、分散剂、紫外吸收剂、抗氧化剂、填料组成；组分B包含或者由多亚甲基多苯基异氰酸酯组成或制成。
2.根据权利要求1所述的聚氨酯涂料，其中组分A或组分B中含有颜料(例如氧化铁绿或氧化铁红)。
3.根据权利要求1所述的聚氨酯涂料，其中所述消泡剂选自分子筛、氧化钙、有机硅消泡剂和聚合物型消泡剂。
4.根据权利要求1所述的聚氨酯涂料，所述紫外吸收剂为紫外线吸收剂UV-531；
所述抗氧化剂例如可以为抗氧剂1010；和/或
所述填料选自滑石粉、碳酸钙粉、高岭土或炭黑。
5.根据权利要求1所述的聚氨酯涂料，其中组分A中的聚酯多元醇中的-OH与组分B中的异氰酸酯中的-NCO的摩尔比为1:1。
6.根据权利要求1所述的聚氨酯涂料，其中聚酯多元醇、蓖麻油、消泡剂、分散剂、紫外吸收剂、抗氧化剂、碳酸钙粉末的质量比为72-88：85-105:1.0-1.3:1.0-1.3:0.9-1.1:0.9-1.1：144-176。
7.根据权利要求1所述的聚氨酯涂料，其中聚酯多元醇、蓖麻油、消泡剂、分散剂、紫外吸收剂、抗氧化剂、碳酸钙粉末的质量比为76-84：90-100:1.1-1.3:1.1-1.3:0.95-1.05:0.95-1.05：150-165；优选地，聚酯多元醇、蓖麻油、消泡剂、分散剂、紫外吸收剂、抗氧化剂、碳酸钙粉末的质量比为80：95:1.2:1.2:1：1：160。
8.根据权利要求1-7中任一项所述的聚氨酯涂料，其中组分A还包括无水硫酸钠和硫酸镁的混合物，其中无水硫酸钠和硫酸镁的质量比为2:1-1:2，优选为1:1.2，且该混合物占组分A和组分B总质量的0.8％-1.2％，优选1％。
9.一种制备防滑的聚氨酯涂料的方法，其包括将包含或者由聚酯多元醇、蓖麻油、消泡剂、分散剂、紫外吸收剂、抗氧化剂、填料组成的原料制成组分A；和/或将包含或者由多亚甲基多苯基异氰酸酯组成的原料制成组分B，其中组分A和组分B如权利要求1-9中任一项所限定的那样。
10.权利要求1-9中任一项所限定聚氨酯涂料在用于铺设路面或墙面中的用途，其包括将本发明中组分A和组分B混匀后涂覆在路面或者墙面；或，无水硫酸钠和无水硫酸镁的混合物在制备增强聚氨涂料的防滑功能中的用途。