CN108264783A - A kind of shell powder paint and preparation method thereof - Google Patents
A kind of shell powder paint and preparation method thereof Download PDFInfo
- Publication number
- CN108264783A CN108264783A CN201810006482.XA CN201810006482A CN108264783A CN 108264783 A CN108264783 A CN 108264783A CN 201810006482 A CN201810006482 A CN 201810006482A CN 108264783 A CN108264783 A CN 108264783A
- Authority
- CN
- China
- Prior art keywords
- shell
- powder paint
- shell powder
- inorganic pigment
- whiting
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
A kind of shell powder paint and preparation method thereof, including oyster shell whiting, plant adhesive and inorganic pigment, wherein, the weight ratio of the shell powder paint is oyster shell whiting 90%, plant adhesive 8%, environment friendly inorganic pigment 2%；The smell and indoor miscellaneous taste that shell powder paint can distribute indoor smoke, infant, patient, pet, mould all have the advantageous effect effectively dispelled, the advantageous effect of carbon monoxide and dust Capacity with suction-operated especially distributed indoors to cigarette；Plant adhesive in shell powder paint is to be extracted the binding material for having sedimentation and flocculating function in cotton core and paper pulp using extraction method, adds reagent without any harmful chemicals, has reached natural harmless advantageous effect；Environment friendly inorganic pigment is applied can play the advantageous effects such as cooling energy-saving, durability are good, colour retention is good in coating.
Description
Technical field
The present invention relates to technical field of coatings, and especially one kind is using oyster shell whiting as major ingredient, plant adhesive and environment friendly inorganic
Pigment is the green of auxiliary material, environmentally friendly shell powder paint and preparation method thereof.
Background technology
In today of people's pay attention to day by day environmental protection, with the deterioration of atmospheric environment and goods and materials improvement of living standard, people
Requirement for the air quality of indoor environment is also increasingly stringenter；Current interior decoration largely uses emulsion paint, paint, compound
The materials such as plank, leather, foam insert, plastic facing, it is serious dirty containing a large amount of volatility toxic compounds in material
Dye living and working environment, the health for endangering people；The dope for inner wall of architecture used in the market is mainly emulsion paint, and emulsion paint is universal
There is the shortcomings of paint film is soft, drying time is long, bin stability is poor, emulsion paint class coating after being moistened, easily grows bacterium,
Phenomena such as generation comes off, changes colour seriously affects service life and indoor beauty；
At present, environment-friendly type coating emerges in an endless stream, it is recognized that most environmentally friendly coating one be water paint, second is that powdery paints；Powder
Last coating is even more to have the advantages that absolutely to form a film, but really can simultaneously inhale from raw material with regard to that can accomplish pure natural no pollution
The coating of Fufen solution pollutions such as formaldehyde within doors, actually rare in the market, therefore, powdery paints, which will be made, using natural material to be
The development trend of following interior wall coating.
Invention content
For overcome the deficiencies in the prior art, the present invention provides a kind of shell powder paint and preparation method thereof, the one kind
By shell by being made after high-temperature calcination, crushing, component part is oyster shell whiting in shell powder paint and preparation method thereof
The calcified materials such as calcium carbonate, calcium oxide, calcium hydroxide, this has the nuisances such as absorption, decomposing formaldehyde, benzene as porous helical
Matter, antibacterial, sterilization, anlistatig function have reached adjusting air humidity, have eliminated peculiar smell, instead of wallpaper, emulsion paint, diatom ooze
Etc. the purpose of traditional coating.
The technical solution used in the present invention is a kind of shell powder paint, including oyster shell whiting, plant adhesive and inorganic
Pigment, wherein, the weight ratio of the shell powder paint is oyster shell whiting 90%, plant adhesive 8%, environment friendly inorganic pigment 2%；
The application method of the shell powder paint is：Because containing various impurity in tap water, therefore, the shell powder paint is dilute
Pure water is used when releasing；Mixer is added in after pure water is weighed first, the shell powder paint after weighing is added in mixer
It is mixed with pure water, wherein, the weight ratio of pure water and shell powder paint is 5:1, stirring is after ten minutes, static clockwise manually
It 10 minutes, stays in after the shell powder paint in mixer fully dissolves water, according to the needs of wall color effect, adds in edible color
Element is mixed colours, and is further continued for stirring 10 minutes so that the mixture of oyster shell whiting and pure water, food coloring in mixer is more
Uniformly, direct first pass spraying or roller coating on metope, metope carries out the time drying of half a day, dried wall after the completion of application
Face carries out second time spraying or application can be completed in roller coating；Requirement is applied in strict accordance with water and oyster shell whiting during coating is diluted
The proportion of material is diluted, in order to avoid causing aberration, the coating after dilution requires to be finished in one hour, in order to avoid cause oyster shell whiting
Coating precipitates, and paint film is uneven；Requirement uniformly sprays or roller coating in coating process, in order to avoid film thickness is caused to differ, influences
Overall effect.
A kind of preparation method of shell powder paint, the specific steps are：Oyster shell whiting preparation → plant adhesive preparation → mixing
Object mixing → drying → crushing → sieving → packaging；The oyster shell whiting is prepared as cleaning shell → immersion → high-temperature calcination
→ cooling → grinding；The plant adhesive is prepared as the binding material by being extracted in cotton core and paper pulp；Described is mixed
It is that oyster shell whiting, plant adhesive, environment friendly inorganic pigment are put into blender with a certain proportion of pure water to fill to close object and be mixed
Divide stirring, obtain the mixture of oyster shell whiting, plant adhesive, environment friendly inorganic pigment；Described drying be the oyster shell whiting that will be obtained,
The mixture of plant adhesive and environment friendly inorganic pigment, which is put into dryer, dries；The crushing is the shell after drying
Oyster shell whiting, plant bonding are obtained after being crushed in the mixture input pulverizer of powder, plant adhesive and environment friendly inorganic pigment
Agent and the mix powder of inorganic pigment；The sieving is oyster shell whiting, plant adhesive and the environment friendly inorganic face after crushing
The mix powder of material obtains standard compliant shell powder paint powder after being screened via 1200 mesh；Described is packaged as
By shell powder paint powder by packaging production line quantitative package；
The beneficial effects of the invention are as follows：The compound of calcium is chiefly used in eliminating smell agent in life, and oyster shell whiting is to lead to natural shell
Manufactured powdered substance after high-temperature calcination, grinding is crossed, component part is the calcified materials such as calcium carbonate, calcium oxide, calcium hydroxide,
This has the function of absorption, decomposing formaldehyde, benzene, TVOC, ammonia and adjusting air humidity, eliminates peculiar smell as porous helical
Function, therefore, shell powder paint can be to smell that indoor smoke, infant, patient, pet, mould are distributed and interiors
Miscellaneous taste all has the advantageous effect effectively dispelled, and the carbon monoxide and dust Capacity especially distributed indoors to cigarette has
The advantageous effect of suction-operated；Plant adhesive in shell powder paint is that will have sedimentation in cotton core and paper pulp using extraction method
It is extracted with the binding material of flocculating function, adds reagent without any harmful chemicals, reached natural harmless beneficial effect
Fruit；Environment friendly inorganic pigment is applied can play the advantageous effects such as cooling energy-saving, durability are good, colour retention is good in coating.
Specific embodiment：
The present invention specific embodiment be：
A kind of shell powder paint, including oyster shell whiting, plant adhesive and inorganic pigment, wherein, the weight of the shell powder paint
Amount ratio is oyster shell whiting 90%, plant adhesive 8%, environment friendly inorganic pigment 2%；
The application method of the shell powder paint is：Because containing various impurity in tap water, therefore, the shell powder paint is dilute
Pure water is used when releasing；Mixer is added in after pure water is weighed first, the shell powder paint after weighing is added in mixer
It is mixed with pure water, wherein, the weight ratio of pure water and shell powder paint is 5:1, stirring is after ten minutes, static clockwise manually
It 10 minutes, stays in after the shell powder paint in mixer fully dissolves water, according to the needs of wall color effect, adds in edible color
Element is mixed colours, and is further continued for stirring 10 minutes so that the mixture of oyster shell whiting and pure water, food coloring in mixer is more
Uniformly, direct first pass spraying or roller coating on metope, metope carries out the time drying of half a day, dried wall after the completion of application
Face carries out second time spraying or application can be completed in roller coating；Requirement is applied in strict accordance with water and oyster shell whiting during coating is diluted
The proportion of material is diluted, in order to avoid causing aberration, the coating after dilution requires to be finished in one hour, in order to avoid cause oyster shell whiting
Coating precipitates, and paint film is uneven；Requirement uniformly sprays or roller coating in coating process, in order to avoid film thickness is caused to differ, influences
Overall effect.
VOC ＜ 1g/kg in the shell powder paint；
Benzene+toluene+ethylbenzene+dimethylbenzene ＜ 50mg/kg in the shell powder paint；
Formaldehyde ＜ 5mg/kg in the shell powder paint；
Soluble heavy metal in the shell powder paint（Lead, chromium ＜ 2.5；Cadmium ＜ 0.5；Mercury ＜ 0.1）mg/kg；
A kind of preparation method of shell powder paint, the specific steps are：
1）It is prepared by oyster shell whiting：
A, shell is cleaned with clear water, it is spare after the residues such as shellfish meat to remove on shell；
B, the shell after cleaning is put into acid solution and impregnated, it is spare after desalination ungrease treatment to carry out, it is acid molten
The pH value of liquid is 3, and soaking time is 120 minutes；
C, the shell after immersion is put into high-temperature calcination stove and calcined, calcination temperature is 1500 degrees Celsius, and calcination time is 60 points
Clock；
D, the shell after calcining, which is transported to after cooling equipment cooling in grinder, to be ground, and the shell after grinding is in powder
Last shape is to get for use to oyster shell whiting；
2）It is prepared by plant adhesive：The binding material with sedimentation and flocculating function is extracted in cotton core and paper pulp using extraction method
It is spare as plant adhesive；
3）, mixture be mixed：By spare oyster shell whiting, plant adhesive, environment friendly inorganic pigment with it is a certain proportion of pure
Water input blender is sufficiently stirred, and obtains the mixture of oyster shell whiting, plant adhesive, environment friendly inorganic pigment, mixing time 25
Minute；
4）Drying：The mixture of obtained oyster shell whiting, plant adhesive and environment friendly inorganic pigment is put into dryer and is dried,
The temperature of drying is 1400 degrees Celsius, and the time of drying is 30 minutes；
5）It crushes：By after drying oyster shell whiting, carry out in the mixture input pulverizer of plant adhesive and environment friendly inorganic pigment
The mix powder of oyster shell whiting, plant adhesive and environment friendly inorganic pigment is obtained after crushing；
6）Sieving：Oyster shell whiting, the mix powder of plant adhesive and environment friendly inorganic pigment after crushing is sieved via 1200 mesh
Standard compliant shell powder paint powder is obtained after being screened；
7）Packaging；Described is packaged as shell powder paint powder by packaging production line quantitative package, and as finished product oyster shell whiting applies
Material.
Claims (7)
1. a kind of shell powder paint, including oyster shell whiting, plant adhesive and inorganic pigment, it is characterized in that：The oyster shell whiting applies
The weight ratio of material is oyster shell whiting 90%, plant adhesive 8%, environment friendly inorganic pigment 2%.
2. a kind of shell powder paint according to claim 1, it is characterized in that：The application method of the shell powder paint
For：Because therefore, pure water is used when which dilutes containing various impurity in tap water；Pure water is claimed first
Mixer is added in after amount, the shell powder paint after weighing is added in mixer and is mixed with pure water, wherein, pure water and shell
The weight ratio of powder coating is 5:1, after ten minutes, static 10 minutes, the oyster shell whiting stayed in mixer applied for stirring clockwise manually
After material fully dissolving water, according to the needs of wall color effect, add in food coloring and mix colours, be further continued for stirring 10 minutes,
So that the mixture of the oyster shell whiting and pure water, food coloring in mixer is more uniformly distributed, the direct first pass spraying on metope
Or roller coating, metope carries out the time drying of half a day after the completion of application, and dried metope carries out second time spraying or roller coating
Complete application；Requirement is diluted in strict accordance with the proportion of water and shell powder paint during coating is diluted, Yi Mianzao
Into aberration, the coating after dilution requires to be finished in one hour, in order to avoid shell powder paint is caused to precipitate, paint film is uneven；Application
Requirement uniformly sprays or roller coating in the process, in order to avoid film thickness is caused to differ, influences overall effect.
3. a kind of shell powder paint according to claim 1, it is characterized in that：VOC ＜ 1g/ in the shell powder paint
kg。
4. a kind of shell powder paint according to claim 1, it is characterized in that：Benzene+toluene+second in the shell powder paint
Benzene+dimethylbenzene ＜ 50mg/kg.
5. a kind of shell powder paint according to claim 1, it is characterized in that：Formaldehyde ＜ 5mg/ in the shell powder paint
kg。
6. a kind of shell powder paint according to claim 1, it is characterized in that：A soluble huge sum of money in the shell powder paint
Belong to（Lead, chromium ＜ 2.5；Cadmium ＜ 0.5；Mercury ＜ 0.1）mg/kg.
7. a kind of preparation method of shell powder paint, it is characterized in that：The specific steps are：
1）It is prepared by oyster shell whiting：
A, shell is cleaned with clear water, it is spare after the residues such as shellfish meat to remove on shell；
B, the shell after cleaning is put into acid solution and impregnated, it is spare after desalination ungrease treatment to carry out, it is acid molten
The pH value of liquid is 3, and soaking time is 120 minutes；
C, the shell after immersion is put into high-temperature calcination stove and calcined, calcination temperature is 1500 degrees Celsius, and calcination time is 60 points
Clock；
D, the shell after calcining, which is transported to after cooling equipment cooling in grinder, to be ground, and the shell after grinding is in powder
Last shape is to get for use to oyster shell whiting；
2）It is prepared by plant adhesive：The binding material with sedimentation and flocculating function is extracted in cotton core and paper pulp using extraction method
It is spare as plant adhesive；
3）Mixture is mixed：By spare oyster shell whiting, plant adhesive, environment friendly inorganic pigment and a certain proportion of pure water
Input blender is sufficiently stirred, and obtains the mixture of oyster shell whiting, plant adhesive, environment friendly inorganic pigment, and mixing time is 25 points
Clock；
4）Drying：The mixture of obtained oyster shell whiting, plant adhesive and environment friendly inorganic pigment is put into dryer and is dried,
The temperature of drying is 1400 degrees Celsius, and the time of drying is 30 minutes；
5）It crushes：By after drying oyster shell whiting, carry out in the mixture input pulverizer of plant adhesive and environment friendly inorganic pigment
The mix powder of oyster shell whiting, plant adhesive and environment friendly inorganic pigment is obtained after crushing；
6）Sieving：Oyster shell whiting, the mix powder of plant adhesive and environment friendly inorganic pigment after crushing is sieved via 1200 mesh
Standard compliant shell powder paint powder is obtained after being screened；
7）Packaging；Described is packaged as shell powder paint powder by packaging production line quantitative package, and as finished product oyster shell whiting applies
Material.