CN109321045A - A kind of water paint and preparation method thereof made of conch meal - Google Patents
A kind of water paint and preparation method thereof made of conch meal Download PDFInfo
- Publication number
- CN109321045A CN109321045A CN201811074037.3A CN201811074037A CN109321045A CN 109321045 A CN109321045 A CN 109321045A CN 201811074037 A CN201811074037 A CN 201811074037A CN 109321045 A CN109321045 A CN 109321045A
- Authority
- CN
- China
- Prior art keywords
- conch meal
- water paint
- water
- preparation
- agent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The water paint and preparation method thereof that the present invention relates to a kind of to make of conch meal is added diatomite, calcium powder, kaolin and other auxiliary agents etc. and is mixed to form the water paint made of conch meal using conch meal as primary raw material.The invention has the benefit that the water paint produced by the present invention made of conch meal, has effects that good permeability, mould proof, decomposition and absorption noxious material, adjusting air humidity；More environmentally-friendly, all raw materials used do not contain lipid or benzene ring substance, and finished product is non-toxic and tasteless；Wearability is higher, has flame retarding function；Application property is good, and construction method is flexible, sprayable also to can be applied.
Description
Technical field
The invention belongs to Paint preparation technologies, and in particular to a kind of water paint and its preparation side with conch meal production
Method.
Background technique
It is all with water as solvent or to make the coating of decentralized medium, it all can be described as water paint.Water paint is divided into two
Major class: the natural water paint and artificial synthetic resin's water paint of natural materials or minerals.The water of artificial synthetic resin's class
Property coating includes water soluble paint, water-reducible coating and water-dispersible paint.Water soluble paint be with water-soluble resin be at
Film object, using polyvinyl alcohol and its various modifiers as representative, in addition to this there are also water-soluble alkyd resin, water-soluble epoxy resin and nothings
Machine polymer waterborne resin etc..
Water paint or emulsion paint currently on the market is most of all airtight, and wall can be made by spraying or be applied to metope surface
Face is gone mouldy, and bacterium is bred；Although harmful substance contents are in national standard hereinafter, but wherein still having the objects of a large amount of harmful human bodies
Matter；But also there are the service life of product is short, it is prone to wear, not environmentally etc. problems.
Summary of the invention
In order to solve the above problems existing in the present technology, the present invention provides a kind of water paints made of conch meal
And preparation method thereof.The manufactured water paint made of conch meal is ventilative, fire-retardant, environmentally friendly, and application property is good.
The technical scheme adopted by the invention is as follows: a kind of water paint made of conch meal, prepared by following raw material and
At the raw material includes: diatomite 5%-10% by weight percentage；Conch meal 40%-55%；Calcium powder 5%-8%；Kaolin
3%-8%；Defoaming agent 0.5%-1%；Thickener 1%-1.5%；Lotion 10%-15%；Conditioning agent 1%-1.5%；Levelling agent
1.5%-2% and deionized water 32%-38%.
Further, the calcium powder is nanometer calcium powder.
Further, the raw material further includes dispersing agent and multifunctional assistant, and the thickener includes the thickening of alkali swelling type
Agent.The additive amount of dispersing agent is 1-1.5%, and the additive amount of multifunctional assistant is 1-5%.
Further, the lotion is styrene-acrylic emulsion.Styrene-acrylic emulsion in the present invention is as carrier, and buying is from German bar
Si Fu company, model ECO-502, tasteless, alkaline-resisting, elasticity is good.
A kind of water paint preparation method made of conch meal, comprising the following steps:
(1) first diatomite, conch meal, calcium powder and kaolin are uniformly mixed, pour into the 30% of deionized water total amount, mixed
Uniformly, it is formed to mixed radix material；
(2) obtained to step (1) to which defoaming agent, thickener, conditioning agent and levelling agent are added in mixed radix material, and remove
Other raw materials outside ionized water stir 15-25 minutes, remaining deionized water are then added, and are uniformly mixed, and form mixture；
(3) mixture that step (2) obtains is ground and is filtered, be again stirring for being uniformly mixed to get with shell
The water paint of powder production.
Further, it in step (1) and step (2), is all made of high speed disperser and is stirred or mixes.
Further, it in step (1), after pouring into deionized water, first stirs at low speed 10 minutes, then high-speed stirred 10 minutes.
Further, in step (2), to which defoaming agent, thickener, conditioning agent and levelling agent are added in mixed radix material, and
Other raw materials in addition to deionized water first stir at low speed 8-12 minutes, then high-speed stirred 8-12 minutes；Then remaining go is added
Ionized water, then high-speed stirred 38-42 minutes is to being uniformly mixed.Further, the speed stirred at low speed be 500-800 turn/
Minute；The speed of the high-speed stirred is 1000-1500 revs/min.
Further, in step (3), it is 200-800nm that mixture, which is ground to partial size,.
It is added during raw material, solid powder will be bit by bit slowly added, and added a part stirring for a moment, waited and dissolve into it
It is afterwards again plus a part of, because all pouring into the short time more difficult can be uniformly mixed.
The invention has the benefit that in preparation process of the present invention reasonable arrangement raw material addition sequence, and according to addition
Raw material difference, and, can be good at merging each constituent, and do not need high energy and disappear using different mixing speed
Consumption, uniformly and conveniently.
The water paint produced by the present invention made of conch meal has good permeability, mould proof, decomposition and absorption Toxic
The effect of matter, adjusting air humidity.Mainly using conch meal as raw material, due to the lumen pore structure in conch meal, so that finished product
With good permeability and mould proof effect；The chitin contained in conch meal also makes finished product have effects that decomposing formaldehyde.
Conch meal specific gravity is higher, and the specific gravity such as diatomite, calcium powder, kaolin difference and the original small compared with conch meal specific gravity is added
Defoaming agent, thickener, conditioning agent and levelling agent etc. is added so that being uniformly dispersed after material mixing in material, can make finished product regardless of
Layer, mixing more evenly, have good physical property.
The water paint produced by the present invention made of conch meal is more environmentally-friendly, and all raw materials used do not contain rouge
Class or benzene ring substance, are all EU criteria environment-friendly products, and finished product is non-toxic and tasteless；
Wearability is higher, has fire-proof function.Contain higher calcium carbonate in finished product of the invention, after being combined with water hardness
It is stronger, very fine and close protective layer can be formed on surface in kind, and can persistently keep stronger hardness, finished product has resistance to
Mill property, anti-flammability；
Application property is good, and construction method is flexible, sprayable also to can be applied；
Have a wide range of application, the water paint produced by the present invention made of conch meal has well for different substrates
Adhesive force.
Specific embodiment
Technical solutions and effects of the present invention is described in further details combined with specific embodiments below.
As illustrated without especially unexpected, each raw material used in the present invention is all industry universal raw material.Dispersing agent it is main at
It is divided into Sodium Polyacrylate, purchases from Hiachuan Industry Co., Ltd., Shenzhen, model H5040；Conditioning agent is purchased from Tao Shi
Chemical company, model X-405, general wetting agent, low bubble color developing is good, can effectively prevent coating floating；Defoaming agent uses two
Kind, it is a kind of to purchase from Hiachuan Industry Co., Ltd., Shenzhen, model F111, there is beneficial foam inhibition effect, dispersibility
Good, from Nuo Pu section of Japan, model NXZ has excellent effect of breaking bubble for another defoaming agent buying；Thickener uses Luo Menha
The association thickener of this company, model TT-935 can effectively improve middle cut and paste degree, and can opening effect is good, splendid mobility
And levelability, another kind are the TVA-9760 of sunrise Industry Group Co., Ltd；Sterilization antiseptic purchases the company from Suzhou, type
Number be KC-10B；Levelling agent is purchased from Hiachuan Industry Co., Ltd., Shenzhen, model 620 and/or 600；Multifunctional assistant
Agent buying is purchased from Dow Chemical, model AMP, styrene-acrylic emulsion from BASF Aktiengesellschaft, model ECO-502.
Embodiment 1
The technical scheme adopted by the invention is as follows: a kind of water paint made of conch meal, prepared by following raw material and
At diatomite 8%；Conch meal 50%；Calcium powder 6%；Kaolin 5%；Defoaming agent 0.8%；Thickener 1.2%；Lotion 12%；It adjusts
Humectant 1.3%；Levelling agent 1.8% and deionized water 36%.
Preparation method, comprising the following steps:
(1) first diatomite, conch meal, calcium powder and kaolin are uniformly mixed, pour into the 30% of deionized water total amount, mixed
Uniformly, it is formed to mixed radix material；
(2) obtained to step (1) to which defoaming agent, thickener, conditioning agent and levelling agent are added in mixed radix material, and remove
Other raw materials outside ionized water stir 20 minutes, remaining deionized water are then added, and are uniformly mixed, and form mixture；
(3) mixture that step (2) obtains is ground and is filtered, be again stirring for being uniformly mixed to get with shell
The water paint of powder production.
Embodiment 2
The technical scheme adopted by the invention is as follows: a kind of water paint made of conch meal, prepared by following raw material and
At diatomite 5%；Conch meal 55%；Nanoscale calcium powder 8%；Kaolin 8%；Defoaming agent 0.5%；Thickener 1.5%；Phenylpropyl alcohol
Lotion 10%；Conditioning agent 1.5%；Levelling agent 1.5%；Dispersing agent 1.5%, sterilization antiseptic 0.1%, 5% He of multifunctional assistant
Deionized water 32%.
Preparation method, comprising the following steps:
(1) first diatomite, conch meal, calcium powder and kaolin are uniformly mixed, pour into high speed disperser, then pour into deionization
The 30% of water inventory, first stirred at low speed 10 minutes with 800 revs/min, then with 1000 revs/min high-speed stirred 10 minutes, mixing
Uniformly, it is formed to mixed radix material；
(2) obtained to step (1) to which defoaming agent, thickener, conditioning agent and levelling agent are added in mixed radix material, and remove
Other raw materials outside ionized water, first stirred at low speed 12 minutes with 500 revs/min, then with 1000 revs/min high-speed stirred 8 minutes,
Then be added remaining deionized water, then with 1000 revs/min high-speed stirred 42 minutes to being uniformly mixed, form mixture；
(3) mixture that step (2) obtains is carried out being ground to partial size as 200nm and is filtered, be again stirring for equal to mixing
It is even to get the water paint made of conch meal.
Embodiment 3
The technical scheme adopted by the invention is as follows: a kind of water paint made of conch meal, prepared by following raw material and
At diatomite 10%；Conch meal 40%；Nanoscale calcium powder 5%；Kaolin 3%；Defoaming agent 1%；Thickener 1%；Styrene-acrylic emulsion
15%；Conditioning agent 1%；Levelling agent 2%；Dispersing agent 1%, sterilization antiseptic 0.5%, multifunctional assistant 1% and deionized water
38%.
Preparation method, comprising the following steps:
(1) first diatomite, conch meal, calcium powder and kaolin are uniformly mixed, pour into high speed disperser, then pour into deionization
The 30% of water inventory, first stirred at low speed 10 minutes with 500 revs/min, further accelerate to 1500 revs/min high-speed stirred 10 minutes,
It is uniformly mixed, is formed to mixed radix material；
(2) obtained to step (1) to which defoaming agent, thickener, conditioning agent and levelling agent are added in mixed radix material, and remove
Other raw materials outside ionized water, first stirred at low speed 8 minutes with 800 revs/min, then with 1000 revs/min high-speed stirred 12 minutes,
Then be added remaining deionized water, then with 1500 revs/min high-speed stirred 38 minutes to being uniformly mixed, form mixture；
(3) mixture that step (2) obtains is carried out being ground to partial size as 800nm and is filtered, be again stirring for equal to mixing
It is even to get the water paint made of conch meal.
The present invention is not limited to above-mentioned preferred forms, anyone can show that other are various under the inspiration of the present invention
The product of form, however, make any variation in its shape or structure, it is all that there is skill identical or similar to the present application
Art scheme, is within the scope of the present invention.
Claims (10)
1. a kind of water paint made of conch meal, which is characterized in that be prepared from the following materials, the raw material is by weight
Percentage includes: diatomite 5%-10%；Conch meal 40%-55%；Calcium powder 5%-8%；Kaolin 3%-8%；Defoaming agent
0.5%-1%；Thickener 1%-1.5%；Lotion 10%-15%；Conditioning agent 1%-1.5%；Levelling agent 1.5%-2% and go from
Sub- water 32%-38%.
2. the water paint according to claim 1 made of conch meal, which is characterized in that the calcium powder is nanometer calcium
Powder.
3. the water paint according to claim 1 made of conch meal, which is characterized in that the raw material further includes dispersion
Agent and multifunctional assistant, the thickener include alkali-swelling type thickener.
4. the water paint according to claim 1 made of conch meal, which is characterized in that the lotion is phenylpropyl alcohol cream
Liquid.
5. a kind of preparation method of the water paint made of conch meal as described in Claims 1-4 is any, feature exist
In, comprising the following steps:
(1) first diatomite, conch meal, calcium powder and kaolin are uniformly mixed, pour into the 30% of deionized water total amount, mixing is equal
It is even, it is formed to mixed radix material；
(2) obtained to step (1) to which defoaming agent, thickener, conditioning agent and levelling agent are added in mixed radix material, and remove deionization
Other raw materials outside water stir 15-25 minutes, remaining deionized water are then added, and are uniformly mixed, and form mixture；
(3) mixture that step (2) obtains is ground and is filtered, be again stirring for being uniformly mixed to get with conch meal system
The water paint of work.
6. the preparation method of the water paint according to claim 5 made of conch meal, which is characterized in that step (1)
In step (2), it is all made of high speed disperser and is stirred or mixes.
7. the preparation method of the water paint according to claim 5 made of conch meal, which is characterized in that step (1)
In, it after pouring into deionized water, first stirs at low speed 10 minutes, then high-speed stirred 10 minutes.
8. the preparation method of the water paint according to claim 5 made of conch meal, which is characterized in that step (2)
In, to which defoaming agent, thickener, conditioning agent and levelling agent, and other raw materials in addition to deionized water, elder generation are added in mixed radix material
It stirs at low speed 8-12 minutes, then high-speed stirred 8-12 minutes；Then remaining deionized water, then high-speed stirred 38-42 points are added
Clock to be uniformly mixed.
9. the preparation method of the water paint according to claim 7 or 8 made of conch meal, which is characterized in that described
The speed stirred at low speed is 500-800 revs/min；The speed of the high-speed stirred is 1000-1500 revs/min.
10. the preparation method of the water paint according to claim 5 made of conch meal, which is characterized in that step (3)
In, it is 200-800nm that mixture, which is ground to partial size,.