CN108219243A - 一种磁性塑料母粒及其制备方法 - Google Patents

一种磁性塑料母粒及其制备方法 Download PDF

Info

Publication number
CN108219243A
CN108219243A CN201711405871.1A CN201711405871A CN108219243A CN 108219243 A CN108219243 A CN 108219243A CN 201711405871 A CN201711405871 A CN 201711405871A CN 108219243 A CN108219243 A CN 108219243A
Authority
CN
China
Prior art keywords
master batch
preparation
magnetic plastics
parts
plastics master
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201711405871.1A
Other languages
English (en)
Inventor
董如兵
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Hefei Good Teng Plastics Technology Co Ltd
Original Assignee
Hefei Good Teng Plastics Technology Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Hefei Good Teng Plastics Technology Co Ltd filed Critical Hefei Good Teng Plastics Technology Co Ltd
Priority to CN201711405871.1A priority Critical patent/CN108219243A/zh
Publication of CN108219243A publication Critical patent/CN108219243A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种磁性塑料母粒及其制备方法。一种磁性塑料母粒及其制备方法包括如下步骤：将聚乙烯60‑90份、四氧化三铁纳米颗粒20‑30份、氧化铁棕10‑15份、润滑剂0.5‑2份、增塑剂5‑8份、纳米二氧化硅颗粒3‑8份、稳定剂1‑3份、抗氧化剂3‑5份混合均匀，双螺杆挤出机造粒。本发明制得的塑料母粒具有磁性和优秀的理化性能，应用广泛，生产工艺简单。

Description

一种磁性塑料母粒及其制备方法
技术领域
本发明涉及塑料技术领域，具体为一种磁性塑料母粒及其制备方法。
背景技术
聚乙烯是由乙烯聚合而成的聚合物，产品发展至今已有60年左右的历史，生产工艺成熟，应用广泛。目前，全球范围内聚乙烯的产量居五大泛用树脂的首位。聚乙烯的种类可依聚合方法、分子量高低、链结构之不同来划分，分为高密度聚乙烯、低密度聚乙烯及线性低密度聚乙烯。
高密度聚乙烯具有较高的耐温、耐油性、耐蒸汽渗透性及抗环境应力开裂性的性能，此外电绝缘性和抗冲击性及耐寒性能也很好，主要应用于吹塑、注塑等领域。低密度聚乙烯由于密度较低，材质最软，主要用在塑胶袋、农业用膜等方面。线性低密度聚乙烯外观与低密度聚乙烯相似，透明性较差些，但表面光泽好，具有低温韧性、高模量、抗弯曲和耐应力开裂性，低温下抗冲击强度较佳等优点。线性低密度聚乙烯的应用领域几乎已渗透到所有低密度聚乙烯的市场。对聚乙烯改性可以扩展其应用领域，目前主要改性主要是增加其强度、韧性及可降解性能，磁性改性较少报道。
发明内容
(一)解决的技术问题
针对现有技术的不足，本发明提供了一种磁性塑料母粒及其制备方法，使聚乙烯塑料母粒具有磁性，扩展其应用领域。
(二)技术方案
为实现上述目的，本发明提供如下技术方案：一种磁性塑料母粒及其制备方法，磁性塑料母粒由以下原料制备：
优选的，磁性塑料母粒的制备包括如下步骤：
(1)四氧化三铁纳米颗粒、氧化铁棕、纳米二氧化硅颗粒过筛；
(2)将聚乙烯、四氧化三铁纳米颗粒、氧化铁棕、润滑剂、增塑剂、纳米二氧化硅颗粒、稳定剂、抗氧化剂按比例混合均匀；
(3)双螺杆挤出机造粒。
优选的，所述双螺杆挤出造粒，其中1-5区的温度分别为180℃、195℃、200℃、210℃、200℃，机头温度200℃，转速为30-50r/min。
优选的，四氧化三铁纳米颗粒粒径5-20nm，氧化铁棕粒径5-20nm，纳米二氧化硅颗粒粒径5-20nm。
优选的，润滑剂为石蜡、硬脂酸、硬脂酸酯的一种或几种的混合物。
优选的，增塑剂为邻苯二甲酸酯、脂肪二羧酸酯、聚酯的一种或几种的混合物。
优选的，稳定剂为硬脂酸镁、硬脂酸钾的一种或几种的混合物。
优选的，抗氧化剂为抗氧剂1010、抗氧剂168、抗氧剂1135、抗氧剂TNP的一种或几种的混合物。
(三)有益效果
本发明提供了一种磁性塑料母粒及其制备方法，具备以下有益效果：
(1)本发明明工艺配方中的四氧化三铁纳米颗粒具有磁性，可对聚乙烯填充进行改性，本发明制备的塑料母粒具有磁性，扩展了聚乙烯塑料的应用范围。
(2)本发明工艺配方科学，具有抗氧化剂、稳定剂、无机填料等成分，可以使制备的塑料母粒具有良好的理化性质。
(3)本发明提供的方法生产工艺简单，耗能少，适合工业化生产。
具体实施方式
下面将结合本发明的实施例，对本发明实施例中的技术方案进行清楚、完整地描述，显然，所描述的实施例仅仅是本发明一部分实施例，而不是全部的实施例。基于本发明中的实施例，本领域普通技术人员在没有做出创造性劳动前提下所获得的所有其他实施例，都属于本发明保护的范围。
实施例1
一种磁性塑料母粒及其制备方法，制备过程如下：
(1)四氧化三铁纳米颗粒、氧化铁棕、纳米二氧化硅颗粒过筛；
(2)将聚乙烯60份、四氧化三铁纳米颗粒20份、氧化铁棕10份、石蜡0.5份、DOP 5份、纳米二氧化硅颗粒3份、硬脂酸钾1份、抗氧剂TNP3份按比例混合均匀；
(3)双螺杆挤出机造粒，其中1-5区的温度分别为180℃、195℃、200℃、210℃、200℃，机头温度200℃，转速为30r/min。
实施例2
一种磁性塑料母粒及其制备方法，制备过程如下：
(1)四氧化三铁纳米颗粒、氧化铁棕、纳米二氧化硅颗粒过筛；
(2)将聚乙烯70份、四氧化三铁纳米颗粒25份、氧化铁棕13份、石蜡1份、DOP 6份、纳米二氧化硅颗粒5份、硬脂酸钾2份、抗氧剂TNP 4份按比例混合均匀；
(3)双螺杆挤出机造粒，其中1-5区的温度分别为180℃、195℃、200℃、210℃、200℃，机头温度200℃，转速为40r/min。
实施例3
一种磁性塑料母粒及其制备方法，制备过程如下：
(1)四氧化三铁纳米颗粒、氧化铁棕、纳米二氧化硅颗粒过筛；
(2)将聚乙烯80份、四氧化三铁纳米颗粒30份、氧化铁棕15份、石蜡1.5份、DOP 8份、纳米二氧化硅颗粒8份、硬脂酸钾3份、抗氧剂TNP5份按比例混合均匀；
(3)双螺杆挤出机造粒，其中1-5区的温度分别为180℃、195℃、200℃、210℃、200℃，机头温度200℃，转速为50r/min。
实施例4
一种磁性塑料母粒及其制备方法，制备过程如下：
(1)四氧化三铁纳米颗粒、氧化铁棕、纳米二氧化硅颗粒过筛；
(2)将聚乙烯90份、四氧化三铁纳米颗粒30份、氧化铁棕15份、硬脂酸2份、DOP 8份、纳米二氧化硅颗粒8份、硬脂酸钾3份、抗氧剂10105份按比例混合均匀；
(3)双螺杆挤出机造粒，其中1-5区的温度分别为180℃、195℃、200℃、210℃、200℃，机头温度200℃，转速为50r/min。
尽管已经示出和描述了本发明的实施例，对于本领域的普通技术人员而言，可以理解在不脱离本发明的原理和精神的情况下可以对这些实施例进行多种变化、修改、替换和变型，本发明的范围由所附权利要求及其等同物限定。

Claims (8)

1.一种磁性塑料母粒及其制备方法，其特征在于，磁性塑料母粒由以下原料制备：
2.根据权利要求1所述的一种磁性塑料母粒及其制备方法，其特征在于，一种磁性塑料母粒的制备包括如下步骤：
(1)四氧化三铁纳米颗粒、氧化铁棕、纳米二氧化硅颗粒过筛；
(2)将聚乙烯、四氧化三铁纳米颗粒、氧化铁棕、润滑剂、增塑剂、纳米二氧化硅颗粒、稳定剂、抗氧化剂按比例混合均匀；
(3)双螺杆挤出机造粒。
3.根据权利要求2所述的一种磁性塑料母粒及其制备方法，其特征在于，所述双螺杆挤出造粒，其中1-5区的温度分别为180℃、195℃、200℃、210℃、200℃，机头温度200℃，转速为30-50r/min。
4.根据权利要求1或2所述的一种磁性塑料母粒及其制备方法，其特征在于，四氧化三铁纳米颗粒粒径5-20nm，氧化铁棕粒径5-20nm，纳米二氧化硅颗粒粒径5-20nm。
5.根据权利要求1或2所述的一种磁性塑料母粒及其制备方法，其特征在于，所述润滑剂为石蜡、硬脂酸、硬脂酸酯的一种或几种的混合物。
6.根据权利要求1或2所述的一种磁性塑料母粒及其制备方法，其特征在于，所述增塑剂为邻苯二甲酸酯、脂肪二羧酸酯、聚酯的一种或几种的混合物。
7.根据权利要求1或2所述的一种磁性塑料母粒及其制备方法，其特征在于，所述稳定剂为硬脂酸镁、硬脂酸钾的一种或几种的混合物。
8.根据权利要求1或2所述的一种磁性塑料母粒及其制备方法，其特征在于，所述抗氧化剂为抗氧剂1010、抗氧剂168、抗氧剂1135、抗氧剂TNP的一种或几种的混合物。
CN201711405871.1A 2017-12-22 2017-12-22 一种磁性塑料母粒及其制备方法 Pending CN108219243A (zh)