CN108192447A - Rock quartz burnt-in sand paint external wall decorative material and its preparation process - Google Patents
Rock quartz burnt-in sand paint external wall decorative material and its preparation process Download PDFInfo
- Publication number
- CN108192447A CN108192447A CN201711472979.2A CN201711472979A CN108192447A CN 108192447 A CN108192447 A CN 108192447A CN 201711472979 A CN201711472979 A CN 201711472979A CN 108192447 A CN108192447 A CN 108192447A
- Authority
- CN
- China
- Prior art keywords
- sand
- burnt
- rock quartz
- external wall
- wall decorative
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
A kind of rock quartz burnt-in sand paint external wall decorative material belongs to the technical field of building outer wall decorative material, by mass percentage, including water 25 32%, Attagel 0.5 1.0%, wetting agent 0.1 0.3%, antifoaming agent 0.03 0.08%, propylene glycol 0.3 0.4%, fungicide 0.1 0.3%, coalescents 1.5 1.7%, rock quartz sliver 10 15%, pure-acrylic emulsion 25 27%, thickener 7 7.5%, coupling agent 1 1.5%, sand 18 22%.It is related to a kind of rock quartz burnt-in sand paint external wall decorative material and its preparation process.The present invention also provides the preparation process of Chinese fir rock quartz burnt-in sand paint external wall decorative material simultaneously, and present invention gained rock quartz burnt-in sand paint external wall decorative material is building energy conservation of new generation, the new decorative material of environmentally protective light-duty, low cost, good decorating effect.
Description
Technical field
The invention belongs to the technical fields of building outer wall decorative material, are related to a kind of rock quartz burnt-in sand paint external wall decorative material
And its preparation process.The rock quartz burnt-in sand paint external wall decorative material of the present invention is building energy conservation of new generation, it is environmentally protective it is light-duty,
The new decorative material of low cost, good decorating effect.
Background technology
With continuous development of the science on decoration, carried out according to country and carried out at heat preservation on building wall face
Reason, anticracking grout face is smeared on insulating layer, is influenced by expanding with heat and contract with cold, and brings the difficulty on decoration to wall face, tiling is afraid of
It comes off, the exterior coating decoration time is not grown, and the degree of cracking resistance is not also strong.With stone material dry suspending, mine resources are inadequate, building office
Building, office building, hotel, which will excavate, spends hundreds of tons of stone materials, and a city, which adds up, must spend several ten million tons of stone materials, and one
Year accumulation gets up to excavate several mountains, and thus cost is too big.According to above actual conditions, with lacquer, texture
Paint is easily stained with sand and dust ash, damage is difficult to repair, and with sandstone sliver paint, fidelity effect is not achieved, and is a kind of color spot with water-water
Coating is too thin not have three-dimensional sense.
Therefore, researching and developing a kind of new decorative material for substituting water-water form coating and reaching required finishing requirements is
Problem to be solved at present.
Invention content
The present invention is to solve the above problems, provide a kind of rock quartz burnt-in sand paint external wall decorative material and its preparation process.
Rock quartz burnt-in sand paint external wall decorative material of the present invention takes into account waterproof, cracking resistance, and good decorating effect is prepared, construction is simple.
The present invention for realize its purpose the technical solution adopted is that：
A kind of rock quartz burnt-in sand paint external wall decorative material, by mass percentage, including water 25-32%, Attagel 0.5-
1.0%, wetting agent 0.1-0.3%, antifoaming agent 0.03-0.08%, propylene glycol 0.3-0.4%, fungicide 0.1-0.3%, film forming
Auxiliary agent 1.5-1.7%, rock quartz sliver 10-15%, pure-acrylic emulsion 25-27%, thickener 7-7.5%, coupling agent 1-1.5%,
Sand 18-22%.
A kind of rock quartz burnt-in sand paint external wall decorative material, by mass percentage, including water 29.3%, Attagel 0.8%,
Wetting agent 0.2%, antifoaming agent 0.05%, propylene glycol 0.35%, fungicide 0.2%, coalescents 1.6%, rock quartz sliver
13%, pure-acrylic emulsion 26%, thickener 7.3%, coupling agent 1.2%, sand 20%.
It is (4-4.2) that the thickener, which includes mass ratio,：DR-180 association thickeners and the polyurethane thickening of (3-3.3)
Agent.
The sand selects the sand that mesh number is 80-120 mesh.
The solid content of the pure-acrylic emulsion is 48-50%.
The wetting agent is anionic wetting agents.
A kind of preparation process of rock quartz burnt-in sand paint external wall decorative material, includes the following steps：
A, Jiang Shui, Attagel, wetting agent, antifoaming agent, propylene glycol, fungicide and coalescents are placed in stirred tank, with 40-
60 revs/min of speed stirring 30-40min, obtains mixed material；
B, rock quartz sliver is added in into above-mentioned mixed material, is stirred evenly；
C, pure-acrylic emulsion is added in into above-mentioned material, and is stirred evenly；
D, thickener is added in above-mentioned material, 30-40min is stirred with 20-40 revs/min of speed, control material is glued
Spend 120-140；
E, sand is added in into above-mentioned material, stirred evenly, obtain rock quartz burnt-in sand paint external wall decorative material.
The beneficial effects of the invention are as follows：
Rock quartz burnt-in sand paint external wall decorative material stability of the present invention is good, tissue morphology stable homogeneous, the normal temperature storage time limit
Up to 15 years or more, after being sprayed at metope, it is true to emulate pattern for no sag, good leveling property.
Rock quartz burnt-in sand paint external wall decorative material of the present invention by the collocation of raw material, ratio it is control combined process, viscous
The control of degree makes the rock quartz finally prepared burnt-in sand paint external wall decorative material that " making dumplings " state of rock quartz burnt-in sand, sand be presented
Son is wrapped in rock quartz sliver, has developed a kind of new decorative material.
By selecting being used in compounding of DR-180 association thickeners and polyurethane thickener and coupling agent, controlling the two
Between and the ratio between the two total amount and coupling agent, the globality of material can be improved, conducive to construction, improve ornament materials spraying
The ductility and plasticity of rock quartz burnt-in sand paint are formed afterwards, and makes the enamelled coating to be formed that there is self-healing ability, when friction etc. deposits enamelled coating
In tiny cut, enamelled coating can be voluntarily compound, avoids the potential hazard of cut, such as over time, cut cracking, tide
Gas and water is graded into enamelled coating internal structure is destroyed, and the cut later stage becomes larger service life for influencing enamelled coating etc.；Simultaneously Attagel addition with
Propylene glycol, pure-acrylic emulsion collective effect, can form the compound with inclusion complex physico-chemical property, which can reduce oxidation,
Light sensitivity and thermal sensitivity are passivated, improves the resistance to ag(e)ing of enamelled coating.
The thickness of rock quartz sliver of the present invention be 0.5-0.6mm, sand select mesh number be 80-120 mesh sand, the design be for
Rock quartz sliver is allowed preferably to wrap up sand, " rock quartz burnt-in sand " state for making presentation is more attractive, the distribution of sand is with equilibrium.Water
Spar sliver it is too thin or it is too thick can all influence burnt-in sand effect, it is blocked up, then coat difficulty, excessively thin, then easy agglomerate and covered effect is poor,
Final " rock quartz burnt-in sand " state is disorderly, and unformed, pattern is unsightly.
Specific embodiment
With reference to specific embodiment, the present invention is further illustrated.
First, specific embodiment
Embodiment 1
For producing 100kg rock quartz burnt-in sand paint external wall decorative materials, including water 29.3kg, Attagel 0.8kg, wetting
Agent 0.2kg, elastic antifoaming agent 0.05kg, propylene glycol 0.35kg, fungicide 0.2kg, coalescents 1.6kg, rock quartz sliver
13kg, pure-acrylic emulsion 26kg, DR-180 association thickener 4.2kg, polyurethane thickener 3.1kg, coupling agent 1.2kg, sand
20kg.The DR-180 association thickeners are Tao Shi DR-180 hydrophobically-modified alkali swelling association thickeners.
Rock quartz burnt-in sand paint external wall decorative material of the present invention is prepared by following methods, is included the following steps：
A, Jiang Shui, Attagel, wetting agent, antifoaming agent, propylene glycol, fungicide and coalescents are placed in stirred tank, with 50
Rev/min speed stirring 30min, obtain mixed material；
B, rock quartz sliver is added in into above-mentioned mixed material, is stirred evenly；
C, pure-acrylic emulsion is added in into above-mentioned material, and is stirred evenly；
D, thickener is added in above-mentioned material, 30min, control material viscosity 130 is stirred with 30 revs/min of speed；
Thickener be plus 9 times water dilution after thickener；
E, sand is added in into above-mentioned material, stirred evenly, obtain rock quartz burnt-in sand paint external wall decorative material.
Embodiment 2
For producing 100kg rock quartz burnt-in sand paint external wall decorative materials, including water 27kg, Attagel 0.5kg, wetting agent
0.3kg, antifoaming agent 0.08kg, propylene glycol 0.32kg, fungicide 0.3kg, coalescents 1.7kg, rock quartz sliver 15kg, pure third
Lotion 27kg, thickener 7.5kg, coupling agent 1.3kg, sand 19kg.
Rock quartz burnt-in sand paint external wall decorative material of the present invention is prepared by following methods, is included the following steps：
A, Jiang Shui, Attagel, wetting agent, antifoaming agent, propylene glycol, fungicide and coalescents are placed in stirred tank, with 60
Rev/min speed stirring 35min, obtain mixed material；
B, rock quartz sliver is at the uniform velocity added in into above-mentioned mixed material, is stirred evenly；Speed is being mixed with rock quartz sliver
In material subject to dispersion.
C, pure-acrylic emulsion is added in into above-mentioned material, and is stirred evenly；
It is added in above-mentioned material D, thickener to be added to 9 times of water dilution after, 30min, control is stirred with 40 revs/min of speed
Material viscosity 130 processed；
E, sand is added in into above-mentioned material, stirred evenly, obtain rock quartz burnt-in sand paint external wall decorative material.
Embodiment 3
For producing 100kg rock quartz burnt-in sand paint external wall decorative materials, including water 26kg, Attagel 0.6kg, wetting agent
0.3kg, antifoaming agent 0.07kg, propylene glycol 0.33kg, fungicide 0.2kg, coalescents 1.6kg, rock quartz sliver 14kg, pure third
Lotion 27kg, thickener 7.4kg, coupling agent 1.5kg, sand 21kg.
Rock quartz burnt-in sand paint external wall decorative material of the present invention is prepared by following methods, is included the following steps：
A, Jiang Shui, Attagel, wetting agent, antifoaming agent, propylene glycol, fungicide and coalescents are placed in stirred tank, with 45
Rev/min speed stirring 33min, obtain mixed material；
B, rock quartz sliver is added in into above-mentioned mixed material, is stirred evenly；
C, pure-acrylic emulsion is added in into above-mentioned material, and is stirred evenly；
It is added in above-mentioned material D, thickener to be added to 9 times of water dilution after, 35min, control is stirred with 25 revs/min of speed
Material viscosity 135 processed；
E, sand is added in into above-mentioned material, stirred evenly, obtain rock quartz burnt-in sand paint external wall decorative material.
Embodiment 4
For producing 100kg rock quartz burnt-in sand paint external wall decorative materials, raw material includes water 32kg, Attagel 0.7kg, profit
Humectant 0.1kg, antifoaming agent 0.06kg, propylene glycol 0.34kg, fungicide 0.3kg, coalescents 1.7kg, rock quartz sliver
13.2kg, pure-acrylic emulsion 25kg, thickener 7.2kg, coupling agent 1.4kg, sand 18kg.
Rock quartz burnt-in sand paint external wall decorative material of the present invention is prepared by following methods, is included the following steps：
A, Jiang Shui, Attagel, wetting agent, antifoaming agent, propylene glycol, fungicide and coalescents are placed in stirred tank, with 55
Rev/min speed stirring 38min, obtain mixed material；
B, rock quartz sliver is added in into above-mentioned mixed material, is stirred evenly；
C, pure-acrylic emulsion is added in into above-mentioned material, and is stirred evenly；
It is added in above-mentioned material D, thickener to be added to 9 times of water dilution after, 33min, control is stirred with 35 revs/min of speed
Material viscosity 125 processed；
E, sand is added in into above-mentioned material, stirred evenly, obtain rock quartz burnt-in sand paint external wall decorative material.
Embodiment 5
For producing 100kg rock quartz burnt-in sand paint external wall decorative materials, including water 29.6kg, Attagel 0.9kg, wetting
Agent 0.2kg, antifoaming agent 0.04kg, propylene glycol 0.36kg, fungicide 0.2kg, coalescents 1.5kg, rock quartz sliver 11kg are pure
Acrylic emulsion 26kg, thickener 7.1kg, coupling agent 1.1kg, sand 22kg.
Rock quartz burnt-in sand paint external wall decorative material of the present invention is prepared by following methods, is included the following steps：
A, Jiang Shui, Attagel, wetting agent, antifoaming agent, propylene glycol, fungicide and coalescents are placed in stirred tank, with 50
Rev/min speed stirring 30min, obtain mixed material；
B, rock quartz sliver is added in into above-mentioned mixed material, is stirred evenly；
C, pure-acrylic emulsion is added in into above-mentioned material, and is stirred evenly；
It is added in above-mentioned material D, thickener to be added to 9 times of water dilution after, 40min, control is stirred with 30 revs/min of speed
Material viscosity 120 processed；
E, sand is added in into above-mentioned material, stirred evenly, obtain rock quartz burnt-in sand paint external wall decorative material.
Embodiment 6
For producing 100kg rock quartz burnt-in sand paint external wall decorative materials, including water 31.8kg, Attagel 1kg, wetting agent
0.2kg, antifoaming agent 0.03kg, propylene glycol 0.37kg, fungicide 0.1kg, coalescents 1.5kg, rock quartz sliver 10kg, pure third
Lotion 27kg, thickener 7kg, coupling agent 1kg, sand 20kg.
Rock quartz burnt-in sand paint external wall decorative material of the present invention is prepared by following methods, is included the following steps：
A, Jiang Shui, Attagel, wetting agent, antifoaming agent, propylene glycol, fungicide and coalescents are placed in stirred tank, with 45
Rev/min speed stirring 35min, obtain mixed material；
B, rock quartz sliver is added in into above-mentioned mixed material, is stirred evenly；
C, pure-acrylic emulsion is added in into above-mentioned material, and is stirred evenly；
It is added in above-mentioned material D, thickener to be added to 9 times of water dilution after, 30min, control is stirred with 30 revs/min of speed
Material viscosity 140 processed；
E, sand is added in into above-mentioned material, stirred evenly, obtain rock quartz burnt-in sand paint external wall decorative material.
Embodiment 7
For producing 100kg rock quartz burnt-in sand paint external wall decorative materials, including water 29.3kg, Attagel 0.8kg, wetting
Agent 0.25kg, antifoaming agent 0.05kg, propylene glycol 0.3kg, fungicide 0.3kg, coalescents 1.6kg, rock quartz sliver 13kg are pure
Acrylic emulsion 26kg, thickener 7.2kg, coupling agent 1.2kg, sand 20kg.
Rock quartz burnt-in sand paint external wall decorative material of the present invention is prepared by following methods, is included the following steps：
A, Jiang Shui, Attagel, wetting agent, antifoaming agent, propylene glycol, fungicide and coalescents are placed in stirred tank, with 55
Rev/min speed stirring 30min, obtain mixed material；
B, rock quartz sliver is added in into above-mentioned mixed material, is stirred evenly；
C, pure-acrylic emulsion is added in into above-mentioned material, and is stirred evenly；
It is added in above-mentioned material D, thickener to be added to 9 times of water dilution after, 40min, control is stirred with 35 revs/min of speed
Material viscosity 130 processed；
E, sand is added in into above-mentioned material, stirred evenly, obtain rock quartz burnt-in sand paint external wall decorative material.
Embodiment 8
For producing 100kg rock quartz burnt-in sand paint external wall decorative materials, including water 30.15kg, Attagel 0.8kg, profit
Humectant 0.2kg, antifoaming agent 0.05kg, propylene glycol 0.4kg, fungicide 0.1kg, coalescents 1.7kg, rock quartz sliver 13kg,
Pure-acrylic emulsion 25kg, thickener 7.3kg, coupling agent 1.3kg, sand 20kg.
Rock quartz burnt-in sand paint external wall decorative material of the present invention is prepared by following methods, is included the following steps：
A, Jiang Shui, Attagel, wetting agent, antifoaming agent, propylene glycol, fungicide and coalescents are placed in stirred tank, with 50
Rev/min speed stirring 40min, obtain mixed material；
B, rock quartz sliver is at the uniform velocity added in into above-mentioned mixed material, is stirred evenly；
C, pure-acrylic emulsion is added in into above-mentioned material, and is stirred evenly；
It is added in above-mentioned material D, thickener to be added to 9 times of water dilution after, 40min, control is stirred with 30 revs/min of speed
Material viscosity 135 processed；
E, sand is added in into above-mentioned material, stirred evenly, obtain rock quartz burnt-in sand paint external wall decorative material.
Embodiment 9
For producing 100kg rock quartz burnt-in sand paint external wall decorative materials, including water 29kg, Attagel 0.8kg, wetting agent
0.3kg, antifoaming agent 0.05kg, propylene glycol 0.35kg, fungicide 0.2kg, coalescents 1.5kg, rock quartz sliver 13kg, pure third
Lotion 26kg, thickener 7.4kg, coupling agent 1.4kg, sand 20kg.
Rock quartz burnt-in sand paint external wall decorative material of the present invention is prepared by following methods, is included the following steps：
A, Jiang Shui, Attagel, wetting agent, antifoaming agent, propylene glycol, fungicide and coalescents are placed in stirred tank, with 45
Rev/min speed stirring 40min, obtain mixed material；
B, rock quartz sliver is added in into above-mentioned mixed material, is stirred evenly；
C, pure-acrylic emulsion is added in into above-mentioned material, and is stirred evenly；
It is added in above-mentioned material D, thickener to be added to 9 times of water dilution after, 40min, control is stirred with 30 revs/min of speed
Material viscosity 130 processed；
E, sand is added in into above-mentioned material, stirred evenly, obtain rock quartz burnt-in sand paint external wall decorative material.
Embodiment 10
For producing 100kg rock quartz burnt-in sand paint external wall decorative materials, including water 28kg, Attagel 0.8kg, wetting agent
0.1kg, antifoaming agent 0.05kg, propylene glycol 0.35kg, fungicide 0.3kg, coalescents 1.6kg, rock quartz sliver 13kg, pure third
Lotion 27kg, thickener 7.3kg, coupling agent 1.5kg, sand 20kg.
Rock quartz burnt-in sand paint external wall decorative material of the present invention is prepared by following methods, is included the following steps：
A, Jiang Shui, Attagel, wetting agent, antifoaming agent, propylene glycol, fungicide and coalescents are placed in stirred tank, with 40
Rev/min speed stirring 30min, obtain mixed material；
B, rock quartz sliver is added in into above-mentioned mixed material, is stirred evenly；
C, pure-acrylic emulsion is added in into above-mentioned material, and is stirred evenly；
It is added in above-mentioned material D, thickener to be added to 9 times of water dilution after, 40min, control is stirred with 20 revs/min of speed
Material viscosity 140 processed；
E, sand is added in into above-mentioned material, stirred evenly, obtain rock quartz burnt-in sand paint external wall decorative material.
2nd, effect test
When the 1st, constructing, with spray gun spraying on metope, when spraying, preferably sprays twice, and first pass sprays thin layer, 3-4h
Afterwards, it according to the sliver point sprayed, then sprays second time, is sprayed by the density of imitative stone material point, bottom drain is not standard.Detection institute into
The performance of paint, as a result such as table 1.
Table 1
2nd, influence of the processing step to material prepared form
By taking embodiment 1 as an example, the process step of the invention is test example, and contrast test, comparison are carried out with other techniques
As a result such as table 2.
Comparative example 1：By water, Attagel, wetting agent, antifoaming agent, propylene glycol, fungicide, coalescents, rock quartz sliver,
Pure-acrylic emulsion, thickener, coupling agent are mixed, stirring at low speed, obtain mixed material, then sand is added in mixed material,
It stirs evenly.
Comparative example 2：By water, Attagel, wetting agent, antifoaming agent, propylene glycol, fungicide, coalescents, pure-acrylic emulsion, increasing
Thick dose, coupling agent mixed, stirring at low speed obtains mixed material, and then rock quartz sliver, sand are added in mixed material,
It stirs evenly.
Comparative example 3：Water, pure-acrylic emulsion are mixed, stirred evenly, rock quartz sliver is added in, stirs evenly, then add in silicon
Magnesia, wetting agent, antifoaming agent, propylene glycol, fungicide, coalescents, thickener, coupling agent are mixed, and add in sand, and stirring is equal
It is even.
Table 2
3rd, raw material selection compares the influence of material prepared with matching
(1) by taking embodiment 1 as an example, (such as silica, swelling are substituted by other compositions with no Attagel or Attagel
Soil or kaolin etc.) or Attagel compared with ornament materials formed by the raw materials used combination of non-present invention, technique used is equal
For embodiment technique, compare material shape and paint performance such as table 3.
Table 3
(2) influence of the thickener to material prepared
The selection of thickener types and the influence with comparison material shape, enamelled coating performance.It is experiment with the embodiment of the present invention 1
Example with other kinds of thickener, changes amount ratio and is compared, and all experiment medium viscosities and other technology controlling and process all control
It is identical, enamelled coating self-healing ability is investigated, as a result such as the following table 4.
Table 4
By above-mentioned table 2-4 it is found that the selection of Attagel and its combined with the collocation of other components, the selection of thickener and its
Collocation with other components combines, the control of raw material dosage relationship, processing step, and synthesis makes finally prepd rock quartz burnt-in sand paint
External wall decorative material performance is good, forms " dumpling " form of rock quartz sliver package sand, and spraying pattern is beautiful.
Claims (7)
1. a kind of rock quartz burnt-in sand paint external wall decorative material, which is characterized in that by mass percentage, including water 25-32%, silicon
Magnesia 0.5-1.0%, wetting agent 0.1-0.3%, antifoaming agent 0.03-0.08%, propylene glycol 0.3-0.4%, fungicide 0.1-
0.3%, coalescents 1.5-1.7%, rock quartz sliver 10-15%, pure-acrylic emulsion 25-27%, thickener 7-7.5%, coupling
Agent 1-1.5%, sand 18-22%.
2. a kind of rock quartz burnt-in sand paint external wall decorative material according to claim 1, which is characterized in that by mass percentage
Meter, including water 29.3%, Attagel 0.8%, wetting agent 0.2%, antifoaming agent 0.05%, propylene glycol 0.35%, fungicide
0.2%, coalescents 1.6%, rock quartz sliver 13%, pure-acrylic emulsion 26%, thickener 7.3%, coupling agent 1.2%, sand
20%.
A kind of 3. rock quartz burnt-in sand paint external wall decorative material according to claim 1, which is characterized in that the thickener packet
Mass ratio is included as (4-4.2)：The DR-180 association thickeners and polyurethane thickener of (3-3.3).
4. a kind of rock quartz burnt-in sand paint external wall decorative material according to claim 1, which is characterized in that the sand selects mesh
Sand of the number for 80-120 mesh.
A kind of 5. rock quartz burnt-in sand paint external wall decorative material according to claim 1, which is characterized in that the pure-acrylic emulsion
Solid content be 48-50%.
6. a kind of rock quartz burnt-in sand paint external wall decorative material according to claim 1, which is characterized in that the wetting agent is
Anionic wetting agents.
7. a kind of preparation process of rock quartz burnt-in sand paint external wall decorative material as described in claim 1, which is characterized in that including with
Lower step：
A, Jiang Shui, Attagel, wetting agent, antifoaming agent, propylene glycol, fungicide and coalescents are placed in stirred tank, with 40-60
Rev/min speed stirring 30-40min, obtain mixed material；
B, rock quartz sliver is added in into above-mentioned mixed material, is stirred evenly；
C, pure-acrylic emulsion is added in into above-mentioned material, and is stirred evenly；
D, thickener is added in above-mentioned material, 30-40min, control material viscosity is stirred with 20-40 revs/min of speed
120-140；
E, sand is added in into above-mentioned material, stirred evenly, obtain rock quartz burnt-in sand paint external wall decorative material.