CN108148341A - 一种综合性能好的复合塑料及其制备方法 - Google Patents
一种综合性能好的复合塑料及其制备方法 Download PDFInfo
- Publication number
- CN108148341A CN108148341A CN201810000663.1A CN201810000663A CN108148341A CN 108148341 A CN108148341 A CN 108148341A CN 201810000663 A CN201810000663 A CN 201810000663A CN 108148341 A CN108148341 A CN 108148341A
- Authority
- CN
- China
- Prior art keywords
- parts
- powder
- mixture
- good combination
- combination property
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种综合性能好的复合塑料及其制备方法，包括以下重量份的原料：ABS 34‑45份、聚苯乙烯10‑20份、秸秆粉末16‑22份、正硅酸四乙酯1.6‑3.5份、纳米石墨0.2‑0.6份、滑石粉2‑5份、塑化剂1‑3份、光稳定剂0.1‑0.5份、抗氧剂1010 0.6‑1.4份、三氧化二锑5‑6份、偶联剂1‑3份、相容剂1.5‑2.8份、硼砂2‑5份和秋葵3‑6份。本发明原料来源广泛，制备工艺简单，通过各种原料之间的相互作用，制备的成品具有良好的冲击性能、阻燃性能、耐真菌腐蚀性能和抗老化性能，还具有低吸水率，满足了人们的使用需求。
Description
技术领域
本发明涉及塑料领域，具体是一种综合性能好的复合塑料。
背景技术
塑料是以单体为原料，通过加聚或缩聚反应聚合而成的高分子化合物，又称树脂，可以自由改变成分及形体样式，由合成树脂及填料、增塑剂、稳定剂、润滑剂、色料等添加剂组成。ABS塑料就是常见的一种塑料，ABS(丙烯腈-丁二烯-苯乙烯)树脂是在聚苯乙烯树脂改性的基础上发展起来的三元共聚物，其中A代表丙烯睛、B代表丁二烯、S代表苯乙烯。ABS塑料无毒、无味，外观呈象牙色半透明，或透明颗粒或粉状。ABS的电绝缘性较好，并且几乎不受温度、湿度和频率的影响，可在大多数环境下使用，不受水、无机盐、碱及多种酸的影响，但可溶于酮类、醛类及氯代烃中，受冰乙酸、植物油等侵蚀会产生应力开裂，ABS的耐候性差，在紫外光的作用下易产生降解，人们需要添加其他组分来改善ABS的这些性能。
发明内容
本发明的目的在于提供一种综合性能好的复合塑料，以解决上述背景技术中提出的问题。
为实现上述目的，本发明提供如下技术方案：
一种综合性能好的复合塑料，包括以下重量份的原料：ABS 34-45份、聚苯乙烯10-20份、秸秆粉末16-22份、正硅酸四乙酯1.6-3.5份、纳米石墨0.2-0.6份、滑石粉2-5份、塑化剂1-3份、光稳定剂0.1-0.5份、抗氧剂1010 0.6-1.4份、三氧化二锑5-6份、偶联剂1-3份、相容剂1.5-2.8份、硼砂2-5份和秋葵3-6份。
作为本发明进一步的方案：秸秆粉末包括甘蔗秸秆粉末、玉米秸秆粉末、甘蔗秸秆粉末、高粱秸秆粉末和大豆秸秆粉末中的至少一种。
作为本发明进一步的方案：三氧化二锑的粒度为1.2-3.45mm，硼砂的粒度为0.85-2.43mm。
所述综合性能好的复合塑料的制备方法，具体步骤如下：
步骤一，将秋葵粉碎并且浸泡在质量分数为70-75％的乙醇水溶液中12-15小时，过滤并且将滤液进行减压蒸馏，然后在35-45摄氏度的真空条件下干燥至水分的质量分数为5-10％，得到秋葵提取物；
步骤二，将秸秆粉末和正硅酸四乙酯浸泡在质量分数为20-25％的氢氧化钠溶液中，浸泡后的产物进行干燥，得到改性秸秆粉末和改性正硅酸四乙酯；
步骤三，将改性秸秆粉末、ABS、聚苯乙烯和硼砂在球磨机中混合并且球磨至240-300目，得到第一混合物；
步骤四，将第一混合物、秋葵提取物、改性正硅酸四乙酯、纳米石墨、三氧化二锑和相容剂在混料机中搅拌4-6分钟，得到第二混合物；
步骤五，向第二混合物中依次加入滑石粉、塑化剂、光稳定剂、抗氧剂1010和偶联剂并且混合均匀，得到第三混合物；
步骤六，将第三混合物放入双螺杆挤出机挤出，即可得到成品。
作为本发明进一步的方案：步骤四中混料机的混合温度为30-40摄氏度，搅拌速度为90-120rpm，步骤五中的混合速度为900-1050rpm。
与现有技术相比，本发明的有益效果是：本发明原料来源广泛，制备工艺简单，通过各种原料之间的相互作用，制备的成品具有良好的冲击性能、阻燃性能、耐真菌腐蚀性能和抗老化性能，还具有低吸水率，满足了人们的使用需求。
具体实施方式
下面结合具体实施方式对本专利的技术方案作进一步详细地说明。
实施例1
一种综合性能好的复合塑料，包括以下重量份的原料：ABS 34份、聚苯乙烯10份、秸秆粉末16份、正硅酸四乙酯1.6份、纳米石墨0.2份、滑石粉2份、塑化剂1份、光稳定剂0.1份、抗氧剂1010 0.6份、三氧化二锑5份、偶联剂1份、相容剂1.5份、硼砂2份和秋葵3份。秸秆粉末包括甘蔗秸秆粉末和甘蔗秸秆粉末的混合物。
所述综合性能好的复合塑料的制备方法，具体步骤如下：
步骤一，将秋葵粉碎并且浸泡在质量分数为72％的乙醇水溶液中13小时，过滤并且将滤液进行减压蒸馏，然后在38摄氏度的真空条件下干燥至水分的质量分数为8％，得到秋葵提取物；
步骤二，将秸秆粉末和正硅酸四乙酯浸泡在质量分数为22％的氢氧化钠溶液中，浸泡后的产物进行干燥，得到改性秸秆粉末和改性正硅酸四乙酯；
步骤三，将改性秸秆粉末、ABS、聚苯乙烯和硼砂在球磨机中混合并且球磨至270目，得到第一混合物；
步骤四，将第一混合物、秋葵提取物、改性正硅酸四乙酯、纳米石墨、三氧化二锑和相容剂在混料机中搅拌5分钟，得到第二混合物；
步骤五，向第二混合物中依次加入滑石粉、塑化剂、光稳定剂、抗氧剂1010和偶联剂并且混合均匀，得到第三混合物；
步骤六，将第三混合物放入双螺杆挤出机挤出，即可得到成品。
实施例2
一种综合性能好的复合塑料，包括以下重量份的原料：ABS 38份、聚苯乙烯12份、秸秆粉末18份、正硅酸四乙酯2.2份、纳米石墨0.3份、滑石粉3.5份、塑化剂1.6份、光稳定剂0.25份、抗氧剂1010 0.9份、三氧化二锑5.2份、偶联剂1.8份、相容剂2份、硼砂3.4份和秋葵4份。三氧化二锑的粒度为1.75mm，硼砂的粒度为1.62mm。
所述综合性能好的复合塑料的制备方法，具体步骤如下：
步骤一，将秋葵粉碎并且浸泡在质量分数为70％的乙醇水溶液中14小时，过滤并且将滤液进行减压蒸馏，然后在40摄氏度的真空条件下干燥至水分的质量分数为6％，得到秋葵提取物；
步骤二，将秸秆粉末和正硅酸四乙酯浸泡在质量分数为24％的氢氧化钠溶液中，浸泡后的产物进行干燥，得到改性秸秆粉末和改性正硅酸四乙酯；
步骤三，将改性秸秆粉末、ABS、聚苯乙烯和硼砂在球磨机中混合并且球磨至300目，得到第一混合物；
步骤四，将第一混合物、秋葵提取物、改性正硅酸四乙酯、纳米石墨、三氧化二锑和相容剂在混料机中搅拌4分钟，得到第二混合物；
步骤五，向第二混合物中依次加入滑石粉、塑化剂、光稳定剂、抗氧剂1010和偶联剂并且混合均匀，得到第三混合物；
步骤六，将第三混合物放入双螺杆挤出机挤出，即可得到成品。
实施例3
一种综合性能好的复合塑料，包括以下重量份的原料：ABS 42份、聚苯乙烯16份、秸秆粉末19份、正硅酸四乙酯2.8份、纳米石墨0.5份、滑石粉4.2份、塑化剂2.5份、光稳定剂0.4份、抗氧剂1010 1.2份、三氧化二锑5.8份、偶联剂2.4份、相容剂2.4份、硼砂4.4份和秋葵5份。秸秆粉末包括玉米秸秆粉末和大豆秸秆粉末的混合物。
所述综合性能好的复合塑料的制备方法，具体步骤如下：
步骤一，将秋葵粉碎并且浸泡在质量分数为75％的乙醇水溶液中13小时，过滤并且将滤液进行减压蒸馏，然后在40摄氏度的真空条件下干燥至水分的质量分数为8％，得到秋葵提取物；
步骤二，将秸秆粉末和正硅酸四乙酯浸泡在质量分数为24％的氢氧化钠溶液中，浸泡后的产物进行干燥，得到改性秸秆粉末和改性正硅酸四乙酯；
步骤三，将改性秸秆粉末、ABS、聚苯乙烯和硼砂在球磨机中混合并且球磨至300目，得到第一混合物；
步骤四，将第一混合物、秋葵提取物、改性正硅酸四乙酯、纳米石墨、三氧化二锑和相容剂在35摄氏度的混料机中以90rpm的转速搅拌4分钟，得到第二混合物；
步骤五，向第二混合物中依次加入滑石粉、塑化剂、光稳定剂、抗氧剂1010和偶联剂并且以1000rpm的转速混合均匀，得到第三混合物；
步骤六，将第三混合物放入双螺杆挤出机挤出，即可得到成品。
实施例4
一种综合性能好的复合塑料，包括以下重量份的原料：ABS 45份、聚苯乙烯20份、秸秆粉末22份、正硅酸四乙酯3.5份、纳米石墨0.6份、滑石粉5份、塑化剂3份、光稳定剂0.5份、抗氧剂1010 1.4份、三氧化二锑6份、偶联剂3份、相容剂2.8份、硼砂5份和秋葵6份。秸秆粉末包括甘蔗秸秆粉末、玉米秸秆粉末、甘蔗秸秆粉末、高粱秸秆粉末和大豆秸秆粉末的混合物。三氧化二锑的粒度为2.68mm，硼砂的粒度为1.36mm。
所述综合性能好的复合塑料的制备方法，具体步骤如下：
步骤一，将秋葵粉碎并且浸泡在质量分数为72％的乙醇水溶液中13小时，过滤并且将滤液进行减压蒸馏，然后在45摄氏度的真空条件下干燥至水分的质量分数为9％，得到秋葵提取物；
步骤二，将秸秆粉末和正硅酸四乙酯浸泡在质量分数为24％的氢氧化钠溶液中，浸泡后的产物进行干燥，得到改性秸秆粉末和改性正硅酸四乙酯；
步骤三，将改性秸秆粉末、ABS、聚苯乙烯和硼砂在球磨机中混合并且球磨至270目，得到第一混合物；
步骤四，将第一混合物、秋葵提取物、改性正硅酸四乙酯、纳米石墨、三氧化二锑和相容剂在36摄氏度的混料机中以120rpm的转速搅拌6分钟，得到第二混合物；
步骤五，向第二混合物中依次加入滑石粉、塑化剂、光稳定剂、抗氧剂1010和偶联剂并且以1050rpm的转速混合均匀，得到第三混合物；
步骤六，将第三混合物放入双螺杆挤出机挤出，即可得到成品。
对比例1
除不含有秋葵，其余组分和制备方法均与实施例3相同。
对实施例1-4的产品和对比例1的产品进行性能测试，测试结果见表1。
表1
从表1中可以看出，实施例1-4的产品在性能上均高于对比例1的产品，可以满足人们的使用需求。
用碱对秸秆粉末改性，然后减肥秸秆粉末、ABS、聚苯乙烯进行混合，再与纳米石墨等进行混合，使得纳米石墨、改性秸秆粉末、硼砂等组分可以均匀分布在ABS、聚苯乙烯等组成的基体中，在聚合物的分子链中引入其他组分，使分子链间形成二维甚至三维交联，减小材料的氢键化程度，降低吸水率、提高阻燃性，再利用偶联剂、交联剂、相容剂等使得各组分形成一个整体，满足人们的使用需求。
对于本领域技术人员而言，显然本发明不限于上述示范性实施例的细节，而且在不背离本发明的精神或基本特征的情况下，能够以其他的具体形式实现本发明。因此，无论从哪一点来看，均应将实施例看作是示范性的，而且是非限制性的，本发明的范围由所附权利要求而不是上述说明限定，因此旨在将落在权利要求的等同要件的含义和范围内的所有变化囊括在本发明内。
此外，应当理解，虽然本说明书按照实施方式加以描述，但并非每个实施方式仅包含一个独立的技术方案，说明书的这种叙述方式仅仅是为清楚起见，本领域技术人员应当将说明书作为一个整体，各实施例中的技术方案也可以经适当组合，形成本领域技术人员可以理解的其他实施方式。
Claims (5)
1.一种综合性能好的复合塑料，其特征在于，包括以下重量份的原料：ABS 34-45份、聚苯乙烯10-20份、秸秆粉末16-22份、正硅酸四乙酯1.6-3.5份、纳米石墨0.2-0.6份、滑石粉2-5份、塑化剂1-3份、光稳定剂0.1-0.5份、抗氧剂1010 0.6-1.4份、三氧化二锑5-6份、偶联剂1-3份、相容剂1.5-2.8份、硼砂2-5份和秋葵3-6份。
2.根据权利要求1所述的综合性能好的复合塑料，其特征在于，所述秸秆粉末包括甘蔗秸秆粉末、玉米秸秆粉末、甘蔗秸秆粉末、高粱秸秆粉末和大豆秸秆粉末中的至少一种。
3.根据权利要求1所述的综合性能好的复合塑料，其特征在于，所述三氧化二锑的粒度为1.2-3.45mm，硼砂的粒度为0.85-2.43mm。
4.一种如权利要求1-3任一所述的综合性能好的复合塑料的制备方法，其特征在于，具体步骤如下：
步骤一，将秋葵粉碎并且浸泡在质量分数为70-75%的乙醇水溶液中12-15小时，过滤并且将滤液进行减压蒸馏，然后在35-45摄氏度的真空条件下干燥至水分的质量分数为5-10%，得到秋葵提取物；
步骤二，将秸秆粉末和正硅酸四乙酯浸泡在质量分数为20-25%的氢氧化钠溶液中，浸泡后的产物进行干燥，得到改性秸秆粉末和改性正硅酸四乙酯；
步骤三，将改性秸秆粉末、ABS、聚苯乙烯和硼砂在球磨机中混合并且球磨至240-300目，得到第一混合物；
步骤四，将第一混合物、秋葵提取物、改性正硅酸四乙酯、纳米石墨、三氧化二锑和相容剂在混料机中搅拌4-6分钟，得到第二混合物；
步骤五，向第二混合物中依次加入滑石粉、塑化剂、光稳定剂、抗氧剂1010和偶联剂并且混合均匀，得到第三混合物；
步骤六，将第三混合物放入双螺杆挤出机挤出，即可得到成品。
5.根据权利要求4所述的综合性能好的复合塑料的制备方法，其特征在于，所述步骤四中混料机的混合温度为30-40摄氏度，搅拌速度为90-120rpm，步骤五中的混合速度为900-1050rpm。