CN108129698A - A kind of plastics violet colorant composition and dyeing particles - Google Patents
A kind of plastics violet colorant composition and dyeing particles Download PDFInfo
- Publication number
- CN108129698A CN108129698A CN201810055224.0A CN201810055224A CN108129698A CN 108129698 A CN108129698 A CN 108129698A CN 201810055224 A CN201810055224 A CN 201810055224A CN 108129698 A CN108129698 A CN 108129698A
- Authority
- CN
- China
- Prior art keywords
- parts
- plastics
- violet colorant
- colorant composition
- particles
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of plastics violet colorant composition and dyeing particles.A kind of plastics violet colorant composition includes 100 120 parts of titanium dioxides, 15 16.5 parts of purple powder, 4.5 5.5 parts of red powder, 0.5 0.6 parts of toner black smokes, 25 35 parts of EBS, 55 65 parts of magnesium stearates；It dyes particles and includes 99.0 99.5 parts of ABS, 0.7 0.75 parts of plastics violet colorant compositions as described above.The defects of plastics violet colorant composition provided by the present invention and dyeing particles will not generate stain, gas trace in the production process of coloured plastics grain, coloring agent composition provided by the invention can carry out plastics good uniform dyeing simultaneously, its durable weatherability is very good, it is very suitable for long-term exposed plastic product, the purple of preparation can reduce the injury to eyesight；In addition, dyeing particles extension tensile property provided by the invention is good, embrittlement is not susceptible to, small to the abrasion of machinery equipment in preparation process, energy conservation and environmental protection.
Description
Technical field
The invention belongs to plastic colorant fields, and in particular to a kind of plastics violet colorant composition and dyeing plastic cement
Grain.
Background technology
Mainly it there are thermoplasticity and thermosetting plastic according to the molecular structure point of synthetic resin：To what, thermoplastic plastic refers to
Heating is the plastic cement for plasticity repeatedly, and dyes particles and be primarily referred to as using toner or Masterbatch as dyeing pigment and auxiliary agent group
The particles of conjunction mainly have the common raw material such as ABS/PP/475/PE/, due to plastic product will and color coordination, take out grain raw material be
Pigment is mixed into raw material, each plastics material is colored, so forming product colour stable and uniform.Dye plastic cement
Grain be primarily referred to as using toner or Masterbatch as dyeing pigment and the particles of auxiliary combination, extensive use in automobile (such as instrument board,
Tool hatch door, wheel cover, reflective mirror case etc.), refrigerator, big strength tools (such as hair drier, blender, food processor,
Grass trimmer etc.), telephone case, typewriter keyboard, recreational vehicle such as golf cart and jet-propelled sledge vehicle etc..
In the prior art, the technological process that is made for dyeing particles is generally divided into following steps：
1st, raw material stoving；
2nd, stain dilution is stood and mixing color, modification agent combine；
3rd, pre- colour mixture-stir evenly toner and raw material in blender is done pre-dispersed；
4th, heating melting stirring in gun barrel；
5th, it squeezes bracing wire, cross water cooling, blowing draining；
6th, pelletizing, sieving, heating stirring drying.
Wherein, the allotment ratio of stain accounts for success or failure key in alloying process, is also easy to produce dispersion and is not easy, stain, gas trace, after
The upper multiple spot geat of section molding application is easily rupturable, brittle failure, and illiquidity causes molding uneven not full, and material coke, stirring are not
Easily, the bad phenomenons such as screw rod is worn, power consumption, and production capacity is bad.
Invention content
Based on problem of the existing technology, the object of the present invention is to provide a kind of function admirable, coloring it is good and not
It influences the plastics violet colorant composition of plastic shaping and dyes particles and preparation method.
The present invention is achieved by the following technical solution：
A kind of plastics include following parts by weight of component with violet colorant composition：
100-120 parts of titanium dioxides, 15-16.5 parts of purple powder, 4.5-5.5 parts of red powder, 0.5-0.6 parts of toner black smokes, 25-
35 parts of EBS, 55-65 parts of magnesium stearates；EBS, that is, the ethylene bis stearamide.
It is further preferred that above-mentioned plastics include following parts by weight of component with violet colorant composition：
110 parts of titanium dioxides, 16 parts of purple powder, 5 parts of red powder, 0.55 part of toner black smoke, 30 parts of EBS, 60 parts of magnesium stearates.
Further, above-mentioned plastics titanium dioxide described in violet colorant composition is rutile-type.
The present invention also provides a kind of dyeing particles to include following parts by weight of component：99.0-99.5 part ABS, 0.7-0.75
Part plastics violet colorant composition as described above.
ABS, that is, the acrylonitrile-butadiene-styrene copolymer is by three kinds of acrylonitrile, butadiene and styrene chemistry
Monomer synthetic copolymer, component content：Acrylonitrile 15-20%, butadiene 15-25%, styrol copolymer 60-65%.
It is further preferred that above-mentioned dyeing particles include following parts by weight of component：99.26691 part ABS, 0.73309 part
Plastics violet colorant composition as described above.
Plastics provided by the present invention violet colorant composition and dyeing particles coloured plastics grain production
The defects of stain, gas trace will not be generated in journey, while coloring agent composition provided by the invention can be good to plastics progress equal
Even dyeing, durable weatherability is very good, is very suitable for long-term exposed plastic product, and the purple of preparation can be reduced pair
The injury of eyesight；In addition, dyeing particles extension tensile property provided by the invention is good, embrittlement is not susceptible to, was being prepared
, energy conservation and environmental protection small to the abrasion of machinery equipment in journey, specifically the reduction of the inventive formulation proportion of goods damageds is horizontal as follows：Polystyrene matter
It measures mass rate of material loss of the proportion of goods damageds not higher than 0.1%, ABS and is not higher than 0.09%；Using the processing procedure power consumption expense of this formula by existing
1,650,000/the year for having technology is reduced to for 1,340,000/year.
Specific embodiment
With reference to specific embodiment, the present invention will be further described.The embodiment is only the preferred implementation of the present invention
Example, is not intended to restrict the invention, for those skilled in the art, the present invention can have various changes and change
Change.All within the spirits and principles of the present invention, any modification, equivalent replacement, improvement and so on should be included in the present invention
Protection domain within.It is the A5878 of Di Gaosha, red powder that ABS used, which is BASF ABS GP35, toner black smoke, in embodiment
Be ARIMOTO 8320, purple powder be the 8850 of ARIMOTO.
Embodiment 1
By 1.1kg rutile type titanium whites, 160g purples powder, 50g red powder, 55g toners black smoke, 0.3kg EBS,
0.6kg magnesium stearates add in blender after mixing, then 99.26691kg ABS are added in blender and are stirred evenly, in gun barrel
Heating melting stirring, through squeezing bracing wire, crossing water cooling, blowing draining；Pelletizing, sieving, heating stirring dry to obtain product.
Embodiment 2
By 1.2kg rutile type titanium whites, 165g purples powder, 52g red powder, 58g toners black smoke, 0.32kg EBS,
0.65kg magnesium stearates add in blender after mixing, then 99kg ABS are added in blender and are stirred evenly, and are heated in gun barrel
Melting stirring, through squeezing bracing wire, crossing water cooling, blowing draining；Pelletizing, sieving, heating stirring dry to obtain product.
Embodiment 3
By 1.02kg rutile type titanium whites, 157g purples powder, 45g red powder, 50g toners black smoke, 0.28kg EBS,
0.55kg magnesium stearates add in blender after mixing, then 99.45kg ABS are added in blender and are stirred evenly, and add in gun barrel
Heat fusing stirs, through squeezing bracing wire, crossing water cooling, blowing draining；Pelletizing, sieving, heating stirring dry to obtain product.
Embodiment 1 to embodiment 3 prepares products obtained therefrom physical property measurement result：It rushes powerful under 18.1MPa, molten condition
Mobility MI not less than 32.8, mean specific gravity 1.056.
Claims (5)
1. a kind of plastics violet colorant composition, which is characterized in that including following parts by weight of component：
100-120 parts of titanium dioxides, 15-16.5 parts of purple powder, 4.5-5.5 parts of red powder, 0.5-0.6 parts of toner black smokes, 25-35 parts
EBS, 55-65 parts of magnesium stearates.
2. plastics according to claim 1 violet colorant composition, which is characterized in that including following parts by weight group
Point：
110 parts of titanium dioxides, 16 parts of purple powder, 5 parts of red powder, 0.55 part of toner black smoke, 30 parts of EBS, 60 parts of magnesium stearates.
3. plastics according to claim 1 or 2 violet colorant composition, which is characterized in that
The titanium dioxide is rutile-type.
4. a kind of dyeing particles, which is characterized in that including following parts by weight of component：
99.0-99.5 parts of ABS, 0.7-0.75 parts of plastics as described in any one in claims 1 to 3 violet colorant group
Close object.
5. dyeing particles according to claim 3, which is characterized in that including following parts by weight of component：
99.26691 parts of ABS, 0.73309 part of plastics as described in any one in claims 1 to 3 are combined with violet colorant
Object.