- oil
- added
- colour
- cera alba
- monoglyceride
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Links
Classifications
-
- C—CHEMISTRY; METALLURGY
- C09—DYES; PAINTS; POLISHES; NATURAL RESINS; ADHESIVES; COMPOSITIONS NOT OTHERWISE PROVIDED FOR; APPLICATIONS OF MATERIALS NOT OTHERWISE PROVIDED FOR
- C09D—COATING COMPOSITIONS, e.g. PAINTS, VARNISHES OR LACQUERS; FILLING PASTES; CHEMICAL PAINT OR INK REMOVERS; INKS; CORRECTING FLUIDS; WOODSTAINS; PASTES OR SOLIDS FOR COLOURING OR PRINTING; USE OF MATERIALS THEREFOR
- C09D191/00—Coating compositions based on oils, fats or waxes; Coating compositions based on derivatives thereof
- C09D191/005—Drying oils
-
- C—CHEMISTRY; METALLURGY
- C09—DYES; PAINTS; POLISHES; NATURAL RESINS; ADHESIVES; COMPOSITIONS NOT OTHERWISE PROVIDED FOR; APPLICATIONS OF MATERIALS NOT OTHERWISE PROVIDED FOR
- C09D—COATING COMPOSITIONS, e.g. PAINTS, VARNISHES OR LACQUERS; FILLING PASTES; CHEMICAL PAINT OR INK REMOVERS; INKS; CORRECTING FLUIDS; WOODSTAINS; PASTES OR SOLIDS FOR COLOURING OR PRINTING; USE OF MATERIALS THEREFOR
- C09D191/00—Coating compositions based on oils, fats or waxes; Coating compositions based on derivatives thereof
- C09D191/06—Waxes
-
- C—CHEMISTRY; METALLURGY
- C09—DYES; PAINTS; POLISHES; NATURAL RESINS; ADHESIVES; COMPOSITIONS NOT OTHERWISE PROVIDED FOR; APPLICATIONS OF MATERIALS NOT OTHERWISE PROVIDED FOR
- C09D—COATING COMPOSITIONS, e.g. PAINTS, VARNISHES OR LACQUERS; FILLING PASTES; CHEMICAL PAINT OR INK REMOVERS; INKS; CORRECTING FLUIDS; WOODSTAINS; PASTES OR SOLIDS FOR COLOURING OR PRINTING; USE OF MATERIALS THEREFOR
- C09D5/00—Coating compositions, e.g. paints, varnishes or lacquers, characterised by their physical nature or the effects produced; Filling pastes
- C09D5/06—Artists' paints
-
- C—CHEMISTRY; METALLURGY
- C09—DYES; PAINTS; POLISHES; NATURAL RESINS; ADHESIVES; COMPOSITIONS NOT OTHERWISE PROVIDED FOR; APPLICATIONS OF MATERIALS NOT OTHERWISE PROVIDED FOR
- C09D—COATING COMPOSITIONS, e.g. PAINTS, VARNISHES OR LACQUERS; FILLING PASTES; CHEMICAL PAINT OR INK REMOVERS; INKS; CORRECTING FLUIDS; WOODSTAINS; PASTES OR SOLIDS FOR COLOURING OR PRINTING; USE OF MATERIALS THEREFOR
- C09D7/00—Features of coating compositions, not provided for in group C09D5/00; Processes for incorporating ingredients in coating compositions
- C09D7/40—Additives
- C09D7/60—Additives non-macromolecular
- C09D7/61—Additives non-macromolecular inorganic
-
- C—CHEMISTRY; METALLURGY
- C09—DYES; PAINTS; POLISHES; NATURAL RESINS; ADHESIVES; COMPOSITIONS NOT OTHERWISE PROVIDED FOR; APPLICATIONS OF MATERIALS NOT OTHERWISE PROVIDED FOR
- C09D—COATING COMPOSITIONS, e.g. PAINTS, VARNISHES OR LACQUERS; FILLING PASTES; CHEMICAL PAINT OR INK REMOVERS; INKS; CORRECTING FLUIDS; WOODSTAINS; PASTES OR SOLIDS FOR COLOURING OR PRINTING; USE OF MATERIALS THEREFOR
- C09D7/00—Features of coating compositions, not provided for in group C09D5/00; Processes for incorporating ingredients in coating compositions
- C09D7/40—Additives
- C09D7/60—Additives non-macromolecular
- C09D7/63—Additives non-macromolecular organic
-
- C—CHEMISTRY; METALLURGY
- C09—DYES; PAINTS; POLISHES; NATURAL RESINS; ADHESIVES; COMPOSITIONS NOT OTHERWISE PROVIDED FOR; APPLICATIONS OF MATERIALS NOT OTHERWISE PROVIDED FOR
- C09D—COATING COMPOSITIONS, e.g. PAINTS, VARNISHES OR LACQUERS; FILLING PASTES; CHEMICAL PAINT OR INK REMOVERS; INKS; CORRECTING FLUIDS; WOODSTAINS; PASTES OR SOLIDS FOR COLOURING OR PRINTING; USE OF MATERIALS THEREFOR
- C09D7/00—Features of coating compositions, not provided for in group C09D5/00; Processes for incorporating ingredients in coating compositions
- C09D7/40—Additives
- C09D7/65—Additives macromolecular
-
- C—CHEMISTRY; METALLURGY
- C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
- C08L—COMPOSITIONS OF MACROMOLECULAR COMPOUNDS
- C08L2205/00—Polymer mixtures characterised by other features
- C08L2205/02—Polymer mixtures characterised by other features containing two or more polymers of the same C08L -group
Abstract
The invention discloses a kind of oil colours, by weight percentage include following component, linseed oil 22.85 ~ 52.9, cera alba 1-3%, monoglyceride 1-3%, desiccant 0.1-0.2%, barium sulfate 15-50%, pigment powder 5-30%.The non-stimulated smell of the pigment, it is safe and non-toxic, human body can be directly contacted, good water solubility is possessed, thus have the characteristics that easy cleaning, it is green product.It solves existing oil colour and glues the technical problems such as pen, oil powder separation, drawing quality can be improved, save material and reduce environmental pollution.
Description
Technical field
The present invention relates to pigment, in particular to a kind of oil colour.
Background technique
As the increasingly upgrading that artist requires painting material, especially oil colour are that artist passes on paint
The painting material most doted on, unstable quality caused by vegetable oil and paint filler are easily separated in traditional oil painting pigment are traditional
The oil colour viscosity of auxiliary rheological agents (rilanit special, beeswax, stearic acid etc.) production is big, easily produces in artist's painting process
Raw viscous stagnant phenomenon of pen.
Summary of the invention
In order to overcome drawbacks described above, the present invention provides a kind of oil colour, modest viscosity, painting effect is good.
The invention is realized by the following technical scheme:
A kind of oil colour includes following component by weight percentage,
Linseed oil 22.85 ~ 52.9%
Cera alba 1-3%
Monoglyceride 1-3%
Desiccant 0.1-0.2%
Barium sulfate 15-50%
Pigment powder 5-30%.
A kind of preparation method of oil colour, includes the following steps:
(1) it takes linseed oil 2.8 ~ 2.9% to be added in reaction kettle, 80 DEG C of set temperature, cera alba 1 ~ 3% is added while stirring
With monoglyceride 1 ~ 3%, after being heated to 75 DEG C, continue stirring 20 minutes, all melts to cera alba and monoglyceride, release, cooling is standby
With;
(2) linseed oil 20 ~ 50% is added in material cylinder, sequentially adds desiccant while stirring under the revolving speed of 200r/min
0.1 ~ 0.2%, barium sulfate 15 ~ 50%, pigment powder 5 ~ 30%, 400r/min disperse 20 minutes, and the semi-finished product that step (1) obtains are added,
It is smooth that pulp surface is dispersed under the revolving speed of 800 r/min, no particle is then sent to hydraulic grinder and is ground to fineness and is less than
30 μm, obtain oil colour.
Beneficial effects of the present invention:
The present invention provides a kind of new oil colours, and non-stimulated smell is safe and non-toxic, can directly contact human body, possess
Good water solubility, thus have the characteristics that easy cleaning, it is green product.It solves existing oil colour and glues pen, oil powder
The technical problems such as separation can be improved drawing quality, save material and reduce environmental pollution.Glycerin monostearate therein is to people
Body nonhazardous has good emulsifiability, each component in oil colour can be made to form uniformly mixed dispersion, reduces
System viscosity, viscosity 3000-5000P, drying time 5-7 days, oil colour was soft, flexible, can also improve its guarantor's type energy
Power.
Specific embodiment
Embodiment 1
(1) it takes linseed oil 2.9% to be added in reaction kettle, 80 DEG C of set temperature, cera alba 1 is added while stirring and list is sweet
Ester 1 after being heated to 75 DEG C, continues stirring 20% minute, all melts to cera alba and monoglyceride, releases, cooling is spare;
(2) linseed oil 50% is added in material cylinder, sequentially adds desiccant while stirring under the revolving speed of 200r/min
0.1%, barium sulfate 15%, pigment powder 30%, 400r/min disperse 20 minutes, the semi-finished product that step (1) obtains are added, in 800 r/
It is smooth that pulp surface is dispersed under the revolving speed of min, no particle is then sent to hydraulic grinder and is ground to fineness less than 30 μm, obtains
Oil colour.
Pigment technology index made from the present embodiment:
Color difference (color difference meter) Δ E 0.98
40 μm of fineness (Hegman grind gage)
Tinting strength, tinting power 102%
Density 1.5g/cm3
Covering power 102%
I grades of fastness rate
Viscosity 5000P
Drying time 6 days
Embodiment 2
(1) it takes linseed oil 2.85% to be added in reaction kettle, 80 DEG C of set temperature, cera alba 2% and list is added while stirring
Sweet ester 2% after being heated to 75 DEG C, continues stirring 20 minutes, all melts to cera alba and monoglyceride, releases, cooling is spare;
(2) linseed oil 20% is added in material cylinder, sequentially adds desiccant while stirring under the revolving speed of 200r/min
0.15%, barium sulfate 48%, pigment powder 25%, 400r/min disperse 20 minutes, the semi-finished product that step (1) obtains are added, in 800 r/
It is smooth that pulp surface is dispersed under the revolving speed of min, no particle is then sent to hydraulic grinder and is ground to fineness less than 30 μm, obtains
Oil colour.
Technical indicator:
Color difference (color difference meter) Δ E 0.95
39 μm of fineness (Hegman grind gage)
Tinting strength, tinting power 105%
Density 2.0g/cm3
Covering power 105%
I grades of fastness rate
Viscosity 3000P
Drying time 6 days
Embodiment 3
(1) it takes linseed oil 2.8% to be added in reaction kettle, 80 DEG C of set temperature, cera alba 3% is added while stirring and list is sweet
Ester 3% after being heated to 75 DEG C, continues stirring 20 minutes, all melts to cera alba and monoglyceride, releases, cooling is spare;
(2) linseed oil 36% is added in material cylinder, sequentially adds desiccant while stirring under the revolving speed of 200r/min
0.2%, barium sulfate 50%, pigment powder 5%, 400r/min disperse 20 minutes, the semi-finished product that step (1) obtains are added, in 800 r/
It is smooth that pulp surface is dispersed under the revolving speed of min, no particle is then sent to hydraulic grinder and is ground to fineness less than 30 μm, obtains
Oil colour.
Technical indicator:
Color difference (color difference meter) Δ E 0.89
39 μm of fineness (Hegman grind gage)
Tinting strength, tinting power 102%
Density 1.8g/cm3
Covering power 102%
I grades of fastness rate
Viscosity 5000P
Drying time 7 days
In each embodiment implementation process, pigment powder, filler, various auxiliary agents should be put into dispersion machine according to formula rate
In, speed of strict control dispersion machine, forms good rotation nest during this, determines that the addition of material is suitable according to material properties
Sequence.Dispersion forms the surface of smooth and beautiful appearance and the lotion of exquisiteness to oil colour completely.
Strict temperature control in dispersion process, when preventing activation temperature excessively high, auxiliary rheological agents control rheological property and disappear, but
Dispersion temperature can not be too low, prevents dispersion not exclusively, the too low effect that cannot give full play to auxiliary rheological agents of activation temperature, so that
Influence the lotion form and the storage stability in later period of product.
Claims (1)
1. a kind of oil colour, it is characterised in that: it by weight percentage include following component,
Linseed oil 22.85 ~ 52.9%
Cera alba 1-3%
Monoglyceride 1-3%
Desiccant 0.1-0.2%
Barium sulfate 15-50%
Pigment powder 5-30%;
A kind of preparation method of oil colour, includes the following steps:
(1) it takes linseed oil 2.8 ~ 2.9% to be added in reaction kettle, 80 DEG C of set temperature, cera alba 1 ~ 3% and list is added while stirring
Sweet ester 1 ~ 3% after being heated to 75 DEG C, continues stirring 20 minutes, all melts to cera alba and monoglyceride, releases, cooling is spare;
(2) in material cylinder be added linseed oil 20 ~ 50%, sequentially added while stirring under the revolving speed of 200r/min desiccant 0.1 ~
0.2%, barium sulfate 15 ~ 50%, pigment powder 5 ~ 30%, 400r/min disperse 20 minutes, and the semi-finished product that step (1) obtains are added,
It is smooth that pulp surface is dispersed under the revolving speed of 800 r/min, no particle is then sent to hydraulic grinder and is ground to fineness less than 30
μm, obtain oil colour.
Priority Applications (1)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
CN201610968681.XA CN106554719B (en) | 2016-10-28 | 2016-10-28 | A kind of oil colour |
Applications Claiming Priority (1)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
CN201610968681.XA CN106554719B (en) | 2016-10-28 | 2016-10-28 | A kind of oil colour |
Publications (2)
Publication Number | Publication Date |
---|---|
CN106554719A CN106554719A (en) | 2017-04-05 |
CN106554719B true CN106554719B (en) | 2019-07-12 |
Family
ID=58443815
Family Applications (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
CN201610968681.XA Active CN106554719B (en) | 2016-10-28 | 2016-10-28 | A kind of oil colour |
Country Status (1)
Country | Link |
---|---|
CN (1) | CN106554719B (en) |
Families Citing this family (4)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
CN106995660B (en) * | 2017-06-02 | 2019-04-05 | 中国科学院包头稀土研发中心 | A kind of novel rare-earth oil colour and preparation method thereof |
CN111393916A (en) * | 2020-05-25 | 2020-07-10 | 苏州德加画材科技有限公司 | Antistatic aging-resistant oil painting pigment |
CN111925679B (en) * | 2020-08-20 | 2021-08-17 | 新乡学院 | Oil painting pigment for fine arts |
CN115584154A (en) * | 2022-10-08 | 2023-01-10 | 天长市嘉丰美术用品有限公司 | Preparation process of water-soluble oil painting pigment |
Citations (3)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
CN102816478A (en) * | 2012-09-11 | 2012-12-12 | 上海实业马利画材有限公司 | Application of thixotropic agent in museum-level oil paint pigment connecting material |
CN104275963A (en) * | 2013-07-09 | 2015-01-14 | 修森经贸发展(上海)有限公司 | Environment-friendly scrawling bar for children |
CN105440764A (en) * | 2015-12-27 | 2016-03-30 | 青岛大方智慧网络科技有限公司 | Waterproof oil paint |
-
2016
- 2016-10-28 CN CN201610968681.XA patent/CN106554719B/en active Active
Patent Citations (3)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
CN102816478A (en) * | 2012-09-11 | 2012-12-12 | 上海实业马利画材有限公司 | Application of thixotropic agent in museum-level oil paint pigment connecting material |
CN104275963A (en) * | 2013-07-09 | 2015-01-14 | 修森经贸发展(上海)有限公司 | Environment-friendly scrawling bar for children |
CN105440764A (en) * | 2015-12-27 | 2016-03-30 | 青岛大方智慧网络科技有限公司 | Waterproof oil paint |
Also Published As
Publication number | Publication date |
---|---|
CN106554719A (en) | 2017-04-05 |
Similar Documents
Publication | Publication Date | Title |
---|---|---|
CN106554719B (en) | A kind of oil colour | |
CN103666090B (en) | Alcohol-soluble environment-friendly printing ink for tipping paper and preparation method thereof | |
CN105368140A (en) | Photo-cured high-temperature colored glass printing ink and preparation method therefor and painting method thereof | |
CN108102506A (en) | Bonding Pearlescent powder paint and preparation method thereof | |
CN104746362A (en) | Water-based nano pigment ink for textile printing | |
CN110387168A (en) | A kind of environmental protection ultraviolet color-changing mill base, preparation method and application | |
CN102719139B (en) | Gloss oil for IMD (In-Mold Decoration) printing ink, IMD printing ink, IMD film and preparation method of gloss oil | |
CN109401395A (en) | Drawing environmentally friendly acrylic paints and preparation method thereof with Jasmine fragrance | |
CN103588419B (en) | Method for preparing quartz plate with changeable colors | |
CN108467630A (en) | A kind of artistic oil painting stick synthetic wax and preparation method thereof | |
CN103382308B (en) | Lac modification method for improving heat resistance of lac varnish | |
CN104962136B (en) | A kind of aqueous carbon black pigment mill base coloured for synthetic leather | |
CN110746808B (en) | Preparation method of solid oil painting pigment | |
CN111925679B (en) | Oil painting pigment for fine arts | |
DE1241605B (en) | Red pigmentation of polymers and plastic natural substances | |
CN108676404B (en) | High-imitation metal powder coating and preparation method thereof | |
CN105885691A (en) | High-wear-resistance wood wax oil and preparation method thereof | |
CN105385071A (en) | Slush-molded PVC material for automotive trim skin and preparation method of slush-molded PVC material | |
US2332031A (en) | Method of producing irregular finishes | |
CN103773114B (en) | A kind of waterborne general color paste and preparation method thereof | |
CN107033782A (en) | A kind of wood product surface does old rear corrosion resistant clear coat and preparation method thereof | |
CN104341855B (en) | A kind of high tenacity modified ultraviolet curing water color ink and preparation method thereof | |
CN114381170B (en) | Soft oil painting stick and preparation method thereof | |
CN115725208A (en) | Pigment for art painting and preparation method thereof | |
CN100532465C (en) | H series tungsten halogen lamp inorganic paint and method for producing same |
Legal Events
Date | Code | Title | Description |
---|---|---|---|
PB01 | Publication | ||
PB01 | Publication | ||
SE01 | Entry into force of request for substantive examination | ||
SE01 | Entry into force of request for substantive examination | ||
GR01 | Patent grant | ||
GR01 | Patent grant |