CN106554719A - A kind of oil colour - Google Patents
A kind of oil colour Download PDFInfo
- Publication number
- CN106554719A CN106554719A CN201610968681.XA CN201610968681A CN106554719A CN 106554719 A CN106554719 A CN 106554719A CN 201610968681 A CN201610968681 A CN 201610968681A CN 106554719 A CN106554719 A CN 106554719A
- Authority
- CN
- China
- Prior art keywords
- oil colour
- oleum lini
- stirring
- monoglyceride
- cera alba
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses a kind of oil colour, by weight percentage including following component, oleum lini 22.85 ~ 52.9, cera alba 1 3%, monoglyceride 1 3%, desiccant 0.1 0.2%, barium sulfate 15 50%, pigment powder 5 30%.The non-stimulated abnormal smells from the patient of the pigment, safety non-toxic, can directly contact human body, the features such as possessing good water solublity, thus there is easy cleaning, be Green Product.The technical barriers such as the viscous pen of existing oil colour, oil meal separation are solved, drawing quality can be improved, material is saved and reduced environmental pollution.
Description
Technical field
The present invention relates to pigment, more particularly to a kind of oil colour.
Background technology
As the increasingly upgrading that artist is required to painting material, particularly oil colour are artist succession paints
The painting material most doted on, caused by traditional oil painting pigment, vegetable oil and paint filler are easily separated, quality is unstable, traditional
Auxiliary rheological agents(Castor oil hydrogenated, Cera Flava, stearic acid etc.)The oil colour viscosity of production is big, easily produces in artist painting process
Stagnant phenomenon of raw viscous pen.
The content of the invention
In order to overcome drawbacks described above, the invention provides a kind of oil colour, modest viscosity, painting effect are good.
The present invention is achieved through the following technical solutions:
A kind of oil colour, by weight percentage including following component,
Oleum lini 22.85 ~ 52.9
Cera alba 1-3%
Monoglyceride 1-3%
Desiccant 0.1-0.2%
Barium sulfate 15-50%
Pigment powder 5-30%.
A kind of preparation method of oil colour, comprises the steps:
(1)Take oleum lini 2.8 ~ 2.9 to be added in reactor, 80 DEG C of design temperature, add cera alba 1 ~ 3 and list sweet while stirring
Fat 1 ~ 3, after being heated to 75 DEG C, continues stirring 20 minutes, treats that cera alba and monoglyceride all melt, releases, cool down standby;
(2)Oleum lini 20 ~ 50 is added in material cylinder, sequentially added under the rotating speed of 200r/min while stirring desiccant 0.1 ~
0.2nd, barium sulfate 15 ~ 50, pigment powder 5 ~ 30,400r/min disperse 20 minutes, add step(1)The semi-finished product of acquisition, 800
Pulp surface is dispersed under the rotating speed of r/min smooth, without granule, be then sent to hydraulic pressure grinder and fineness be ground to less than 30 m,
Obtain oil colour.
Beneficial effects of the present invention:
The invention provides a kind of new oil colour, non-stimulated abnormal smells from the patient, safety non-toxic, can directly contact human body, possess good
Water solublity, thus have easy cleaning the features such as, be Green Product.Solve the viscous pen of existing oil colour, oil meal to separate
Deng technical barrier, drawing quality can be improved, material is saved and is reduced environmental pollution.Glyceryl monostearate therein to human body without
Poison, with good emulsifiability, the dispersion of each component formation mix homogeneously in oil colour can be made, system is reduced
Viscosity, viscosity 3000-5000P, 5-7 days drying time, oil colour is soft, flexible, can also improve its guarantor's type ability.
Specific embodiment
Embodiment 1
(1)Take oleum lini 2.9 to be added in reactor, 80 DEG C of design temperature, add cera alba 1 and monoglyceride 1 while stirring, plus
Heat continues stirring 20 minutes to after 75 DEG C, treats that cera alba and monoglyceride all melt, releases, cool down standby;
(2)Oleum lini 50 is added in material cylinder, desiccant 0.1, sulphuric acid is sequentially added under the rotating speed of 200r/min while stirring
Barium 15, pigment powder 30,400r/min disperse 20 minutes, add step(1)The semi-finished product of acquisition, under the rotating speed of 800 r/min
Be dispersed to pulp surface smooth, without granule, be then sent to hydraulic pressure grinder and fineness be ground to less than 30 m, obtain oil colour.
Pigment technology index obtained in the present embodiment:
Aberration(Color difference meter) Δ E 0.98
Fineness(Hegman grind gage) 40µm
Tinting strength, tinting power 102%
Density 1.5g/cm
Covering power 102%
Fastness rate I levels
Viscosity 5000P
6 days drying times
Embodiment 2
(1)Take oleum lini 2.85 to be added in reactor, 80 DEG C of design temperature, add cera alba 2 and monoglyceride 2 while stirring,
After being heated to 75 DEG C, continue stirring 20 minutes, treat that cera alba and monoglyceride all melt, release, cool down standby;
(2)Oleum lini 20 is added in material cylinder, desiccant 0.15, sulphuric acid is sequentially added under the rotating speed of 200r/min while stirring
Barium 48, pigment powder 25,400r/min disperse 20 minutes, add step(1)The semi-finished product of acquisition, under the rotating speed of 800 r/min
Be dispersed to pulp surface smooth, without granule, be then sent to hydraulic pressure grinder and fineness be ground to less than 30 m, obtain oil colour.
Technical specification:
Aberration(Color difference meter) Δ E 0.95
Fineness(Hegman grind gage) 39µm
Tinting strength, tinting power 105%
Density 2.0g/cm
Covering power 105%
Fastness rate I levels
Viscosity 3000P
6 days drying times
Embodiment 3
(1)Take oleum lini 2.8 to be added in reactor, 80 DEG C of design temperature, add cera alba 3 and monoglyceride 3 while stirring, plus
Heat continues stirring 20 minutes to after 75 DEG C, treats that cera alba and monoglyceride all melt, releases, cool down standby;
(2)Oleum lini 36 is added in material cylinder, desiccant 0.2, sulphuric acid is sequentially added under the rotating speed of 200r/min while stirring
Barium 50, pigment powder 5,400r/min disperse 20 minutes, add step(1)The semi-finished product of acquisition, divide under the rotating speed of 800 r/min
Be dissipated to pulp surface smooth, without granule, be then sent to hydraulic pressure grinder and fineness be ground to less than 30 m, obtain oil colour.
Technical specification:
Aberration(Color difference meter) Δ E 0.89
Fineness(Hegman grind gage) 39µm
Tinting strength, tinting power 102%
Density 1.8g/cm
Covering power 102%
Fastness rate I levels
Viscosity 5000P
7 days drying times
In each embodiment implementation process, pigment powder, filler, various auxiliary agents should be put in dispersion machine according to formula proportion, this
During strict control dispersion machine speed, form good rotation nest, determine the order of addition of material according to material propertiess.Dispersion
Form the surface of smooth and beautiful appearance and the mastic of exquisiteness completely to oil colour.
Strict temperature control in dispersive process, when preventing activation temperature too high, auxiliary rheological agents control rheological property disappears, but
Dispersion temperature can not be too low, prevents dispersion incomplete, the too low effect that can not give full play to auxiliary rheological agents of activation temperature, so that
Affect the mastic form and the storage stability in later stage of product.
Claims (2)
1. a kind of oil colour, it is characterised in that:Include following component by weight percentage,
Oleum lini 22.85 ~ 52.9
Cera alba 1-3%
Monoglyceride 1-3%
Desiccant 0.1-0.2%
Barium sulfate 15-50%
Pigment powder 5-30%.
2. a kind of preparation method of oil colour according to claim 1, comprises the steps:
(1)Take oleum lini 2.8 ~ 2.9 to be added in reactor, 80 DEG C of design temperature, add cera alba 1 ~ 3 and list sweet while stirring
Fat 1 ~ 3, after being heated to 75 DEG C, continues stirring 20 minutes, treats that cera alba and monoglyceride all melt, releases, cool down standby;
(2)Oleum lini 20 ~ 50 is added in material cylinder, sequentially added under the rotating speed of 200r/min while stirring desiccant 0.1 ~
0.2nd, barium sulfate 15 ~ 50, pigment powder 5 ~ 30,400r/min disperse 20 minutes, add step(1)The semi-finished product of acquisition, 800
Pulp surface is dispersed under the rotating speed of r/min smooth, without granule, be then sent to hydraulic pressure grinder and fineness be ground to less than 30 m,
Obtain oil colour.