CN105086749A - Coating for air energy water heater and preparing method thereof - Google Patents
Coating for air energy water heater and preparing method thereof Download PDFInfo
- Publication number
- CN105086749A CN105086749A CN201510479014.0A CN201510479014A CN105086749A CN 105086749 A CN105086749 A CN 105086749A CN 201510479014 A CN201510479014 A CN 201510479014A CN 105086749 A CN105086749 A CN 105086749A
- Authority
- CN
- China
- Prior art keywords
- water heater
- coating
- air
- source water
- powder
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a coating for an air energy water heater. The coating is composed of, by mass, 20%-30% of epoxy resin, 20-%-30% of polyester resin, 10%-20% of titanium dioxide, 1%-3% of flatting agents, 1%-3% of benzoin, 6%-10% of high light barium sulfate, 15%-25% of 05 ultramarine and 2%-4% of 190 iron oxide red. A preparing method includes the following steps that all components are added to a material mixing machine to be mixed for 2 minutes to 3 minutes, melt extrusion is conducted at the temperature of 125 DEG C, materials extruded in a melt extrusion mode are grinded into powder through a powder grinding machine, the ground powder is packaged, and 10 kg of powder is contained per bag. The coating has the advantages of being environmentally friendly, good in quality and the like.
Description
Technical field
The present invention relates to a kind of air-source water heater coating and preparation method thereof, be applied to the process for processing field of air-source water heater.
Background technology
In the process of manufacture of air-source water heater, in order to increase overall aesthetic property and prevent the shell of air-source water heater from getting rusty, processing staff can to spray paint on the shell of air-source water heater, but containing pollutents such as dimethylbenzene in existing paint, so not only can cause environmental pollution, and very large injury can be produced to human body.
Summary of the invention
For solving the defect of prior art, the invention discloses a kind of environmental protection, the measured air-source water heater coating of matter and preparation method thereof.
The invention discloses a kind of air-source water heater coating, according to mass percent, composed of the following components: epoxy resin 20%-30%, vibrin 20%-30%, titanium dioxide 10%-20%, flow agent 1%-3%, residence cease fragrant 1%-3%, high light barium 6%-10%, 05 ultramarine 15%-25%, 190 iron oxide red 2%-4%.
Further, as preferably, the invention discloses a kind of high light white powder, be made up of following component, comprise: epoxy resin 25%, vibrin 25%, titanium dioxide 15%, flow agent 2%, residence breath perfume 2%, high light barium 8%, 05 ultramarine 20%, 190 iron oxide red 3%.
Further, the high light white powder of one of the present invention, preparation process is as follows:
Step one: according to above-mentioned mass percent, joins above-mentioned each component in mixer and mixes 2-3 minute;
Step 2: join in twin screw extruder by material mixed in step one, melt extrudes under the condition of 125 DEG C;
Step 3: use pulverizing mill to be clayed into power by the material melt extruded in step 3;
Step 4: packed by the powder ground in step 3, often wraps 10 ㎏.
By mixed material is joined in twin screw extruder, and melt extrude under the condition of 125 DEG C, therefore epoxy resin and vibrin cross-linking effect good, fastness is high, the surface being used in air-source water heater is not easily fallen, long service life, in addition because all components are not all containing pollutent, therefore environment protecting is relatively good, safe and reliable.
Embodiment
The invention discloses a kind of air-source water heater coating, according to mass percent, composed of the following components: epoxy resin 20%-30%, vibrin 20%-30%, titanium dioxide 10%-20%, flow agent 1%-3%, residence cease fragrant 1%-3%, high light barium 6%-10%, 05 ultramarine 15%-25%, 190 iron oxide red 2%-4%.
Further, as preferably, the invention discloses a kind of high light white powder, be made up of following component, comprise: epoxy resin 25%, vibrin 25%, titanium dioxide 15%, flow agent 2%, residence breath perfume 2%, high light barium 8%, 05 ultramarine 20%, 190 iron oxide red 3%.
Further, the high light white powder of one of the present invention, preparation process is as follows:
Step one: according to above-mentioned mass percent, joins above-mentioned each component in mixer and mixes 2-3 minute;
Step 2: join in twin screw extruder by material mixed in step one, melt extrudes under the condition of 125 DEG C;
Step 3: use pulverizing mill to be clayed into power by the material melt extruded in step 3;
Step 4: packed by the powder ground in step 3, often wraps 10 ㎏.
Embodiment 1
To prepare 100 ㎏ air-source water heater coating of the present invention
Step one: 25 ㎏ epoxy resin, 25 ㎏ vibrin, 15 ㎏ titanium dioxides, 2 ㎏ flow agents, 2 ㎏ residence breath perfume, 8 ㎏ height light barium, 20 ㎏ 05 ultramarines, 3 ㎏ 190 iron oxide reds are joined in mixer and mix 2 minutes;
Step 2: join in twin screw extruder by material mixed in step one, melt extrudes under the condition of 125 DEG C;
Step 3: use pulverizing mill to be clayed into power by the material melt extruded in step 3;
Step 4: packed by the powder ground in step 3, often wraps 10 ㎏.
Embodiment 2
To prepare 100 ㎏ air-source water heater coating of the present invention
Step one: 30 ㎏ epoxy resin, 22 ㎏ vibrin, 10 ㎏ titanium dioxides, 3 ㎏ flow agents, 3 ㎏ residence breath perfume, 10 ㎏ height light barium, 20 ㎏ 05 ultramarines, 2 ㎏ 190 iron oxide reds are joined in mixer and mix 2 minutes;
Step 2: join in twin screw extruder by material mixed in step one, melt extrudes under the condition of 125 DEG C;
Step 3: use pulverizing mill to be clayed into power by the material melt extruded in step 3;
Step 4: packed by the powder ground in step 3, often wraps 10 ㎏.
Last it is noted that above embodiment only in order to illustrate the present invention and and unrestricted technical scheme described in the invention; Therefore, although this specification sheets with reference to each above-mentioned embodiment to present invention has been detailed description, those of ordinary skill in the art should be appreciated that and still can modify to the present invention or equivalent to replace; And all do not depart from technical scheme and the improvement thereof of the spirit and scope of the present invention, it all should be encompassed in right of the present invention.
Claims (3)
1. an air-source water heater coating, it is characterized in that: according to mass percent, composed of the following components: epoxy resin 20%-30%, vibrin 20%-30%, titanium dioxide 10%-20%, flow agent 1%-3%, residence cease fragrant 1%-3%, high light barium 6%-10%, 05 ultramarine 15%-25%, 190 iron oxide red 2%-4%.
2. a kind of air-source water heater coating according to claim 1, it is characterized in that: according to mass percent, be made up of following component, comprise: epoxy resin 25%, vibrin 25%, titanium dioxide 15%, flow agent 2%, residence breath perfume 2%, high light barium 8%, 05 ultramarine 20%, 190 iron oxide red 3%.
3. a kind of air-source water heater coating according to claim 1 and 2, is characterized in that: preparation process is as follows:
Step one: according to above-mentioned mass percent, joins above-mentioned each component in mixer and mixes 2-3 minute;
Step 2: join in twin screw extruder by material mixed in step one, melt extrudes under the condition of 125 DEG C;
Step 3: use pulverizing mill to be clayed into power by the material melt extruded in step 3;
Step 4: packed by the powder ground in step 3, often wraps 10 ㎏.