CN105176202A - Oil painting stick and preparation method thereof - Google Patents
Oil painting stick and preparation method thereof Download PDFInfo
- Publication number
- CN105176202A CN105176202A CN201510688492.2A CN201510688492A CN105176202A CN 105176202 A CN105176202 A CN 105176202A CN 201510688492 A CN201510688492 A CN 201510688492A CN 105176202 A CN105176202 A CN 105176202A
- Authority
- CN
- China
- Prior art keywords
- preparation
- weight part
- oil painting
- painting stick
- solid substances
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention provides an oil painting stick and a preparation method thereof. The oil painting stick is composed of the following components in parts by weight: 3-5 parts of paraffin, 3-5 parts of white beeswax, 10-20 parts of hardening oil, 10-20 parts of synthetic wax, 15-25 parts of white oil, 30-50 parts of superfine talcum powder and 3-8 parts of environment-friendly pigment. The oil painting stick has the advantages of environment friendliness, no toxicity, delicate and smooth hand feeling, favorable spreadability, excellent color overprinting and mixing properties, bright color, thicker painting layer, superfine coating and better tactile sensation.
Description
Technical field
The present invention relates to a kind of draw tool material, particularly a kind of artistic oil painting stick and preparation method thereof.
Background technology
Modal graphic products mainly artistic oil painting stick and wax crayon in the market.
Wax crayon exists that colouring is uneven, and color is bright-coloured not, and it is undesirable to draw performance, and it is even not for being in particular in that painting is retouched, and layer is thinner, and opacifying power is poor.
Comparatively speaking, the feel of artistic oil painting stick is fine and smooth, and spreadability is good, folded look, colour mixture excellent performance, but the drawing feel of artistic oil painting stick in the market also exists problem that is not smooth, that have astringent sense.
Summary of the invention
The object of the invention is to overcome prior art deficiency, artistic oil painting stick of a kind of environment-protecting asepsis, lovely luster, drawing excellent property and preparation method thereof is provided.
On the one hand, the invention provides a kind of artistic oil painting stick, it consists of the following composition: paraffin 3-5 weight part; Cera alba 3-5 weight part; Winterized stearin 10-20 weight part; Synthetic wax 10-20 weight part; White oil 15-25 weight part; Superfine talcum powder 30-50 weight part; And environmental-friendly pigment 3-8 weight part.
In an embodiment of artistic oil painting stick of the present invention, described synthetic wax is prepared from by stearic acid and magnesiumcarbonate.
In another embodiment of artistic oil painting stick of the present invention, described white oil is cosmetic grade white oil.
On the other hand, the invention provides the preparation method of above-mentioned artistic oil painting stick, comprise the steps:
Paraffin, cera alba, winterized stearin, synthetic wax and white oil are mixed by predetermined proportion, carry out first time melt processed afterwards, in the liquid after fusing, add environmental-friendly pigment, Homogeneous phase mixing post-treatment obtains the first solid substances;
Carry out second time melt processed to described first material, and add superfine talcum powder in the liquid after fusing, Homogeneous phase mixing post-treatment obtains the second solid substances;
Third time melt processed is carried out to described second solid substances, obtains described artistic oil painting stick by moulding process afterwards.
In an embodiment of preparation method of the present invention, described first time the temperature of melt processed be 70-90 DEG C.
In another embodiment of preparation method of the present invention, described second time melt processed and described third time melt processed temperature be 70-95 DEG C.
In another embodiment of preparation method of the present invention, described processing comprises the liquid after by fusing and carries out cooling process.
In another embodiment of preparation method of the present invention, the temperature of described cooling process is 8-14 DEG C.
In another embodiment of preparation method of the present invention, also comprise and utilize three-roll grinder to grind described first solid substances and described second solid substances.
In another embodiment of preparation method of the present invention, the particle fineness of described first solid substances and described second solid substances is 10-30 micron.
Compared with prior art, artistic oil painting stick of the present invention has the following advantages:
1, environment-protecting asepsis, tasteless; Adopt environmental-friendly pigment to replace the original pigment used, the substances content that heavy metal etc. is detrimental to health is far below international limit standard;
2, feel is fine and smooth, smooth, spreadability is good, folded color contamination look excellent performance, and color is vivid, and drawing layer thickens, coating is ultra-fine, more has texture;
3, long quality-guarantee period, can persistence in the shady and cool dry ventilation, indoor lower than 50 DEG C;
4, close structure, resistance to fracture is strong, not frangibility and loss;
5, formula environmental protection, production process is to human body, environmental nonpollution, and the recyclable re-using of scrap stock in production process, recycle is worth high, and economical effectiveness is obvious.
Embodiment
According to specific embodiment, technical scheme of the present invention is described further below.Protection scope of the present invention is not limited to following examples, enumerates these examples and does not only limit the present invention in any way for exemplary purpose.
A kind of artistic oil painting stick of the present invention consists of the following composition: paraffin 3-5 weight part; Cera alba 3-5 weight part; Winterized stearin 10-20 weight part; Synthetic wax 10-20 weight part; White oil 15-25 weight part; Superfine talcum powder 30-50 weight part; And environmental-friendly pigment 3-8 weight part.
The present invention's white oil used is preferably made up grade white oil, and cera alba is preferably pure natural cera alba.
The present invention's synthetic wax used is prepared from by stearic acid and magnesiumcarbonate, prepare preferably by following technique: add stearic acid 10 weight part, magnesiumcarbonate 5 weight part in a kettle., temperature controls at 210 DEG C ± 2 DEG C, low speed uniform stirring continues to be heated to temperature and reaches 315 ± 2 DEG C, quantitatively slowly inject the stearic acid of 85 weight parts again, injection process is rapid in two steps, first 2 hours are injected with 400 ml/min, then enlargement discharge to 600 ml/min is until stearic acid has been noted, stop insulation, obtained synthetic wax after cooling.
Winterized stearin, pure natural cera alba that the present invention is used, paraffin, superfine talcum powder, white oil, and environmental-friendly pigment is commercially available, wherein winterized stearin can purchased from Jiangsu Zhong Ding grease factory, and paraffin can purchased from Sinopec Shanghai branch office, pure natural cera alba can purchased from orchard, Hebei wax company limited, and white oil can purchased from upper sea cowry specialization work.The equal type product of other companies in the equal available markets of above starting material replaces.
For environmental-friendly pigment, there is no particular restriction for its color, as long as can not produce detrimentally affect to object of the present invention, those skilled in the art easily can select suitable environmental-friendly pigment according to required artistic oil painting stick.As black series pigments can such as but be not limited only to be carbon black; Same, the pigment of red colour system, blue series, green system, yellow system can be one or more, not specific single restriction, as long as rear and required consistent of allotment.
The present invention also provides the preparation method of above-mentioned artistic oil painting stick, comprises the steps:
Paraffin, cera alba, winterized stearin, synthetic wax and white oil are mixed by predetermined proportion, carry out first time melt processed afterwards, in the liquid after fusing, add environmental-friendly pigment, Homogeneous phase mixing post-treatment obtains the first solid substances of fine sheet;
Carry out second time melt processed to described first material, and add superfine talcum powder in the liquid after fusing, Homogeneous phase mixing post-treatment obtains the second solid substances of fine sheet;
Third time melt processed is carried out to described second solid substances, forms liquid state, obtain described artistic oil painting stick by moulding process afterwards.
In above-mentioned steps, the temperature of melt processed is 70-90 DEG C for the first time, and the temperature of second time melt processed and for the third time melt processed is 70-95 DEG C.
In above-mentioned steps, described processing comprises the liquid after by fusing and carries out cooling process, and the temperature of cooling process is 8-14 DEG C.
In above-mentioned steps, comprise further and utilize three-roll grinder to grind the first solid substances and the second solid substances, grinding the particle fineness obtained is 10-30 micron.
Artistic oil painting stick preparation after, through QC check and accept surface without breakage meet artistic oil painting stick examination criteria and be qualified product, winder wraps up in mark, Processing Criterion mounted box, vanning on request, environmental protection, nontoxic, beautiful in colour, easily painted, the not painting material of easy fracture, long quality-guarantee period can be processed into.
Unless otherwise defined, term used herein is the implication that those skilled in the art understand usually.
By the following examples the present invention is described in further detail.
Embodiment
The blue artistic oil painting stick of embodiment 1
Composition of raw materials is as follows: 3 weight part paraffin, 3 weight part pure natural cera albas, 14 weight part winterized stearins, 14 weight part synthetic waxs, 20 weight part cosmetic grade white oils, 41 weight part superfine talcum powders, 1 weight part phthalocyanine blue b and 4 weight part titanium dioxides.
First 3 weight part paraffin, 3 weight part pure natural cera albas, 14 weight part winterized stearins, 14 weight part synthetic waxs, 20 weight part cosmetic grade white oils are quantitatively added in a kettle., temperature is controlled melt at 70-90 DEG C, quantitatively add environmental-friendly pigment (1 weight part phthalocyanine blue b and 4 weight part titanium dioxides) afterwards, cooling process is carried out at 8-14 DEG C after Homogeneous phase mixing, after to be ground to the fineness of 10-30 micron through three-roll grinder, obtain an abrasive.
Abrasive is returned refuse temperature in reactor be set in 90 ± 5 DEG C dissolve completely after quantitatively add 41 weight part superfine talcum powders when stirring, cooling process is carried out at 8-14 DEG C after Homogeneous phase mixing, after reach the fineness of 10-30 micron through three-roll grinder grinding, obtain regrind material.
Regrind material temperature of fusion is set in 90 ± 5 DEG C, and after fusing, temperature controls at about 70 DEG C injection molding machines shaping through cryogenic condensation technology completely, obtains the sliding artistic oil painting stick of blue silk;
The red artistic oil painting stick of embodiment 2
Composition of raw materials is as follows: 3 weight part paraffin, 3 weight part pure natural cera albas, 14 weight part winterized stearins, 14 weight part synthetic waxs, 20 weight part cosmetic grade white oils, 41 weight part superfine talcum powders, 4 weight part permanent bordeauxs and 1 weight part titanium dioxide.
First quantitatively add in a kettle. 3 weight part paraffin, 3 weight part pure natural cera albas, 14 weight part winterized stearins, 14 weight part synthetic waxs, 20 weight part cosmetic grade white oil temperature control after 70-90 DEG C of fusing, quantitatively add environmental-friendly pigment (4 weight part permanent bordeauxs and 1 weight part titanium dioxide), cooling process is carried out at 8-14 DEG C after Homogeneous phase mixing, after to be ground to the fineness of 10-30 micron through three-roll grinder, obtain an abrasive.
Abrasive is returned refuse temperature in reactor be set in 90 ± 5 DEG C dissolve completely after quantitatively add 41 weight part superfine talcum powders when stirring, cooling process is carried out at 8-14 DEG C after Homogeneous phase mixing, after reach the fineness of 10-30 micron through three-roll grinder grinding, obtain regrind material.
Regrind material temperature of fusion is set in 90 ± 5 DEG C, and after fusing, temperature controls at about 70 DEG C injection molding machines shaping through cryogenic condensation technology completely, obtains the sliding artistic oil painting stick of red silk.
The yellow artistic oil painting stick of embodiment 3
Composition of raw materials is as follows: 3 weight part paraffin, 3 weight part pure natural cera albas, 14 weight part winterized stearins, 14 weight part synthetic waxs, 20 weight part cosmetic grade white oils, 41 weight part superfine talcum powders, 4 weight part organic yellows and 1 weight part titanium dioxide.
First quantitatively add in a kettle. 3 weight part paraffin, 3 weight part pure natural cera albas, 14 weight part winterized stearins, 14 weight part synthetic waxs, 20 weight part cosmetic grade white oil temperature control after 70-90 DEG C of fusing, quantitatively add environmental-friendly pigment (4 weight part organic yellows and 1 weight part titanium dioxide), cooling process is carried out at 8-14 DEG C after Homogeneous phase mixing, after to be ground to the fineness of 10-30 micron through three-roll grinder, obtain an abrasive.
Abrasive is returned refuse temperature in reactor be set in 90 ± 5 DEG C dissolve completely after quantitatively add 41 weight part superfine talcum powders when stirring, cooling process is carried out at 8-14 DEG C after Homogeneous phase mixing, after reach the fineness of 10-30 micron through three-roll grinder grinding, obtain regrind material.
Regrind material temperature of fusion is set in 90 ± 5 DEG C, and after fusing, temperature controls at about 70 DEG C injection molding machines shaping through cryogenic condensation technology completely, obtains the sliding artistic oil painting stick of yellow silk.
Embodiment 4 black artistic oil painting stick
Composition of raw materials is as follows: 3 weight part paraffin, 3 weight part pure natural cera albas, 14 weight part winterized stearins, 14 weight part synthetic waxs, 20 weight part cosmetic grade white oils, 42 weight part superfine talcum powders, 4 weight part element carbon blacks.
First quantitatively add in a kettle. 3 weight part paraffin, 3 weight part pure natural cera albas, 14 weight part winterized stearins, 14 weight part synthetic waxs, 20 weight part cosmetic grade white oil temperature control after 70-90 DEG C of fusing, quantitatively add environmental-friendly pigment (4 weight part element carbon black), carry out cooling process at 8-14 DEG C after Homogeneous phase mixing, after be ground to 10-30 micron through three-roll grinder fineness obtain an abrasive.
Abrasive return refuse temperature in reactor be set in 90 ± 5 DEG C dissolve completely after quantitatively add 42 weight part superfine talcum powders when stirring, cooling process is carried out at 8-14 DEG C after Homogeneous phase mixing, after reach the fineness of 10-30 micron through three-roll grinder grinding, obtain regrind material.
Regrind material temperature of fusion is set in 90 ± 5 DEG C, and after fusing, temperature controls at about 70 DEG C injection molding machines shaping through cryogenic condensation technology completely, obtains the sliding artistic oil painting stick of black silk.
As a comparison, the artistic oil painting stick obtained with the above embodiment of the present invention compares test to artistic oil painting stick Shanghai Truecolor Stationery Co., Ltd. produced.
Describe performance:
Draw on special drawing paper with above-mentioned two kinds of artistic oil painting sticks, paper of all easily adhering both found that, can repeat to tint, but in the process of drawing, find that product that the present invention does is obviously more smooth, without astringent sense.
Colour brightness:
Above-mentioned two kinds of artistic oil painting sticks are utilized to paint on special drawing paper, through comparing the more bright-coloured exquisiteness of artistic oil painting stick color and luster finding that the present invention produces, without folder look phenomenon; Artistic oil painting stick of the present invention by by pigment and stopping composition separately grinding, more can ensure that the mesh-of-grind of pigment arrives bright requirement in preparation.
Fracture resistence force:
Take out after 1 hour in thermostat container artistic oil painting stick to be measured being placed in 37 ± 2 DEG C, immediately across being placed on two fulcrums of 4 centimetres, at two fulcrum central authorities applied loads, be placed in force part with ergometer, plus load power during measure sample fracture, as fracture resistence force.
Comparative example and embodiment sample respectively sample 10, then calculate fracture resistence force mean value.The fracture resistence force of comparative example is 5N; And the fracture resistence force of embodiment of the present invention sample is 5.5N, comparatively comparative example improves 10%.
Those skilled in the art it should be noted that embodiment described in the invention is only exemplary, can make other replacements various, changes and improvements within the scope of the invention.Thus, the invention is not restricted to above-mentioned embodiment, and be only defined by the claims.
Claims (10)
1. an artistic oil painting stick, consists of the following composition:
2. artistic oil painting stick as claimed in claim 1, wherein said synthetic wax is prepared from by stearic acid and magnesiumcarbonate.
3. artistic oil painting stick as claimed in claim 1, wherein said white oil is cosmetic grade white oil.
4. the preparation method of artistic oil painting stick as claimed any one in claims 1 to 3, comprises the steps:
Paraffin, cera alba, winterized stearin, synthetic wax and white oil are mixed by predetermined proportion, carry out first time melt processed afterwards, in the liquid after fusing, add environmental-friendly pigment, Homogeneous phase mixing post-treatment obtains the first solid substances;
Carry out second time melt processed to described first material, and add superfine talcum powder in the liquid after fusing, Homogeneous phase mixing post-treatment obtains the second solid substances;
Third time melt processed is carried out to described second solid substances, obtains described artistic oil painting stick by moulding process afterwards.
5. preparation method as claimed in claim 4, wherein said first time the temperature of melt processed be 70-90 DEG C.
6. preparation method as claimed in claim 4, wherein said second time melt processed and described third time melt processed temperature be 70-95 DEG C.
7. preparation method as claimed in claim 4, wherein said processing comprises the liquid after by fusing and carries out cooling process.
8. preparation method as claimed in claim 7, the temperature of wherein said cooling process is 8-14 DEG C.
9. preparation method as claimed in claim 4, also comprises and utilizes three-roll grinder to grind described first solid substances and described second solid substances.
10. preparation method as claimed in claim 9, the particle fineness of wherein said first solid substances and described second solid substances is 10-30 micron.