CN105176202B - Artistic oil painting stick and preparation method thereof - Google Patents
Artistic oil painting stick and preparation method thereof Download PDFInfo
- Publication number
- CN105176202B CN105176202B CN201510688492.2A CN201510688492A CN105176202B CN 105176202 B CN105176202 B CN 105176202B CN 201510688492 A CN201510688492 A CN 201510688492A CN 105176202 B CN105176202 B CN 105176202B
- Authority
- CN
- China
- Prior art keywords
- parts
- weight
- preparation
- painting stick
- oil painting
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The present invention provides a kind of artistic oil painting stick and preparation method thereof, and artistic oil painting stick consists of the following composition:The parts by weight of paraffin 35, the parts by weight of cera alba 35, the parts by weight of fixed oil 10 20, the parts by weight of synthetic wax 10 20, the parts by weight of white oil 15 25, the parts by weight of superfine talcum powder 30 50, the parts by weight of environmental-friendly pigment 38.The artistic oil painting stick of the present invention is environment-protecting and non-poisonous, and feel is fine and smooth, smooth, and spreadability is good, folds color contamination color excellent performance, and color is vivid, and drawing figure layer thickens, and coating is ultra-fine, more there is texture.
Description
Technical field
The present invention relates to a kind of draw tool material, more particularly to a kind of artistic oil painting stick and preparation method thereof.
Background technology
Most common graphic products are mainly artistic oil painting stick and wax crayon in the market.
Wax crayon, which exists, paints uneven, and color is not bright-coloured enough, draws that performance is undesirable, and it is not equal enough to be in particular in that painting is retouched
Even, for figure layer than relatively thin, covering power is poor.
Comparatively, the feel of artistic oil painting stick is fine and smooth, and spreadability is good, folds color, colour mixture excellent performance, but oil in the market
Also presence is not smooth for the drawing feel of picture rod, has the problem of astringent sense.
The content of the invention
It is an object of the invention to overcome prior art insufficient, there is provided one kind is environment-protecting and non-poisonous, bright in colour, drawing performance is excellent
Good artistic oil painting stick and preparation method thereof.
On the one hand, the present invention provides a kind of artistic oil painting stick, and it is consisted of the following composition:Paraffin 3-5 parts by weight;Cera alba 3-5
Parts by weight;Fixed oil 10-20 parts by weight;Synthetic wax 10-20 parts by weight;White oil 15-25 parts by weight;Superfine talcum powder 30-50 weights
Measure part;And environmental-friendly pigment 3-8 parts by weight.
In an embodiment of the artistic oil painting stick of the present invention, the synthetic wax is prepared by stearic acid and magnesium carbonate.
In another embodiment of the artistic oil painting stick of the present invention, the white oil is cosmetic grade white oil.
On the other hand, the present invention provides the preparation method of above-mentioned artistic oil painting stick, comprises the following steps:
Paraffin, cera alba, fixed oil, synthetic wax and white oil are mixed by predetermined ratio, carried out afterwards for the first time
Melt processed, environmental-friendly pigment is added into the liquid after fusing, uniformly mix post-processing and obtain the first solid material;
Second of melt processed is carried out to the first material, and superfine talcum powder is added into the liquid after fusing,
Even mixing post-processing obtains the second solid material;
Third time melt processed is carried out to second solid material, the artistic oil painting stick is obtained by moulding process afterwards.
In an embodiment of the preparation method of the present invention, the temperature of the first time melt processed is 70-90 DEG C.
In another embodiment of the preparation method of the present invention, second of melt processed and the third time melt
The temperature for changing processing is 70-95 DEG C.
In another embodiment of the preparation method of the present invention, the processing includes the liquid progress after fusing is cold
But handle.
In another embodiment of the preparation method of the present invention, the temperature of the cooling treatment is 8-14 DEG C.
It is also solid to described first using three-roll grinder in another embodiment of the preparation method of the present invention
State material and second solid material are ground.
In another embodiment of the preparation method of the present invention, first solid material and second solid
The grain fineness of material is 10-30 microns.
Compared with prior art, artistic oil painting stick of the invention has the following advantages:
1st, it is environment-protecting and non-poisonous, tasteless;The pigment for replacing using originally using environmental-friendly pigment, makes heavy metal etc. be detrimental to health
Content of material be far below international limit standard;
2nd, feel is fine and smooth, smooth, spreadability is good, folded color contamination color excellent performance, and color is vivid, and drawing figure layer thickens, coating
It is ultra-fine, more there is texture;
3rd, long shelf-life, can persistence in the shady and cool dry ventilation in the interior less than 50 DEG C;
4th, close structure, resistance to fracture is strong, is not easily broken and is lost;
5th, formula environmental protection, production process is to human body, environmental nonpollution, and the leftover pieces in production process are recyclable again sharp
With recycle value is high, and economic effect is obvious.
Embodiment
Technical scheme is described further below according to specific embodiment.Protection scope of the present invention is unlimited
In following examples, these examples are enumerated merely for exemplary purpose without limiting the invention in any way.
A kind of artistic oil painting stick of the present invention consists of the following composition:Paraffin 3-5 parts by weight;Cera alba 3-5 parts by weight;Fixed oil
10-20 parts by weight;Synthetic wax 10-20 parts by weight;White oil 15-25 parts by weight;Superfine talcum powder 30-50 parts by weight;And environmental protection
Pigment 3-8 parts by weight.
White oil used in the present invention is preferably cosmetic grade white oil, and cera alba is preferably pure natural cera alba.
Synthetic wax used in the present invention is prepared by stearic acid and magnesium carbonate, is preferably prepared by following technique:Anti-
The parts by weight of stiffened resin acid 10 in kettle, the parts by weight of magnesium carbonate 5 are answered, at 210 DEG C ± 2 DEG C, low speed uniform stirring continues to add temperature control
Heat to temperature reaches 315 ± 2 DEG C, then is quantitatively slowly injected into the stearic acid of 85 parts by weight, and injection process is rapid in two steps, first with
400 ml/mins are injected 2 hours, and then enlargement discharge to 600 ml/mins is untill stearic acid has been noted, stopping insulation,
Synthetic wax is made after cooling.
Fixed oil, pure natural cera alba used in the present invention, paraffin, superfine talcum powder, white oil, and environmental-friendly pigment are
Commercially available, wherein fixed oil is purchased from Jiangsu Zhong Ding greases factory, and paraffin is purchased from Sinopec Shanghai branch company, pure natural cera alba
Hebei orchard wax Co., Ltd is purchased from, white oil is purchased from sea cowry specialization work.Other in the equal available markets of above raw material
The equal type product of company replaces.
For environmental-friendly pigment, there is no particular restriction for its color, is as long as harmful effect will not be produced to the purpose of the present invention
Can, those skilled in the art easily can select suitable environmental-friendly pigment according to required artistic oil painting stick.Such as black series pigments
For example but can be not limited only to be carbon black;Likewise, red colour system, blue series, green are, the pigment of yellow class can be one kind
Or a variety of, not specific single limitation, as long as consistent with required after allotment.
The present invention also provides the preparation method of above-mentioned artistic oil painting stick, comprises the following steps:
Paraffin, cera alba, fixed oil, synthetic wax and white oil are mixed by predetermined ratio, carried out afterwards for the first time
Melt processed, environmental-friendly pigment is added into the liquid after fusing, uniformly mix post-processing and obtain the first solid of fine sheet
Material;
Second of melt processed is carried out to the first material, and superfine talcum powder is added into the liquid after fusing,
Even mixing post-processing obtains the second solid material of fine sheet;
Third time melt processed is carried out to second solid material, liquid condition is formed, is obtained afterwards by moulding process
To the artistic oil painting stick.
In above-mentioned steps, the temperature of first time melt processed is 70-90 DEG C, and second of melt processed and third time melt
The temperature of processing is 70-95 DEG C.
In above-mentioned steps, the processing includes the liquid after fusing carrying out cooling treatment, and the temperature of cooling treatment is
8-14℃。
In above-mentioned steps, further comprise carrying out the first solid material and the second solid material using three-roll grinder
Grinding, the grain fineness for grinding to obtain is 10-30 microns.
After prepared by artistic oil painting stick, check and accept surface through QC and without breakage meet artistic oil painting stick examination criteria and be qualified products, coil paper
Machine wraps up in mark, on request processing criterion mounted box, vanning, you can is processed into environmentally friendly, nontoxic, beautiful in colour, coloring is easy, not easily broken
Split, the painting material of long shelf-life.
Unless otherwise defined, term used herein is the implication that those skilled in the art are generally understood that.
The present invention is described in further detail by the following examples.
Embodiment
1 blue artistic oil painting stick of embodiment
Composition of raw materials is as follows:3 parts by weight paraffin, the pure natural cera alba of 3 parts by weight, 14 parts by weight fixed oils, 14 parts by weight
Synthetic wax, 20 parts by weight cosmetic grade white oils, 41 parts by weight superfine talcum powders, 1 parts by weight phthalocyanine blue b and 4 parts by weight titanium dioxides.
Be quantitatively adding in a kettle first 3 parts by weight paraffin, the pure natural cera alba of 3 parts by weight, 14 parts by weight fixed oils,
14 parts by weight synthetic waxs, 20 parts by weight cosmetic grade white oils, temperature control is melted at 70-90 DEG C, is quantitatively adding ring afterwards
Protect pigment (1 parts by weight phthalocyanine blue b and 4 parts by weight titanium dioxides), uniformly mixing after 8-14 DEG C carry out cooling treatment, after through three
Roller mill is ground to the fineness of 10-30 microns, obtains an abrasive.
By abrasive return refuse temperature in reactor be set in 90 ± 5 DEG C dissolve completely after stirring feelings
41 parts by weight superfine talcum powders are quantitatively adding under condition, uniformly mixing after 8-14 DEG C carry out cooling treatment, after through three rollers grind
Machine grinds the fineness for reaching 10-30 microns, obtains secondary abrasive.
Secondary abrasive fusion temperature is set in 90 ± 5 DEG C, is completely melt that rear temperature control is injected at 70 DEG C or so
Type machine is molded by cryogenic condensation technology, is obtained blue silk and is slided artistic oil painting stick;
2 red artistic oil painting stick of embodiment
Composition of raw materials is as follows:3 parts by weight paraffin, the pure natural cera alba of 3 parts by weight, 14 parts by weight fixed oils, 14 parts by weight
Synthetic wax, 20 parts by weight cosmetic grade white oils, 41 parts by weight superfine talcum powders, 4 parts by weight permanent bordeauxs and 1 parts by weight titanium dioxide.
Be quantitatively adding in a kettle first 3 parts by weight paraffin, the pure natural cera alba of 3 parts by weight, 14 parts by weight fixed oils,
14 parts by weight synthetic waxs, 20 parts by weight cosmetic grade white oil temperature controls are quantitatively adding environmental-friendly pigment (4 weights after 70-90 DEG C of fusing
Measure part permanent bordeaux and 1 parts by weight titanium dioxide), uniformly carry out cooling treatment at 8-14 DEG C after mixing, after ground through three-roll grinder
The fineness of 10-30 microns is ground to, obtains an abrasive.
By abrasive return refuse temperature in reactor be set in 90 ± 5 DEG C dissolve completely after stirring feelings
41 parts by weight superfine talcum powders are quantitatively adding under condition, uniformly mixing after 8-14 DEG C carry out cooling treatment, after through three rollers grind
Machine grinds the fineness for reaching 10-30 microns, obtains secondary abrasive.
Secondary abrasive fusion temperature is set in 90 ± 5 DEG C, is completely melt that rear temperature control is injected at 70 DEG C or so
Type machine is molded by cryogenic condensation technology, is obtained red silk and is slided artistic oil painting stick.
The yellow artistic oil painting stick of embodiment 3
Composition of raw materials is as follows:3 parts by weight paraffin, the pure natural cera alba of 3 parts by weight, 14 parts by weight fixed oils, 14 parts by weight
Synthetic wax, 20 parts by weight cosmetic grade white oils, 41 parts by weight superfine talcum powders, 4 parts by weight everbright fast yellows and 1 parts by weight titanium dioxide.
Be quantitatively adding in a kettle first 3 parts by weight paraffin, the pure natural cera alba of 3 parts by weight, 14 parts by weight fixed oils,
14 parts by weight synthetic waxs, 20 parts by weight cosmetic grade white oil temperature controls are quantitatively adding environmental-friendly pigment (4 weights after 70-90 DEG C of fusing
Measure part everbright fast yellow and 1 parts by weight titanium dioxide), uniformly carry out cooling treatment at 8-14 DEG C after mixing, after ground through three-roll grinder
The fineness of 10-30 microns is ground to, obtains an abrasive.
By abrasive return refuse temperature in reactor be set in 90 ± 5 DEG C dissolve completely after stirring feelings
41 parts by weight superfine talcum powders are quantitatively adding under condition, uniformly mixing after 8-14 DEG C carry out cooling treatment, after through three rollers grind
Machine grinds the fineness for reaching 10-30 microns, obtains secondary abrasive.
Secondary abrasive fusion temperature is set in 90 ± 5 DEG C, is completely melt that rear temperature control is injected at 70 DEG C or so
Type machine is molded by cryogenic condensation technology, is obtained yellow silk and is slided artistic oil painting stick.
The black artistic oil painting stick of embodiment 4
Composition of raw materials is as follows:3 parts by weight paraffin, the pure natural cera alba of 3 parts by weight, 14 parts by weight fixed oils, 14 parts by weight
Synthetic wax, 20 parts by weight cosmetic grade white oils, 42 parts by weight superfine talcum powders, 4 parts by weight element carbon blacks.
Be quantitatively adding in a kettle first 3 parts by weight paraffin, the pure natural cera alba of 3 parts by weight, 14 parts by weight fixed oils,
14 parts by weight synthetic waxs, 20 parts by weight cosmetic grade white oil temperature controls are quantitatively adding environmental-friendly pigment (4 weights after 70-90 DEG C of fusing
Measure part element carbon black), uniformly carry out cooling treatment at 8-14 DEG C after mixing, after through three-roll grinder be ground to 10-30 microns
Fineness obtains an abrasive.
Abrasive return refuse temperature in reactor be set in 90 ± 5 DEG C dissolve completely after stirring situation
Under be quantitatively adding 42 parts by weight superfine talcum powders, uniformly mixing after 8-14 DEG C carry out cooling treatment, after through three-roll grinder
Grinding reaches the fineness of 10-30 microns, obtains secondary abrasive.
Secondary abrasive fusion temperature is set in 90 ± 5 DEG C, is completely melt rear temperature control in 70 DEG C or so injection mouldings
Machine is molded by cryogenic condensation technology, is obtained black silk and is slided artistic oil painting stick.
The artistic oil painting stick that Shanghai Truecolor Stationery Co., Ltd. is produced as a comparison, made from the above embodiment of the present invention
Artistic oil painting stick is compared experiment.
Describe performance:
Drawn with above two artistic oil painting stick on special drawing paper, as a result find that both of which is easily adhered paper, Ke Yichong
Overcoating color, but find that the present invention does obvious more smooth, the no astringent sense of product during drawing.
Colour brightness:
Painted using above two artistic oil painting stick on special drawing paper, warp is it was found that the artistic oil painting stick that the present invention is produced
The more bright-coloured exquisiteness of color and luster, no folder color phenomenon;The present invention artistic oil painting stick in preparation by the way that pigment and inserts are separately ground,
It can more ensure that the fineness of grind of pigment reaches bright requirement.
Fracture resistence force:
Artistic oil painting stick to be measured was placed in 37 ± 2 DEG C of insulating box after 1 hour and taken out, immediately across be placed at a distance of 4 centimetres two
On individual fulcrum, apply load in two fulcrum centers, force part, plus load when measurement sample is broken are placed in dynamometer
Power, as fracture resistence force.
Comparative example and embodiment sample respectively sampling 10, then calculate fracture resistence force average value.Comparative example resists
Folding power is 5N;And the fracture resistence force of sample of the embodiment of the present invention is 5.5N, 10% is improved compared with comparative example.
Those skilled in the art should be noted that embodiment described in the invention is only exemplary, can be
Various other replacements, changes and improvements are made in the scope of the present invention.Thus, the invention is not restricted to above-mentioned embodiment, and only
It is defined by the claims.
Claims (10)
1. a kind of artistic oil painting stick, is consisted of the following composition:
2. artistic oil painting stick as claimed in claim 1, wherein the synthetic wax is prepared by stearic acid and magnesium carbonate.
3. artistic oil painting stick as claimed in claim 1, wherein the white oil is cosmetic grade white oil.
4. the preparation method of artistic oil painting stick as claimed any one in claims 1 to 3, comprises the following steps:
Paraffin, cera alba, fixed oil, synthetic wax and white oil are mixed by predetermined ratio, carry out first time fusing afterwards
Processing, environmental-friendly pigment is added into the liquid after fusing, is uniformly mixed post-processing and is obtained the first solid material;
Second of melt processed is carried out to the first material, and superfine talcum powder is added into the liquid after fusing, it is uniformly mixed
Close post-processing and obtain the second solid material;
Third time melt processed is carried out to second solid material, the artistic oil painting stick is obtained by moulding process afterwards.
5. preparation method as claimed in claim 4, wherein the temperature of the first time melt processed is 70-90 DEG C.
6. preparation method as claimed in claim 4, wherein second of melt processed and the third time melt processed
Temperature is 70-95 DEG C.
7. preparation method as claimed in claim 4, wherein the processing includes the liquid after fusing carrying out cooling treatment.
8. preparation method as claimed in claim 7, wherein the temperature of the cooling treatment is 8-14 DEG C.
9. preparation method as claimed in claim 4, also using three-roll grinder to first solid material and described
Second solid material is ground.
10. preparation method as claimed in claim 9, wherein the particle of first solid material and second solid material
Fineness is 10-30 microns.