CN108117345A - 一种仿蘑菇石层及其应用、保温装饰板及其制作方法 - Google Patents
一种仿蘑菇石层及其应用、保温装饰板及其制作方法 Download PDFInfo
- Publication number
- CN108117345A CN108117345A CN201711416166.1A CN201711416166A CN108117345A CN 108117345 A CN108117345 A CN 108117345A CN 201711416166 A CN201711416166 A CN 201711416166A CN 108117345 A CN108117345 A CN 108117345A
- Authority
- CN
- China
- Prior art keywords
- parts
- mushroom rock
- rock layer
- heat insulating
- decorative board
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种仿蘑菇石层及其应用，仿蘑菇石层的组分为快硬水泥30份～35份；硅微粉3份～5份；可再分散胶粉2份～5份；发泡陶粒砂10份～15份；减水剂0.5份～1份；短纤维0.2份；石英砂45份～55份；水适量，该仿蘑菇石层可以用于建筑材料。本发明还公开了包含该仿蘑菇石层的保温装饰板以及制作方法。本发明外形美观，产品性能稳定、安全、可靠，能够实现工厂批量生产，便于进行现场施工，利于简化施工流程、缩短工期、降低施工危险性，施工质量高、效果好，同时具有良好的环保性，并且制作成本较低。
Description
技术领域
本发明属于建筑外墙材料领域，特别涉及一种仿蘑菇石层及其应用、保温装饰板及其制作方法。
背景技术
目前在建筑物外墙体做保温装饰时，通常采用以下方式：1、外挂保温板，然后进行装饰层施工；2、涂抹或喷涂保温浆料，然后进行装饰层施工。
上述施工方式存在如下缺点：保温层、保护层和饰面层需要三次或三次以上施工来完成，现场湿法作业量大，施工周期长，高空作业时间长，致使危险因素增高，高空作业易造成施工质量无保证。
另外，目前很多保温装饰施工还存在着如下的缺陷：1、采用真石材料作为装饰面层，由于其自量较大，不易固定，日久易脱落，增加了造成高空坠落物伤人事故的可能性；2、现有的包括真石材料在内的很多装饰面层材料粘合和固定困难，因而也难以采取先做好装饰板再进行墙体施工的方式；3、由于环保要求严格，限制石材的开采，而且石材的成本较高，使得石材的利用受到了限制；4、保温装饰产品强度低，抗污能力差，产品性能不稳定。
发明内容
本发明要解决的技术问题是，提供一种仿蘑菇石层及其应用、保温装饰板及其制作方法，通过该仿蘑菇石层及其制成的保温装饰板的优良特性来简化施工，提高施工效果，并具有良好的环保性和使用经济性。
为解决上述技术问题，本发明的仿蘑菇石层所采用的技术方案是：
一种仿蘑菇石层，由如下按重量份计的组分配制而成：
快硬水泥，30份～35份；硅微粉，3份～5份；可再分散胶粉，2份～5份；发泡陶粒砂，10份～15份；减水剂，0.5份～1份；短纤维，0.2份；石英砂，45份～55份；水适量。
在上述技术方案中，添加快硬水泥可以缩短砂浆的终凝时间，提高生产效率。本技术方案中添加硅微粉与可再分散胶粉，有利于提高砂浆的抗压、抗折强度以及防水性，使其在使用过程中粘结强度仍在增大，至少十年内仍能保持稳定的粘结强度、抗折强度和抗压强度，防水性和抗老化性与普通砼相比大大提高。本技术方案中添加质量较轻的陶粒发泡闭孔颗粒取代砂石做填料，其密度只有花岗石材的三分之一，使仿蘑菇石层的自重大大减轻，与其他物体粘贴或锚固更加简单方便，不易脱落，利于现场施工，施工效果好。本技术方案中添加了减水剂，可以改变砂浆和易性，提高砂浆的早期强度。本技术方案中添加了短纤维，可以提高制成品的抗裂性，提高抗折强度。
通过本技术方案制成的仿蘑菇石层具有稳定的粘结强度、抗折强度和抗压强度以及优异的防水性和抗老化性，产品更加稳定、安全、可靠。本发明的仿蘑菇石层具有良好的环保性，并且制作成本较低。
作为改进，所述快硬水泥为硫铝酸盐水泥，达到缩短砂浆的终凝时间，提高生产效率的目的。所述短纤维为聚丙烯纤维，达到提高制成品的抗裂性，提高抗折强度的目的。
作为改进，所述石英砂的粒径为0.5mm～1.5mm,所述发泡陶粒砂的粒径不大于5mm，有利于减轻仿蘑菇石制品的自重。
上述的仿蘑菇石层可以用于建筑材料中，例如保温装饰板，使得所制成的建筑材料具有稳定的粘结强度、抗折强度和抗压强度以及优异的防水性和抗老化性，产品更加稳定、安全、可靠；并且有利于减轻所制成的建筑材料的自重，从而与其他物体粘贴或锚固更加简单方便，不易脱落，利于现场施工，施工效果好，施工后拆卸、修复和翻新也更加方便；同时也有利于所制成的建筑材料在工厂进行批量生产，批量生产之后再进行现场施工，有利于简化施工流程、缩短工期、降低施工危险性、提高和稳定施工质量；另外还有利于提高所制成的建筑材料的环保性，同时降低制作成本。
本发明还提供了一种包含上述的仿蘑菇石层的装饰板。采用上述的仿蘑菇石层所制成的装饰板具有稳定的粘结强度、抗折强度和抗压强度以及优异的防水性和抗老化性，产品更加稳定、安全、可靠；并且自重大大减轻，与其他物体粘贴或锚固更加简单方便，不易脱落，利于现场施工，施工效果好，施工后拆卸、修复和翻新也更加方便；同时也有利于装饰板在工厂进行批量生产，批量生产之后再进行现场施工，利于简化施工流程、缩短工期、降低施工危险性、提高施工质量；另外还有利于提高所制成的装饰板的环保性，同时降低制作成本。
本发明还提供了一种保温装饰板，包括保温层、增强网片、装饰面层、涂色层以及封闭层，其中装饰面层为上述的仿蘑菇石层。
该保温装饰板采用了上述的仿蘑菇石层、而不是真石材料作为装饰面层，所使用的仿蘑菇石层具有稳定的粘结强度、抗折强度和抗压强度以及优异的防水性和抗老化性，能够增强保温装饰板的稳定性、安全性、可靠性；并且自重以及保温装饰板的整重大大减轻，与其他物体粘贴或锚固更加简单方便，不易脱落，利于现场施工，施工效果好，施工后拆卸、修复和翻新也更加方便；同时具有良好的环保性，制作成本较低。该保温装饰板具有增强网片，能够进一步提高仿蘑菇石层的抗折强度，也进一步提高了保温装饰板的整体强度。上述的封闭层由纳米封闭剂形成，纳米封闭剂是一种混凝土渗透性材料，应用到混凝土表面可显著增强抗污能力，强力阻止液体和污渍渗透到基材，可增强基材表面光泽，增亮基材颜色。该保温装饰板表面具有封闭层使其更加美观、耐用，产品性能更加稳定、安全、可靠。
具有上述结构的该保温装饰板可在工厂批量生产，然后再进行现场施工，从而能够将原来施工现场三步或者三步以上的施工流程可以简化成一步完成，大大缩短工期，有利于降低施工危险性，提高施工质量。
作为改进，所述保温层为聚苯乙烯板、改性聚苯乙烯板或挤塑聚苯板，保温效果好。
作为改进，所述增强网片为钢丝网或玻璃纤维网格布，可以提供优异的增强作用。
本发明还提供了一种上述的保温装饰板的制作方法，包括以下步骤：
S1：将上述的按重量份计的各组分搅拌成浆；
S2：将浆料倒入蘑菇石面模具，振实并摊平，然后铺增强网片，再次倒入浆料并摊平后放置保温板，浆料初凝后拆除模具进行养护；
S4：养护完毕后进行着色，待着色面干燥后，喷涂纳米封闭剂。
由于所制成的保温装饰板采用了上述的仿蘑菇石层、而不是真石材料作为装饰面层，因而具有稳定的粘结强度、抗折强度和抗压强度以及优异的防水性和抗老化性，进一步增强了产品的稳定性、安全性、可靠性；并且自重大大减轻，与其他物体粘贴或锚固更加简单方便，不易脱落，利于现场施工，施工效果好，施工后拆卸、修复和翻新也更加方便；同时具有良好的环保性，制作成本较低。按上述步骤所制成的保温装饰板具有增强网片，能够进一步提高仿蘑菇石层的抗折强度，也进一步提高了保温装饰板的整体强度。按上述步骤制成的保温装饰板具有封闭层，封闭层由纳米封闭剂形成，纳米封闭剂是一种混凝土渗透性材料，应用到混凝土表面可显著增强抗污能力，强力阻止液体和污渍渗透到基材，可增强基材表面光泽，增亮基材颜色。该保温装饰板表面具有封闭层使其更加美观、耐用，产品性能更加稳定、安全、可靠。
利用该制作方法可在工厂批量生产上述的保温装饰板，然后再进行现场施工，从而能够将原来施工现场三步或者三步以上的施工流程可以简化成一步完成，大大缩短工期，有利于降低施工危险性，提高施工质量。
作为改进，所述模具内模层为硅胶，从而使所得到的仿蘑菇石层具有仿真度高的特点。
综上，本发明产品性能稳定、安全、可靠，能够实现工厂批量生产，便于进行现场施工，利于简化施工流程、缩短工期、降低施工危险性，施工质量高、效果好，同时具有良好的环保性和美观性，并且制作成本较低。
具体实施方式
实施例一：
一种仿蘑菇石层，由如下按重量份计的组分配制而成：
快硬水泥30份；硅微粉3份；可再分散胶粉2份；发泡陶粒砂10份；减水剂0.5份；短纤维0.2份；石英砂45份，其余为合适量水(本实施例中水灰比1：3.3)。其中快硬水泥选用硫铝酸盐水泥，短纤维选用聚丙烯纤维，石英砂的粒径为0.5mm,发泡陶粒砂的粒径不大于5mm，密度300kg/m3。
按下面的步骤制作保温装饰板：
S1：将上述的按重量份计的各组分搅拌成浆。
S2：将一些浆料倒入蘑菇石面模具中，振实并摊平，然后在摊平面铺增强网片(钢丝网或无碱玻璃纤维网格布)，在增强网片上再次倒入浆料并摊平后放置保温板(聚苯乙烯板、改性聚苯乙烯板或挤塑聚苯板)，保温板位于外侧，增强网片铺设于仿蘑菇石层之内。浆料初凝后拆除模具进行养护(养护即为自然条件下的自然凝固过程，可以在室内或者室外，若是在室外则根据需要设置遮光防晒等装置，具体养护时间根据需要确定，下同)。
上面所使用的蘑菇石面模具可以采用如下方式得到：首先制作真石感强的模种(用真的蘑菇石作为模种也可)，然后再由模种翻制成模具。模具是有硅胶层和树脂层组成的软硬复合模具，硅胶作为内模层，所制作出的仿蘑菇石层仿真度高。
S3：养护完毕后，在带有不规则凹凸面的仿蘑菇石层上进行着色处理，增加美感。最后在着色后的产品表面喷涂纳米封闭剂(可使用现有的纳米封闭剂)作为封闭层，喷涂前应保持喷涂面干燥整洁，喷涂时不能淋雨或洒水，涂抹后12小时内不能淋雨和暴晒。
利用上述步骤所制成的保温装饰板包括保温层、增强网片、装饰面层、涂色层以及封闭层。
实施例二：
一种仿蘑菇石层，由如下按重量份计的组分配制而成：
快硬水泥32.5份；硅微粉4份；可再分散胶粉3.5份；发泡陶粒砂12.5份；减水剂0.75份；短纤维0.2份；石英砂50份，其余为合适量水(本实施例中水灰比1：3.3)。其中快硬水泥选用硫铝酸盐水泥，短纤维选用聚丙烯纤维，石英砂的粒径为1mm,发泡陶粒砂的粒径不大于5mm，密度300kg/m3。
按下面的步骤制作保温装饰板：
S1：将上述的按重量份计的各组分搅拌成浆。
S2：将一些浆料倒入蘑菇石面模具中，振实并摊平，然后在摊平面铺增强网片(钢丝网或无碱玻璃纤维网格布)，在增强网片上再次倒入浆料并摊平后放置保温板(聚苯乙烯板、改性聚苯乙烯板或挤塑聚苯板)，保温板位于外侧，增强网片铺设于仿蘑菇石层之内。浆料初凝后拆除模具进行养护(养护即为自然条件下的自然凝固过程，可以在室内或者室外，若是在室外则根据需要设置遮光防晒等装置，具体养护时间根据需要确定，下同)。
所使用的蘑菇石面模具可以采用如下方式得到：首先制作真石感强的模种(用真的蘑菇石作为模种也可)，然后再由模种翻制成模具。模具是有硅胶层和树脂层组成的软硬复合模具，硅胶作为内模层，所制作出的仿蘑菇石层仿真度高。
S3：养护完毕后，在带有不规则凹凸面的仿蘑菇石层上进行着色处理，增加美感。最后在着色后的产品表面喷涂纳米封闭剂(可使用现有的纳米封闭剂)作为封闭层，喷涂前应保持喷涂面干燥整洁，喷涂时不能淋雨或洒水，涂抹后12小时内不能淋雨和暴晒。
利用上述步骤所制成的保温装饰板包括保温层、增强网片、装饰面层、涂色层以及封闭层。
实施例三：
一种仿蘑菇石层，由如下按重量份计的组分配制而成：
快硬水泥35份；硅微粉5份；可再分散胶粉5份；发泡陶粒砂15份；减水剂1份；短纤维0.2份；石英砂55份，其余为合适量水(本实施例中水灰比1：3.3)。其中快硬水泥选用硫铝酸盐水泥，短纤维选用聚丙烯纤维，石英砂的粒径为1.5mm,发泡陶粒砂的粒径不大于5mm，密度300kg/m3。
按下面的步骤制作保温装饰板：
S1：将上述的按重量份计的各组分搅拌成浆。
S2：将一些浆料倒入蘑菇石面模具中，振实并摊平，然后在摊平面铺增强网片(钢丝网或无碱玻璃纤维网格布)，在增强网片上再次倒入浆料并摊平后放置保温板(聚苯乙烯板、改性聚苯乙烯板或挤塑聚苯板)，保温板位于外侧，增强网片铺设于仿蘑菇石层之内。浆料初凝后拆除模具进行养护(养护即为自然条件下的自然凝固过程，可以在室内或者室外，若是在室外则根据需要设置遮光防晒等装置，具体养护时间根据需要确定，下同)。
所使用的蘑菇石面模具可以采用如下方式得到：首先制作真石感强的模种(用真的蘑菇石作为模种也可)，然后再由模种翻制成模具。模具是有硅胶层和树脂层组成的软硬复合模具，硅胶作为内模层，所制作出的仿蘑菇石层仿真度高。
S3：养护完毕后，在带有不规则凹凸面的仿蘑菇石层上进行着色处理，增加美感。最后在着色后的产品表面喷涂纳米封闭剂(可使用现有的纳米封闭剂)作为封闭层，喷涂前应保持喷涂面干燥整洁，喷涂时不能淋雨或洒水，涂抹后12小时内不能淋雨和暴晒。
利用上述步骤所制成的保温装饰板包括保温层、增强网片、装饰面层、涂色层以及封闭层。
上述实施例中，浆料的厚度可以根据需要调整。
上面结合具体实施方式以及实施例对本发明进行了进一步的说明，但本发明并不限于上述具体实施方式和实施例，在本领域普通技术人员所具备的知识范围内，还可以在不脱离本发明宗旨的前提下做出各种变化。
Claims (10)
1.一种仿蘑菇石层，由如下按重量份计的组分配制而成：
快硬水泥，30份～35份；
硅微粉，3份～5份；
可再分散胶粉，2份～5份；
发泡陶粒砂，10份～15份；
减水剂，0.5份～1份；
短纤维，0.2份；
石英砂，45份～55份；
水适量。
2.根据权利要求1所述的一种仿蘑菇石层，其特征在于：所述快硬水泥为硫铝酸盐水泥；所述短纤维为聚丙烯纤维。
3.根据权利要求1所述的一种仿蘑菇石层，其特征在于：所述石英砂的粒径为0.5mm～1.5mm，所述发泡陶粒砂的粒径不大于5mm。
4.权利要求1至3中任一项在建筑材料中的应用。
5.一种包含权利要求1至3中任一项的装饰板。
6.一种保温装饰板，其特征在于：包括保温层、增强网片、装饰面层、涂色层以及封闭层，其中装饰面层为权利要求1至3中任一项所述的仿蘑菇石层。
7.根据权利要求6所述的一种保温装饰板，其特征在于：所述保温层为聚苯乙烯板、改性聚苯乙烯板或挤塑聚苯板。
8.根据权利要求6所述的一种保温装饰板，其特征在于：所述增强网片为钢丝网或玻璃纤维网格布。
9.一种权利要求6所述的保温装饰板的制作方法，包括以下步骤：
S1：将权利要求1至3中任一项所述的按重量份计的各组分搅拌成浆；
S2：将浆料倒入蘑菇石面模具，振实并摊平，然后铺增强网片，再次倒入浆料并摊平后放置保温板，浆料初凝后拆除模具进行养护；
S3：养护完毕后进行着色，待着色面干燥后，喷涂纳米封闭剂。
10.根据权利要求9所述的一种保温装饰板的制作方法，其特征在于：所述模具内模层为硅胶。