CN108046844A - A kind of red copper glaze and preparation method thereof - Google Patents
A kind of red copper glaze and preparation method thereof Download PDFInfo
- Publication number
- CN108046844A CN108046844A CN201711275996.7A CN201711275996A CN108046844A CN 108046844 A CN108046844 A CN 108046844A CN 201711275996 A CN201711275996 A CN 201711275996A CN 108046844 A CN108046844 A CN 108046844A
- Authority
- CN
- China
- Prior art keywords
- glaze
- red copper
- preparation
- heating rate
- kiln
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of red copper glaze and preparation method thereof, its technical recipe is calculated by mass percentage, is made of lithium feldspar powder 54 67%, talcum 4 11%, kaolin 3 11%, zinc oxide 1 4%, barium carbonate 2 6%, quartz 5 10%, potassium feldspar 1 6%, iron oxide 2 5%.Its preparation method is:It is sufficiently mixed and is added in grinding pot after component is weighed by formula, it adds in and is equivalent to 45% 50% moisture of dry powder weight and is ground, the concentration of glaze slip of milled is adjusted to 48 ± 1 degree of true specific gravity, with glaze spraying gimmick glazing on green body, ground-coat enamel glazed thickness 1mm 1.5mm, it is burnt till again into carrying out oxidation with 1230 DEG C 1250 DEG C of temperature in kiln after drying, the most kiln discharge after natural cooling afterwards, it is colour-stable that glaze is made, glaze paint dumb light, the red copper glaze of high yield rate obtains the red copper glaze of impermeable, the resistance to rapid heat cycle of product made from the glaze.
Description
Technical field
The present invention relates to glaze preparation fields more particularly to a kind of red copper glaze and preparation method thereof.
Background technology
Red copper glaze is super-low expansion glaze, and exclusive cooperation low bulk green body uses.At present, substantial amounts of thermal-resisting ceramic vessel,
It is light glaze in pot class product;And this kind of ceramic pot, pot class product are after the medium for extended time such as storage water, it may appear that infiltration
Situations such as, unstable product quality.For this purpose, a kind of impermeable and glaze paint dumb light the low expansion ceramic glaze of exploitation is existing market
Blank.
The content of the invention
Therefore, for it is above-mentioned the problem of, present invention aims at provide a kind of red copper glaze and preparation method thereof, the red copper glaze
Glaze is colour-stable, glaze paint dumb light, high yield rate so that product obtained is impermeable, resistance to rapid heat cycle.
To achieve these goals, the technical solution adopted in the present invention is:
A kind of red copper glaze, technical recipe are calculated by mass percentage, are made of following component with content:Lithium feldspar powder 54-67%,
Talcum 4-11%, kaolin 3-11%, zinc oxide 1-4%, barium carbonate 2-6%, quartz 5-10%, potassium feldspar 1-6%, iron oxide 2-5%.
The present invention breaches the limitation of traditional glaze, the adjustment being made up of glaze, and the obtained coefficient of expansion is low, heat impact strength is good
The good, glaze of glaze paint dumb light;And the glaze and the good combination of green body, product are impermeable.
Another object of the present invention is to provide a kind of preparation method of above-mentioned red copper glaze, each component is weighed by formula
After be sufficiently mixed add in grinding pot in, add in be equivalent to dry powder weight 45%-50% moisture be ground 12-15 it is small when,
Middle material:Ball:Water ratio is 1:1.5:0.65, the good concentration of glaze slip of ball milling is then adjusted to 48 ± 1 degree of true specific gravity, hand is decorated with glaze spraying
Method glazing is on green body, glazed thickness 1mm -1.5mm, again into carrying out 8-11 with 1230 DEG C -1250 DEG C of temperature in kiln after drying
The oxidation of hour is burnt till, the kiln discharge after natural cooling, and the red copper glaze is made.
As one of above-mentioned preparation method preferred embodiment, when adding water grinding 12-15 small after carry out testing graininess, granularity is surveyed
325 mesh sieves were tried, glaze slip screen over-size is in 0.1%-0.3%.
As one of above-mentioned preparation method preferred embodiment, the heating that the oxidation is burnt till is divided into three phases, first rank
Section:Room temperature controls 3 DEG C/min of heating rate, second stage to 650 DEG C:650-1050 DEG C, 3.5 DEG C of heating rate of control/
Min, three phases:1050-1250 DEG C, 2 DEG C/min of heating rate is controlled, until during maximum temperature, keeps the temperature 30min.
The principle that the present invention realizes is:The raw material for selecting spodumene, these coefficients of expansion of lithium feldspar low, by the body of glaze
The coefficient of expansion is controlled 100 × 10-7Within, make it that there is relatively uniform expansion character with green body;On this basis introduce magnesium,
The materials such as barium, zinc are adjusted, and realize magnesium-aluminium-silicon three-phase congruent melting, and glaze water is enable to be melted at 1230-1250 DEG C, good with green body
With reference to product is made to reach impermeable effect;The addition of appropriate iron oxide can widen the firing range of glaze, improve high temperature and glue
The parameters such as degree, elasticity.In addition, by the control of green body water absorption rate below 3%, make glaze melting that can there is good knot with green body
It closes.By controlling the melting temperature of glaze, it is specially the reasonable sial proportioning of lithium minerals and clay minerals, is in glaze water and begins
Melt temperature range or so, to ensure glaze paint matte effect.
Specific embodiment
In order to which the purpose of the present invention, technical solution, good effect is more clearly understood, by following embodiment to this hair
It is bright to be further elaborated.Description below for specific embodiment is only used for explaining the present invention, does not limit this hair
It is bright.
In addition, except illustrating, percentage of the present invention is mass percent.
Embodiment 1
A kind of red copper glaze, technical recipe are calculated by mass percentage, are made of following component with content:Lithium feldspar powder 56%, talcum
11%th, kaolin 10%, zinc oxide 3%, barium carbonate 2%, quartz 8%, potassium feldspar 5%, iron oxide 5%.
It is sufficiently mixed and is added in grinding pot after each component is weighed by above-mentioned formula, addition is equivalent to dry powder weight
45%-50% moisture be ground 12 it is small when, wherein expecting:Ball:Water ratio is 1:1.5:0.65, it is 325 sieve to glaze using number
Slurry is filtered, then the good concentration of glaze slip of ball milling is adjusted to concentration as true specific gravity by the residue rate tailed over subject to 0.1%-0.3%
48 ± 1 degree, glaze slip is sprayed on using glaze spraying gimmick in billet surface, goes out glaze and nebulizes, glazed thickness 1mm-1.5mm, after drying
Again into kiln with 1230 DEG C -1250 DEG C of temperature carry out 8 it is small when oxidation burn till, wherein, the heating which burns till is divided into three
A stage, first stage:Room temperature controls 3 DEG C/min of heating rate, second stage to 650 DEG C:650-1050 DEG C, control
3.5 DEG C/min of heating rate, three phases:1050-1250 DEG C, 2 DEG C/min of heating rate is controlled, until during maximum temperature, is protected
Warm 30min, then the kiln discharge after natural cooling, is made red copper glaze.
Embodiment 2
A kind of red copper glaze, technical recipe are calculated by mass percentage, are made of following component with content:Lithium feldspar powder 63%, talcum
9%th, kaolin 9%, zinc oxide 1%, barium carbonate 4%, quartz 9%, potassium feldspar 2%, iron oxide 3%.
It is sufficiently mixed and is added in grinding pot after each component is weighed by above-mentioned formula, addition is equivalent to dry powder weight
45%-50% moisture be ground 13 it is small when, wherein expecting:Ball:Water ratio is 1:1.5:0.65, it is 325 sieve to glaze using number
Slurry is filtered, then the good concentration of glaze slip of ball milling is adjusted to concentration as true specific gravity by the residue rate tailed over subject to 0.1%-0.3%
48 ± 1 degree, glaze slip is sprayed on using glaze spraying gimmick in billet surface, goes out glaze and nebulizes, glazed thickness 1mm-1.5mm, after drying
Again into kiln with 1230 DEG C -1250 DEG C of temperature carry out 10 it is small when oxidation burn till, wherein, the heating which burns till is divided into three
A stage, first stage:Room temperature controls 3 DEG C/min of heating rate, second stage to 650 DEG C:650-1050 DEG C, control
3.5 DEG C/min of heating rate, three phases:1050-1250 DEG C, 2 DEG C/min of heating rate is controlled, until during maximum temperature, is protected
Warm 30min, then the kiln discharge after natural cooling, is made red copper glaze.
Embodiment 3
A kind of red copper glaze, technical recipe are calculated by mass percentage, are made of following component with content:Lithium feldspar powder 67%, talcum
6%th, kaolin 6%, zinc oxide 2%, barium carbonate 5%, quartz 7%, potassium feldspar 3%, iron oxide 4%.
It is sufficiently mixed and is added in grinding pot after each component is weighed by above-mentioned formula, addition is equivalent to dry powder weight
45%-50% moisture be ground 15 it is small when, wherein expecting:Ball:Water ratio is 1:1.5:0.65, it is 325 sieve to glaze using number
Slurry is filtered, then the good concentration of glaze slip of ball milling is adjusted to concentration as true specific gravity by the residue rate tailed over subject to 0.1%-0.3%
48 ± 1 degree, glaze slip is sprayed on using glaze spraying gimmick in billet surface, goes out glaze and nebulizes, glazed thickness 1mm-1.5mm, after drying
Again into kiln with 1230 DEG C -1250 DEG C of temperature carry out 11 it is small when oxidation burn till, wherein, the heating which burns till is divided into three
A stage, first stage:Room temperature controls 3 DEG C/min of heating rate, second stage to 650 DEG C:650-1050 DEG C, control
3.5 DEG C/min of heating rate, three phases:1050-1250 DEG C, 2 DEG C/min of heating rate is controlled, until during maximum temperature, is protected
Warm 30min, then the kiln discharge after natural cooling, is made red copper glaze.
Colour-stable, the glaze paint dumb light using red copper glaze glaze made from the formula described in above-described embodiment 1-3 and preparation method, into
Product rate is high so that product obtained is impermeable, resistance to rapid heat cycle.
The above described is only a preferred embodiment of the present invention, it is not intended to limit the scope of the present invention
For those skilled in the art, it is various corresponding to make other for technical solution that can be as described above and design
Change and deform, and all these change and deform the protection domain that should all belong to the claims in the present invention.
Claims (4)
1. a kind of red copper glaze, it is characterised in that:Its technical recipe is calculated by mass percentage, is made of following component with content:Lithium
Feldspar powder 54-67%, talcum 4-11%, kaolin 3-11%, zinc oxide 1-4%, barium carbonate 2-6%, quartz 5-10%, potassium feldspar 1-
6%th, iron oxide 2-5%.
2. a kind of preparation method of red copper glaze as described in claim 1, which is characterized in that filled after each component is weighed by formula
Point mixing add in grinding pot in, add in be equivalent to dry powder weight 45%-50% moisture be ground 12-15 it is small when, wherein expecting:
Ball:Water ratio is 1:1.5:0.65, the good concentration of glaze slip of ball milling is then adjusted to 48 ± 1 degree of true specific gravity, is applied with glaze spraying decoration technique
Glaze is on green body, glazed thickness 1mm-1.5mm, after drying again into kiln with 1230 DEG C -1250 DEG C of temperature carry out 8-11 it is small when
Oxidation burn till, the kiln discharge after natural cooling, be made the red copper glaze.
3. a kind of preparation method of red copper glaze as claimed in claim 2, it is characterised in that:After when adding water grinding 12-15 small
Testing graininess is carried out, testing graininess crosses 325 mesh sieves, and glaze slip screen over-size is in 0.1%-0.3%.
4. a kind of preparation method of red copper glaze as claimed in claim 2, it is characterised in that:The heating that the oxidation is burnt till is divided into
Three phases, first stage:Room temperature controls 3 DEG C/min of heating rate, second stage to 650 DEG C:650-1050 DEG C, control
3.5 DEG C/min of heating rate processed, three phases:1050-1250 DEG C, 2 DEG C/min of heating rate is controlled, until during maximum temperature,
Keep the temperature 30min.