CN108033766A - A kind of production method of boccaro hometown - Google Patents
A kind of production method of boccaro hometown Download PDFInfo
- Publication number
- CN108033766A CN108033766A CN201711155626.XA CN201711155626A CN108033766A CN 108033766 A CN108033766 A CN 108033766A CN 201711155626 A CN201711155626 A CN 201711155626A CN 108033766 A CN108033766 A CN 108033766A
- Authority
- CN
- China
- Prior art keywords
- clay
- boccaro
- mud
- red stone
- stone ware
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
A kind of production method of boccaro hometown, hard boccaro and soft boccaro raw ore are carried out first it is selected after, processing is eluriated, after filtering out aqueous 21% filter cake, again raw material hard Red Stone Ware, high-al clay, potassium feldspar, soft Red Stone Ware, magnesium soil, clay, spodumene enters ball mill processing respectively, be ground to 250 mesh 10000-hole sieves full by, drying, finally dispensing is carried out by formula ratio enter mill progress fine grinding again, fineness for 250 mesh 10000-hole sieves full by, add water that mud is made, then it is 21% mud cake the mud made to be pressed into moisture content with mud press, after aging 7 days, practiced more than 2 times with vacuum deairing machine, obtain purple clay section.Advantage is：Raw material sources are extensive, of low cost, good product quality, and cost is low, high efficiency, the purple casserole of firing, product thermostabilization is good, is heated to 460 DEG C and is put into 20 DEG C of cold water and exchanges do not burst three times, good heat conductivity, napkin paper is placed on the inside, and catching fire is on fire immediately, high mechanical strength.
Description
Technical field
The invention belongs to purple sand material field, a kind of more particularly to improved on the basis of traditional purple clay develops
The production method of the new boccaro hometown for aiming at daily marmite come.
Background technology
Boccaro is a kind of ceramic between pottery and porcelain, and red stoneware product is with a long history, various in style, it is special
Point is compact structure, and larger close to porcelain, intensity, particle is tiny, and fracture is conchoidal or stone shape.Boccaro ware not rest, but
Mud true qualities are made full use of, burn till that rear color and luster is gentle, and quaint honest, boccaro ware face also has matt effect, can both weaken luminous energy
Reflection, and implements form, the dramatic effects of decoration and itself natural colored can be clearly showed, liked deeply by people as craftwork
Love.Purple casserole is the metal material and chemistry that harmful health can be got rid of using high-quality natural boccaro Seiko ceramic liner
Coating, is perfectly safe human body harmless.But arrive the purple that soup-stock there is presently no high heat-resisting and high thermal stability, is done suitable for specialty
The purple sand pug of marmite.
The content of the invention
The technical problem to be solved in the present invention is to provide a kind of production method of boccaro hometown, which is used to make
Boccaro marmite, product thermostabilization is good, good heat conductivity, high mechanical strength.
A kind of production method of boccaro hometown, it is comprised the following steps that：
Pug formula weight percent forms：
Hard Red Stone Ware：32% -50%, high-al clay：10% -20%, potassium feldspar：2.2% -8%, soft Red Stone Ware：
10% -20%, magnesium soil：5% -10%, clay：5% -10%, spodumene：5% -10%；
Pug makes procedure of processing：
Hard boccaro and soft boccaro raw ore are carried out first it is selected after, after aqueous 21% filter cake is eluriated, filtered out in processing, then
Raw material hard Red Stone Ware, high-al clay, potassium feldspar, soft Red Stone Ware, magnesium soil, clay, spodumene enter ball mill processing, mill respectively
To 250 mesh 10000-hole sieves full by drying is spare, and finally carrying out dispensing by formula ratio again enters mill progress fine grinding, and fineness is 250 mesh
10000-hole sieve full by, add water that mud is made, it is 21% mud cake that the mud made, which is then pressed into moisture content, with mud press, aging 7
After it, practiced more than 2 times with vacuum deairing machine, obtain purple clay section.
Further, pug formula weight percent composition is：Rigid Red Stone Ware：38.5%th, soft Red Stone Ware：19.8%th,
High-al clay：15.3%th, potassium feldspar：2.2%th, ripe magnesium soil：8.1%th, clay：8.3%th, spodumene：7.8%.
Beneficial effects of the present invention：
Raw material sources are extensive, of low cost, and good product quality, cost is low, high efficiency, and the purple casserole of firing, product thermostabilization is good,
It is heated to 460 degree and is put into 20 degree of cold water and exchanges do not burst three times, napkin paper, is placed on the inside catching fire immediately by good heat conductivity
It is on fire, high mechanical strength.The chemical composition range of boccaro hometown (purple clay section) product：SiO2：45% -65%, Al2O3：
20% -35%, Fe2O3：6% -9%, MgO：3% -6%, CaO：1.5% -3%, Li2O：1% -2%, burn and lose:3%-
6%.
Embodiment
Embodiment 1
Boccaro hometown formula：Rigid Red Stone Ware：38.5kg, soft Red Stone Ware：19.8kg, high-al clay：15.3kg, potassium feldspar：
2.2kg, ripe magnesium soil：8.1kg, clay：8.3kg, spodumene：7.8kg；
Pug makes procedure of processing：
Hard boccaro and soft boccaro raw ore are carried out first it is selected after, after aqueous 21% filter cake is eluriated, filtered out in processing, then
Raw material hard Red Stone Ware, high-al clay, potassium feldspar, soft Red Stone Ware, magnesium soil, clay, spodumene enter ball mill processing, mill respectively
To 250 mesh 10000-hole sieves full by drying is spare, and finally carrying out dispensing by formula ratio again enters mill progress fine grinding, and fineness is 250 mesh
10000-hole sieve full by, add water that mud is made, it is 21% mud cake that the mud made, which is then pressed into moisture content, with mud press, aging 7
After it, practiced more than 2 times with vacuum deairing machine, obtain purple clay section.
Embodiment 2
Boccaro hometown formula：Hard Red Stone Ware：32kg, high-al clay：20kg, potassium feldspar：8kg, soft Red Stone Ware：It is 15kg, magnesia
Soil：10kg, clay：10kg, spodumene：5kg；
Pug makes procedure of processing：
Hard boccaro and soft boccaro raw ore are carried out first it is selected after, after aqueous 21% filter cake is eluriated, filtered out in processing, then
Raw material hard Red Stone Ware, high-al clay, potassium feldspar, soft Red Stone Ware, magnesium soil, clay, spodumene enter ball mill processing, mill respectively
To 250 mesh 10000-hole sieves full by drying is spare, and finally carrying out dispensing by formula ratio again enters mill progress fine grinding, and fineness is 250 mesh
10000-hole sieve full by, add water that mud is made, it is 21% mud cake that the mud made, which is then pressed into moisture content, with mud press, aging 7
After it, practiced more than 2 times with vacuum deairing machine, obtain purple clay section.
Embodiment 3
Boccaro hometown formula：Hard Red Stone Ware：50kg, high-al clay：10kg, potassium feldspar：7kg, soft Red Stone Ware：It is 13kg, magnesia
Soil：5kg, clay：5kg, spodumene：10kg；
Pug makes procedure of processing：
Hard boccaro and soft boccaro raw ore are carried out first it is selected after, after aqueous 21% filter cake is eluriated, filtered out in processing, then
Raw material hard Red Stone Ware, high-al clay, potassium feldspar, soft Red Stone Ware, magnesium soil, clay, spodumene enter ball mill processing, mill respectively
To 250 mesh 10000-hole sieves full by drying is spare, and finally carrying out dispensing by formula ratio again enters mill progress fine grinding, and fineness is 250 mesh
10000-hole sieve full by, add water that mud is made, it is 21% mud cake that the mud made, which is then pressed into moisture content, with mud press, aging 7
After it, practiced more than 2 times with vacuum deairing machine, obtain purple clay section.
The chemical composition range of boccaro hometown (purple clay section) product of 1- of embodiment of the present invention embodiments 3：SiO2：
45% -65%, Al2O3：20% -35%, Fe2O3：6% -9%, MgO：3% -6%, CaO：1.5% -3%, Li2O：
1% -2%, burn and lose:3% -6%.
The performance indicator of the product mud of the embodiment of the present invention 1：
1、SiO2：64%th, Al2O3：23%th, Fe2O3：6.58%th, MgO：3%th, CaO：1.6%th, Li2O：1%th, K2O：0.31、
TiO2：0.5%th, NaO：0.02%.
2nd, plastic index is：Mud speed rate≤100 second；Proportion, proportion 1.75T/m are measured with Baume3；
3rd, compression strength >=4.5 (Mpa), plasticity index >=5.5 (kg.cm).
The purple clay section of the embodiment of the present invention 1 is burnt till into purple casserole, firing temperature is 1280 DEG C.Obtained product thermostabilization
Property it is good, be heated to 460 degree and be put into 20 degree of cold water and exchange do not burst three times, and napkin paper is placed on the inside catching fire rises immediately
Fire, high mechanical strength.
It these are only the specific embodiment of the present invention, be not intended to limit the invention, for those skilled in the art
For member, the invention may be variously modified and varied.Any modification within the spirit and principles of the invention, being made,
Equivalent substitution, improvement etc., should all be included in the protection scope of the present invention.
Claims (2)
1. a kind of production method of boccaro hometown, it is characterized in that：
Pug formula weight percent forms：
Hard Red Stone Ware：32% -50%, high-al clay：10% -20%, potassium feldspar：2.2% -8%, soft Red Stone Ware：
10% -20%, magnesium soil：5% -10%, clay：5% -10%, spodumene：5% -10%；
Pug makes procedure of processing：
Hard boccaro and soft boccaro raw ore are carried out first it is selected after, after aqueous 21% filter cake is eluriated, filtered out in processing, then
Raw material hard Red Stone Ware, high-al clay, potassium feldspar, soft Red Stone Ware, magnesium soil, clay, spodumene enter ball mill processing, mill respectively
To 250 mesh 10000-hole sieves full by drying is spare, and finally carrying out dispensing by formula ratio again enters mill progress fine grinding, and fineness is 250 mesh
10000-hole sieve full by, add water that mud is made, it is 21% mud cake that the mud made, which is then pressed into moisture content, with mud press, aging 7
After it, practiced more than 2 times with vacuum deairing machine, obtain purple clay section.
2. the production method of the boccaro hometown according to claim, it is characterized in that：Pug formula weight percent forms：Firmly
Property Red Stone Ware：38.5%th, soft Red Stone Ware：19.8%th, high-al clay：15.3%th, potassium feldspar：2.2%th, ripe magnesium soil：8.1%th,
Clay：8.3%th, spodumene：7.8%.