CN108016204A - A kind of preparation process of PP building materials and ornaments film - Google Patents
A kind of preparation process of PP building materials and ornaments film Download PDFInfo
- Publication number
- CN108016204A CN108016204A CN201711248672.4A CN201711248672A CN108016204A CN 108016204 A CN108016204 A CN 108016204A CN 201711248672 A CN201711248672 A CN 201711248672A CN 108016204 A CN108016204 A CN 108016204A
- Authority
- CN
- China
- Prior art keywords
- printing
- building materials
- maturation
- prepared
- priemr
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of preparation process of PP building materials and ornaments film, include the following steps：PRIMER inorganic agents dispensing, printing surface treatment, maturation, printing ink inorganic agent dispensing, decorative pattern printing, bottom surface processing, maturation, detection.A kind of preparation process of disclosed PP building materials and ornaments film, one layer of PP adhesive plaster is selected to carry out printing treatment to its surface, using five layers of printing form, and last two layers is selected bright face and cloudy surface to present a contrast, so as to be formed with relief effect of decorative patterns, compared to the PP building materials of two layers traditional of fitting form, it is few with material, cost is low, and overall texture is strong, and solid layer feeling is good.
Description
Technical field
The present invention relates to a kind of building materials and ornaments film, and in particular to a kind of preparation process of PP building materials and ornaments film.
Background technology
Building film material material is the New Building Materials to grow up from the 1970s, belongs to the coating in field of textiles
Fabric, is the 5th kind of construction material after steel, cement, timber and glass, it can have in existing building materials application
Difficult field, it is such as large-scale or ultra-large type is built and used without pillar, the incomparable superiority of traditional building material is provided with,
Expand the application range of construction material.It has moulding light and handy freedom, beauty, printing opacity, energy-saving and environmental protection, excellent anti-flammability
Energy, anti-fouling and self-cleaning performance, the advantages that safe life is long, it is widely used in coliseum mainly as semipermanent construction material
The buildings such as shop, shopping field, show ground, entrance gallery, public place of entertainment, parking lot, plant sightseeing dome and gas station.Due to 2008
Year Beijing Olympic Games stadiums " Bird's Nest " etc. successfully build up and come into operation, and Shanghai World's Fairs in 2010 and construction of Guangzhou Asian Games stadiums
The distinguished gathering of the Hui Deng worlds is held, and the development of membrane material at home has come into a rapid growth period.Membrane material is building film knot
The key of structure, and China's research and application are started late, technical merit is relatively low, and most of membrane material also relies primarily on import.
Generally it is leading using PVC in building materials film at home, it does not have three-dimensional sense, and overall texture is poor, does not apply to high want
The building demand asked.
The content of the invention
Goal of the invention：The purpose of the invention is to make up the deficiencies in the prior art, there is provided a kind of PP building materials and ornaments film
Preparation process, using PP as the leading building materials film formed, overall texture is strong, and level is good and three-dimensional sense is strong.
Technical solution：A kind of preparation process of PP building materials and ornaments film, includes the following steps：
A, PRIMER inorganic agents dispensing：Surface conditioning agent PRIEMR and ethyl acetate solvent are pressed 1:1 is prepared, and is used
Pneumatic blender is stirred 10 15min with 150 200r/min speed, until PRIEMR treatment fluids are uniformly without muddiness；
B, surface treatment is printed：Use printing machine that the prepared PRIEMR treatment fluids of step a are printed in PP blanket surfaces with 100 mesh
On, print speed printing speed 60-80m/min, is then put into baking oven dry 10 20s at 40 50 DEG C by the PP adhesive plasters printed；
C, maturation：Processed good PP adhesive plasters are positioned over ripening chamber, 48 72h of maturation at a temperature of 30 50 DEG C；
D, printing ink inorganic agent dispensing：By red, yellow, blue, polishes and ethyl acetate solvent, according to 2:3:1:4:2 ratios are added to print
In black bucket, 10 15min are stirred to prepare printing ink inorganic agent with 150 200r/min rotating speeds, the printing ink inorganic agent of preparation disperses
Uniformly, no loose colour；
E, decorative pattern prints：Using printing machine by prepared printing ink inorganic agent, decorative pattern printing is carried out using five version printing modes, its
Middle fourth edition carries out bright face printing, the 5th edition progress cloudy surface printing, and bright mist contrast forms the three-dimensional sense of decorative pattern, print speed printing speed 60
~ 80m/min, oven for drying is sent into after printing, and it is 40 ~ 50 DEG C to control oven temperature；.
F, bottom surface is handled：Use printing machine that the prepared PRIEMR treatment fluids of step a are printed in PP adhesive plasters bottom with 100 mesh
On face, baking oven dry 10 20s at 40 50 DEG C are then placed in；
G, maturation：Processed good PP adhesive plasters are positioned over ripening chamber, maturation 48h obtains PP building materials dress at a temperature of 30 50 DEG C
Adorn film finished product；
H, detect：The finished product prepared to step g judges whether to take off with the inking intensity of tape-stripping test top layer printing ink
Ink.
Beneficial effect：A kind of preparation process of disclosed PP building materials and ornaments film, selects one layer of PP adhesive plaster to it
Surface carries out printing treatment, and using five layers of printing form, and last two layers is selected bright face and cloudy surface to present a contrast, so as to be formed
With relief effect of decorative patterns, compared to the PP building materials of two layers traditional of fitting form, it is few with material, and cost is low, and overall matter
Sense is strong, and solid layer feeling is good.
Embodiment
With reference to specific embodiment, the invention will be further described：
A kind of preparation process of disclosed PP building materials and ornaments film, includes the following steps：
A, PRIMER inorganic agents dispensing：Surface conditioning agent PRIEMR and ethyl acetate solvent are pressed 1:1 is prepared, and is used
Pneumatic blender is stirred 10 15min with 150 200r/min speed, until PRIEMR treatment fluids are uniformly without muddiness；
B, surface treatment is printed：Use printing machine that the prepared PRIEMR treatment fluids of step a are printed in PP blanket surfaces with 100 mesh
On, print speed printing speed 60-80m/min, is then put into baking oven dry 10 20s at 40 50 DEG C by the PP adhesive plasters printed；
C, maturation：Processed good PP adhesive plasters are positioned over ripening chamber, 48 72h of maturation at a temperature of 30 50 DEG C；
D, printing ink inorganic agent dispensing：By red, yellow, blue, polishes and ethyl acetate solvent, according to 2:3:1:4:2 ratios are added to print
In black bucket, 10 15min are stirred to prepare printing ink inorganic agent with 150 200r/min rotating speeds, the printing ink inorganic agent of preparation disperses
Uniformly, no loose colour；
E, decorative pattern prints：Using printing machine by prepared printing ink inorganic agent, decorative pattern printing is carried out using five version printing modes, its
Middle fourth edition carries out bright face printing, the 5th edition progress cloudy surface printing, and bright mist contrast forms the three-dimensional sense of decorative pattern, print speed printing speed 60
~ 80m/min, oven for drying is sent into after printing, and it is 40 ~ 50 DEG C to control oven temperature；.
F, bottom surface is handled：Use printing machine that the prepared PRIEMR treatment fluids of step a are printed in PP adhesive plasters bottom with 100 mesh
On face, baking oven dry 10 20s at 40 50 DEG C are then placed in；
G, maturation：Processed good PP adhesive plasters are positioned over ripening chamber, maturation 48h obtains PP building materials dress at a temperature of 30 50 DEG C
Adorn film finished product；
H, detect：The finished product prepared to step g judges whether to take off with the inking intensity of tape-stripping test top layer printing ink
Ink.
The above is only the preferred embodiment of the present invention, it is noted that for the ordinary skill people of the art
For member, without departing from the technical principles of the invention, some improvements and modifications can also be made, these improvements and modifications
Also it should be regarded as protection scope of the present invention.
Claims (1)
1. a kind of preparation process of PP building materials and ornaments film, it is characterised in that include the following steps：
A, PRIMER inorganic agents dispensing：Surface conditioning agent PRIEMR and ethyl acetate solvent are pressed 1:1 is prepared, and is used
Pneumatic blender is stirred 10 15min with 150 200r/min speed, until PRIEMR treatment fluids are uniformly without muddiness；
B, surface treatment is printed：Use printing machine that the prepared PRIEMR treatment fluids of step a are printed in PP blanket surfaces with 100 mesh
On, print speed printing speed 60-80m/min, is then put into baking oven dry 10 20s at 40 50 DEG C by the PP adhesive plasters printed；
C, maturation：Processed good PP adhesive plasters are positioned over ripening chamber, 48 72h of maturation at a temperature of 30 50 DEG C；
D, printing ink inorganic agent dispensing：By red, yellow, blue, polishes and ethyl acetate solvent, according to 2:3:1:4:2 ratios are added to print
In black bucket, 10 15min are stirred to prepare printing ink inorganic agent with 150 200r/min rotating speeds, the printing ink inorganic agent of preparation disperses
Uniformly, no loose colour；
E, decorative pattern prints：Using printing machine by prepared printing ink inorganic agent, decorative pattern printing is carried out using five version printing modes, its
Middle fourth edition carries out bright face printing, and the 5th edition progress cloudy surface printing, print speed printing speed is 60 ~ 80m/min, and baking oven is sent into after printing and is dried
Dry, it is 40 ~ 50 DEG C to control oven temperature；
F, bottom surface is handled：Use printing machine that the prepared PRIEMR treatment fluids of step a are printed in PP adhesive plasters bottom surface with 100 mesh
On, it is then placed in baking oven dry 10 20s at 40 50 DEG C；
G, maturation：Processed good PP adhesive plasters are positioned over ripening chamber, maturation 48h obtains PP building materials dress at a temperature of 30 50 DEG C
Adorn film finished product；
H, detect：The finished product prepared to step g judges whether to take off with the inking intensity of tape-stripping test top layer printing ink
Ink.