CN107867820A - A kind of manufacture craft of boccaro iron sand kettle - Google Patents
A kind of manufacture craft of boccaro iron sand kettle Download PDFInfo
- Publication number
- CN107867820A CN107867820A CN201610864129.6A CN201610864129A CN107867820A CN 107867820 A CN107867820 A CN 107867820A CN 201610864129 A CN201610864129 A CN 201610864129A CN 107867820 A CN107867820 A CN 107867820A
- Authority
- CN
- China
- Prior art keywords
- boccaro
- kettle
- iron sand
- base substrate
- bottle body
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
A kind of manufacture craft of boccaro iron sand kettle, it is main made using bottle body base substrate, kettle base substrate annex is made, bottle body ornament annex makes, kettle base substrate installation, kettle are completed the step of burning till, pass through the improvement to traditional dark-red enameled pottery manufacture craft, and selection uses special boccaro orpiment gold mud material, not only iron-holder is high for boccaro iron sand kettle made of making, heat conduction and extremely efficient in preserving heat, and the boccaro iron sand kettle is during to boil water, iron ion and a variety of dimension secondary elements can be discharged, and plays demineralized water and brings healthcare function.After being made tea by using boccaro iron sand kettle, perfume is neither lost, is unlikely to deteriorate, good permeability, and without ripe soup smell road, can also adsorbed tealeaves, durable excellent performance, retain tealeaves fragrance time length.The features such as boccaro iron sand kettle also has impurities few simultaneously, non-corrosive, easily cleans, and texture is strong.
Description
Technical field
The invention belongs to ceramic purple sand industry field, specific to using the making of boccaro orpiment gold mud material and decoration dark-red enameled pottery
Method, and provide a kind of boccaro iron sand kettle manufacture craft.
Background technology
Ceramic tea-pot is since the Ming and Qing times produce, to having there is centuries history at present, particularly in south China
Gradually come into vogue the custom made tea with teapot in area, and earthenware pot of Yixing has the reality of " neither taking perfume (or spice) by force, and without ripe soup gas " because of it
The main apparatus drunk tea is suddenly become with advantage.Dark-red enameled pottery, which not only has to make tea, cooks the practical value of perfume, while due also to its mud
Special fastidious, the exquisite careful, profile of workmanship of material does not fawn that original, intension is mild and roundabout implicit, and is used as a kind of handicraft to have one yet
Fixed practicality and the value of collection.From the eighties, dark-red enameled pottery just turns into recourse both at home and abroad and seeks one of handicraft of Tibetan.
Dark-red enameled pottery can substantially be divided into " light goods " and " flower goods " from profile.And " light goods " dark-red enameled pottery in general its moulding phase
To simple, pug is single, but does manual work and require high, " flower goods " dark-red enameled pottery be on the basis of " light goods " dark-red enameled pottery, it is more by using
Kind purple sand pug is decorated, and can be fabricated to a variety of dark-red enameled pottery of many different pattern shapes, color, particularly can be nature
Many such as pines, bamboo, plum, melon and fruit, animal all embody and incorporated in dark-red enameled pottery works in boundary, and this is also what dark-red enameled pottery was worth
Key point.The pug for being first dark-red enameled pottery is basic, and only good pug can just produce high-quality product, therefore select
Reliable in quality, pug are pure, add purple sand pug made of chemical industry pigment white silk without any.Next to that one dark-red enameled pottery will be passed through it is several
Ten procedures up to a hundred.Only road procedure is elaborated, and just kettle can be made snugly to embody the gentle of purple clay, can just be made
The basis of " shape have fastidious ", can just make " money " and " work(" of different dark-red enameled potteries have be compared to each other it is basic.Good dark-red enameled pottery
Stream except kettle, button, lid, shoulder, abdomen, ring foot should coordinate with bottle body overall ratio outer, the transition of point, line, surface is transferred also very
It is important.The molding decorative of dark-red enameled pottery is also particularly significant again, between the various natural pugs particularly used on dark-red enameled pottery
Colour match, the selection of various modelling patterns, the factor such as size of size, also all determine the attractive in appearance of dark-red enameled pottery and appreciate
Value and reserve value.
The making of dark-red enameled pottery is made the transition from traditional works to high-end works at present, and the pug of dark-red enameled pottery also has common pug
Develop to high-quality pug.Particularly the selection of pug, the making of dark-red enameled pottery have begun to focus on green, beneficial health guarantor
The development of strong aspect, this is also the inevitable development trend of boccaro from now on.
The content of the invention
The purpose of the present invention is the above-mentioned deficiency for existing dark-red enameled pottery technology, there is provided a kind of boccaro iron sand kettle
Manufacture craft.
The manufacture craft of the present invention is realized using following technical scheme：
A kind of manufacture craft of boccaro iron sand kettle, comprises the following steps：
(1) boccaro iron sand bottle body base substrate makes：First the boccaro orpiment gold mud material bought is put into cylinder, and covered on pug
Film paper makes its old more than 15 days, reach mud it is substantially stabilized after, then take out boccaro orpiment gold mud material, slice is repeatedly equal
It is even to pat to 4mm thickness, and 15-20 minutes are put only, further according to the size specification of done boccaro iron sand kettle, first measured, afterwards handle
The type of breaking into is patted with plastics while slice rolls, cut off unnecessary portion, finally bright got up with kettle processed is special for beating
Bottle body base substrate polish in repairing, wait after putting 30 minutes only, then carry out second of polishing sizing.
(2) making of boccaro iron sand kettle base substrate annex：Respectively the spout of a teapot to be made, and lid pug be placed on model
It is interior, boccaro iron sand kettle base substrate annex is obtained by way of extruding, is then repaired spout of a teapot, the base substrate annex with lid
Polishing.
(3) making of boccaro iron sand bottle body ornament annex：For the ornament base substrate needed in boccaro iron sand bottle body, divide
Not according to the moulding for proposing meter, such as pine, bamboo, plum, melon and fruit, first pug is put into the mould of ornament, passes through the side of extruding
Formula obtains the base substrate annex of boccaro iron sand kettle ornament, then such as pine of needs, bamboo, plum, melon and fruit base substrate annex are repaired
Polishing, wait after putting 40 minutes only, carry out second of polishing sizing.Put only again after drying 120 minutes, then according to it is required not
Tinted with green mud, yellow mud, red soil with color, then after putting 180 minutes and drying only, tinted for the second time i.e. available respectively
Boccaro iron sand kettle ornament annex.
(4) installation of boccaro iron sand kettle base substrate：The connection method of spout base substrate and bottle body base substrate, using identical kettle pug processed
Mud be formed by connecting, and connected in connection using 35-45 degree slope angle, it is special bright with kettle processed after 1.5-3 hours to be dried
Pin reparation, after wait dries 1 hour, then carry out second of polishing sizing.The ornament annex of bottle body equally selects identical pug
Mud be formed by connecting, and pass through it is secondary repairing polishing sizing.
(5) boccaro iron sand kettle is burnt till：Before teapot base substrate is burnt till, first teapot is put into and dried in the air under indoor 20-25 DEG C of normal temperature
Dry 5-8 hours, then iron sand kettle is placed in the drying room that temperature is 60-80 DEG C and dries 5-7 hours, make teapot enter klining into when due to
The temperature difference is not in fission, then teapot base substrate is sent into kiln, slowly risen between 10%-12% by its moisture control
Between warm to 150 DEG C -180 DEG C, after being incubated 2-3 hours, then temperature is stepped up, maximum temperature is controlled at 1180 DEG C -1250 DEG C
Between, then progressively cool, just taken out after stopping 2 hours again when dropping to 100 DEG C, then when starting to cool to 50 DEG C or so needed for
The boccaro iron sand kettle of finished product.
Wherein, the position of the spout of a teapot opening described in step (3) is preferably in 1/3 high -2/3 eminence of bottle body.
First base substrate is progressively dried before described step (4), general 48-60 hours in winter, hour summer 36-48, the spring
Autumn is 40 hours.Teapot is so can ensure that when burning till certain plasticity, and yield rate is higher.Rear pot lid is burnt till all may be used
It is any to exchange orientation, can be with pot mouth kissing, the quasi- seam of lid is tight, and space (or displacement tolerance) therebetween is in 0.3mm
Within.
For avoid between pot lid and bottle body occur lose circle or bore it is wide the defects of, using first complete bottle body making, especially
It is the general requirement for using pot lid base substrate size 0.3mm bigger than pot mouth base substrate, when drying on the coincideing of pot mouth and pot lid
First pot lid base substrate is placed on the pot mouth of bottle body base substrate, this is due to the shrinkage factor of the bottle body base substrate original bigger than pot lid base substrate
Cause, so reach and circle is neither lost after lid is put up and there can not be loose requirement.
A kind of manufacture craft of boccaro iron sand kettle of the present invention, described step (1) are making boccaro iron sand kettle
During circle kettle shape, the egative film and bottle body of bottle body are using the method for forming is patted, and when making boccaro iron sand kettle quadrangular jar, its technique is using straight
Type connection method is connected into, when making boccaro iron sand kettle flower kettle, its technique is using branch's connection method of forming.
A kind of manufacture craft of boccaro iron sand kettle of the present invention, its material selection boccaro orpiment gold mud material make and
Into.
A kind of manufacture craft of boccaro iron sand kettle of the present invention, its boccaro iron sand bottle body ornament annex selected,
Such as pine, bamboo, plum, melon and fruit decoration pug color selection, using green mud, yellow mud, red soil, black mud as key colour, in specific color
During collocation application, all voluntarily configured according to works requirement by producer.
Beneficial effects of the present invention
The present invention uses special boccaro orpiment gold mud material by the improvement to traditional dark-red enameled pottery manufacture craft, and selection,
Not only iron-holder is high for boccaro iron sand kettle made of making, heat conduction and extremely efficient in preserving heat, and the boccaro iron sand kettle is during to boil water, energy
Iron ion and a variety of dimension secondary elements are discharged, and plays demineralized water and brings healthcare function.By using boccaro iron sand Hu Pao
After tea, perfume is neither lost, is unlikely to deteriorate, good permeability, and without ripe soup smell road, can also adsorbed tealeaves, durable excellent performance, retain tea
The leaf fragrance time is grown.The features such as boccaro iron sand kettle also has impurities few simultaneously, non-corrosive, easily cleans, and texture is strong.
Embodiment
Embodiment 1
A kind of manufacture craft of boccaro iron sand kettle, specifically comprises the following steps：
(1) boccaro iron sand bottle body base substrate makes：First the boccaro orpiment gold mud material bought is put into cylinder, and covered on pug
Film paper makes its old 20 days, reach mud it is substantially stabilized after, then take out boccaro orpiment gold mud material, slice uniformly clapped repeatedly
Get to 4mm thickness, and put 15 minutes, further according to the size specification of done boccaro iron sand kettle, first measured only, after slice is rolled
The type of breaking into is patted with plastics while coming, cuts off unnecessary portion, it is finally special bright for patting the bottle body base of getting up with kettle processed
Body polished in repairing, waits after putting 30 minutes only, then carry out second of polishing sizing.
(2) making of boccaro iron sand kettle base substrate annex：Respectively the spout of a teapot to be made, and lid pug be placed on model
It is interior, boccaro iron sand kettle base substrate annex is obtained by way of extruding, is then repaired spout of a teapot, the base substrate annex with lid
Polishing.
(3) making of boccaro iron sand bottle body ornament annex：For the ornament base substrate needed in boccaro iron sand bottle body, divide
Not according to the moulding for proposing meter, such as pine, bamboo, plum, melon and fruit, first pug is put into the mould of ornament, passes through the side of extruding
Formula obtains the base substrate annex of boccaro iron sand kettle ornament, then such as pine of needs, bamboo, plum, melon and fruit base substrate annex are repaired
Polishing, wait after putting 40 minutes only, carry out second of polishing sizing.Put only again after drying 120 minutes, then according to it is required not
Tinted with green mud, yellow mud, red soil with color, then after putting 180 minutes and drying only, tinted for the second time i.e. available respectively
Boccaro iron sand kettle ornament annex.
(4) installation of boccaro iron sand kettle base substrate：The connection method of spout base substrate and bottle body base substrate, using identical kettle pug processed
Mud be formed by connecting, the position of spout of a teapot opening is selected in 1/3 eminence of bottle body, and in connection using 38 degree slope angles companies
Connect, with the special bright pin reparation of kettle processed after 2.2 hours to be dried, after wait dries 1 hour, then carry out second of polishing sizing.Kettle
The ornament annex of body is equally formed by connecting from the mud of identical pug, and passes through secondary repairing polishing sizing.
(5) boccaro iron sand kettle is burnt till：Before teapot base substrate is burnt till, first teapot is put into and dries 8 under indoor 20 DEG C of normal temperature
Hour, then it is that 5-7 hours are dried in 75 DEG C of drying room that iron sand kettle, which is placed on temperature, make teapot enter klining into when because the temperature difference will not
Fission, then teapot base substrate is sent into kiln 10% by its moisture control, be slowly warming up to 170 DEG C, insulation 2.5
After hour, then temperature is stepped up, maximum temperature is controlled at 1210 DEG C, then progressively cools, 2 are stopped again when dropping to 100 DEG C
After hour, then the just boccaro iron sand kettle of finished product needed for taking-up when starting to cool to 50 DEG C or so.
Embodiment 2
A kind of manufacture craft of boccaro iron sand kettle, specifically comprises the following steps：
(1) boccaro iron sand bottle body base substrate makes：First the boccaro orpiment gold mud material bought is put into cylinder, and covered on pug
Film paper makes its old 22 days, reach mud it is substantially stabilized after, then take out boccaro orpiment gold mud material, slice uniformly clapped repeatedly
Get to 4mm thickness, and put 17 minutes, further according to the size specification of done boccaro iron sand kettle, first measured only, after slice is rolled
The type of breaking into is patted with plastics while coming, cuts off unnecessary portion, it is finally special bright for patting the bottle body base of getting up with kettle processed
Body polished in repairing, waits after putting 30 minutes only, then carry out second of polishing sizing.
(2) making of boccaro iron sand kettle base substrate annex：Respectively the spout of a teapot to be made, and lid pug be placed on model
It is interior, boccaro iron sand kettle base substrate annex is obtained by way of extruding, is then repaired spout of a teapot, the base substrate annex with lid
Polishing.
(3) making of boccaro iron sand bottle body ornament annex：For the ornament base substrate needed in boccaro iron sand bottle body, divide
Not according to the moulding for proposing meter, such as pine, bamboo, plum, melon and fruit, first pug is put into the mould of ornament, passes through the side of extruding
Formula obtains the base substrate annex of boccaro iron sand kettle ornament, then such as pine of needs, bamboo, plum, melon and fruit base substrate annex are repaired
Polishing, wait after putting 40 minutes only, carry out second of polishing sizing.Put only again after drying 120 minutes, then according to it is required not
Tinted with green mud, yellow mud, red soil with color, then after putting 180 minutes and drying only, tinted for the second time i.e. available respectively
Boccaro iron sand kettle ornament annex.
(4) installation of boccaro iron sand kettle base substrate：The connection method of spout base substrate and bottle body base substrate, using identical kettle pug processed
Mud be formed by connecting, the position of spout of a teapot opening is selected in 1/3 eminence of bottle body, and in connection using 40 degree slope angles companies
Connect, with the special bright pin reparation of kettle processed after 2.3 hours to be dried, after wait dries 1 hour, then carry out second of polishing sizing.Kettle
The ornament annex of body is equally formed by connecting from the mud of identical pug, and passes through secondary repairing polishing sizing.
(5) boccaro iron sand kettle is burnt till：Before teapot base substrate is burnt till, first teapot is put into and dries 7 under indoor 22 DEG C of normal temperature
Hour, then it is to be dried 6 hours in 70 DEG C of drying room that iron sand kettle, which is placed on temperature, make teapot enter klining into when because the temperature difference will not go out
Now fission, then teapot base substrate is sent into kiln, be slowly warming up between 165 DEG C DEG C 11% by its moisture control, be incubated
After 2.4 hours, then temperature is stepped up, maximum temperature is controlled at 1220 DEG C, is then progressively cooled, is stopped again when dropping to 100 DEG C
The boccaro iron sand kettle of finished product needed for just being taken out after staying 2 hours, then when starting to cool to 50 DEG C or so.
Embodiment 3
A kind of manufacture craft of boccaro iron sand kettle, specifically comprises the following steps：
(1) boccaro iron sand bottle body base substrate makes：First the boccaro orpiment gold mud material bought is put into cylinder, and covered on pug
Film paper makes its old 21 days, reach mud it is substantially stabilized after, then take out boccaro orpiment gold mud material, slice uniformly clapped repeatedly
Get to 4mm thickness, and put 18 minutes, further according to the size specification of done boccaro iron sand kettle, first measured only, after slice is rolled
The type of breaking into is patted with plastics while coming, cuts off unnecessary portion, it is finally special bright for patting the bottle body base of getting up with kettle processed
Body polished in repairing, waits after putting 30 minutes only, then carry out second of polishing sizing.
(2) making of boccaro iron sand kettle base substrate annex：Respectively the spout of a teapot to be made, and lid pug be placed on model
It is interior, boccaro iron sand kettle base substrate annex is obtained by way of extruding, is then repaired spout of a teapot, the base substrate annex with lid
Polishing.
(3) making of boccaro iron sand bottle body ornament annex：For the ornament base substrate needed in boccaro iron sand bottle body, divide
Not according to the moulding for proposing meter, such as pine, bamboo, plum, melon and fruit, first pug is put into the mould of ornament, passes through the side of extruding
Formula obtains the base substrate annex of boccaro iron sand kettle ornament, then such as pine of needs, bamboo, plum, melon and fruit base substrate annex are repaired
Polishing, wait after putting 40 minutes only, carry out second of polishing sizing.Put only again after drying 120 minutes, then according to it is required not
Tinted with green mud, yellow mud, red soil with color, then after putting 180 minutes and drying only, tinted for the second time i.e. available respectively
Boccaro iron sand kettle ornament annex.
(4) installation of boccaro iron sand kettle base substrate：The connection method of spout base substrate and bottle body base substrate, using identical kettle pug processed
Mud be formed by connecting, the position of spout of a teapot opening is selected in 2/3 eminence of bottle body, and in connection using 45 degree slope angles companies
Connect, with the special bright pin reparation of kettle processed after 2.5 hours to be dried, after wait dries 1 hour, then carry out second of polishing sizing.Kettle
The ornament annex of body is equally formed by connecting from the mud of identical pug, and passes through secondary repairing polishing sizing.
(5) boccaro iron sand kettle is burnt till：Before teapot base substrate is burnt till, first teapot is put into and dries 6 under indoor 25 DEG C of normal temperature
Hour, then it is to be dried 5.5 hours in 72 DEG C of drying room that iron sand kettle, which is placed on temperature, make teapot enter klining into when because the temperature difference will not
Fission, then teapot base substrate is sent into kiln 10.5% by its moisture control, be slowly warming up to 160 DEG C, insulation
After 2.8 hours, then temperature is stepped up, maximum temperature is controlled at 1200 DEG C, is then progressively cooled, is stopped again when dropping to 100 DEG C
The boccaro iron sand kettle of finished product needed for just being taken out after staying 2 hours, then when starting to cool to 50 DEG C or so.
The invention provides a kind of thinking and method, it is many to implement method and the approach of the technical scheme, above institute
State only is the preferred embodiment of the present invention.It should be pointed out that to those of ordinary skill in the art, this hair is not being departed from
On the premise of bright principle, some improvements and modifications can also be made, these improvements and modifications also should be regarded as the protection model of the present invention
In enclosing, the available prior art of each part being not known in the present embodiment is realized.
Claims (7)
1. a kind of manufacture craft of boccaro iron sand kettle, it is characterised in that the manufacture craft comprises the following steps：
(1) boccaro iron sand bottle body base substrate makes：First the boccaro orpiment gold mud material bought is put into cylinder, and the lid film on pug
Paper makes its old more than 15 days, reach mud it is substantially stabilized after, then take out boccaro orpiment gold mud material, slice uniformly clapped repeatedly
4mm thickness is got to, and puts 15-20 minutes only, further according to the size specification of done boccaro iron sand kettle, is first measured, afterwards slice
The type of breaking into is patted with plastics while rolling, cuts off unnecessary portion, it is finally special bright for patting the kettle of getting up with kettle processed
Body base substrate polished in repairing, waits after putting 30 minutes only, then carry out second of polishing sizing.
(2) making of boccaro iron sand kettle base substrate annex：Respectively the spout of a teapot to be made, and lid pug be placed in model, lead to
The mode for crossing extruding obtains boccaro iron sand kettle base substrate annex, then carries out repairing polishing spout of a teapot, the base substrate annex with lid.
(3) making of boccaro iron sand bottle body ornament annex：For the ornament base substrate needed in boccaro iron sand bottle body, difference root
According to the moulding for proposing meter, such as pine, bamboo, plum, melon and fruit, first pug is put into the mould of ornament, obtained by way of extruding
Repairing polishing is carried out to the base substrate annex of boccaro iron sand kettle ornament, then such as pine of needs, bamboo, plum, melon and fruit base substrate annex,
Wait after putting 40 minutes only, carry out second of polishing sizing.Put only again after drying 120 minutes, then according to required different face
Color is tinted with green mud, yellow mud, red soil respectively, then after putting 180 minutes and drying only, is tinted can obtain boccaro for the second time
Iron sand kettle ornament annex.
(4) installation of boccaro iron sand kettle base substrate：The connection method of spout base substrate and bottle body base substrate, using the mud of identical kettle pug processed
Slurry is formed by connecting, and is connected in connection using 35-45 degree slope angle, is repaiied after 1.5-3 hours to be dried with the special bright pin of kettle processed
It is multiple, after wait dries 1 hour, then carry out second of polishing sizing.The ornament annex of bottle body equally selects the mud of identical pug
Slurry is formed by connecting, and passes through secondary repairing polishing sizing.
(5) boccaro iron sand kettle is burnt till：Before teapot base substrate is burnt till, first teapot is put into and dries 5-8 under indoor 20-25 DEG C of normal temperature
Hour, then it is that 5-7 hours are dried in 60-80 DEG C of drying room that iron sand kettle, which is placed on temperature, make teapot enter klining into when due to the temperature difference
Be not in fission, then teapot base substrate is sent into kiln, be slowly warming up between 10%-12% by its moisture control
Between 150 DEG C -180 DEG C, after being incubated 2-3 hours, then temperature being stepped up, maximum temperature is controlled between 1180 DEG C -1250 DEG C,
Then progressively cool, just taken out after stopping 2 hours again when dropping to 100 DEG C, then when starting to cool to 50 DEG C or so needed for finished product
Boccaro iron sand kettle.
2. the manufacture craft of a kind of boccaro iron sand kettle according to claim 1, it is characterised in that wherein step (3) is described
Spout of a teapot opening position preferably in 1/3 high -2/3 eminence of bottle body.
A kind of 3. manufacture craft of boccaro iron sand kettle according to claim 1, it is characterised in that described step (4) it
Preceding first progressively to dry base substrate, general 48-60 hours in winter, hour summer 36-48, season in spring and autumn is 40 hours.So burning
Into when can ensure that teapot has certain plasticity, yield rate is higher.Burning till rear pot lid all can arbitrarily exchange orientation, can be with pot mouth
Kissing, the quasi- seam of lid is tight, and space (or displacement tolerance) therebetween is within 0.3mm.
4. the manufacture craft of a kind of boccaro iron sand kettle according to claim 1, it is characterised in that to avoid pot lid and bottle body
Between there is the defects of losing circle or wide bore, using the making for first completing bottle body, particularly on the coincideing of pot mouth and pot lid, one
As use pot lid base substrate size 0.3mm bigger than pot mouth base substrate requirement, pot lid base substrate is first placed on bottle body base substrate when drying
Pot mouth, this is due to the reason for shrinkage factor of bottle body base substrate is bigger than pot lid base substrate, is so reached after lid puts up
Loose requirement can not be had again by neither losing circle.
5. the manufacture craft of a kind of boccaro iron sand kettle according to claim 1, it is characterised in that described step (1) exists
When making the circle kettle shape of boccaro iron sand kettle, the egative film and bottle body of bottle body are making boccaro iron sand kettle side using the method for forming is patted
During kettle, its technique uses straight forming connection method, and when making boccaro iron sand kettle flower kettle, its technique is using branch's connection shaping
Method.
A kind of 6. manufacture craft of boccaro iron sand kettle according to claim 1, it is characterised in that its material selection boccaro stone
Gold pug is made.
A kind of 7. manufacture craft of boccaro iron sand kettle according to claim 1, it is characterised in that its boccaro iron sand selected
Bottle body ornament annex, such as pine, bamboo, plum, melon and fruit decoration pug color selection, are basic using green mud, yellow mud, red soil, black mud
Tone, when specific colour match is applied, all voluntarily configured according to works requirement by producer.