CN104890437A - Brown undertone canvas - Google Patents
Brown undertone canvas Download PDFInfo
- Publication number
- CN104890437A CN104890437A CN201510261244.XA CN201510261244A CN104890437A CN 104890437 A CN104890437 A CN 104890437A CN 201510261244 A CN201510261244 A CN 201510261244A CN 104890437 A CN104890437 A CN 104890437A
- Authority
- CN
- China
- Prior art keywords
- parts
- turn
- rotating speed
- uniformly dispersed
- dispersion machine
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a brown undertone canvas. A preparation method of the brown undertone canvas includes the steps: (1) coating gel resin on the surface of a fabric, and then drying the gel resin in an oven at the temperature of 100-120 DEG C to obtain a gel resin layer; (2) coating prime paint on the surface of the gel resin layer, and drying the prime paint in the oven at the temperature of 90-100 DEG C to form a prime paint layer; (3) coating colorant paint on the surface of a bottom layer, and drying the colorant paint in the oven at the temperature of 90-100 DEG C to form a colorant layer; (4) finally, coating brown undertone top paint on the colorant layer, and drying the brown undertone top paint in the oven at the temperature of 70-85 DEG C. The speed of the fabric penetrating the oven is 6-7 meters per minute. The brown undertone canvas is fine in waterproof performance, saturation and drape effect, bright in color, colorful and not easy to fade.
Description
Technical field
The present invention relates to painting supply technical field, especially relate to a kind of painting canvas with coloured undertone.
Background technology
Tradition painting canvas is all generally the white end, though can be used for traditional drawing, during for decoration paintings such as modern abstractionism, white background painting canvas cannot give play to effect; The painting canvas of colored shading can make bright in luster, and can save the trouble that artist draws background, background colour is directly completed by coating process, uniform in color, has saturation degree, hangs down and feel, better than the painting canvas effect at the white end for decorative effect.But the painting canvas kind of current colored shading is single, is mostly the collocation of various color, is difficult to meet the need of market.
Summary of the invention
For the problems referred to above that prior art exists, the applicant provides a kind of brown undertone painting canvas.Painting canvas water resistance of the present invention is good, not easily decolours, bright color, colorful, and saturation degree and hanging down is felt.
Technical scheme of the present invention is as follows:
A kind of brown undertone painting canvas, the preparation method of described brown undertone painting canvas is as follows:
The making of A, gel resin:
(1) by pure-acrylic emulsion 20 parts, deionized water 10 parts, rotating speed be 2000-3000 turn/dispersion machine of min in be uniformly dispersed;
(2) add clean plasm 20 parts in the mixed solution prepared in last step, rotating speed be 3000-3500 turn/dispersion machine of min in be uniformly dispersed;
The making of B, subbing:
(1) by 400 parts, calcium carbonate, talcum powder 50 parts, 998 titanium dioxide 50 parts, deionized water 150 parts, rotating speed be 2000-3000 turn/dispersion machine of min in be uniformly dispersed;
(2) add weaving emulsion 150 parts, clean plasm 100 parts in the mixed solution prepared in last step, rotating speed be 3000-3500 turn/dispersion machine of min in be uniformly dispersed;
(3) add dispersant 4 parts, defoamer 1 part, 1 part, brightening agent, emulsion adjuvant 1 part, coalescents 5 parts in the mixed solution prepared in last step, rotating speed be 3000-3500 turn/dispersion machine of min in be uniformly dispersed;
The making of C, mill base coating:
(1) by 400 parts, calcium carbonate, talcum powder 50 parts, 998 titanium dioxide 50 parts, deionized water 150 parts, 10 parts, pigment powder, rotating speed be 2000-3000 turn/dispersion machine of min in be uniformly dispersed;
(2) add weaving emulsion 150 parts, clean plasm 100 parts in the mixed solution prepared in last step, rotating speed be 3000-3500 turn/dispersion machine of min in be uniformly dispersed;
(3) add dispersant 4 parts, defoamer 1 part, 1 part, brightening agent, emulsion adjuvant 1 part, coalescents 5 parts in the mixed solution prepared in last step, rotating speed be 3000-3500 turn/dispersion machine of min in be uniformly dispersed;
The making of D, brown undertone coating materials:
(1) by 200 parts, calcium carbonate, 998 titanium dioxide 200 parts, silica 15 parts, brown undertone 100 parts, deionized water 200 parts, rotating speed be 2000-3000 turn/dispersion machine of min in be uniformly dispersed;
(2) add weaving emulsion 350 parts, clean plasm 100 parts in the mixed solution prepared in last step, rotating speed be 3000-3500 turn/dispersion machine of min in be uniformly dispersed;
(3) add dispersant 4 parts, defoamer 1 part, 1 part, brightening agent, emulsion adjuvant 5 parts, coalescents 5 parts, glycerine 5 parts in the mixed solution prepared in last step, rotating speed be 2000-3000 turn/dispersion machine of min in be uniformly dispersed;
E, by steps A, B, C, D make four kinds of coating by coating machine evenly on fabric, make brown undertone coating painting canvas:
(1) gel resin that steps A makes is applied to the surface of fabric, dries in the baking oven of 100-120 DEG C, form gel resin layer;
(2) then the subbing that step B makes is applied to the surface of gel resin layer, dries in the baking oven of 90-100 DEG C, form subbing layer;
(3) then the mill base coating that step C makes is applied to the surface of bottom, dries in the baking oven of 90-100 DEG C, form color paste layer;
(4) be finally coated on color paste layer by the brown undertone coating materials that step D makes, dry in the baking oven of 70-85 DEG C, fabric is 6 ms/min to 7 ms/min through the speed of baking oven.
Described clean plasm is polyvinyl alcohol.Described weaving emulsion is aqueous polyurethane emulsion.
Described emulsion adjuvant is AMP-95.
Described pigment powder is that Changzhou Eastern Mountain Hua Cai factory produces.
Described fabric is cotton gauze.
The technique effect that the present invention is useful is:
1, painting canvas of the present invention adds the mill base of specialty preparation, makes product shape bright color, colorful, the product pole that special technique is made be not easy decolouring.
2, painting canvas of the present invention adds Weak solvent especially, and make color beautiful abundant, effect is true to nature, broad colour gamut, splendid color representation power, waterproof, wear-resistantly not easily decolours; Outdoor expressive force is lasting, can resist the impact of UV light, prevents color fading and have strong non-oxidizability.
3, painting canvas of the present invention adopts ep-type material, not containing benezene, and toluene, dimethylbenzene, the toxic solvents such as cyclohexanone, taste is minimum, good adhesive force, quick-drying.
Detailed description of the invention
Below in conjunction with embodiment, the present invention is specifically described.
Embodiment 1
A kind of brown undertone painting canvas, the preparation method of described brown undertone painting canvas is as follows:
The making of A, gel resin:
(1) by pure-acrylic emulsion 20 parts, deionized water 10 parts, rotating speed be 2000-3000 turn/dispersion machine of min in be uniformly dispersed;
(2) add clean plasm 20 parts in the mixed solution prepared in last step, rotating speed be 3000-3500 turn/dispersion machine of min in be uniformly dispersed;
The making of B, subbing:
(1) by 400 parts, calcium carbonate, talcum powder 50 parts, 998 titanium dioxide 50 parts, deionized water 150 parts, rotating speed be 2000-3000 turn/dispersion machine of min in be uniformly dispersed;
(2) add weaving emulsion 150 parts, clean plasm 100 parts in the mixed solution prepared in last step, rotating speed be 3000-3500 turn/dispersion machine of min in be uniformly dispersed;
(3) add dispersant 4 parts, defoamer 1 part, 1 part, brightening agent, emulsion adjuvant 1 part, coalescents 5 parts in the mixed solution prepared in last step, rotating speed be 3000-3500 turn/dispersion machine of min in be uniformly dispersed;
The making of C, mill base coating:
(1) by 400 parts, calcium carbonate, talcum powder 50 parts, 998 titanium dioxide 50 parts, deionized water 150 parts, 10 parts, pigment powder, rotating speed be 2000-3000 turn/dispersion machine of min in be uniformly dispersed;
(2) add weaving emulsion 150 parts, clean plasm 100 parts in the mixed solution prepared in last step, rotating speed be 3000-3500 turn/dispersion machine of min in be uniformly dispersed;
(3) add dispersant 4 parts, defoamer 1 part, 1 part, brightening agent, emulsion adjuvant 1 part, coalescents 5 parts in the mixed solution prepared in last step, rotating speed be 3000-3500 turn/dispersion machine of min in be uniformly dispersed;
The making of D, brown undertone coating materials:
(1) by 200 parts, calcium carbonate, 998 titanium dioxide 200 parts, silica 15 parts, brown undertone 100 parts, deionized water 200 parts, rotating speed be 2000-3000 turn/dispersion machine of min in be uniformly dispersed;
(2) add weaving emulsion 350 parts, clean plasm 100 parts in the mixed solution prepared in last step, rotating speed be 3000-3500 turn/dispersion machine of min in be uniformly dispersed;
(3) add dispersant 4 parts, defoamer 1 part, 1 part, brightening agent, emulsion adjuvant 5 parts, coalescents 5 parts, glycerine 5 parts in the mixed solution prepared in last step, rotating speed be 2000-3000 turn/dispersion machine of min in be uniformly dispersed;
E, by steps A, B, C, D make four kinds of coating by coating machine evenly on fabric, make brown undertone coating painting canvas:
(1) gel resin that steps A makes is applied to the surface of fabric, dries in the baking oven of 100 DEG C, form gel resin layer;
(2) then the subbing that step B makes is applied to the surface of gel resin layer, dries in the baking oven of 100 DEG C, form subbing layer;
(3) then the mill base coating that step C makes is applied to the surface of bottom, dries in the baking oven of 90 DEG C, form color paste layer;
(4) be finally coated on color paste layer by the brown undertone coating materials that step D makes, dry in the baking oven of 70 DEG C, fabric is 6 ms/min to 7 ms/min through the speed of baking oven.
Described weaving emulsion is aqueous polyurethane emulsion, described clean plasm is polyvinyl alcohol, described pigment powder is that Changzhou Eastern Mountain Hua Cai factory produces, described emulsion adjuvant is AMP-95, and described dispersant is TX-4, defoamer is dimethicone, brightening agent is talan, coalescents is propandiol butyl ether; Described fabric is cotton gauze.
Embodiment 2
A kind of brown undertone painting canvas, the preparation method of described brown undertone painting canvas is as follows:
The making of A, gel resin:
(1) by pure-acrylic emulsion 20 parts, deionized water 10 parts, rotating speed be 2000-3000 turn/dispersion machine of min in be uniformly dispersed;
(2) add clean plasm 20 parts in the mixed solution prepared in last step, rotating speed be 3000-3500 turn/dispersion machine of min in be uniformly dispersed;
The making of B, subbing:
(1) by 400 parts, calcium carbonate, talcum powder 50 parts, 998 titanium dioxide 50 parts, deionized water 150 parts, rotating speed be 2000-3000 turn/dispersion machine of min in be uniformly dispersed;
(2) add weaving emulsion 150 parts, clean plasm 100 parts in the mixed solution prepared in last step, rotating speed be 3000-3500 turn/dispersion machine of min in be uniformly dispersed;
(3) add dispersant 4 parts, defoamer 1 part, 1 part, brightening agent, emulsion adjuvant 1 part, coalescents 5 parts in the mixed solution prepared in last step, rotating speed be 3000-3500 turn/dispersion machine of min in be uniformly dispersed;
The making of C, mill base coating:
(1) by 400 parts, calcium carbonate, talcum powder 50 parts, 998 titanium dioxide 50 parts, deionized water 150 parts, 10 parts, pigment powder, rotating speed be 2000-3000 turn/dispersion machine of min in be uniformly dispersed;
(2) add weaving emulsion 150 parts, clean plasm 100 parts in the mixed solution prepared in last step, rotating speed be 3000-3500 turn/dispersion machine of min in be uniformly dispersed;
(3) add dispersant 4 parts, defoamer 1 part, 1 part, brightening agent, emulsion adjuvant 1 part, coalescents 5 parts in the mixed solution prepared in last step, rotating speed be 3000-3500 turn/dispersion machine of min in be uniformly dispersed;
The making of D, brown undertone coating materials:
(1) by 200 parts, calcium carbonate, 998 titanium dioxide 200 parts, silica 15 parts, brown undertone 100 parts, deionized water 200 parts, rotating speed be 2000-3000 turn/dispersion machine of min in be uniformly dispersed;
(2) add weaving emulsion 350 parts, clean plasm 100 parts in the mixed solution prepared in last step, rotating speed be 3000-3500 turn/dispersion machine of min in be uniformly dispersed;
(3) add dispersant 4 parts, defoamer 1 part, 1 part, brightening agent, emulsion adjuvant 5 parts, coalescents 5 parts, glycerine 5 parts in the mixed solution prepared in last step, rotating speed be 2000-3000 turn/dispersion machine of min in be uniformly dispersed;
E, by steps A, B, C, D make four kinds of coating by coating machine evenly on fabric, make brown undertone coating painting canvas:
(1) gel resin that steps A makes is applied to the surface of fabric, dries in the baking oven of 120 DEG C, form gel resin layer;
(2) then the subbing that step B makes is applied to the surface of gel resin layer, dries in the baking oven of 90 DEG C, form bottom;
(3) then the mill base coating that step C makes is applied to the surface of bottom, dries in the baking oven of 100 DEG C, form color paste layer;
(4) be finally coated on color paste layer by the brown undertone coating materials that step D makes, dry in the baking oven of 85 DEG C, fabric is 6 ms/min to 7 ms/min through the speed of baking oven.
Described weaving emulsion is aqueous polyurethane emulsion, described clean plasm is polyvinyl alcohol, described pigment powder is that Changzhou Eastern Mountain Hua Cai factory produces, described emulsion adjuvant is AMP-95, and described dispersant is TX-4, defoamer is dimethicone, brightening agent is talan, coalescents is propandiol butyl ether; Described fabric is cotton gauze.
Embodiment 3
A kind of brown undertone painting canvas, the preparation method of described brown undertone painting canvas is as follows:
The making of A, gel resin:
(1) by pure-acrylic emulsion 20 parts, deionized water 10 parts, rotating speed be 2000-3000 turn/dispersion machine of min in be uniformly dispersed;
(2) add clean plasm 20 parts in the mixed solution prepared in last step, rotating speed be 3000-3500 turn/dispersion machine of min in be uniformly dispersed;
The making of B, subbing:
(1) by 400 parts, calcium carbonate, talcum powder 50 parts, 998 titanium dioxide 50 parts, deionized water 150 parts, rotating speed be 2000-3000 turn/dispersion machine of min in be uniformly dispersed;
(2) add weaving emulsion 150 parts, clean plasm 100 parts in the mixed solution prepared in last step, rotating speed be 3000-3500 turn/dispersion machine of min in be uniformly dispersed;
(3) add dispersant 4 parts, defoamer 1 part, 1 part, brightening agent, emulsion adjuvant 1 part, coalescents 5 parts in the mixed solution prepared in last step, rotating speed be 3000-3500 turn/dispersion machine of min in be uniformly dispersed;
The making of C, mill base coating:
(1) by 400 parts, calcium carbonate, talcum powder 50 parts, 998 titanium dioxide 50 parts, deionized water 150 parts, 10 parts, pigment powder, rotating speed be 2000-3000 turn/dispersion machine of min in be uniformly dispersed;
(2) add weaving emulsion 150 parts, clean plasm 100 parts in the mixed solution prepared in last step, rotating speed be 3000-3500 turn/dispersion machine of min in be uniformly dispersed;
(3) add dispersant 4 parts, defoamer 1 part, 1 part, brightening agent, emulsion adjuvant 1 part, coalescents 5 parts in the mixed solution prepared in last step, rotating speed be 3000-3500 turn/dispersion machine of min in be uniformly dispersed;
The making of D, brown undertone coating materials:
(1) by 200 parts, calcium carbonate, 998 titanium dioxide 200 parts, silica 15 parts, brown undertone 100 parts, deionized water 200 parts, rotating speed be 2000-3000 turn/dispersion machine of min in be uniformly dispersed;
(2) add weaving emulsion 350 parts, clean plasm 100 parts in the mixed solution prepared in last step, rotating speed be 3000-3500 turn/dispersion machine of min in be uniformly dispersed;
(3) add dispersant 4 parts, defoamer 1 part, 1 part, brightening agent, emulsion adjuvant 5 parts, coalescents 5 parts, glycerine 5 parts in the mixed solution prepared in last step, rotating speed be 2000-3000 turn/dispersion machine of min in be uniformly dispersed;
E, by steps A, B, C, D make four kinds of coating by coating machine evenly on fabric, make brown undertone coating painting canvas:
(1) gel resin that steps A makes is applied to the surface of fabric, dries in the baking oven of 110 DEG C, form gel resin layer;
(2) then the subbing that step B makes is applied to the surface of gel resin layer, dries in the baking oven of 100 DEG C, form bottom;
(3) then the mill base coating that step C makes is applied to the surface of bottom, dries in the baking oven of 95 DEG C, form color paste layer;
(4) be finally coated on color paste layer by the brown undertone coating materials that step D makes, dry in the baking oven of 80 DEG C, fabric is 6 ms/min to 7 ms/min through the speed of baking oven.
Described weaving emulsion is aqueous polyurethane emulsion, described clean plasm is polyvinyl alcohol, described pigment powder is that Changzhou Eastern Mountain Hua Cai factory produces, described emulsion adjuvant is AMP-95, and described dispersant is TX-4, defoamer is dimethicone, brightening agent is talan, coalescents is propandiol butyl ether; Described fabric is cotton gauze.
Claims (6)
1. a brown undertone painting canvas, is characterized in that the preparation method of described brown undertone painting canvas is as follows:
The making of A, gel resin:
(1) by pure-acrylic emulsion 20 parts, deionized water 10 parts, rotating speed be 2000-3000 turn/dispersion machine of min in be uniformly dispersed;
(2) add clean plasm 20 parts in the mixed solution prepared in last step, rotating speed be 3000-3500 turn/dispersion machine of min in be uniformly dispersed;
The making of B, subbing:
(1) by 400 parts, calcium carbonate, talcum powder 50 parts, 998 titanium dioxide 50 parts, deionized water 150 parts, rotating speed be 2000-3000 turn/dispersion machine of min in be uniformly dispersed;
(2) add weaving emulsion 150 parts, clean plasm 100 parts in the mixed solution prepared in last step, rotating speed be 3000-3500 turn/dispersion machine of min in be uniformly dispersed;
(3) add dispersant 4 parts, defoamer 1 part, 1 part, brightening agent, emulsion adjuvant 1 part, coalescents 5 parts in the mixed solution prepared in last step, rotating speed be 3000-3500 turn/dispersion machine of min in be uniformly dispersed;
The making of C, mill base coating:
(1) by 400 parts, calcium carbonate, talcum powder 50 parts, 998 titanium dioxide 50 parts, deionized water 150 parts, 10 parts, pigment powder, rotating speed be 2000-3000 turn/dispersion machine of min in be uniformly dispersed;
(2) add weaving emulsion 150 parts, clean plasm 100 parts in the mixed solution prepared in last step, rotating speed be 3000-3500 turn/dispersion machine of min in be uniformly dispersed;
(3) add dispersant 4 parts, defoamer 1 part, 1 part, brightening agent, emulsion adjuvant 1 part, coalescents 5 parts in the mixed solution prepared in last step, rotating speed be 3000-3500 turn/dispersion machine of min in be uniformly dispersed;
The making of D, brown undertone coating materials:
(1) by 200 parts, calcium carbonate, 998 titanium dioxide 200 parts, silica 15 parts, brown undertone 100 parts, deionized water 200 parts, rotating speed be 2000-3000 turn/dispersion machine of min in be uniformly dispersed;
(2) add weaving emulsion 350 parts, clean plasm 100 parts in the mixed solution prepared in last step, rotating speed be 3000-3500 turn/dispersion machine of min in be uniformly dispersed;
(3) add dispersant 4 parts, defoamer 1 part, 1 part, brightening agent, emulsion adjuvant 5 parts, coalescents 5 parts, glycerine 5 parts in the mixed solution prepared in last step, rotating speed be 2000-3000 turn/dispersion machine of min in be uniformly dispersed;
E, by steps A, B, C, D make four kinds of coating by coating machine evenly on fabric, make brown undertone coating painting canvas:
(1) gel resin that steps A makes is applied to the surface of fabric, dries in the baking oven of 100-120 DEG C, form gel resin layer;
(2) then the subbing that step B makes is applied to the surface of gel resin layer, dries in the baking oven of 90-100 DEG C, form subbing layer;
(3) then the mill base coating that step C makes is applied to the surface of bottom, dries in the baking oven of 90-100 DEG C, form color paste layer;
(4) be finally coated on color paste layer by the brown undertone coating materials that step D makes, dry in the baking oven of 70-85 DEG C, fabric is 6 ms/min to 7 ms/min through the speed of baking oven.
2. brown undertone painting canvas according to claim 1, is characterized in that described clean plasm is polyvinyl alcohol.
3. brown undertone painting canvas according to claim 1, is characterized in that described weaving emulsion is water-based
Polyaminoester emulsion.
4. brown undertone painting canvas according to claim 1, is characterized in that described emulsion adjuvant is AMP-95.
5. brown undertone painting canvas according to claim 1, is characterized in that described pigment powder is that Changzhou Eastern Mountain Hua Cai factory produces.
6. brown undertone painting canvas according to claim 1, is characterized in that described fabric is cotton gauze.