CN109228797A - A kind of production method of waterproof stereo cut-paper - Google Patents
A kind of production method of waterproof stereo cut-paper Download PDFInfo
- Publication number
- CN109228797A CN109228797A CN201811211021.2A CN201811211021A CN109228797A CN 109228797 A CN109228797 A CN 109228797A CN 201811211021 A CN201811211021 A CN 201811211021A CN 109228797 A CN109228797 A CN 109228797A
- Authority
- CN
- China
- Prior art keywords
- paper
- cut
- waterproof
- water
- rice paper
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to stereo cut-paper technical fields, more particularly to a kind of production method of waterproof stereo cut-paper, the invention discloses a kind of production methods of waterproof stereo cut-paper, the stereo cut-paper produced has excellent waterproof, corrosion resistant, toughness and stiffness, effectively extends the holding time of stereo cut-paper.During rice paper surface treatment, coating material crosses water process after smearing, can hole to rice paper surface, seam add stifled, reduce water in the diffusion on rice paper；The coating of rice paper surface waterproofing coating, the waterproof performance of rice paper can not only effectively be promoted, also add the toughness and stiffness of rice paper, reduce the soft risk to collapse after stereo cut-paper is placed for a long time, the case where waterproof coating that the addition of nano-titanium dioxide forms rice paper surface in water-repellent paint has sterilization and self-cleaning function, and stereo cut-paper surface from mildewing can effectively be avoided to change colour.
Description
Technical field
The present invention relates to stereo cut-paper technical fields, and in particular to a kind of production method of waterproof stereo cut-paper.
Background technique
Chinese paper-cut be it is a kind of texturing line is cut on paper with scissors or icking tool, for decorateeing life or cooperating other folk customs living
Dynamic folk art.In China, paper-cut has extensive mass foundation, blends in the social life of people of all nationalities, is the various people
The movable important component of custom.Common paper-cut is broadly divided into plane paper-cut and stereo cut-paper two major classes.
Plane paper-cut is the patterned artistic works of the hollow out rich in civil implied meaning, beautiful and generous, the also traditional craft in China
Production art.However as the increasing aesthetic needs of people, plane paper-cut is bad in the picture for showing multi-level complexity
Hold and shadow artistic effect, its own aesthetic feeling generated have been difficult to meet the requirement of people.
Stereo cut-paper works, as the term suggests it is that the situation of works, moulding should at least have convex-concave sense or two dimension to three-dimensional several
The feature of what shape.It is briefly exactly to stack multi-ply paper during making paper-cut product to cut quarter together, to according to sample
By each layer, its corresponding pattern is bonded together into space pattern again with adhesive means after drawing that quarter (cutting) comes out is produced.It is vertical
Body paper-cut is the shadow artistic effect that the three-dimensional art works based on three-dimensional space have sufficiently used spatial art to generate, the sense of reality
By strong, the visual effect and sensory effects generated is more liked that therefore, stereo handicraft article increasingly receives people by people
Welcome.
The waterproofness of traditional stereo cut-paper and toughness are poor, the easy moisture absorption expansion of paper wood, mildew after long-term storage, and then lead
Cause collapsing and damaging for stereo cut-paper external form.
Summary of the invention
In view of the above problems, the invention discloses a kind of production method of waterproof stereo cut-paper, the stereo cut-paper produced
With preferable waterproofness, toughness and stiffness, permanent storage is not easy moisture absorption mildew, damage.
In order to achieve the above purpose, the following technical solution is employed by the present invention:
A kind of production method of waterproof stereo cut-paper, comprising the following steps:
(1) quarter rice paper to be cut is chosen, coating material is uniformly smeared on rice paper surface, is then put into the rice paper after coating
30-50min is impregnated in 10-45 DEG C of water；
(2) rice paper after immersion is taken out and blots its moisture with towel or Water adsorption towel or absorbent cotton, then dehumidified with dry paper,
A layer paper is rolled with rolling pin later, it is separately formed to flattening one by one；
(3) rice paper after flattening is uniformly coated using water-repellent paint, the rice paper after coating is then put into 45-60
DEG C baking oven in dried, dry 50-90min after, by rice paper take out room temperature stand 120min or more, obtain waterproof rice paper；
(4) waterproof rice paper drawing and material paper are stacked in simultaneously in the engraving of turquoise wax composition, then use at least two
Acute angle, which is greater than 0.1 degree of pointer less than 45 degree, to carry out the stacker in engraving to cut quarter；
(5) stacker after carving will be cut to say good-bye as individual paper-cut, glue spraying drying process then is carried out to paper-cut surface；
(6) the paper-cut fragment after being dried glue spraying, section are placed on the layer of full page paving by level superposition, to paving layer
On piece, section, layer paper-cut thermoprint paper-cut finished product is made.
Preferably, coating material described in step (1) is mixed by talcum powder and flour 1:1-1.5 in mass ratio.
Preferably, water-repellent paint described in step (3) includes: 10-12 parts of aqueous polyurethane, dimethyl-silicon by weight
20-35 parts oily, 2-8 parts of acrylic acid, 3-5 parts of nano-titanium dioxide, 2-5 parts of emulsifier, 3-7 parts of dispersing agent and deionized water 50-
65 parts.
Preferably, the preparation method of the water-repellent paint includes the following steps: (a) by nano-titanium dioxide, acrylic acid, cream
Agent is add to deionized water with dispersing agent, and is stirred 30-50min under the speed of 250-300r/min, is mixed
It is combined a point A；(b) dimethicone is added in aqueous polyurethane, and is carried out under conditions of 45-65 DEG C, 80-100r/min
It is stirred, after mixing 30-60min, mixed component A obtained in step a is instilled into dimethyl-silicon with the speed of 20ml/min
With the mixture of aqueous polyurethane, mixed component A is cooled the temperature to after dripping off and is continued to stir 60-90min oil, and waterproof is made
Coating.
Preferably, the emulsifier is any in odium stearate, stearyl lactate and diacetyl tartarate monoglyceride
Kind.
Preferably, the dispersing agent is in vinyl bis-stearamides, glyceryl monostearate and glyceryl tristearate
It is any one or more.
Preferably, the coating thickness of water-repellent paint is 50-80um in step (3).
Preferably, the quantity for spray of glue is 30-60gm in step (5)-2, drying temperature is 30-50 DEG C.
Using above-mentioned technical solution, the beneficial effect that the present invention reaches is:
The present invention improves waterproof, corrosion resistant, toughness and the stiffness of stereo cut-paper by the setting of reasonable technique, extends
The holding time of stereo cut-paper.During rice paper surface treatment, coating material crosses water process after smearing, can be to rice paper table
The hole in face, seam add stifled, reduce water in the diffusion on rice paper；The coating of rice paper surface waterproofing coating, can not only be effective
The waterproof performance for promoting rice paper, also adds the toughness and stiffness of rice paper, reduces soft after stereo cut-paper is placed for a long time collapse
Risk, the waterproof coating that the addition of nano-titanium dioxide forms rice paper surface in water-repellent paint has sterilization and self-cleaning
Function, can effectively avoid stereo cut-paper surface from mildewing change colour the case where.
Specific embodiment
In order to make the object, technical scheme and advantages of the embodiment of the invention clearer, below in conjunction with the embodiment of the present invention,
Technical scheme in the embodiment of the invention is clearly and completely described, it is clear that described embodiment is the present invention one
Divide embodiment, instead of all the embodiments.Based on the embodiments of the present invention, those of ordinary skill in the art are not making
Every other embodiment obtained, shall fall within the protection scope of the present invention under the premise of creative work.
Embodiment 1:
A kind of production method of waterproof stereo cut-paper, comprising the following steps:
(1) quarter rice paper to be cut is chosen, coating material is uniformly smeared on rice paper surface, the rice paper after coating is then put into 10
DEG C water in impregnate 30min；
(2) rice paper after immersion is taken out and blots its moisture with towel or Water adsorption towel or absorbent cotton, then dehumidified with dry paper,
A layer paper is rolled with rolling pin later, it is separately formed to flattening one by one；
(3) rice paper after flattening is uniformly coated using water-repellent paint, the rice paper after coating is then put into 45 DEG C
Baking oven in dried, dry 60min after, by rice paper take out room temperature stand 120min or more, obtain waterproof rice paper；
(4) waterproof rice paper drawing and material paper are stacked in simultaneously in the engraving of turquoise wax composition, then use at least two
Acute angle, which is greater than 0.1 degree of pointer less than 45 degree, to carry out the stacker in engraving to cut quarter；
(5) stacker after carving will be cut to say good-bye as individual paper-cut, glue spraying drying process then is carried out to paper-cut surface；
(6) the paper-cut fragment after being dried glue spraying, section are placed on the layer of full page paving by level superposition, to paving layer
On piece, section, layer paper-cut thermoprint paper-cut finished product is made.
Coating material is mixed by talcum powder and flour 1:1 in mass ratio in step (1).
Water-repellent paint includes: 10 parts of aqueous polyurethane, 20 parts of dimethicone, acrylic acid 8 by weight in step (3)
Part, 3 parts of nano-titanium dioxide, 2 parts of emulsifier, 3 parts and 60 parts of deionized water of dispersing agent.
The preparation method of water-repellent paint includes the following steps: (a) by nano-titanium dioxide, acrylic acid, emulsifier and dispersion
Agent is add to deionized water, and is stirred 35min under the speed of 250r/min, obtains mixed component A；(b) by diformazan
Base silicone oil is added in aqueous polyurethane, and mixing is stirred at 45 DEG C, under conditions of 85r/min, will after mixing 30min
Mixed component A obtained is instilled with the speed of 20ml/min in the mixture of dimethicone and aqueous polyurethane in step a, is mixed
It is combined and stirring 70min is cooled the temperature to and continued after a point A is dripped off, water-repellent paint is made.
Emulsifier is any in odium stearate, stearyl lactate and diacetyl tartarate monoglyceride.
Dispersing agent is any or more in vinyl bis-stearamides, glyceryl monostearate and glyceryl tristearate
Kind.
The coating thickness of water-repellent paint is 50um in step (3).
The quantity for spray of glue is 50gm in step (5)-2, drying temperature is 30 DEG C.
Embodiment 2:
A kind of production method of waterproof stereo cut-paper, comprising the following steps:
(1) quarter rice paper to be cut is chosen, coating material is uniformly smeared on rice paper surface, the rice paper after coating is then put into 15
DEG C water in impregnate 45min；
(2) rice paper after immersion is taken out and blots its moisture with towel or Water adsorption towel or absorbent cotton, then dehumidified with dry paper,
A layer paper is rolled with rolling pin later, it is separately formed to flattening one by one；
(3) rice paper after flattening is uniformly coated using water-repellent paint, the rice paper after coating is then put into 50 DEG C
Baking oven in dried, dry 70min after, by rice paper take out room temperature stand 120min or more, obtain waterproof rice paper；
(4) waterproof rice paper drawing and material paper are stacked in simultaneously in the engraving of turquoise wax composition, then use at least two
Acute angle, which is greater than 0.1 degree of pointer less than 45 degree, to carry out the stacker in engraving to cut quarter；
(5) stacker after carving will be cut to say good-bye as individual paper-cut, glue spraying drying process then is carried out to paper-cut surface；
(6) the paper-cut fragment after being dried glue spraying, section are placed on the layer of full page paving by level superposition, to paving layer
On piece, section, layer paper-cut thermoprint paper-cut finished product is made.
Coating material is mixed by talcum powder and flour 1:1-1.1 in mass ratio in step (1).
Water-repellent paint includes: 12 parts of aqueous polyurethane, 25 parts of dimethicone, acrylic acid 4 by weight in step (3)
Part, 4 parts of nano-titanium dioxide, 4 parts of emulsifier, 4 parts and 55 parts of deionized water of dispersing agent.
The preparation method of water-repellent paint includes the following steps: (a) by nano-titanium dioxide, acrylic acid, emulsifier and dispersion
Agent is add to deionized water, and is stirred 30min under the speed of 260r/min, obtains mixed component A；(b) by diformazan
Base silicone oil is added in aqueous polyurethane, and mixing is stirred at 50 DEG C, under conditions of 90r/min, will after mixing 40min
Mixed component A obtained is instilled with the speed of 20ml/min in the mixture of dimethicone and aqueous polyurethane in step a, is mixed
It is combined and stirring 80min is cooled the temperature to and continued after a point A is dripped off, water-repellent paint is made.
Emulsifier is any in odium stearate, stearyl lactate and diacetyl tartarate monoglyceride.
Dispersing agent is any or more in vinyl bis-stearamides, glyceryl monostearate and glyceryl tristearate
Kind.
The coating thickness of water-repellent paint is 60um in step (3).
The quantity for spray of glue is 40gm in step (5)-2, drying temperature is 35 DEG C.
Embodiment 3:
A kind of production method of waterproof stereo cut-paper, comprising the following steps:
(1) quarter rice paper to be cut is chosen, coating material is uniformly smeared on rice paper surface, the rice paper after coating is then put into 25
DEG C water in impregnate 35min；
(2) rice paper after immersion is taken out and blots its moisture with towel or Water adsorption towel or absorbent cotton, then dehumidified with dry paper,
A layer paper is rolled with rolling pin later, it is separately formed to flattening one by one；
(3) rice paper after flattening is uniformly coated using water-repellent paint, the rice paper after coating is then put into 55 DEG C
Baking oven in dried, dry 50min after, by rice paper take out room temperature stand 120min or more, obtain waterproof rice paper；
(4) waterproof rice paper drawing and material paper are stacked in simultaneously in the engraving of turquoise wax composition, then use at least two
Acute angle, which is greater than 0.1 degree of pointer less than 45 degree, to carry out the stacker in engraving to cut quarter；
(5) stacker after carving will be cut to say good-bye as individual paper-cut, glue spraying drying process then is carried out to paper-cut surface；
(6) the paper-cut fragment after being dried glue spraying, section are placed on the layer of full page paving by level superposition, to paving layer
On piece, section, layer paper-cut thermoprint paper-cut finished product is made.
Coating material is mixed by talcum powder and flour 1:1-1.2 in mass ratio in step (1).
Water-repellent paint includes: 11 parts of aqueous polyurethane, 30 parts of dimethicone, acrylic acid 6 by weight in step (3)
Part, 4 parts of nano-titanium dioxide, 5 parts of emulsifier, 5 parts and 65 parts of deionized water of dispersing agent.
The preparation method of water-repellent paint includes the following steps: (a) by nano-titanium dioxide, acrylic acid, emulsifier and dispersion
Agent is add to deionized water, and is stirred 45min under the speed of 270r/min, obtains mixed component A；(b) by diformazan
Base silicone oil is added in aqueous polyurethane, and mixing is stirred at 55 DEG C, under conditions of 80r/min, will after mixing 50min
Mixed component A obtained is instilled with the speed of 20ml/min in the mixture of dimethicone and aqueous polyurethane in step a, is mixed
It is combined and stirring 60min is cooled the temperature to and continued after a point A is dripped off, water-repellent paint is made.
Emulsifier is any in odium stearate, stearyl lactate and diacetyl tartarate monoglyceride.
Dispersing agent is any or more in vinyl bis-stearamides, glyceryl monostearate and glyceryl tristearate
Kind.
The coating thickness of water-repellent paint is 70um in step (3).
The quantity for spray of glue is 30gm in step (5)-2, drying temperature is 40 DEG C.
Embodiment 4:
A kind of production method of waterproof stereo cut-paper, comprising the following steps:
(1) quarter rice paper to be cut is chosen, coating material is uniformly smeared on rice paper surface, the rice paper after coating is then put into 35
DEG C water in impregnate 50min；
(2) rice paper after immersion is taken out and blots its moisture with towel or Water adsorption towel or absorbent cotton, then dehumidified with dry paper,
A layer paper is rolled with rolling pin later, it is separately formed to flattening one by one；
(3) rice paper after flattening is uniformly coated using water-repellent paint, the rice paper after coating is then put into 55 DEG C
Baking oven in dried, dry 90min after, by rice paper take out room temperature stand 120min or more, obtain waterproof rice paper；
(4) waterproof rice paper drawing and material paper are stacked in simultaneously in the engraving of turquoise wax composition, then use at least two
Acute angle, which is greater than 0.1 degree of pointer less than 45 degree, to carry out the stacker in engraving to cut quarter；
(5) stacker after carving will be cut to say good-bye as individual paper-cut, glue spraying drying process then is carried out to paper-cut surface；
(6) the paper-cut fragment after being dried glue spraying, section are placed on the layer of full page paving by level superposition, to paving layer
On piece, section, layer paper-cut thermoprint paper-cut finished product is made.
Coating material is mixed by talcum powder and flour 1:1-1.4 in mass ratio in step (1).
Water-repellent paint includes: 10 parts of aqueous polyurethane, 30 parts of dimethicone, acrylic acid 2 by weight in step (3)
Part, 5 parts of nano-titanium dioxide, 3 parts of emulsifier, 7 parts and 50 parts of deionized water of dispersing agent.
The preparation method of water-repellent paint includes the following steps: (a) by nano-titanium dioxide, acrylic acid, emulsifier and dispersion
Agent is add to deionized water, and is stirred 40min under the speed of 280r/min, obtains mixed component A；(b) by diformazan
Base silicone oil is added in aqueous polyurethane, and mixing is stirred at 60 DEG C, under conditions of 100r/min, will after mixing 55min
Mixed component A obtained is instilled with the speed of 20ml/min in the mixture of dimethicone and aqueous polyurethane in step a, is mixed
It is combined and stirring 90min is cooled the temperature to and continued after a point A is dripped off, water-repellent paint is made.
Emulsifier is any in odium stearate, stearyl lactate and diacetyl tartarate monoglyceride.
Dispersing agent is any or more in vinyl bis-stearamides, glyceryl monostearate and glyceryl tristearate
Kind.
The coating thickness of water-repellent paint is 80um in step (3).
The quantity for spray of glue is 40gm in step (5)-2, drying temperature is 45 DEG C.
Embodiment 5:
A kind of production method of waterproof stereo cut-paper, comprising the following steps:
(1) quarter rice paper to be cut is chosen, coating material is uniformly smeared on rice paper surface, the rice paper after coating is then put into 45
DEG C water in impregnate 40min；
(2) rice paper after immersion is taken out and blots its moisture with towel or Water adsorption towel or absorbent cotton, then dehumidified with dry paper,
A layer paper is rolled with rolling pin later, it is separately formed to flattening one by one；
(3) rice paper after flattening is uniformly coated using water-repellent paint, the rice paper after coating is then put into 60 DEG C
Baking oven in dried, dry 80min after, by rice paper take out room temperature stand 120min or more, obtain waterproof rice paper；
(4) waterproof rice paper drawing and material paper are stacked in simultaneously in the engraving of turquoise wax composition, then use at least two
Acute angle, which is greater than 0.1 degree of pointer less than 45 degree, to carry out the stacker in engraving to cut quarter；
(5) stacker after carving will be cut to say good-bye as individual paper-cut, glue spraying drying process then is carried out to paper-cut surface；
(6) the paper-cut fragment after being dried glue spraying, section are placed on the layer of full page paving by level superposition, to paving layer
On piece, section, layer paper-cut thermoprint paper-cut finished product is made.
Coating material is mixed by talcum powder and flour 1:1.5 in mass ratio in step (1).
Water-repellent paint includes: 11 parts of aqueous polyurethane, 35 parts of dimethicone, acrylic acid 5 by weight in step (3)
Part, 5 parts of nano-titanium dioxide, 3 parts of emulsifier, 7 parts and 60 parts of deionized water of dispersing agent.
The preparation method of water-repellent paint includes the following steps: (a) by nano-titanium dioxide, acrylic acid, emulsifier and dispersion
Agent is add to deionized water, and is stirred 50min under the speed of 300r/min, obtains mixed component A；(b) by diformazan
Base silicone oil is added in aqueous polyurethane, and mixing is stirred at 65 DEG C, under conditions of 95r/min, will after mixing 60min
Mixed component A obtained is instilled with the speed of 20ml/min in the mixture of dimethicone and aqueous polyurethane in step a, is mixed
It is combined and stirring 80min is cooled the temperature to and continued after a point A is dripped off, water-repellent paint is made.
Emulsifier is any in odium stearate, stearyl lactate and diacetyl tartarate monoglyceride.
Dispersing agent is any or more in vinyl bis-stearamides, glyceryl monostearate and glyceryl tristearate
Kind.
The coating thickness of water-repellent paint is 80um in step (3).
The quantity for spray of glue is 60gm in step (5)-2, drying temperature is 50 DEG C.
The above embodiments are merely illustrative of the technical solutions of the present invention, rather than its limitations；Although with reference to the foregoing embodiments
Invention is explained in detail, those skilled in the art should understand that: it still can be to aforementioned each implementation
Technical solution documented by example is modified or equivalent replacement of some of the technical features；And these modification or
Replacement, the spirit and scope for technical solution of various embodiments of the present invention that it does not separate the essence of the corresponding technical solution.
Claims (8)
1. a kind of production method of waterproof stereo cut-paper, it is characterised in that: the following steps are included:
(1) quarter rice paper to be cut is chosen, coating material is uniformly smeared on rice paper surface, the rice paper after coating is then put into 10-45
DEG C water in impregnate 30-50min；
(2) rice paper after immersion is taken out and blots its moisture with towel or Water adsorption towel or absorbent cotton, then dehumidified with dry paper, later
A layer paper is rolled with rolling pin, it is separately formed to flattening one by one；
(3) rice paper after flattening is uniformly coated using water-repellent paint, the rice paper after coating is then put into 45-60 DEG C
It is dried in baking oven, after drying 50-90min, rice paper is taken out into room temperature and stands 120min or more, obtains waterproof rice paper；
(4) waterproof rice paper drawing and material paper are stacked in simultaneously in the engraving of turquoise wax composition, then use at least two acute angles
The stacker in engraving is carried out greater than 0.1 degree of pointer less than 45 degree to cut quarter；
(5) stacker after carving will be cut to say good-bye as individual paper-cut, glue spraying drying process then is carried out to paper-cut surface；
(6) the paper-cut fragment after being dried glue spraying, section are placed on the layer of full page paving by level superposition, on the layer of paving
Paper-cut finished product is made in piece, section, layer paper-cut thermoprint.
2. a kind of production method of waterproof stereo cut-paper according to claim 1, it is characterised in that: described in step (1)
Coating material is mixed by talcum powder and flour 1:1-1.5 in mass ratio.
3. a kind of production method of waterproof stereo cut-paper according to claim 1, it is characterised in that: described in step (3)
Water-repellent paint includes: 10-12 parts of aqueous polyurethane, 20-35 parts of dimethicone, 2-8 parts of acrylic acid, nanometer two by weight
3-5 parts of titanium oxide, 2-5 parts of emulsifier, 3-7 parts and deionized water 50-65 parts of dispersing agent.
4. a kind of production method of waterproof stereo cut-paper according to claim 3, it is characterised in that: the water-repellent paint
Preparation method includes the following steps: that nano-titanium dioxide, acrylic acid, emulsifier and dispersing agent are add to deionized water by (a),
And it is stirred 30-50min under the speed of 250-300r/min, obtain mixed component A；(b) dimethicone is added to
In aqueous polyurethane, and it is stirred mixing under conditions of 45-65 DEG C, 80-100r/min, after mixing 30-60min, will walk
Mixed component A obtained is instilled with the speed of 20ml/min in the mixture of dimethicone and aqueous polyurethane in rapid a, mixing
Component A is cooled the temperature to after dripping off and is continued to stir 60-90min, and water-repellent paint is made.
5. a kind of production method of waterproof stereo cut-paper according to claim 3, it is characterised in that: the emulsifier is hard
It is any in resin acid sodium, stearyl lactate and diacetyl tartarate monoglyceride.
6. a kind of production method of waterproof stereo cut-paper according to claim 3, it is characterised in that: the dispersing agent is second
It is any one or more in alkenyl bis-stearamides, glyceryl monostearate and glyceryl tristearate.
7. a kind of production method of waterproof stereo cut-paper according to claim 1, it is characterised in that: waterproof in step (3)
The coating thickness of coating is 50-80um.
8. a kind of production method of waterproof stereo cut-paper according to claim 1, it is characterised in that: glue in step (5)
Quantity for spray be 30-60gm-2, drying temperature is 30-50 DEG C.