CN206438343U - Change colour wallpaper - Google Patents
Change colour wallpaper Download PDFInfo
- Publication number
- CN206438343U CN206438343U CN201620548542.7U CN201620548542U CN206438343U CN 206438343 U CN206438343 U CN 206438343U CN 201620548542 U CN201620548542 U CN 201620548542U CN 206438343 U CN206438343 U CN 206438343U
- Authority
- CN
- China
- Prior art keywords
- layer
- wallpaper
- discoloration
- parts
- base paper
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The utility model provides a kind of discoloration wallpaper, wherein the wallpaper includes base paper layer and photochromic layer, the photochromic layer is that heat discoloration powder is layered on the base paper layer with least one of pattern and word shape.Above-mentioned discoloration wallpaper, the heat discoloration powder of photochromic layer, which can be varied with temperature, shows different pattern, word or colors, enriches the visual experience of wallpaper, increases the aesthetics and interest of wallpaper.
Description
Technical field
The utility model is related to wallpaper field, more particularly to a kind of discoloration wallpaper.
Background technology
In recent years, wallpaper was because of material environmental protection, sound-insulation and heat-insulation, lovely luster, and good visual effect and short construction period etc. are more
Weight advantage, at home and abroad increasing consumer's selection wallpaper, has been the trend trend of current wall surfacing using wallpaper.
At the same time, as the improvement of people's living standards, people not only rest on aesthetic to wallpaper,
Through starting to pursue more features.Many consumers like the wallpaper of different colours, while by discoloration prompt temperature, because
This, develop it is a can according to weather thermograde change color, the wallpaper of different colour bands is formed on wallpaper, is had become
Consumer urgent demand.
Utility model content
Based on this, it is necessary to there is no temperature sensing function for wallpaper, though and indoor coating has its user of temperature sensing function
Method is complicated, long in time limit, the problem of inconvenience is changed, and proposes a kind of discoloration wallpaper.
The utility model proposes a kind of discoloration wallpaper, wherein the wallpaper includes base paper layer and photochromic layer, the change
Chromatograph is that heat discoloration powder is layered on the base paper layer with least one of pattern and word shape.
In one of which embodiment, the photochromic layer is at least two heat discoloration powder respectively with pattern and word
At least one shape be layered on the base paper layer.
In one of which embodiment, the photochromic layer also includes pulp layer, and the pulp layer is layered in the discoloration
Side of the layer away from the base paper layer and pulp layer is transparent.
In one of which embodiment, the pulp layer is layered between the photochromic layer and the base paper layer.
In one of which embodiment, the photochromic layer thickness is 0.1mm~5mm.
In one of which embodiment, the thickness of the pulp layer is 0.1mm~5mm.
Above-mentioned discoloration wallpaper, the heat discoloration powder of photochromic layer, which can be varied with temperature, shows different pattern, word or face
Color, enriches the visual experience of wallpaper, increases the aesthetics and interest of wallpaper；
Above-mentioned discoloration wallpaper, the heat discoloration powder of photochromic layer can show different patterns, word or color according to temperature,
Visual cues temperature change, points out consumer to go out plus clothing or regulation indoor temperature；
Above-mentioned discoloration wallpaper, preparation method is simple, raw material environmental protection, to free of air pollution, construction time section, can be faster after finishing
Move in.
Brief description of the drawings
Fig. 1 is the discoloration wallpaper structural representation of embodiment 1；
Fig. 2 is the discoloration wallpaper temperature-sensitive display schematic diagram of embodiment 2；
Fig. 3 is the discoloration wallpaper structural representation of embodiment 5.
Embodiment
The purpose of this utility model is to provide a kind of discoloration wallpaper, and the discoloration wallpaper can be shown under different temperature conditionss
Color, pattern or word it is different, the visual experience of wallpaper can be enriched, increase the aesthetic degree and interest of wallpaper.In addition, should
Discoloration wallpaper can show different colors, pattern or word, temperature indicator change according to temperature.
Discoloration wallpaper of the present utility model, including base paper layer and photochromic layer, photochromic layer be heat discoloration powder with pattern and
At least one of word shape is layered on base paper layer.
It is preferred that, photochromic layer is that at least two heat discoloration powder are laminated with least one of pattern and word shape respectively
On base paper layer.
It is preferred that, photochromic layer include pulp layer, pulp layer be layered in side of the photochromic layer away from the base paper layer and
The pulp layer is transparent.
It is preferred that, photochromic layer includes pulp layer, and pulp layer is layered between the photochromic layer and the base paper layer.
It is preferred that, photochromic layer thickness is 0.1mm~5mm, it is furthermore preferred that photochromic layer thickness is 0.1mm~0.5mm.
It is preferred that, slurry layer thickness is 0.1mm~5mm, it is furthermore preferred that slurry layer thickness is 0.3mm~5mm.
It is preferred that, pulp layer is prepared by existing slurry.
It is furthermore preferred that pulp layer is prepared by following slurry, the slurry is in terms of parts by weight, including following components：
It is preferred that, foaming agent can be azodicarbonamide.
It is preferred that, plasticizer can be epoxidized soybean oil.
It is preferred that, stabilizer can be potassium zinc composite stabilizer.
It is preferred that, thickener can be the one or more in lithium magnesium silicate and aluminium-magnesium silicate.
It is preferred that, rate of drying conditioning agent can be the one or more in 1,3-BDO, n-butanol.
It is preferred that, base paper layer can be the one or more in non-woven fabrics, pure paper or PVC plastic.
It is preferred that, the basic discoloring temperature of heat discoloration powder is：-5℃、0℃、5℃、10℃、16℃、21℃、31℃、33
DEG C, the one or more in 38 DEG C.During discoloration, it can become by coloured bleach or by coloured without discoloration with cataclysm or progressively
Color.By taking red heat discoloration powder as an example, it is in 31 DEG C of discolorations, and temperature is red when being less than 31 DEG C, and temperature is nothing when being higher than 31 DEG C
Color.
It is preferred that, heat discoloration powder basic colors is：In black, red, yellow, green, blueness, navy blue, black
It is one or more of.
Specifically, the preferred preparation method of discoloration wallpaper of the present utility model is：
Slurry is prepared, including：
Step A:The dioctyl phthalate that parts by weight are 5-20 parts is mixed with the vinyl chloride that parts by weight are 30-50 parts
Even obtained mixture A；
Step B：By the foaming agent, the D80 environmentally friendly solvents oil that parts by weight are 1-5 parts, parts by weight that parts by weight are 1-2 parts
Number is 10-30 parts of calcium carbonate, parts by weight are 10-30 parts plasticizer, the stabilizer that parts by weight are 1-5 parts, parts by weight
The well mixed obtained mixture B of mixture A that number is 10-20 parts of titanium dioxide and parts by weight are 35-70 parts；
Step C：By the thickener that parts by weight are 1-3 parts, the rate of drying conditioning agent that parts by weight are 1-3 parts and again
It is 73-197 parts of the well mixed obtained slurries of mixture B to measure number.
Photochromic layer is prepared, by heat discoloration powder or at least two heat discoloration powder respectively with least one in pattern and word
Plant shape coating or be printed on base paper layer, prepare the photochromic layer that thickness is 0.1mm~5mm.
Pulp layer is prepared, slurry is coated or discoloration layer surface is printed on, the pulp layer that thickness is 0.1mm~5mm is prepared.
Another preferred preparation method is：
Slurry is prepared, including：
Step A:The dioctyl phthalate that parts by weight are 5-20 parts is mixed with the vinyl chloride that parts by weight are 30-50 parts
Even obtained mixture A；
Step B：By the foaming agent, the D80 environmentally friendly solvents oil that parts by weight are 1-5 parts, parts by weight that parts by weight are 1-2 parts
Number is 10-30 parts of calcium carbonate, parts by weight are 10-30 parts plasticizer, the stabilizer that parts by weight are 1-5 parts, parts by weight
The well mixed obtained mixture B of mixture A that number is 10-20 parts of titanium dioxide and parts by weight are 35-70 parts；
Step C：By the thickener that parts by weight are 1-3 parts, the rate of drying conditioning agent that parts by weight are 1-3 parts and again
It is 73-197 parts of the well mixed obtained slurries of mixture B to measure number.
Pulp layer is prepared, slurry is coated or discoloration layer surface is printed on, the pulp layer that thickness is 0.1mm~5mm is prepared.
Photochromic layer is prepared, by heat discoloration powder or at least two heat discoloration powder with least one of pattern and word shape
Shape coats or is printed on slurry layer surface, prepares the photochromic layer that thickness is 0.1mm~5mm.
The utility model is further described with reference to specific embodiment.
Embodiment 1
Using non-woven fabrics as base paper layer, blue heat discoloration powder and yellow temperature-sensitive are sprayed in the way of interval on non-woven fabrics
Color-change powder prepares the photochromic layer of 0.1mm thickness, is prepared in side coating thickness of the photochromic layer away from base paper layer for 5mm slurries transparent
Pulp layer, discoloration wallpaper A1 is made.
Refer to shown in Fig. 1, the photochromic layer that discoloration wallpaper A1 is included on base paper layer 1, base paper layer 1 includes blue heat discoloration
Pulp layer 3 covered with layer of transparent on layer band 21 and yellow heat discoloration layer band 22, photochromic layer, becomes at a certain temperature
Color wallpaper A1 shows blue stripe, yellow cord or blue yellow alternate striped.
Embodiment 2
Using PVC plastic as base paper layer, slurry of a layer thickness for 0.1mm is sprayed in PVC plastic as pulp layer,
The side for coating slurry sprays different temperature-sensitive powder, to form the photochromic layer with certain pattern or word, the present embodiment
In be the red heat discoloration powder of spraying to form flower motif, yellow heat discoloration powder sprays temperature-sensitive powder to form cloud pattern
Thickness be 0.5mm, discoloration wallpaper A2 is made.
Refer to shown in Fig. 2, discoloration wallpaper A2 can show the flower motif of red, the cloud figure of yellow at a certain temperature
Case shows the flower motif of red and the cloud pattern of yellow simultaneously.
Embodiment 3
Using common paper as base paper layer, one layer of 0.5mm thickness pulp layer slurry is sprayed in common paper as pulp layer,
The blue heat discoloration powder of side interval spraying for coating slurry prepares the photochromic layer that thickness is 1mm, and discoloration wallpaper A3 is made.
Discoloration wallpaper A3 shows blue stripe or does not show blue stripe at a certain temperature.
Embodiment 4
Using non-woven fabrics as base paper layer, blue heat discoloration powder, green heat discoloration powder, red sense are sprayed on non-woven fabrics
Warm color-change powder, the mixture of black heat discoloration powder are coating the side high temperature printing one of heat discoloration powder as photochromic layer
The transparent slurry of layer, is made discoloration wallpaper A4.
Wallpaper A4 change colour at different temperature, can have blueness, green, the red, visual effect of black respectively.
Embodiment 5
Weigh 5g dioctyl phthalates to add in agitator, then weigh 30g vinyl chloride and add in agitator with 2000r/min
Stir；1g azodicarbonamides, 1gD80 environmentally friendly solvents oil, 10g calcium carbonate, 10g epoxidized soybean oils, 1g potassium zinc is weighed to answer
Close and stirred in the blue heat discoloration powder addition agitator of stabilizer, 10g titanium dioxides, 5g with 2000r/min；Weigh 1g silicic acid
Magnesium lithium, 1g n-butanols are added to be stirred in agitator with 2000r/min；The pulp layer slurry that viscosity is 15000cps is made
B1。
Weigh 5g dioctyl phthalates to add in agitator, then weigh 30g vinyl chloride and add in agitator with 2000r/min
Stir；1g azodicarbonamides, 1gD80 environmentally friendly solvents oil, 10g calcium carbonate, 10g epoxidized soybean oils, 1g potassium zinc is weighed to answer
Close and stirred in stabilizer, 10g titanium dioxides, 5g yellow heat discolorations powder addition agitator with 2000r/min；Weigh 1g silicic acid
Magnesium lithium, 1g n-butanols are added to be stirred in agitator with 2000r/min；The pulp layer slurry that viscosity is 17000cps is made
B2。
Pulp layer slurry B1, B2 high temperature in the way of interval are printed in non-woven fabrics base paper, discoloration wallpaper A5 is made.
Refer to shown in Fig. 3, the photochromic layer that discoloration wallpaper A5 is included on base paper layer 1, base paper layer 1 includes blue heat discoloration
Layer band 21 and yellow heat discoloration layer band 22, the wallpaper A5 that changes colour at a certain temperature show blue stripe, yellow cord or
Blue yellow alternate striped.
Embodiment 6
Weigh 20g dioctyl phthalates to add in agitator, then weigh 50g vinyl chloride and add in agitator with 2500r/
Min stirs；Weigh 2g azodicarbonamides, 5gD80 environmentally friendly solvents oil, 30g calcium carbonate, 30g epoxidized soybean oils, 5g potassium zinc
Compound stabilizer, 20g titanium dioxides are added to be stirred in agitator with 2500r/min；Weigh 3g lithium magnesium silicates, 3g1,3- fourths two
Alcohol is added to be stirred in agitator with 2500r/min；The pulp layer slurry B3 that viscosity is 20000cps is made.
Weigh 20g dioctyl phthalates to add in agitator, then weigh 50g vinyl chloride and add in agitator with 2500r/
Min stirs；Weigh 2g azodicarbonamides, 5gD80 environmentally friendly solvents oil, 30g calcium carbonate, 30g epoxidized soybean oils, 5g potassium zinc
The blue heat discoloration powder of compound stabilizer, 20g titanium dioxides, 35g is added to be stirred in agitator with 2500r/min；Weigh 3g
Lithium magnesium silicate, 3g1,3- butanediols are added to be stirred in agitator with 2500r/min；The slurry that viscosity is 20000cps is made
Layer slurry B4.
Weigh 20g dioctyl phthalates to add in agitator, then weigh 50g vinyl chloride and add in agitator with 2500r/
Min stirs；Weigh 2g azodicarbonamides, 5gD80 environmentally friendly solvents oil, 30g calcium carbonate, 30g epoxidized soybean oils, 5g potassium zinc
Compound stabilizer, 20g titanium dioxides, 35g black heat discolorations powder are added to be stirred in agitator with 2500r/min；Weigh 3g
Lithium magnesium silicate, 3g1,3- butanediols are added to be stirred in agitator with 2500r/min；The slurry that viscosity is 20000cps is made
Layer slurry B5.
Pulp layer slurry B4 is printed in non-woven fabrics base paper with plum blossom design high temperature, by pulp layer slurry B5 with certain
Word high temperature is printed in non-woven fabrics base paper, and the scope high temperature printing slurry beyond pulp layer slurry B4 or B5 is printed with high temperature
Layer slurry B3, is made discoloration wallpaper A6.
Change colour wallpaper A6 blue plum blossom design or black letters pattern at a certain temperature, or discoloration wallpaper A6 is certain
At a temperature of show blue plum blossom design and black letters pattern simultaneously.
Embodiment 7
Weigh 20g dioctyl phthalates to add in agitator, then weigh 50g vinyl chloride and add in agitator with 2500r/
Min stirs；Weigh 2g azodicarbonamides, 5gD80 environmentally friendly solvents oil, 30g calcium carbonate, 30g epoxidized soybean oils, 5g potassium zinc
The blue heat discoloration powder of compound stabilizer, 20g titanium dioxides, 5g, the green heat discoloration powder of 5g, 5g yellow heat discolorations powder, 5g are black
Color sensation temperature color-change powder is added to be stirred in agitator with 2500r/min；3g lithium magnesium silicates, the addition of 3g1,3- butanediols is weighed to stir
Mix in bucket and to be stirred with 2500r/min；The pulp layer slurry B6 that viscosity is 19000cps is made.
Pulp layer slurry B6 is sprayed in PVC plastic base paper, discoloration wallpaper A7 is made.
The color that discoloration wallpaper A7 is shown is varied with temperature, and different colors are presented at different temperature.
Embodiment 8
Weigh 10g dioctyl phthalates to add in agitator, then weigh 40g vinyl chloride and add in agitator with 2500r/
Min stirs；Weigh 1.5g azodicarbonamides, 3gD80 environmentally friendly solvents oil, 20g calcium carbonate, 20g epoxidized soybean oils, 4g potassium
The blue heat discoloration powder of zinc composite stabilizer, 17g titanium dioxides, 4g, the green heat discoloration powder of 3g, 5g yellow heat discolorations powder, 1g
Black heat discoloration powder is added to be stirred in agitator with 2500r/min；2g lithium magnesium silicates, 2g1,3- butanediols is weighed to add
Stirred in agitator with 2500r/min；The pulp layer slurry B7 that viscosity is 19000cps is made.
Pulp layer slurry B7 is sprayed on non-woven fabrics, discoloration wallpaper A8 is made.
The color that discoloration wallpaper A8 is shown is varied with temperature, and different colors are presented at different temperature.
Embodiment described above only expresses several embodiments of the present utility model, and it describes more specific and detailed,
But therefore it can not be interpreted as the limitation to the utility model the scope of the claims.It should be pointed out that for the common of this area
For technical staff, without departing from the concept of the premise utility, various modifications and improvements can be made, these all belong to
In protection domain of the present utility model.Therefore, the protection domain of the utility model patent should be determined by the appended claims.
Claims (3)
1. one kind discoloration wallpaper, it is characterised in that the wallpaper includes base paper layer and photochromic layer, and the photochromic layer is at least two
Heat discoloration powder is planted to be layered on the base paper layer with least one of pattern and word shape respectively；
It is described discoloration wallpaper also include pulp layer, the pulp layer be layered in side of the photochromic layer away from the base paper layer and
The pulp layer is transparent.
2. discoloration wallpaper according to claim 1, it is characterised in that the photochromic layer thickness is 0.1mm~5mm.
3. discoloration wallpaper according to claim 1 or 2, it is characterised in that the thickness of the pulp layer is 0.1mm~5mm.