CN211592067U

CN211592067U - Dyeing veneer full-matte open water-based wood paint coating layer structure

Info

Publication number: CN211592067U
Application number: CN201922328998.9U
Authority: CN
Inventors: 杨玉嵩; 王暖和; 饶小胜
Original assignee: Dongguan Coatmark New Material Co ltd
Current assignee: Dongguan Coatmark New Material Co ltd
Priority date: 2019-12-23
Filing date: 2019-12-23
Publication date: 2020-09-29
Anticipated expiration: 2029-12-23

Abstract

The utility model discloses a full matte open waterborne wood lacquer application layer structure of dyeing veneer, including dyeing veneer, waterborne treating agent layer, first waterborne open transparent priming paint layer, second waterborne open transparent priming paint layer and the full matte open transparent finish paint layer of waterborne; the aqueous treating agent layer is coated on the surface of the dyed wood skin layer, and the surface of the aqueous treating agent layer is provided with a first polishing layer; the first aqueous open transparent primer layer is coated on the first polishing layer, and the surface of the first aqueous open transparent primer layer is provided with a second polishing layer. Through set gradually aqueous finishing agent layer, the open transparent priming paint layer of first waterborne, the open transparent priming paint layer of second waterborne and the full dumb open transparent finish paint layer of waterborne on the surface on dyeing veneer layer to the cooperation forms each layer of polishing, makes to combine firmly between each layer, is difficult for droing, and can reach better visual effect, makes the beautiful appearance of dyeing veneer see-through out completely, satisfies the needs that use.

Description

Dyeing veneer full-matte open water-based wood paint coating layer structure

Technical Field

The utility model belongs to the technical field of the coating technique and specifically relates to indicate a full dumb open waterborne wood lacquer application layer structure of dyeing veneer.

Background

The dyed veneer is a beautiful and delicate novel decorative material manufactured by utilizing a high-tech processing technology to perform defect treatment and coloring on natural veneer, is generally called as dyed veneer, is beneficial to supplement of the natural veneer, leaves a color imagination space for designers due to the flexibility of color and luster, and adds a plurality of colors to the living environment.

In order to protect the dyed veneer, the transparent paint is generally sprayed on the dyed veneer, however, the coating structure formed by the existing transparent paint is simple and easy, is easy to fall off, has poor visual effect, and cannot enable the beautiful appearance of the dyed veneer to be completely seen through. Therefore, there is a need for improvements in current coating configurations.

SUMMERY OF THE UTILITY MODEL

In view of this, the present invention provides a full-matte open water-based wood paint coating layer structure for dyed veneers, which can effectively solve the problems of easy falling off and poor visual effect of the existing coating structure.

In order to achieve the above purpose, the utility model adopts the following technical scheme:

a coating layer structure of a dyed veneer fully-matte open water-based wood paint comprises a dyed veneer layer, a water-based treating agent layer, a first water-based open transparent primer layer, a second water-based open transparent primer layer and a water-based fully-matte open transparent finish paint layer; the aqueous treating agent layer is coated on the surface of the dyed wood skin layer, and the surface of the aqueous treating agent layer is provided with a first polishing layer; the first aqueous open transparent primer layer is coated on the first polishing layer, and the surface of the first aqueous open transparent primer layer is provided with a second polishing layer; the second aqueous open transparent primer layer is coated on the second polishing layer, and the surface of the second aqueous open transparent primer layer is provided with a third polishing layer; the water-based full-matte open transparent finish paint layer is coated on the third polishing layer.

Preferably, the aqueous treatment agent used in the aqueous treatment agent layer is TB-MP 9101.

Preferably, the first water-based open transparent primer layer adopts a water-based open transparent primer with the model number of TB-MP 9101.

Preferably, the second water-based open transparent primer layer adopts a water-based open transparent primer with the model number of TB-MP 9101.

Preferably, the water-based full-matte open transparent top coat adopted by the water-based full-matte open transparent top coat layer is TB-MP 9201-1.

Compared with the prior art, the utility model obvious advantage and beneficial effect have, particularly, can know by above-mentioned technical scheme:

through set gradually aqueous finishing agent layer, the open transparent priming paint layer of first waterborne, the open transparent priming paint layer of second waterborne and the full dumb open transparent finish paint layer of waterborne on the surface on dyeing veneer layer to the cooperation forms each layer of polishing, makes to combine firmly between each layer, is difficult for droing, and can reach better visual effect, makes the beautiful appearance of dyeing veneer see-through out completely, satisfies the needs that use.

To illustrate the structural features and functions of the present invention more clearly, the present invention will be described in detail with reference to the accompanying drawings and specific embodiments.

Drawings

Fig. 1 is a schematic cross-sectional view of a preferred embodiment of the present invention.

The attached drawings indicate the following:

10. dyed wood skin layer 20, aqueous treatment agent layer

21. First abrasive layer 30, first aqueous open clear primer layer

31. Second polishing layer 40, second aqueous open clear primer layer

41. A third polished layer 50, a water-based full-matte open transparent top coat layer.

Detailed Description

Referring to fig. 1, a specific structure of a preferred embodiment of the present invention is shown, which includes a dyed wood skin layer 10, an aqueous treating agent layer 20, a first aqueous open transparent primer layer 30, a second aqueous open transparent primer layer 40, and an aqueous full matte open transparent top coat layer 50.

The aqueous treating agent layer 20 is coated on the surface of the dyed wood skin layer 10, and the surface of the aqueous treating agent layer 20 is provided with a first polishing layer 21; the aqueous treatment agent used in the aqueous treatment agent layer 20 is TB-MP 9101.

The first aqueous open transparent primer layer 30 is coated on the first polishing layer 21, and the surface of the first aqueous open transparent primer layer 30 has a second polishing layer 31; the first water-based open transparent primer layer 30 is a water-based open transparent primer having a model number of TB-MP 9101.

The second aqueous open transparent primer layer 40 is coated on the second polishing layer 31, and the surface of the second aqueous open transparent primer layer 40 is provided with a third polishing layer 41; the second water-based open transparent primer layer 40 adopts water-based open transparent primer with the model number of TB-MP 9101.

The aqueous fully matte open clear topcoat layer 50 is coated on the third polished layer 41. The type of the water-based full-matte open transparent finish paint adopted by the water-based full-matte open transparent finish paint layer 50 is TB-MP 9201-1.

Detailed description the manufacturing process of this embodiment is as follows:

firstly, performing veneer treatment such as white blank treatment, filling, light grinding, soot blowing and the like on dyed veneers, and controlling the water content to be 8-12% to obtain the dyed veneers 10.

Then, spraying the aqueous treating agent on the surface of the dyed veneer layer 10, thinly spraying a gun for uniform spraying, controlling the temperature to be 15-25 g/m/pass, and drying for more than or equal to 8 hours under the conditions of ventilation with the humidity of 40-70% and good air circulation at the temperature of 30 +/-3 ℃ to form an aqueous treating agent layer 20, and carrying out the next operation after ensuring sufficient drying.

Then, the surface of the aqueous treating agent layer 20 is lightly polished and smoothed, soot is blown, and sand is not leaked, and all parts, corners, edges and corners, etc. cannot be sanded through by using a 320# to 400# zinc powder sandpaper, which directly affects the quality of the following product and cannot be viewed lightly, thereby forming a first polished layer 21 on the surface of the aqueous treating agent layer 20.

Then, spraying a water-based open transparent primer on the surface of the first polishing layer 21, uniformly spraying a cross, controlling the temperature to be 60-80 g/M/pass, drying for more than or equal to 4 hours under the conditions of 30 +/-3 ℃, 40-70% humidity ventilation and good air circulation, forming a first water-based open transparent primer layer 30, and carrying out the next operation after ensuring sufficient drying.

Then, the raised burr portions were lightly ground to the surface of the first aqueous open transparent primer layer 30 with 400# zinc powder sandpaper, soot was blown, no sand was leaked, all portions, corners, edges and edges, etc. could not be sanded through, which directly affected the subsequent product quality and did not make it easy to see, thereby forming the second ground layer 31 on the surface of the first aqueous open transparent primer layer 30.

Then, the surface of the second polishing layer 31 is sprayed with the veneer open transparent primer, a cross is uniformly sprayed, the drying is controlled to be 60-80 g/M/pass, the second aqueous open transparent primer layer 40 is formed after drying is more than or equal to 4 hours under the conditions that the temperature is 30 +/-3 ℃, the humidity is 40-70% and ventilation and good air circulation are carried out, and the next operation is carried out after full drying is ensured.

Then, the raised burr portions are lightly ground and leveled on the surface of the second aqueous open transparent primer layer 40 with 400# zinc powder sandpaper, soot is blown, sand is not leaked, all the portions, edges, corners and the like cannot be sanded through, which directly affects the quality of the following product and cannot be lightly seen, thereby forming a third ground layer 41 on the surface of the second aqueous open transparent primer layer 40.

Finally, spraying the water-based full-matte open transparent finish paint on the surface of the third polished layer 41, uniformly spraying 1 cross paint, and controlling 80-100 g/M to be no sagging phenomenon. Leveling for 8-10 minutes at room temperature (if the room temperature is lower than 25 ℃, the leveling time needs to be prolonged), drying for at least 4 hours in a drying room with good flowing air, ensuring the temperature to be the best at 30 +/-3 ℃, controlling the humidity to be 40-70%, maintaining a paint film for at least more than 8 hours to form a water-based full-matte open transparent finish paint layer 50, and packaging for shipment.

The utility model discloses a design focus lies in: through set gradually aqueous finishing agent layer, the open transparent priming paint layer of first waterborne, the open transparent priming paint layer of second waterborne and the full dumb open transparent finish paint layer of waterborne on the surface on dyeing veneer layer to the cooperation forms each layer of polishing, makes to combine firmly between each layer, is difficult for droing, and can reach better visual effect, makes the beautiful appearance of dyeing veneer see-through out completely, satisfies the needs that use.

The above description is only a preferred embodiment of the present invention, and is not intended to limit the technical scope of the present invention, so that any slight modifications, equivalent changes and modifications made by the technical spirit of the present invention to the above embodiments are all within the scope of the technical solution of the present invention.

Claims

1. The utility model provides a full dumb open waterborne wood lacquer application layer structure of dyeing veneer which characterized in that: the paint comprises a dyed wood skin layer, a water-based treating agent layer, a first water-based open transparent primer layer, a second water-based open transparent primer layer and a water-based full-matte open transparent finish paint layer; the aqueous treating agent layer is coated on the surface of the dyed wood skin layer, and the surface of the aqueous treating agent layer is provided with a first polishing layer; the first aqueous open transparent primer layer is coated on the first polishing layer, and the surface of the first aqueous open transparent primer layer is provided with a second polishing layer; the second aqueous open transparent primer layer is coated on the second polishing layer, and the surface of the second aqueous open transparent primer layer is provided with a third polishing layer; the water-based full-matte open transparent finish paint layer is coated on the third polishing layer.

2. The full-matte open water-borne wood paint coating layer structure of the dyed veneers as claimed in claim 1, which is characterized in that: the type of the aqueous treating agent adopted by the aqueous treating agent layer is TB-MP 9101.

3. The full-matte open water-borne wood paint coating layer structure of the dyed veneers as claimed in claim 1, which is characterized in that: the first water-based open transparent primer layer adopts water-based open transparent primer with the model number of TB-MP 9101.

4. The full-matte open water-borne wood paint coating layer structure of the dyed veneers as claimed in claim 1, which is characterized in that: the water-based open transparent primer adopted by the second water-based open transparent primer layer is TB-MP 9101.

5. The full-matte open water-borne wood paint coating layer structure of the dyed veneers as claimed in claim 1, which is characterized in that: the water-based full-matte open transparent finish paint adopted by the water-based full-matte open transparent finish paint layer is TB-MP9201-1 in model number.