TWI612111B - BZ glaze paint material composition and painting method - Google Patents

Description

BZ glaze paint material composition and painting method

The present invention relates to a paint material composition, and more particularly to a BZ glaze paint material composition and a painting method.

As a kind of painting element, painting materials are an important part of the art of painting. Different materials express different artistic languages in decorative painting and produce different visual effects. In recent years, with the development of industrial technology, new types of painting materials have emerged in an endless stream. The innovation of new materials has promoted the development of painting art, supporting the artist's continuous exploration of the style and painting techniques of the works, through the harmonious combination of materials and unexpected performance techniques. Create a new visual language that makes the work more expressive and artistic.

The aesthetic orientation of traditional painting is accurate flat shape, complete visual space, elegant and layered color, and new painting materials change people's traditional aesthetic orientation. The focus of painting also transitions from pure hand-painting to screen production. The concern, including the sense of form and dimension of the work, people try to use the external features of the new painting materials and the inherent physical and chemical properties to produce the paintings, from the traditional "artist to talk with materials" to "artists let materials talk ".

In the late 1950s, former Soviet scientists Belousov and Zhabotinskii discovered in chemical experiments that when the appropriate conditions were met, the chemical substances involved in the reaction seemed to receive macroscopically. a unified command, the appearance of color or pattern self-organization Like, to form a consistent behavior in space and time, people call this phenomenon "chemical oscillation", and select the first letter of the name of the two-dimensional scientist, referred to as "BZ reaction."

Jingdezhen high-temperature color glaze porcelain plate painting is the modern invention of Jingdezhen. The porcelain plate painting is divided into glaze color, underglaze color and high temperature color glaze. It is a traditional craft from ancient times to the present. The high temperature color glaze has risen in the past half century.

When the existing high-temperature color glaze porcelain plate painting process is fired at a high temperature of 1300 to 1500 degrees, the color glaze will change color and become more vivid various saturated pigments, but various pigments are incompatible, unlike other paintings, such as Oil painting, gouache, watercolor, etc., the blending of various color glazes is not pure and unsaturated.

The main object of the present invention is to provide a BZ glaze paint material composition and a painting method.

The invention provides a BZ glaze paint material composition: a painting material composition made of natural mineral toner, synthetic resin and vinegar, adding color glaze, white color glaze and colorless glaze. Wherein the color glaze is composed of 60% by weight to 40% by weight of high temperature resistant color glaze mineral and 40% by weight to 60% by weight of water, the white color glaze consisting of 60% by weight of high temperature resistant white glaze mineral and 40% by weight A water composition consisting of 40% by weight of high temperature resistant colorless glaze mineral and 60% by weight of water. Wherein the natural mineral toner has a content weight of 5%, the synthetic resin has a content weight of 3%, and the vinegar has a content weight of 2% based on the total weight of the composition. Wherein the composition also has a lubricant having a weight percentage of no more than 3%. Wherein the composition also has a bactericide, the bactericide having a weight percentage of not more than 2%.

The composition disclosed in the present invention can be used as a drawing material, wherein each component raw material is It can be conveniently obtained on the market, and the raw materials of the components are mixed according to the corresponding ratios, and according to the steps and the process conditions disclosed in the present invention, the art works with the overall shape as an irregular pattern can be obtained, and many works have been auctioned. The market has achieved good returns. At the same time, the technical solutions disclosed in the present invention can also be used in the decoration and decoration industry, for example, the production of background walls, etc., so that it has high market value. Moreover, the preparation of the composition of the drawing material and the drawing of the invention can be carried out manually by the artist according to experience, or can be carried out by means of modern industrial technology and industrial production, and provides a variety of ways for the production of such works.

The invention and innovation of "BZ Art" high-temperature color glaze porcelain plate painting has solved the integration, penetration and evolution of various color glazes into various colors of the world, adding artistic charm to the world.

The invention and creation of "BZ Art" BZ high temperature color glaze is a technological revolution in history. It not only changes the fusion of various color glazes, but also makes the hue more pure, saturated and more gorgeous.

For a better understanding of the features and technical aspects of the present invention, reference should be made to the accompanying drawings.

1 is a BZ art drawing picture drawn in accordance with Embodiment 1 of the present invention.

2 is a BZ art drawing picture drawn in accordance with Embodiment 2 of the present invention.

3 is a BZ art drawing picture drawn in accordance with Embodiment 3 of the present invention.

4 is a BZ art drawing picture drawn in accordance with Embodiment 4 of the present invention.

Figure 5 is a BZ art drawing picture drawn in accordance with Embodiment 5 of the present invention.

Figure 6 is a BZ art drawing picture drawn in accordance with Embodiment 6 of the present invention.

Figure 7 is a BZ art drawing picture drawn in accordance with Embodiment 7 of the present invention.

Figure 8 is a BZ art drawing picture drawn in accordance with Embodiment 8 of the present invention.

Figure 9 is a BZ art drawing picture drawn in accordance with Embodiment 9 of the present invention.

Figure 10 is a BZ art drawing picture drawn in accordance with Embodiment 10 of the present invention.

Figure 11 is a BZ art drawing picture drawn in accordance with Embodiment 11 of the present invention.

The invention provides a BZ glaze paint material composition: from natural mineral toner, synthetic resin, vinegar and propylene (wherein, vinegar and propylene, also known as ethylene propylene), which is formed by copolymerization of vinyl acetate and butyl acrylate as main functional monomers. a drawing material composition prepared by using a water-soluble polymer resin, Vinyl acetate-acrylate, is added to a color glaze, a white color glaze, and a colorless glaze, wherein the color glaze is from 60 wt% to 40 wt%. a high temperature resistant color glaze mineral consisting of 40% by weight to 60% by weight of water, the white tinting glaze consisting of 60% by weight of high temperature resistant white glaze mineral and 40% by weight of water, the tonal color glaze being 40% by weight It is composed of high temperature resistant colorless glaze mineral and 60% by weight of water.

Further, in order to enhance the fluidity of the paint material composition of the present invention, a lubricant may be added to the above-mentioned paint material composition, and the lubricant may have a weight percentage of not more than 3%. Moreover, in order to improve the stability of the final art work and prolong the storage time, it is also possible to add a bactericide according to the above-mentioned paint material composition, and the bactericide has a weight percentage of not more than 2%.

The invention also provides a painting method for the above-mentioned paint material composition, which comprises the steps of making a canvas, making a bottom layer, drawing a picture, post-processing and the like.

First, make a canvas, select the natural linen of the appropriate size as the canvas according to the size of the screen, and waterproof and reinforce it. For example, the weight ratio of rabbit skin glue to water is 1:10. Make a glue, and evenly brush the canvas two or three times with the glue. After each brushing, it should be completely dried before the next brushing. Among them, the rabbit skin glue and water are made into a glue liquid, and the process of water-repellent tanning is adopted, and the tanning process needs continuous mixing.

Secondly, the bottom layer is made, the primer is painted on the linen cloth, and the canvas is primed and tinted, and can be made according to the weight ratio of 1 part water: 1 part titanium white powder: 1 part white powder: 1 part polyvinyl acetate. Forming the primer, applying the primer to the canvas as a bottom layer, and then drying it sufficiently; Pick up the picture, fix the bottom level of the canvas to the back board, and make a proper amount of the BZ glaze paint material composition according to paragraph [0014] according to the size of the canvas. After fully stirring, add high temperature resistant minerals and water according to the following. The weight ratio is matched to form red glaze, yellow glaze, blue glaze, green glaze, purple glaze, orange glaze and cyan glaze: the red glaze mineral and water ratio is 60%: 40%, yellow glaze mineral and water ratio is 55%: 45%, blue glaze mineral and water ratio is 65%: 35%, green glaze mineral and water ratio is 63%: 37 %, purple glaze mineral and water ratio is 70%: 30%, orange glaze mineral and water ratio is 68%: 32%, cyan glaze mineral and water ratio is 71%: 29%, After fully stirring, evenly spread the canvas; after 5-10 minutes, uniformly add natural mineral black powder or white powder, the weight of the black powder or white powder is 5% of the total weight of the BZ glaze paint material composition, with time The canvas of the transition is gradually irregular, and the canvas is in the final pattern after about 12 hours.

Finally, post-processing, waiting for the pattern to be fixed, the horizontal still canvas into The line is dried and naturally dried to a full temperature of 48-72 hours under normal temperature conditions. After being sufficiently dried, the patterned canvas is removed from the backing plate, and conventional operations such as boxing are performed as needed.

Hereinafter, FIGS. 1 to 11 are BZ art drawing pictures drawn according to Examples 1 to 11 of the present invention.

Example 1: Making a 180cm × 95cm BZ art painting

Manufacture of BZ glaze paint material composition: a painting material composition made of natural mineral toner (content 5 g), synthetic resin (content 3 g), vinegar C (content 2 g) is added to the color glaze, a white color glaze and a clear color glaze, wherein the color glaze is composed of 60% by weight to 40% by weight of high temperature resistant color glaze mineral and 40% by weight to 60% by weight of water, the white color glaze is 60% by weight The high temperature resistant white glaze mineral consists of 40% by weight of high temperature resistant colorless glaze mineral and 60% by weight of water, and 40% by weight of water.

In this embodiment, a BZ glaze paint material composition is used as an irregular BZ pattern art painting of 180 cm×95 cm, which is divided into process steps of making a canvas, making a bottom layer, drawing a picture, and post-processing.

Steps to make a canvas:

According to the size of the screen, select the natural linen of the appropriate size as the canvas, and waterproof and reinforce it. For example, make the rabbit skin glue and water into a glue ratio of 1:10, and evenly apply the cloth with the glue. Up to three times, each time the brush needs to be completely dried before the next brushing. Among them, the rabbit skin glue and water are made into a glue liquid, and the process of water-repellent tanning is adopted, and the tanning process needs continuous mixing.

Making the bottom layer step: brushing the bottom material on the linen cloth, and bottoming and coloring the canvas, which can be made according to the weight ratio of 1 part water: 1 part titanium white powder: 1 part white powder: 1 part polyvinyl acetate. bottom The primer was applied to the canvas as a primer and then dried thoroughly.

Step of drawing picture: Fix the level of the finished canvas on the back plate, and make a proper amount of the BZ glaze paint material composition according to paragraph [0031] according to the size of the canvas. After fully stirring, add the high temperature resistant mineral and water according to the following weight ratio. The ratio is red glaze, yellow glaze, blue glaze, green glaze, purple glaze, orange glaze and cyan glaze: red glaze mineral and water ratio is 60%: 40% The yellow glaze mineral and water ratio is 55%: 45%, the blue glaze mineral and water ratio is 65%: 35%, and the green glaze mineral and water ratio is 63%: 37%. Purple glaze mineral and water ratio is 70%: 30%, orange glaze mineral and water ratio is 68%: 32%, cyan glaze mineral and water ratio is 71%: 29%, fully stirred Afterwards, evenly spread the canvas; after 5-10 minutes, uniformly add natural mineral black powder or white powder, the weight of the black powder or white powder is 5% of the total weight of the BZ glaze paint material composition, as time goes by The canvas gradually became irregular and the canvas was in the final pattern after about 12 hours.

Finally, post-processing is carried out. After the pattern is fixed, the horizontal still canvas is dried, and naturally dried to a full temperature for 48-72 hours under normal temperature conditions. After being sufficiently dried, the patterned canvas is removed from the backing plate, and conventional operations such as boxing are performed as needed.

Example 2: Making a 180cm x 95cm BZ art painting

Manufacture of BZ glaze paint material composition: a painting material composition made of natural mineral toner (content 5 g), synthetic resin (content 3 g), vinegar C (content 2 g) a color glaze, a white color glaze, and a clear color glaze, wherein the color glaze is composed of 60% by weight to 40% by weight of high temperature resistant color glaze mineral and 40% by weight to 60% by weight of water, the white color glaze The material consisted of 60% by weight of high temperature resistant white glaze mineral and 40% by weight of water, which consisted of 40% by weight of high temperature resistant colorless glaze mineral and 60% by weight of water.

In this embodiment, the BZ glaze paint material composition BZ pattern art painting work prepared above is used, and the methods and steps used are basically the same as those in the first embodiment, and the same is not described again. It should be noted that in the drawing picture step, an appropriate amount of the BZ glaze paint material composition as described in paragraph [0047] is prepared according to the size of the canvas, and after fully stirring, the high temperature resistant mineral and the water are added according to the following weight ratio to form a red color. Glaze, yellow glaze, blue glaze, green glaze, purple glaze, orange glaze and cyan glaze: red glaze mineral and water ratio 60%: 40%, yellow glaze minerals and Water ratio is 55%: 45%, blue glaze mineral and water ratio is 65%: 35%, green glaze mineral and water ratio is 63%: 37%, purple glaze mineral and water The ratio is 70%: 30%, the orange glaze mineral and water ratio is 68%: 32%, the cyan glaze mineral and water ratio is 71%: 29%, after fully stirring, evenly spread the canvas; After 5-10 minutes of standing, the natural mineral black powder or white powder is uniformly added, and the weight of the black powder or white powder is 5% of the total weight of the BZ glaze paint material composition, and the canvas gradually becomes irregular pattern with time. The canvas was in the final pattern after about 12 hours.

Finally, post-processing, waiting for the pattern to be fixed, the horizontal still canvas into The line is dried and naturally dried to a full temperature of 48-72 hours under normal temperature conditions. After being sufficiently dried, the patterned canvas is removed from the backing plate, and conventional operations such as boxing are performed as needed.

Example 3: Making a 180cm x 95cm BZ art painting

Manufacture of BZ glaze paint material composition: a painting material composition made of natural mineral toner (content 5 g), synthetic resin (content 3 g), vinegar C (content 2 g) is added to the color glaze, a white color glaze and a clear color glaze, wherein the color glaze is composed of 60% by weight to 40% by weight of high temperature resistant color glaze mineral and 40% by weight to 60% by weight of water, the white color glaze is 60% by weight The high temperature resistant white glaze mineral consists of 40% by weight of high temperature resistant colorless glaze mineral and 60% by weight of water, and 40% by weight of water.

In this embodiment, an irregular BZ art painting work is drawn using the BZ glaze paint material composition prepared above, and the methods and steps used are basically the same as those in the first embodiment, and the same is not described again. It should be noted that in the step of drawing a picture, an appropriate amount of the BZ glaze paint material composition as described in paragraph [0059] is prepared according to the size of the canvas, and after fully stirring, the high temperature resistant mineral and the water are added in proportion to the following weight ratios to form a red color. Glaze, yellow glaze, blue glaze, green glaze, purple glaze, orange glaze and cyan glaze: red glaze mineral and water ratio 60%: 40%, yellow glaze minerals and Water ratio is 55%: 45%, blue glaze mineral and water ratio is 65%: 35%, green glaze mineral and water ratio is 63%: 37%, purple glaze mineral and water The ratio is 70%: 30%, the orange glaze mineral and water ratio is 68%: 32%, and the cyan glaze mineral and water ratio is 71%: 29%. After fully stirring, evenly spread the canvas; after 5-10 minutes, uniformly add natural mineral black powder or white powder, the weight of the black powder or white powder is 5% of the total weight of the BZ glaze paint material composition, with time The canvas of the transition is gradually irregular, and the canvas is in the final pattern after about 12 hours.

Finally, post-processing is carried out. After the pattern is fixed, the horizontal still canvas is dried, and naturally dried to a full temperature for 48-72 hours under normal temperature conditions. After being sufficiently dried, the patterned canvas is removed from the backing plate, and conventional operations such as boxing are performed as needed.

Example 4: Making a 180cm x 95cm BZ art painting

Manufacture of BZ glaze paint material composition: a painting material composition made of natural mineral toner (content 5 g), synthetic resin (content 3 g), vinegar C (content 2 g) is added to the color glaze, a white color glaze and a clear color glaze, wherein the color glaze is composed of 60% by weight to 40% by weight of high temperature resistant color glaze mineral and 40% by weight to 60% by weight of water, the white color glaze is 60% by weight The high temperature resistant white glaze mineral consists of 40% by weight of high temperature resistant colorless glaze mineral and 60% by weight of water, and 40% by weight of water.

In this embodiment, the BZ glaze paint material composition BZ pattern art painting work prepared above is used, and the methods and steps used are basically the same as those in the first embodiment, and the same is not described again. It should be noted that in the step of drawing the picture, an appropriate amount of the BZ glaze paint material composition as described in paragraph [0071] is prepared according to the size of the canvas, and after fully stirring, the high temperature resistant mineral and the water are added in proportion to the following weight ratios to form a red color. Glaze, yellow glaze, blue glaze, green glaze, purple glaze, orange glaze and cyan glaze: red glaze mineral and water ratio 60%: 40%, yellow glaze minerals and Water ratio is 55%: 45%, Blue glaze mineral and water ratio is 65%: 35%, green glaze mineral and water ratio is 63%: 37%, purple glaze mineral and water ratio is 70%: 30%, orange The glaze mineral and water ratio is 68%: 32%, the cyan glaze mineral and water ratio is 71%: 29%, after fully mixing, evenly spread the canvas; after 5-10 minutes, evenly add natural minerals. The substance black powder or white powder, the weight of the black powder or white powder is 5% of the total weight of the BZ glaze paint material composition, and the canvas gradually becomes irregular pattern with time, and the canvas is in a final pattern after about 12 hours.

Finally, post-processing is carried out. After the pattern is fixed, the horizontal still canvas is dried, and naturally dried to a full temperature for 48-72 hours under normal temperature conditions. After being sufficiently dried, the patterned canvas is removed from the backing plate, and conventional operations such as boxing are performed as needed.

Example 5: Making a 120cm x 90cm BZ art painting

Manufacture of BZ glaze paint material composition: a painting material composition made of natural mineral toner (content 5 g), synthetic resin (content 3 g), vinegar C (content 2 g) is added to the color glaze, a white color glaze and a clear color glaze, wherein the color glaze is composed of 60% by weight to 40% by weight of high temperature resistant color glaze mineral and 40% by weight to 60% by weight of water, the white color glaze is 60% by weight The high temperature resistant white glaze mineral consists of 40% by weight of high temperature resistant colorless glaze mineral and 60% by weight of water, and 40% by weight of water.

In this embodiment, the BZ glaze paint material composition BZ pattern art painting work prepared above is used, and the methods and steps used are basically the same as those in the first embodiment, and the same is not described again. Need to explain in the drawing screen step, according to the size of the canvas to make the right amount [0083] The BZ glaze paint material composition is fully stirred, and then added with high temperature resistant minerals and water according to the following weight ratio to form red glaze, yellow glaze, blue glaze, green glaze , purple glaze, orange glaze and cyan glaze: red glaze mineral and water ratio is 60%: 40%, yellow glaze mineral and water ratio is 55%: 45%, blue glaze ore The ratio of material to water is 65%: 35%, the ratio of mineral and water of green glaze is 63%: 37%, the ratio of mineral and water of purple glaze is 70%: 30%, orange glaze minerals and The water ratio is 68%: 32%, the ratio of mineral and water of cyan glaze is 71%: 29%. After fully stirring, evenly spread the canvas; after 5-10 minutes, evenly add natural mineral black powder or white powder. The weight of the black powder or white powder is 5% of the total weight of the BZ glaze paint material composition, and the canvas gradually becomes an irregular pattern over time, and the canvas is in a final pattern after about 12 hours.

Finally, post-processing is carried out. After the pattern is fixed, the horizontal still canvas is dried, and naturally dried to a full temperature for 48-72 hours under normal temperature conditions. After being sufficiently dried, the patterned canvas is removed from the backing plate, and conventional operations such as boxing are performed as needed.

Example 6: Making 55cm×55cm BZ high temperature color glazed porcelain plate painting

Kaolin (especially the unique kaolin in Jingdezhen) is added with water, the ratio is 7:3, and the mixture is stirred into a blank shape, and then pressed into a flat plate of different sizes, such as a mirror, with a thickness of 2 to 3 cm. It is not dried in the sun, it can be dried in about a week; various color glazes are made of pure natural high-temperature minerals and water: Red glaze mineral and water ratio is 55%: 45%, yellow glaze mineral and water ratio is 50%: 50%, blue glaze mineral and water ratio is 60%: 40%, green The glaze mineral and water ratio is 58%: 42%, the purple glaze mineral and water ratio is 65%: 35%, the orange glaze mineral and water ratio is 63%: 37%, cyan glaze The mineral and water ratio is 66%: 34%; after obtaining the above various color glazes, a white color glaze and a colorless glaze are added to the various color glazes, wherein the white color glaze is composed of 70wt% of high temperature resistant white glaze mineral and 30wt% water, the atone color glaze consists of 30wt% high temperature resistant colorless glaze mineral and 70wt% water: 10g per 500g red glaze White color glaze and 5g colorless glaze, add 15g white color glaze and 10g colorless glaze per 500g yellow glaze, add 20g white color glaze and 15g per 500g blue glaze Colorless glaze, adding 25g white glaze and 20g colorless glaze per 500g green glaze, adding 30g white glaze and 15g colorless per 500g purple glaze Material, 35g white tinting glaze and 20g colorless per 500g orange glaze Color glaze, 40g white color glaze and 25g colorless glaze are added to each 500g cyan glaze; various high-temperature color glaze paints obtained by the above ratio are applied to various color glazes in porcelain painting Interphase fusion, which makes the hue more pure, more saturated, and more splendid, is also included in the scope of protection of the present application.

Thereafter, the color glazes of the various color glazes after adding the white color glaze and the colorless glaze are drawn in the following steps: first, red, yellow, blue, green, purple, orange, and blue are respectively applied to the dried porcelain. Just on the board. Of course, the above is only the most preferred embodiment. Similarly, in accordance with the above-mentioned ratio and coloring order, the BZ artistic effect can be similarly achieved by using only the various color glazes including at least three kinds of red, yellow and blue added white color glaze and a clear color glaze.

It is advisable to create high-temperature color glaze porcelain paintings in September-October in Jingdezhen, and it is best to make porcelain paintings under this temperature and humidity.

When entering the kiln, it is best to use the gas kiln, followed by the electric kiln and the coal kiln. The first day of the kiln firing is controlled at a temperature of 500-600 degrees, and the next day is controlled at a high temperature of 600-800 degrees. After three days of control at a high temperature of 1,300-1,350 degrees, the fire can be stopped and placed in the kiln for three to four days to cool naturally and the outside weather temperature is close to the kiln.

Example 7: Making 180cm × 120cm BZ art painting plexiglass

In addition to BZ high-temperature color glazed porcelain paintings and BZ art painting fabrics, BZ art paintings can still be realized on plexiglass. Among them, BZ plexiglass is directly purchased on the market, and the painting methods and steps are the same as canvas and porcelain painting. of. After painting, the plexiglass is at normal temperature (about Indoor zero to ~50 degrees) under the shade.

Example 8: Making 180cm × 120cm BZ art painting plexiglass

In addition to BZ high-temperature color glazed porcelain paintings and BZ art painting fabrics, BZ art paintings can still be realized on plexiglass. Among them, BZ plexiglass is directly purchased on the market, and the painting methods and steps are the same as canvas and porcelain painting. of. After painting, the plexiglass is dried in the natural environment (within a room temperature of ~50 degrees).

Example 9: Making 170cm×84cm BZ high temperature color glazed porcelain plate painting

Kaolin (especially the unique kaolin in Jingdezhen) is added with water, the ratio is 7:3, and the mixture is stirred into a blank shape, and then pressed into a flat plate of different sizes, such as a mirror, with a thickness of 2 to 3 cm. Do not dry in the sun, about a week or so; all kinds of color glaze is made of pure natural high temperature minerals plus water ratio: red glaze mineral and water ratio is 55%: 45%, yellow glaze The mineral and water ratio is 50%: 50%, the blue glaze mineral and water ratio is 60%: 40%, the green glaze mineral and water ratio is 58%: 42%, purple glaze The mineral and water ratio is 65%: 35%, the orange glaze mineral and water ratio is 63%: 37%, and the cyan glaze mineral and water ratio is 66%: 34%; After the glaze, a white color glaze and a colorless glaze are added to the various color glazes, wherein the white color glaze is composed of 70% by weight of high temperature resistant white glaze mineral and 30% by weight of water. The colorless glaze consists of 30% by weight of high temperature resistant colorless glaze mineral and 70% by weight of water: Add 10g white color glaze and 5g colorless glaze to each 500g red glaze, add 15g white color glaze and 10g colorless glaze per 500g yellow glaze, add every 500g blue glaze 20g white color glaze and 15g colorless glaze, add 25g white color glaze and 20g colorless glaze per 500g green glaze, add 30g white color glaze and 15g per 500g purple glaze a colorless glaze, adding 35g of white toning glaze and 20g of colorless glaze per 500g of orange glaze, adding 40g of white toning glaze and 25g of colorless glaze per 500g of cyan glaze; The various high-temperature color glaze paints obtained in the matching are used for the fusion of various color glazes in the porcelain plate painting, and the hue is more pure, more saturated and more splendid, and is also included in the protection scope of the present application.

Example 10: Making a 170 cm × 84 cm high temperature color glazed porcelain plate painting

Kaolin (especially the unique kaolin in Jingdezhen) is added with water, the ratio is 7:3, and the mixture is stirred into a blank shape, and then pressed into a flat plate of different sizes, such as a mirror, with a thickness of 2 to 3 cm. It is not dried in the sun, it can be dried in about a week; various color glazes are made of pure natural high-temperature minerals and water: Red glaze mineral and water ratio is 55%: 45%, yellow glaze mineral and water ratio is 50%: 50%, blue glaze mineral and water ratio is 60%: 40%, green The glaze mineral and water ratio is 58%: 42%, the purple glaze mineral and water ratio is 65%: 35%, the orange glaze mineral and water ratio is 63%: 37%, cyan glaze The mineral and water ratio is 66%: 34%; after obtaining the above various color glazes, a white color glaze and a colorless glaze are added to the various color glazes, wherein the white color glaze is composed of 70wt% of high temperature resistant white glaze mineral and 30wt% water, the atone color glaze consists of 30wt% high temperature resistant colorless glaze mineral and 70wt% water: 10g per 500g red glaze White color glaze and 5g colorless glaze, add 15g white color glaze and 10g colorless glaze per 500g yellow glaze, add 20g white color glaze and 15g per 500g blue glaze Colorless glaze, adding 25g white glaze and 20g colorless glaze per 500g green glaze, adding 30g white glaze and 15g colorless per 500g purple glaze Material, per 500g orange glaze added 35g and 20g white glaze no toner hue Color glaze, 40g white color glaze and 25g colorless glaze are added to each 500g cyan glaze; various high temperature color glaze paints obtained by the above ratio are used in porcelain stencil painting between various color glazes The fusion, the hue is more pure, more saturated, more splendid, and is also included in the scope of protection of the present application.

Example 11: Making a 170 cm × 84 cm high temperature color glazed porcelain plate

Kaolin (especially the unique kaolin in Jingdezhen) is added with water, the ratio is 7:3, and the mixture is stirred into a blank shape, and then pressed into a flat plate of different sizes, such as a mirror, with a thickness of 2 to 3 cm. Do not dry in the sun, about a week or so; all kinds of color glaze is made of pure natural high temperature minerals plus water ratio: red glaze mineral and water ratio is 55%: 45%, yellow glaze The mineral and water ratio is 50%: 50%, the blue glaze mineral and water ratio is 60%: 40%, the green glaze mineral and water ratio is 58%: 42%, purple glaze The mineral and water ratio is 65%: 35%, the orange glaze mineral and water ratio is 63%: 37%, and the cyan glaze mineral and water ratio is 66%: 34%; After the glaze, a white color glaze and a colorless glaze are added to the various color glazes, wherein the white color glaze is composed of 70% by weight of high temperature resistant white glaze mineral and 30% by weight of water. The colorless glaze consists of 30% by weight of high temperature resistant colorless glaze mineral and 70% by weight of water: Add 10g white color glaze and 5g colorless glaze to each 500g red glaze, add 15g white color glaze and 10g colorless glaze per 500g yellow glaze, add every 500g blue glaze 20g white color glaze and 15g colorless glaze, add 25g white color glaze and 20g colorless glaze per 500g green glaze, add 30g white color glaze and 15g per 500g purple glaze a colorless glaze, adding 35g of white toning glaze and 20g of colorless glaze per 500g of orange glaze, adding 40g of white toning glaze and 25g of colorless glaze per 500g of cyan glaze; The various high-temperature color glaze paints obtained in the matching are used for the fusion of various color glazes in the porcelain plate painting, and the hue is more pure, more saturated and more splendid, and is also included in the protection scope of the present application.

The above is only the preferred embodiment of the present invention, and is not intended to limit the scope of the invention, and the equivalents of the present invention and the equivalents of the drawings are all included in the present invention. Within the scope of protection.

Claims (4)

A BZ glaze paint material composition: a painting material composition made of natural mineral toner, synthetic resin and vinegar, adding color glaze, white color glaze and colorless glaze, wherein the color The glaze is composed of 60% by weight to 40% by weight of high temperature resistant color glaze mineral and 40% by weight to 60% by weight of water, the white color glaze consisting of 60% by weight of high temperature resistant white glaze mineral and 40% by weight of water, The clear color glaze is composed of 40% by weight of high temperature resistant colorless glaze mineral and 60% by weight of water; wherein the natural mineral toner has a content weight of 5% based on the total weight of the composition, the synthetic resin The content weight is 3%, and the vinegar content is 2% by weight. The BZ glaze paint material composition according to claim 1, wherein the composition further comprises a lubricant having a weight percentage of not more than 3%. The BZ glaze paint material composition according to claim 1, wherein the composition further comprises a bactericide having a weight percentage of not more than 2%. A painting method for a BZ glaze paint material composition, the method comprising: making a canvas, selecting a natural linen of a suitable size as a canvas according to a screen size, performing waterproofing and reinforcement treatment on the same; making a bottom layer, and painting the bottom on the canvas Material, base and color the canvas, and then fully dry; and draw a picture, the bottom layer of the canvas is fixed horizontally to the back plate, according to the size of the canvas to make an appropriate amount of BZ glaze paint material composition as claimed in claim 1, fully After mixing, the high temperature resistant color glaze mineral and water are added according to the following weight ratio. The high temperature resistant color glaze mineral contains red glaze mineral, yellow glaze mineral, blue glaze mineral, green Glaze minerals, purple glaze minerals, orange glaze minerals and cyan glaze minerals, forming red glaze, yellow glaze, blue glaze, green glaze, purple glaze, orange glaze and cyan Glaze: red glaze mineral and water ratio is 60%: 40%, yellow glaze mineral and water ratio is 55%: 45%, blue glaze mineral and water ratio is 65%: 35 %, green glaze mineral and water ratio is 63%: 37%, purple glaze mineral and water ratio is 70%: 30%, orange glaze mineral and water ratio is 68%: 32%, The cyan glaze mineral and water ratio is 71%: 29%.