WO2017120759A1 - Bz glaze painting pigment composition and painting method using same - Google Patents

Bz glaze painting pigment composition and painting method using same Download PDF

Info

Publication number
WO2017120759A1
WO2017120759A1 PCT/CN2016/070663 CN2016070663W WO2017120759A1 WO 2017120759 A1 WO2017120759 A1 WO 2017120759A1 CN 2016070663 W CN2016070663 W CN 2016070663W WO 2017120759 A1 WO2017120759 A1 WO 2017120759A1
Authority
WO
WIPO (PCT)
Prior art keywords
glaze
mineral
weight
painting
water
Prior art date
Application number
PCT/CN2016/070663
Other languages
French (fr)
Chinese (zh)
Inventor
张利
Original Assignee
张利
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 张利 filed Critical 张利
Priority to RU2018124618A priority Critical patent/RU2721015C2/en
Priority to PCT/CN2016/070663 priority patent/WO2017120759A1/en
Priority to JP2018536201A priority patent/JP6761864B2/en
Publication of WO2017120759A1 publication Critical patent/WO2017120759A1/en

Abstract

Disclosed is a BZ glaze painting pigment composition. The pigment composition consists of a painting material composition added with varying proportions of a colored glaze, a white toning glaze and a colorless toning glaze, the painting material composition being prepared from a natural mineral pigment powder, a synthetic resin and a vinyl acetate-acrylate. Also disclosed is a painting method using the BZ glaze painting pigment composition, comprising the following steps: preparing a canvas, applying a base coat, and painting a picture. In the step of painting the picture, a suitable amount of the BZ glaze painting pigment composition is prepared according to the size of the canvas. The composition is then thoroughly stirred before adding a heat-resistant mineral and water in a specific weight ratio to form a red glaze material, a yellow glaze material, a blue glaze material, a green glaze material, a purple glaze material, an orange glaze material and a cyan glaze material respectively. The glaze materials are then mixed to obtain an artistic BZ painting with an overall shape composed of irregular patterns.

Description

BZ釉绘画颜料材料组合物及绘画方法BZ glaze paint material composition and painting method 技术领域Technical field
本发明涉及绘画颜料材料组合物，尤其涉及一种BZ釉绘画颜料材料组合物及绘画方法。The present invention relates to a paint material composition, and more particularly to a BZ glaze paint material composition and a painting method.
背景技术Background technique
绘画材料作为一种绘画要素，是绘画艺术的重要组成部分，不同材料在装饰绘画中表达不同的艺术语言，产生不同的视觉效果。近年来，随着工业技术的发展，新型绘画材料层出不穷，新材料的创新推动了绘画艺术的发展，支撑了艺术家对作品风格、绘画技法的不断探索，通过材料的和谐组合和出人意料的表现技巧，创造出新的视觉语言，使作品更富表现力和艺术感染力。As a kind of painting element, painting materials are an important part of the art of painting. Different materials express different artistic languages in decorative painting and produce different visual effects. In recent years, with the development of industrial technology, new types of painting materials have emerged in an endless stream. The innovation of new materials has promoted the development of painting art, supporting the artist's continuous exploration of the style and painting techniques of the works, through the harmonious combination of materials and unexpected performance techniques. Create a new visual language that makes the work more expressive and artistic.
传统绘画的审美取向是有准确的平面造型、完整的视觉空间、优雅而有层次的色彩，而新型绘画材料改变了人们传统的审美取向，绘画的重心也从纯粹的手工描绘过渡到对画面制作的关注，包括作品的形式感及维度，人们尝试着利用新型绘画材料的外部特点及内在的物理化学特性进行绘画作品的制作，表现形式从传统的“艺术家用材料说话”到“艺术家让材料说话”。The aesthetic orientation of traditional painting is accurate flat shape, complete visual space, elegant and layered color, and new painting materials change people's traditional aesthetic orientation. The focus of painting also transitions from pure hand-painting to screen production. The concern, including the sense of form and dimension of the work, people try to use the external features of the new painting materials and the inherent physical and chemical properties to produce the paintings, from the traditional "artist to talk with materials" to "artists let materials talk ".
二十世纪五十年代末，前苏联科学家别罗索夫(Belousov)和柴波廷斯基(Zhabotinskii)在化学实验中发现，当满足适当条件时，参加反应的化学物质在宏观上好像接到某种统一命令，出现色彩或图案的自组织现象，形成空间和时间上的一致行为，人们将这一现象称为“化学振荡”，并选取两位科学家名字的首字母，简称为“BZ反应”。In the late 1950s, former Soviet scientists Belousov and Zhabotinskii discovered in chemical experiments that when the appropriate conditions were met, the chemical substances involved in the reaction seemed to receive macroscopically. A unified command, the appearance of color or pattern self-organization, forming a consistent behavior in space and time, people call this phenomenon "chemical oscillation", and select the first letter of the name of two scientists, referred to as "BZ reaction ".
景德镇高温颜色釉瓷板画，是景德镇近现代的发明创造，瓷板画分釉上彩、釉下彩和高温颜色釉，是从古至今的传统工艺，近半个世纪以来高温颜色釉兴起。Jingdezhen high-temperature color glaze porcelain plate painting is the modern invention of Jingdezhen. The porcelain plate painting is divided into glaze color, underglaze color and high temperature color glaze. It is a traditional craft from ancient times to the present. The high temperature color glaze has risen in the past half century.
现有的高温颜色釉瓷板画工艺经过1300度到1500度高温烧制时，颜色釉会出现变色，变成更鲜艳的各种饱和色素，但各种色素是不相融的，不像其它画种，如油画、水粉、水彩等，其各种颜色釉料之间的相融不纯正、不饱和。When the existing high-temperature color glaze porcelain plate painting process is fired at a high temperature of 1300 to 1500 degrees, the color glaze will change color and become more vivid various saturated pigments, but the various pigments are incompatible, unlike other Painting species, such as oil painting, gouache, watercolor, etc., the blending of various color glazes is not pure and unsaturated.
发明内容Summary of the invention
本发明的主要目的在于提供一种BZ釉绘画颜料材料组合物及绘画方法。The main object of the present invention is to provide a BZ glaze paint material composition and a painting method.
本发明提供了一种BZ釉绘画颜料材料组合物：由天然矿物质色粉、合成树脂、醋丙所制成的绘画材料组合物加入颜色釉料、白色调色釉料以及无色调色釉料，其中所述颜色釉料由60wt％至40wt％的耐高温颜色釉料矿物质和40wt％至60wt％的水组成，所述白色调色釉料由60wt％的耐高温白色釉料矿物质和40wt％的水组成，所述无色调 色釉料由40wt％的耐高温无色釉料矿物质和60wt％的水组成。The invention provides a BZ glaze paint material composition: a paint material composition made of natural mineral toner, synthetic resin and vinegar, adding color glaze, white color glaze and colorless glaze Wherein the color glaze is composed of 60% by weight to 40% by weight of high temperature resistant color glaze mineral and 40% by weight to 60% by weight of water, the white color glaze consisting of 60% by weight of high temperature resistant white glaze minerals and 40% by weight of water, the colorless The glaze consists of 40% by weight of high temperature resistant colorless glaze mineral and 60% by weight of water.
其中，基于该组合物的总重量，所述天然矿物质色粉的含量为5wt％，所述合成树脂的含量为3wt％，所述醋丙的含量为2wt％。Wherein, the content of the natural mineral toner is 5% by weight, the content of the synthetic resin is 3% by weight, and the content of the vinegar is 2% by weight based on the total weight of the composition.
其中，该组合物还有润滑剂，该润滑剂的重百分比含量不超过3％。Wherein, the composition also has a lubricant, and the lubricant has a weight percentage of not more than 3%.
其中，该组合物还有杀菌剂，该杀菌剂的重百分比含量不超过2％。Wherein, the composition also has a bactericide, and the bactericide has a weight percentage of not more than 2%.
本发明涉及的可作为绘画材料的组合物，其中各组分原料均可方便地在市场上取得，将各组分原料按照相应配比进行混合，并根据本发明涉及的步骤及工艺条件使用，可获得整体造型为不规则图案的美术作品，多件作品已在拍卖市场取得很好的回报，同时，本发明涉及的技术方案还可用于装饰装修行业中，例如背景墙面的制作等，故具有较高的市场价值。而且，本发明制备绘画材料组合物及绘制作品的操作，既可以由艺术家根据经验手工完成，也可以利用现代的工业技术，采用工业化生产的方式进行，为此类作品的生产提供了多种方式。The invention relates to a composition which can be used as a drawing material, wherein each component raw material can be conveniently obtained on the market, and the raw materials of each component are mixed according to the corresponding ratio, and are used according to the steps and process conditions involved in the present invention. The art works with an overall pattern of irregular patterns can be obtained, and many works have achieved good returns in the auction market. At the same time, the technical solutions involved in the present invention can also be used in the decoration and decoration industry, for example, the production of background walls, etc. Has a high market value. Moreover, the preparation of the composition of the drawing material and the drawing of the invention can be carried out manually by the artist according to experience, or can be carried out by means of modern industrial technology and industrial production, and provides various ways for the production of such works. .
“BZ艺术”高温颜色釉瓷板画的发明与创新解决了各种颜色釉料之间的相融、渗透、演变成大千世界的各种色彩，给世界增添了艺术的魅力。The invention and innovation of "BZ Art" high-temperature color glaze porcelain plate painting has solved the integration, penetration and evolution of various color glazes into various colors of the world, adding artistic charm to the world.
“BZ艺术”BZ高温颜色釉的发明创造与成功实现，是有史以来的技术革命，不但改变了各种颜色釉料之间相融合更使色相更纯、更饱和、更绚烂。The invention and creation of "BZ Art" BZ high temperature color glaze is a technological revolution in history. It not only changes the fusion of various color glazes, but also makes the hue more pure, saturated and more gorgeous.
附图说明DRAWINGS
图1是根据本发明的实施例1所绘制的BZ艺术绘画画面。1 is a BZ art drawing picture drawn in accordance with Embodiment 1 of the present invention.
图2是根据本发明的实施例2所绘制的BZ艺术绘画画面。2 is a BZ art drawing picture drawn in accordance with Embodiment 2 of the present invention.
图3是根据本发明的实施例3所绘制的BZ艺术绘画画面。3 is a BZ art drawing picture drawn in accordance with Embodiment 3 of the present invention.
图4是根据本发明的实施例4所绘制的BZ艺术绘画画面。4 is a BZ art drawing picture drawn in accordance with Embodiment 4 of the present invention.
图5是根据本发明的实施例5所绘制的BZ艺术绘画画面。Figure 5 is a BZ art drawing picture drawn in accordance with Embodiment 5 of the present invention.
图6是根据本发明的实施例6所绘制的BZ艺术绘画画面。Figure 6 is a BZ art drawing picture drawn in accordance with Embodiment 6 of the present invention.
图7是根据本发明的实施例7所绘制的BZ艺术绘画画面。Figure 7 is a BZ art drawing picture drawn in accordance with Embodiment 7 of the present invention.
图8是根据本发明的实施例8所绘制的BZ艺术绘画画面。Figure 8 is a BZ art drawing picture drawn in accordance with Embodiment 8 of the present invention.
图9是根据本发明的实施例9所绘制的BZ艺术绘画画面。Figure 9 is a BZ art drawing picture drawn in accordance with Embodiment 9 of the present invention.
图10是根据本发明的实施例10所绘制的BZ艺术绘画画面。Figure 10 is a BZ art drawing picture drawn in accordance with Embodiment 10 of the present invention.
图11是根据本发明的实施例11所绘制的BZ艺术绘画画面。Figure 11 is a BZ art drawing picture drawn in accordance with Embodiment 11 of the present invention.
具体实施方式detailed description
为使能更进一步了解本发明的特征及技术内容，请参阅以下有关本发明的详细说明与附图，然而所附图式仅提供参考与说明用，并非用来对本发明加以限制。 For a better understanding of the features and technical aspects of the present invention, reference should be made to the accompanying drawings.
本发明提供一种BZ釉绘画颜料材料组合物：由天然矿物质色粉、合成树脂、醋丙(其中，醋丙又称乙丙。是以醋酸乙烯和丙烯酸丁酯为主要功能单体共聚而成的水性高分子树脂，英文Vinyl acetate-acrylate)所制成的绘画材料组合物加入颜色釉料、白色调色釉料以及无色调色釉料，其中该颜色釉料由60wt％至40wt％的耐高温颜色釉料矿物质和40wt％至60wt％的水组成，该白色调色釉料由60wt％的耐高温白色釉料矿物质和40wt％的水组成，该无色调色釉料由40wt％的耐高温无色釉料矿物质和60wt％的水组成。The invention provides a BZ glaze paint material composition: from natural mineral toner, synthetic resin, vinegar and propylene (wherein, vinegar and propylene are also called ethylene propylene. The copolymer is composed of vinyl acetate and butyl acrylate as main functional monomers. A drawing material composition prepared by using a water-based polymer resin, Vinyl acetate-acrylate, is added to a color glaze, a white color glaze, and a colorless glaze, wherein the color glaze is from 60 wt% to 40 wt%. a high temperature resistant color glaze mineral consisting of 40% by weight to 60% by weight of water, the white tinting glaze consisting of 60% by weight of high temperature resistant white glaze mineral and 40% by weight of water, the tonal color glaze being 40% by weight It is composed of high temperature resistant colorless glaze mineral and 60% by weight of water.
另外，为增强本发明的绘画颜料材料组合物的流动性，可以在上述绘画颜料材料组合物加入润滑剂，该润滑剂的重百分比含量不超过3％。而且，为提高最终美术作品的稳定性，延长保存时间，还可比在上述绘画颜料材料组合物加入杀菌剂，该杀菌剂的重百分比含量不超过2％。Further, in order to enhance the fluidity of the paint material composition of the present invention, a lubricant may be added to the above-mentioned paint material composition, and the lubricant may have a weight percentage of not more than 3%. Moreover, in order to improve the stability of the final art work and prolong the storage time, it is also possible to add a bactericide according to the above-mentioned paint material composition, and the bactericide has a weight percentage of not more than 2%.
本发明还提供上述绘画颜料材料组合物的绘画方法，该方法包含制作画布、制作底层、绘制画面、后期处理等工艺步骤组成。The invention also provides a painting method for the above-mentioned paint material composition, which comprises the steps of making a canvas, making a bottom layer, drawing a picture, post-processing and the like.
首先，制作画布，根据画面大小选择适合尺寸的天然亚麻布作为画布，对其进行防水、加固处理，将兔皮胶与水以1：10的重量比制成胶液，并用该胶液均匀涂刷画布二至三次，每次涂刷需完全干燥后再进行下次涂刷。其中，兔皮胶与水制成胶液中采用隔水熬制的工艺，熬制过程需进行持续搅拌。First, make a canvas, select the natural linen of the appropriate size as the canvas according to the size of the screen, waterproof and reinforce it, and make the glue of the rabbit skin glue and water in a weight ratio of 1:10, and evenly apply the glue. Brush the canvas two or three times, and then apply it completely after each brushing. Among them, the rabbit skin glue and water are made into a glue liquid, and the process of water-repellent tanning is adopted, and the tanning process needs continuous stirring.
其次，制作底层，在所述亚麻布上涂刷底料，对画布进行打底及调色，可按照1份水：1份钛白粉：1份垩白粉：1份聚醋酸乙烯的重量比制成底料，将该底料涂刷在画布上作为底层，然后充分干燥；Secondly, the bottom layer is made, the primer is painted on the linen cloth, and the canvas is primed and tinted, and can be made according to the weight ratio of 1 part water: 1 part titanium white powder: 1 part white powder: 1 part polyvinyl acetate. Forming the primer, applying the primer to the canvas as a bottom layer, and then drying it sufficiently;
接者，绘制画面，将完成底层的画布水平固定于背板，根据画布尺寸制作适量的所述BZ釉绘画颜料材料组合物，充分搅拌后加入耐高温矿物质与水按照以下重量比进行配比，分别形成红色釉料、黄色釉料、蓝色釉料、绿色釉料、紫色釉料、橙色釉料和青色釉料：Pick up the picture, fix the bottom layer of the canvas to the back plate horizontally, and make an appropriate amount of the BZ glaze paint material composition according to the size of the canvas. After mixing, add the high temperature resistant mineral and water according to the following weight ratio. , forming red glaze, yellow glaze, blue glaze, green glaze, purple glaze, orange glaze and cyan glaze:
红色釉料矿物质和水配比为60％：40％，Red glaze mineral and water ratio is 60%: 40%,
黄色釉料矿物质和水配比为55％：45％，The yellow glaze mineral and water ratio is 55%: 45%.
蓝色釉料矿物质和水配比为65％：35％，Blue glaze mineral and water ratio is 65%: 35%,
绿色釉料矿物质和水配比为63％：37％，The green glaze mineral and water ratio is 63%: 37%,
紫色釉料矿物质和水配比为70％：30％，Purple glaze mineral and water ratio is 70%: 30%,
橙色釉料矿物质和水配比为68％：32％，Orange glaze mineral and water ratio is 68%: 32%,
青色釉料矿物质和水配比为71％：29％， The ratio of mineral and water for cyan glaze is 71%: 29%.
充分搅拌后，均匀涂满画布；放置5-10分钟后均匀加入天然矿物质黑粉或白粉，该黑粉或白粉的重量为所述BZ釉绘画颜料材料组合物总重5％，随着时间的推移画布逐渐呈不规则图案，约12小时后画布呈最终图案。After fully stirring, evenly spread the canvas; after 5-10 minutes, uniformly add natural mineral black powder or white powder, the weight of the black powder or white powder is 5% of the total weight of the BZ glaze paint material composition, with time The canvas of the transition is gradually irregular, and the canvas is in the final pattern after about 12 hours.
最后进行后期处理，等待图案固定不变后，水平静止画布进行干燥，在常温条件下，自然干燥至完全(干燥时间为48-72小时)。待充分干燥后将带有图案的画布从背板取下，根据需要进行加框等常规操作。Finally, post-treatment is carried out. After the pattern is fixed, the horizontal still canvas is dried, and naturally dried to completeness under normal temperature conditions (drying time is 48-72 hours). After being sufficiently dried, the patterned canvas is removed from the backing plate, and conventional operations such as boxing are performed as needed.
以下，图1～图11是根据本发明的实施例1～11所绘制的BZ艺术绘画画面。Hereinafter, FIGS. 1 to 11 are BZ art drawing pictures drawn according to Examples 1 to 11 of the present invention.
实施例1：制作180cm×95cm BZ艺术绘画作品Example 1: Making a 180cm × 95cm BZ art painting
制造BZ釉绘画颜料材料组合物：由天然矿物质色粉(含量5克)、合成树脂(含量3克)、醋丙(含量2克)所制成的绘画材料组合物加入颜色釉料、白色调色釉料以及无色调色釉料，其中该颜色釉料由60wt％至40wt％的耐高温颜色釉料矿物质和40wt％至60wt％的水组成，该白色调色釉料由60wt％的耐高温白色釉料矿物质和40wt％的水组成，该无色调色釉料由40wt％的耐高温无色釉料矿物质和60wt％的水组成。Manufacture of BZ glaze paint material composition: painting material composition made of natural mineral toner (content 5 g), synthetic resin (content 3 g), vinegar c (2 g) added color glaze, white a color glaze and a clear color glaze, wherein the color glaze is composed of 60% by weight to 40% by weight of high temperature resistant color glaze mineral and 40% by weight to 60% by weight of water, the white color glaze is 60% by weight It is composed of a high temperature resistant white glaze mineral and 40% by weight of water, which is composed of 40% by weight of high temperature resistant colorless glaze mineral and 60% by weight of water.
本实施例使用BZ釉绘画颜料材料组合物作180cm×95cm的不规则BZ图案艺术绘画作品，分为制作画布、制作底层、绘制画面、后期处理等工艺步骤。In this embodiment, a BZ glaze paint material composition is used as an irregular BZ pattern art painting of 180 cm×95 cm, which is divided into process steps of making a canvas, making a bottom layer, drawing a picture, and post-processing.
制作画布步骤：Steps to make a canvas:
根据画面大小选择适合尺寸的天然亚麻布作为画布，对其进行防水、加固处理，例如，将兔皮胶与水以1：10的重量比制成胶液，并用该胶液均匀涂刷画布二至三次，每次涂刷需完全干燥后再进行下次涂刷。其中，兔皮胶与水制成胶液中采用隔水熬制的工艺，熬制过程需进行持续搅拌。According to the size of the screen, select the natural linen of the appropriate size as the canvas, and waterproof and reinforce it. For example, make the rabbit skin glue and water into a glue ratio of 1:10, and evenly apply the cloth with the glue. Up to three times, each time the brush needs to be completely dried before the next brushing. Among them, the rabbit skin glue and water are made into a glue liquid, and the process of water-repellent tanning is adopted, and the tanning process needs continuous stirring.
制作底层步骤：在所述亚麻布上涂刷底料，对画布进行打底及调色，可按照1份水：1份钛白粉：1份垩白粉：1份聚醋酸乙烯的重量比制成底料，将该底料涂刷在画布上作为底层，然后充分干燥。Making the bottom layer step: brushing the bottom material on the linen cloth, and bottoming and coloring the canvas, which can be made according to the weight ratio of 1 part water: 1 part titanium white powder: 1 part white powder: 1 part polyvinyl acetate. The primer is applied to the canvas as a primer and then dried thoroughly.
绘制画面步骤：将完成底层的画布水平固定于背板，根据画布尺寸制作适量的上述BZ釉绘画颜料材料组合物，充分搅拌后加入耐高温矿物质与水按照以下重量比进行配比，分别形成红色釉料、黄色釉料、蓝色釉料、绿色釉料、紫色釉料、橙色釉料和青色釉料：Steps of drawing the picture: Fix the bottom layer of the canvas horizontally on the back plate, and make an appropriate amount of the BZ glaze paint material composition according to the size of the canvas. After fully stirring, add the high temperature resistant mineral and water according to the following weight ratio to form, respectively, Red glaze, yellow glaze, blue glaze, green glaze, purple glaze, orange glaze and cyan glaze:
红色釉料矿物质和水配比为60％：40％，Red glaze mineral and water ratio is 60%: 40%,
黄色釉料矿物质和水配比为55％：45％，The yellow glaze mineral and water ratio is 55%: 45%.
蓝色釉料矿物质和水配比为65％：35％，Blue glaze mineral and water ratio is 65%: 35%,
绿色釉料矿物质和水配比为63％：37％， The green glaze mineral and water ratio is 63%: 37%,
紫色釉料矿物质和水配比为70％：30％，Purple glaze mineral and water ratio is 70%: 30%,
橙色釉料矿物质和水配比为68％：32％，Orange glaze mineral and water ratio is 68%: 32%,
青色釉料矿物质和水配比为71％：29％，The ratio of mineral and water for cyan glaze is 71%: 29%.
充分搅拌后，均匀涂满画布；放置5-10分钟后均匀加入天然矿物质黑粉或白粉，该黑粉或白粉的重量为所述BZ釉绘画颜料材料组合物总重5％，随着时间的推移画布逐渐呈不规则图案，约12小时后画布呈最终图案。After fully stirring, evenly spread the canvas; after 5-10 minutes, uniformly add natural mineral black powder or white powder, the weight of the black powder or white powder is 5% of the total weight of the BZ glaze paint material composition, with time The canvas of the transition is gradually irregular, and the canvas is in the final pattern after about 12 hours.
最后进行后期处理，等待图案固定不变后，水平静止画布进行干燥，在常温条件下，自然干燥至完全(干燥时间为48-72小时)。待充分干燥后将带有图案的画布从背板取下，根据需要进行加框等常规操作。Finally, post-treatment is carried out. After the pattern is fixed, the horizontal still canvas is dried, and naturally dried to completeness under normal temperature conditions (drying time is 48-72 hours). After being sufficiently dried, the patterned canvas is removed from the backing plate, and conventional operations such as boxing are performed as needed.
实施例2：制作180cm×95cm BZ艺术绘画作品Example 2: Making a 180cm x 95cm BZ art painting
制造BZ釉绘画颜料材料组合物：由天然矿物质色粉(含量5克)、合成树脂(含量3克)、醋丙(含量2克)所制成的绘画材料组合物加入颜色釉料、白色调色釉料以及无色调色釉料，其中该颜色釉料由60wt％至40wt％的耐高温颜色釉料矿物质和40wt％至60wt％的水组成，该白色调色釉料由60wt％的耐高温白色釉料矿物质和40wt％的水组成，该无色调色釉料由40wt％的耐高温无色釉料矿物质和60wt％的水组成。Manufacture of BZ glaze paint material composition: painting material composition made of natural mineral toner (content 5 g), synthetic resin (content 3 g), vinegar c (2 g) added color glaze, white a color glaze and a clear color glaze, wherein the color glaze is composed of 60% by weight to 40% by weight of high temperature resistant color glaze mineral and 40% by weight to 60% by weight of water, the white color glaze is 60% by weight It is composed of a high temperature resistant white glaze mineral and 40% by weight of water, which is composed of 40% by weight of high temperature resistant colorless glaze mineral and 60% by weight of water.
本实施例使用上述制成的BZ釉绘画颜料材料组合物BZ图案艺术绘画作品，所采用的方法和步骤与实施例1基本相同，此外不再赘述相同之处。需要说明在绘制画面步骤中，根据画布尺寸制作适量的所述BZ釉绘画颜料材料组合物，充分搅拌后加入耐高温矿物质与水按照以下重量比进行配比，分别形成红色釉料、黄色釉料、蓝色釉料、绿色釉料、紫色釉料、橙色釉料和青色釉料：In this embodiment, the BZ glaze paint material composition BZ pattern art painting work prepared above is used, and the methods and steps used are basically the same as those in Embodiment 1, and the same points will not be described again. It should be noted that in the step of drawing a picture, an appropriate amount of the BZ glaze paint material composition is prepared according to the size of the canvas, and the mixture is mixed with high-temperature minerals and water according to the following weight ratio to form a red glaze and a yellow glaze respectively. Material, blue glaze, green glaze, purple glaze, orange glaze and cyan glaze:
红色釉料矿物质和水配比为60％：40％，Red glaze mineral and water ratio is 60%: 40%,
黄色釉料矿物质和水配比为55％：45％，The yellow glaze mineral and water ratio is 55%: 45%.
蓝色釉料矿物质和水配比为65％：35％，Blue glaze mineral and water ratio is 65%: 35%,
绿色釉料矿物质和水配比为63％：37％，The green glaze mineral and water ratio is 63%: 37%,
紫色釉料矿物质和水配比为70％：30％，Purple glaze mineral and water ratio is 70%: 30%,
橙色釉料矿物质和水配比为68％：32％，Orange glaze mineral and water ratio is 68%: 32%,
青色釉料矿物质和水配比为71％：29％，The ratio of mineral and water for cyan glaze is 71%: 29%.
充分搅拌后，均匀涂满画布；放置5-10分钟后均匀加入天然矿物质黑粉或白粉，该黑粉或白粉的重量为所述BZ釉绘画颜料材料组合物总重5％，随着时间的推移画布逐渐呈不规则图案，约12小时后画布呈最终图案。After fully stirring, evenly spread the canvas; after 5-10 minutes, uniformly add natural mineral black powder or white powder, the weight of the black powder or white powder is 5% of the total weight of the BZ glaze paint material composition, with time The canvas of the transition is gradually irregular, and the canvas is in the final pattern after about 12 hours.
最后进行后期处理，等待图案固定不变后，水平静止画布进行干燥，在常温条件下， 自然干燥至完全(干燥时间为48-72小时)。待充分干燥后将带有图案的画布从背板取下，根据需要进行加框等常规操作。Finally, post-processing is performed, and after the pattern is fixed, the horizontal still canvas is dried, under normal temperature conditions, Naturally dry to complete (drying time is 48-72 hours). After being sufficiently dried, the patterned canvas is removed from the backing plate, and conventional operations such as boxing are performed as needed.
实施例3：制作180cm×95cm BZ艺术绘画作品Example 3: Making a 180cm x 95cm BZ art painting
制造BZ釉绘画颜料材料组合物：由天然矿物质色粉(含量5克)、合成树脂(含量3克)、醋丙(含量2克)所制成的绘画材料组合物加入颜色釉料、白色调色釉料以及无色调色釉料，其中该颜色釉料由60wt％至40wt％的耐高温颜色釉料矿物质和40wt％至60wt％的水组成，该白色调色釉料由60wt％的耐高温白色釉料矿物质和40wt％的水组成，该无色调色釉料由40wt％的耐高温无色釉料矿物质和60wt％的水组成。Manufacture of BZ glaze paint material composition: painting material composition made of natural mineral toner (content 5 g), synthetic resin (content 3 g), vinegar c (2 g) added color glaze, white a color glaze and a clear color glaze, wherein the color glaze is composed of 60% by weight to 40% by weight of high temperature resistant color glaze mineral and 40% by weight to 60% by weight of water, the white color glaze is 60% by weight It is composed of a high temperature resistant white glaze mineral and 40% by weight of water, which is composed of 40% by weight of high temperature resistant colorless glaze mineral and 60% by weight of water.
本实施例使用上述制成的BZ釉绘画颜料材料组合物而绘制不规则BZ艺术绘画作品，所采用的方法和步骤与实施例1基本相同，此外不再赘述相同之处。需要说明在绘制画面步骤中，根据画布尺寸制作适量的所述BZ釉绘画颜料材料组合物，充分搅拌后加入耐高温矿物质与水按照以下重量比进行配比，分别形成红色釉料、黄色釉料、蓝色釉料、绿色釉料、紫色釉料、橙色釉料和青色釉料：In this embodiment, an irregular BZ art painting work is drawn using the BZ glaze paint material composition prepared above, and the methods and steps used are basically the same as those in Embodiment 1, and the same points will not be described again. It should be noted that in the step of drawing a picture, an appropriate amount of the BZ glaze paint material composition is prepared according to the size of the canvas, and the mixture is mixed with high-temperature minerals and water according to the following weight ratio to form a red glaze and a yellow glaze respectively. Material, blue glaze, green glaze, purple glaze, orange glaze and cyan glaze:
红色釉料矿物质和水配比为60％：40％，Red glaze mineral and water ratio is 60%: 40%,
黄色釉料矿物质和水配比为55％：45％，The yellow glaze mineral and water ratio is 55%: 45%.
蓝色釉料矿物质和水配比为65％：35％，Blue glaze mineral and water ratio is 65%: 35%,
绿色釉料矿物质和水配比为63％：37％，The green glaze mineral and water ratio is 63%: 37%,
紫色釉料矿物质和水配比为70％：30％，Purple glaze mineral and water ratio is 70%: 30%,
橙色釉料矿物质和水配比为68％：32％，Orange glaze mineral and water ratio is 68%: 32%,
青色釉料矿物质和水配比为71％：29％，The ratio of mineral and water for cyan glaze is 71%: 29%.
充分搅拌后，均匀涂满画布；放置5-10分钟后均匀加入天然矿物质黑粉或白粉，该黑粉或白粉的重量为所述BZ釉绘画颜料材料组合物总重5％，随着时间的推移画布逐渐呈不规则图案，约12小时后画布呈最终图案。After fully stirring, evenly spread the canvas; after 5-10 minutes, uniformly add natural mineral black powder or white powder, the weight of the black powder or white powder is 5% of the total weight of the BZ glaze paint material composition, with time The canvas of the transition is gradually irregular, and the canvas is in the final pattern after about 12 hours.
最后进行后期处理，等待图案固定不变后，水平静止画布进行干燥，在常温条件下，自然干燥至完全(干燥时间为48-72小时)。待充分干燥后将带有图案的画布从背板取下，根据需要进行加框等常规操作。Finally, post-treatment is carried out. After the pattern is fixed, the horizontal still canvas is dried, and naturally dried to completeness under normal temperature conditions (drying time is 48-72 hours). After being sufficiently dried, the patterned canvas is removed from the backing plate, and conventional operations such as boxing are performed as needed.
实施例4：制作180cm×95cm BZ艺术绘画作品Example 4: Making a 180cm x 95cm BZ art painting
制造BZ釉绘画颜料材料组合物：由天然矿物质色粉(含量5克)、合成树脂(含量3克)、醋丙(含量2克)所制成的绘画材料组合物加入颜色釉料、白色调色釉料以及无色调色釉料，其中该颜色釉料由60wt％至40wt％的耐高温颜色釉料矿物质和40wt％至60wt％的水组成，该白色调色釉料由60wt％的耐高温白色釉料矿物质和40wt％的水组成， 该无色调色釉料由40wt％的耐高温无色釉料矿物质和60wt％的水组成。Manufacture of BZ glaze paint material composition: painting material composition made of natural mineral toner (content 5 g), synthetic resin (content 3 g), vinegar c (2 g) added color glaze, white a color glaze and a clear color glaze, wherein the color glaze is composed of 60% by weight to 40% by weight of high temperature resistant color glaze mineral and 40% by weight to 60% by weight of water, the white color glaze is 60% by weight High temperature resistant white glaze mineral and 40% by weight water, The clear color glaze consists of 40% by weight of high temperature resistant colorless glaze mineral and 60% by weight of water.
本实施例使用上述制成的BZ釉绘画颜料材料组合物BZ图案艺术绘画作品，所采用的方法和步骤与实施例1基本相同，此外不再赘述相同之处。需要说明在绘制画面步骤中，根据画布尺寸制作适量的所述BZ釉绘画颜料材料组合物，充分搅拌后加入耐高温矿物质与水按照以下重量比进行配比，分别形成红色釉料、黄色釉料、蓝色釉料、绿色釉料、紫色釉料、橙色釉料和青色釉料：In this embodiment, the BZ glaze paint material composition BZ pattern art painting work prepared above is used, and the methods and steps used are basically the same as those in Embodiment 1, and the same points will not be described again. It should be noted that in the step of drawing a picture, an appropriate amount of the BZ glaze paint material composition is prepared according to the size of the canvas, and the mixture is mixed with high-temperature minerals and water according to the following weight ratio to form a red glaze and a yellow glaze respectively. Material, blue glaze, green glaze, purple glaze, orange glaze and cyan glaze:
红色釉料矿物质和水配比为60％：40％，Red glaze mineral and water ratio is 60%: 40%,
黄色釉料矿物质和水配比为55％：45％，The yellow glaze mineral and water ratio is 55%: 45%.
蓝色釉料矿物质和水配比为65％：35％，Blue glaze mineral and water ratio is 65%: 35%,
绿色釉料矿物质和水配比为63％：37％，The green glaze mineral and water ratio is 63%: 37%,
紫色釉料矿物质和水配比为70％：30％，Purple glaze mineral and water ratio is 70%: 30%,
橙色釉料矿物质和水配比为68％：32％，Orange glaze mineral and water ratio is 68%: 32%,
青色釉料矿物质和水配比为71％：29％，The ratio of mineral and water for cyan glaze is 71%: 29%.
充分搅拌后，均匀涂满画布；放置5-10分钟后均匀加入天然矿物质黑粉或白粉，该黑粉或白粉的重量为所述BZ釉绘画颜料材料组合物总重5％，随着时间的推移画布逐渐呈不规则图案，约12小时后画布呈最终图案。After fully stirring, evenly spread the canvas; after 5-10 minutes, uniformly add natural mineral black powder or white powder, the weight of the black powder or white powder is 5% of the total weight of the BZ glaze paint material composition, with time The canvas of the transition is gradually irregular, and the canvas is in the final pattern after about 12 hours.
最后进行后期处理，等待图案固定不变后，水平静止画布进行干燥，在常温条件下，自然干燥至完全(干燥时间为48-72小时)。待充分干燥后将带有图案的画布从背板取下，根据需要进行加框等常规操作。Finally, post-treatment is carried out. After the pattern is fixed, the horizontal still canvas is dried, and naturally dried to completeness under normal temperature conditions (drying time is 48-72 hours). After being sufficiently dried, the patterned canvas is removed from the backing plate, and conventional operations such as boxing are performed as needed.
实施例5：制作120cm×90cm BZ艺术绘画作品Example 5: Making a 120cm x 90cm BZ art painting
制造BZ釉绘画颜料材料组合物：由天然矿物质色粉(含量5克)、合成树脂(含量3克)、醋丙(含量2克)所制成的绘画材料组合物加入颜色釉料、白色调色釉料以及无色调色釉料，其中该颜色釉料由60wt％至40wt％的耐高温颜色釉料矿物质和40wt％至60wt％的水组成，该白色调色釉料由60wt％的耐高温白色釉料矿物质和40wt％的水组成，该无色调色釉料由40wt％的耐高温无色釉料矿物质和60wt％的水组成。Manufacture of BZ glaze paint material composition: painting material composition made of natural mineral toner (content 5 g), synthetic resin (content 3 g), vinegar c (2 g) added color glaze, white a color glaze and a clear color glaze, wherein the color glaze is composed of 60% by weight to 40% by weight of high temperature resistant color glaze mineral and 40% by weight to 60% by weight of water, the white color glaze is 60% by weight It is composed of a high temperature resistant white glaze mineral and 40% by weight of water, which is composed of 40% by weight of high temperature resistant colorless glaze mineral and 60% by weight of water.
本实施例使用上述制成的BZ釉绘画颜料材料组合物BZ图案艺术绘画作品，所采用的方法和步骤与实施例1基本相同，此外不再赘述相同之处。需要说明在绘制画面步骤中，根据画布尺寸制作适量的所述BZ釉绘画颜料材料组合物，充分搅拌后加入耐高温矿物质与水按照以下重量比进行配比，分别形成红色釉料、黄色釉料、蓝色釉料、绿色釉料、紫色釉料、橙色釉料和青色釉料：In this embodiment, the BZ glaze paint material composition BZ pattern art painting work prepared above is used, and the methods and steps used are basically the same as those in Embodiment 1, and the same points will not be described again. It should be noted that in the step of drawing a picture, an appropriate amount of the BZ glaze paint material composition is prepared according to the size of the canvas, and the mixture is mixed with high-temperature minerals and water according to the following weight ratio to form a red glaze and a yellow glaze respectively. Material, blue glaze, green glaze, purple glaze, orange glaze and cyan glaze:
红色釉料矿物质和水配比为60％：40％， Red glaze mineral and water ratio is 60%: 40%,
黄色釉料矿物质和水配比为55％：45％，The yellow glaze mineral and water ratio is 55%: 45%.
蓝色釉料矿物质和水配比为65％：35％，Blue glaze mineral and water ratio is 65%: 35%,
绿色釉料矿物质和水配比为63％：37％，The green glaze mineral and water ratio is 63%: 37%,
紫色釉料矿物质和水配比为70％：30％，Purple glaze mineral and water ratio is 70%: 30%,
橙色釉料矿物质和水配比为68％：32％，Orange glaze mineral and water ratio is 68%: 32%,
青色釉料矿物质和水配比为71％：29％，The ratio of mineral and water for cyan glaze is 71%: 29%.
充分搅拌后，均匀涂满画布；放置5-10分钟后均匀加入天然矿物质黑粉或白粉，该黑粉或白粉的重量为所述BZ釉绘画颜料材料组合物总重5％，随着时间的推移画布逐渐呈不规则图案，约12小时后画布呈最终图案。After fully stirring, evenly spread the canvas; after 5-10 minutes, uniformly add natural mineral black powder or white powder, the weight of the black powder or white powder is 5% of the total weight of the BZ glaze paint material composition, with time The canvas of the transition is gradually irregular, and the canvas is in the final pattern after about 12 hours.
最后进行后期处理，等待图案固定不变后，水平静止画布进行干燥，在常温条件下，自然干燥至完全(干燥时间为48-72小时)。待充分干燥后将带有图案的画布从背板取下，根据需要进行加框等常规操作。Finally, post-treatment is carried out. After the pattern is fixed, the horizontal still canvas is dried, and naturally dried to completeness under normal temperature conditions (drying time is 48-72 hours). After being sufficiently dried, the patterned canvas is removed from the backing plate, and conventional operations such as boxing are performed as needed.
实施例6：制作55cm×55cm BZ高温颜色釉瓷板画Example 6: Making 55cm×55cm BZ high temperature color glazed porcelain plate painting
高岭土(尤其是景德镇当地独有的高岭土)加水，配比为7：3参与搅拌成坯状，再用铁杖杆等压成平整如镜的大小不一的板块，厚度在2～3cm，然后不在阳光直晒下阴干，大约在一周左右即可；Kaolin (especially the unique kaolin in Jingdezhen) is added with water, and the ratio is 7:3. It is stirred into a billet, and then pressed into a flat plate of different sizes, such as a mirror, with a thickness of 2 to 3 cm. Do not dry in the sun, about a week or so;
各种颜色釉料由纯天然的耐高温矿物质加水配比而成：Various color glazes are made from pure natural high temperature minerals and water:
红色釉料矿物质和水配比为55％：45％，Red glaze mineral and water ratio is 55%: 45%,
黄色釉料矿物质和水配比为50％：50％，The yellow glaze mineral and water ratio is 50%: 50%,
蓝色釉料矿物质和水配比为60％：40％，Blue glaze mineral and water ratio is 60%: 40%,
绿色釉料矿物质和水配比为58％：42％，Green glaze mineral and water ratio is 58%: 42%,
紫色釉料矿物质和水配比为65％：35％，Purple glaze mineral and water ratio is 65%: 35%,
橙色釉料矿物质和水配比为63％：37％，Orange glaze mineral and water ratio is 63%: 37%,
青色釉料矿物质和水配比为66％：34％；Cyan glaze mineral and water ratio is 66%: 34%;
在得到上述各种颜色釉料后，在各种颜色釉料中加入白色调色釉料和无色调色釉料，其中所述白色调色釉料由70wt％的耐高温白色釉料矿物质和30wt％的水组成，所述无色调色釉料由30wt％的耐高温无色釉料矿物质和70wt％的水组成：After obtaining the above various color glazes, a white color glaze and a colorless glaze are added to the various color glazes, wherein the white color glaze is composed of 70% by weight of high temperature resistant white glaze minerals and 30wt% water composition, the clear color glaze consists of 30wt% high temperature resistant colorless glaze mineral and 70wt% water:
每500g红色釉料中添加10g白色调色釉料和5g无色调色釉料，Add 10g white color glaze and 5g colorless glaze to every 500g red glaze.
每500g黄色釉料中添加15g白色调色釉料和10g无色调色釉料，Add 15g white tinting glaze and 10g colorless glaze to every 500g yellow glaze.
每500g蓝色釉料中添加20g白色调色釉料和15g无色调色釉料，Add 20g white tinting glaze and 15g colorless glaze to every 500g blue glaze.
每500g绿色釉料中添加25g白色调色釉料和20g无色调色釉料， Add 25g white tinting glaze and 20g colorless glaze to every 500g green glaze.
每500g紫色釉料中添加30g白色调色釉料和15g无色调色釉料，Add 30g white color glaze and 15g colorless glaze to every 500g purple glaze.
每500g橙色釉料中添加35g白色调色釉料和20g无色调色釉料，35g white tinting glaze and 20g colorless glaze are added to each 500g orange glaze.
每500g青色釉料中添加40g白色调色釉料和25g无色调色釉料；40g white color glaze and 25g colorless glaze are added to each 500g cyan glaze;
采用上述配比得到的各种高温颜色釉绘画颜料应用于瓷板画绘画时各种颜色釉料之间相融合，更使色相更纯、更饱和、更绚烂，在此也纳入本申请的保护范围。The various high-temperature color glaze paints obtained by the above ratios are used in the combination of various color glazes in porcelain painting, and the hue is more pure, more saturated and more splendid, and is also included in the protection of the present application. range.
其后将加入白色调色釉料和无色调色釉料之后的各种颜色釉料按作画步骤和顺序为：先画红、黄、蓝、绿、紫、橙、青分别涂在阴干的瓷板上即可。当然，以上只是最优选的实施方式。同样地，按照上述配比和涂色次序，仅使用至少包括红、黄、蓝三种加入白色调色釉料和无色调色釉料之后的各种颜色釉料，可同样实现BZ艺术效果。Thereafter, the color glazes of the various color glazes after adding the white color glaze and the colorless glaze are drawn in the following steps: first, red, yellow, blue, green, purple, orange, and blue are respectively applied to the dried porcelain. Just on the board. Of course, the above is only the most preferred embodiment. Similarly, in accordance with the above-mentioned ratio and coloring order, the BZ artistic effect can be similarly achieved by using only the various color glazes including at least three kinds of red, yellow and blue added white color glaze and a clear color glaze.
创作高温颜色釉瓷板画时间以景德镇9月-10月为宜，在该温度和湿度下做瓷板画最好。It is advisable to create high-temperature color glaze porcelain paintings in September-October in Jingdezhen, and it is best to make porcelain paintings under this temperature and humidity.
进窑烧制时最好使用气窑，次之为电窑、柴窑，进窑烧制瓷板第一天温度控制在500-600度高温，第二天控制在600-800度高温，第三天控制在1300-1350度高温，即可停止烧制用火，在窑内放置三到四天自然降温和外面天气温度接近再出窑即可。When entering the kiln, it is best to use the gas kiln, followed by the electric kiln and the coal kiln. The first day of the kiln firing is controlled at a temperature of 500-600 degrees, and the next day is controlled at a high temperature of 600-800 degrees. After three days of control at a high temperature of 1,300-1,350 degrees, the fire can be stopped and placed in the kiln for three to four days to cool naturally and the outside weather temperature is close to the kiln.
实施例7：制作180cm×120cm BZ艺术绘画作品有机玻璃Example 7: Making 180cm × 120cm BZ art painting plexiglass
除了BZ高温颜色釉瓷板画及BZ艺术绘画布之外，在有机玻璃上仍可实现BZ艺术绘画作品，其中，BZ有机玻璃直接在市场上购买，绘画方法和步骤同画布和瓷板画一样的。绘画完后，有机玻璃在自然常温(约室内零度～50度之内)下阴干而成。In addition to BZ high-temperature color glazed porcelain paintings and BZ art painting fabrics, BZ art paintings can still be realized on plexiglass. Among them, BZ plexiglass is directly purchased on the market, and the painting methods and steps are the same as canvas and porcelain painting. of. After painting, the plexiglass is dried in the natural room temperature (about 0 to 50 degrees indoors).
实施例8：制作180cm×120cm BZ艺术绘画作品有机玻璃Example 8: Making 180cm × 120cm BZ art painting plexiglass
除了BZ高温颜色釉瓷板画及BZ艺术绘画布之外，在有机玻璃上仍可实现BZ艺术绘画作品，其中，BZ有机玻璃直接在市场上购买，绘画方法和步骤同画布和瓷板画一样的。绘画完后，有机玻璃在自然常温(约室内零度～50度之内)下阴干而成。In addition to BZ high-temperature color glazed porcelain paintings and BZ art painting fabrics, BZ art paintings can still be realized on plexiglass. Among them, BZ plexiglass is directly purchased on the market, and the painting methods and steps are the same as canvas and porcelain painting. of. After painting, the plexiglass is dried in the natural room temperature (about 0 to 50 degrees indoors).
实施例9：制作170cm×84cm BZ高温颜色釉瓷板画Example 9: Making 170cm×84cm BZ high temperature color glazed porcelain plate painting
高岭土(尤其是景德镇当地独有的高岭土)加水，配比为7：3参与搅拌成坯状，再用铁杖杆等压成平整如镜的大小不一的板块，厚度在2～3cm，然后不在阳光直晒下阴干，大约在一周左右即可；Kaolin (especially the unique kaolin in Jingdezhen) is added with water, and the ratio is 7:3. It is stirred into a billet, and then pressed into a flat plate of different sizes, such as a mirror, with a thickness of 2 to 3 cm. Do not dry in the sun, about a week or so;
各种颜色釉料由纯天然的耐高温矿物质加水配比而成：Various color glazes are made from pure natural high temperature minerals and water:
红色釉料矿物质和水配比为55％：45％，Red glaze mineral and water ratio is 55%: 45%,
黄色釉料矿物质和水配比为50％：50％，The yellow glaze mineral and water ratio is 50%: 50%,
蓝色釉料矿物质和水配比为60％：40％，Blue glaze mineral and water ratio is 60%: 40%,
绿色釉料矿物质和水配比为58％：42％， Green glaze mineral and water ratio is 58%: 42%,
紫色釉料矿物质和水配比为65％：35％，Purple glaze mineral and water ratio is 65%: 35%,
橙色釉料矿物质和水配比为63％：37％，Orange glaze mineral and water ratio is 63%: 37%,
青色釉料矿物质和水配比为66％：34％；Cyan glaze mineral and water ratio is 66%: 34%;
在得到上述各种颜色釉料后，在各种颜色釉料中加入白色调色釉料和无色调色釉料，其中所述白色调色釉料由70wt％的耐高温白色釉料矿物质和30wt％的水组成，所述无色调色釉料由30wt％的耐高温无色釉料矿物质和70wt％的水组成：After obtaining the above various color glazes, a white color glaze and a colorless glaze are added to the various color glazes, wherein the white color glaze is composed of 70% by weight of high temperature resistant white glaze minerals and 30wt% water composition, the clear color glaze consists of 30wt% high temperature resistant colorless glaze mineral and 70wt% water:
每500g红色釉料中添加10g白色调色釉料和5g无色调色釉料，Add 10g white color glaze and 5g colorless glaze to every 500g red glaze.
每500g黄色釉料中添加15g白色调色釉料和10g无色调色釉料，Add 15g white tinting glaze and 10g colorless glaze to every 500g yellow glaze.
每500g蓝色釉料中添加20g白色调色釉料和15g无色调色釉料，Add 20g white tinting glaze and 15g colorless glaze to every 500g blue glaze.
每500g绿色釉料中添加25g白色调色釉料和20g无色调色釉料，Add 25g white tinting glaze and 20g colorless glaze to every 500g green glaze.
每500g紫色釉料中添加30g白色调色釉料和15g无色调色釉料，Add 30g white color glaze and 15g colorless glaze to every 500g purple glaze.
每500g橙色釉料中添加35g白色调色釉料和20g无色调色釉料，35g white tinting glaze and 20g colorless glaze are added to each 500g orange glaze.
每500g青色釉料中添加40g白色调色釉料和25g无色调色釉料；40g white color glaze and 25g colorless glaze are added to each 500g cyan glaze;
采用上述配比得到的各种高温颜色釉绘画颜料应用于瓷板画绘画时各种颜色釉料之间相融合，更使色相更纯、更饱和、更绚烂，在此也纳入本申请的保护范围。The various high-temperature color glaze paints obtained by the above ratios are used in the combination of various color glazes in porcelain painting, and the hue is more pure, more saturated and more splendid, and is also included in the protection of the present application. range.
实施例10：制作170cm×84cm高温颜色釉瓷板画Example 10: Making a 170 cm × 84 cm high temperature color glazed porcelain plate painting
高岭土(尤其是景德镇当地独有的高岭土)加水，配比为7：3参与搅拌成坯状，再用铁杖杆等压成平整如镜的大小不一的板块，厚度在2～3cm，然后不在阳光直晒下阴干，大约在一周左右即可；Kaolin (especially the unique kaolin in Jingdezhen) is added with water, and the ratio is 7:3. It is stirred into a billet, and then pressed into a flat plate of different sizes, such as a mirror, with a thickness of 2 to 3 cm. Do not dry in the sun, about a week or so;
各种颜色釉料由纯天然的耐高温矿物质加水配比而成：Various color glazes are made from pure natural high temperature minerals and water:
红色釉料矿物质和水配比为55％：45％，Red glaze mineral and water ratio is 55%: 45%,
黄色釉料矿物质和水配比为50％：50％，The yellow glaze mineral and water ratio is 50%: 50%,
蓝色釉料矿物质和水配比为60％：40％，Blue glaze mineral and water ratio is 60%: 40%,
绿色釉料矿物质和水配比为58％：42％，Green glaze mineral and water ratio is 58%: 42%,
紫色釉料矿物质和水配比为65％：35％，Purple glaze mineral and water ratio is 65%: 35%,
橙色釉料矿物质和水配比为63％：37％，Orange glaze mineral and water ratio is 63%: 37%,
青色釉料矿物质和水配比为66％：34％；Cyan glaze mineral and water ratio is 66%: 34%;
在得到上述各种颜色釉料后，在各种颜色釉料中加入白色调色釉料和无色调色釉料，其中所述白色调色釉料由70wt％的耐高温白色釉料矿物质和30wt％的水组成，所述无色调色釉料由30wt％的耐高温无色釉料矿物质和70wt％的水组成：After obtaining the above various color glazes, a white color glaze and a colorless glaze are added to the various color glazes, wherein the white color glaze is composed of 70% by weight of high temperature resistant white glaze minerals and 30wt% water composition, the clear color glaze consists of 30wt% high temperature resistant colorless glaze mineral and 70wt% water:
每500g红色釉料中添加10g白色调色釉料和5g无色调色釉料， Add 10g white color glaze and 5g colorless glaze to every 500g red glaze.
每500g黄色釉料中添加15g白色调色釉料和10g无色调色釉料，Add 15g white tinting glaze and 10g colorless glaze to every 500g yellow glaze.
每500g蓝色釉料中添加20g白色调色釉料和15g无色调色釉料，Add 20g white tinting glaze and 15g colorless glaze to every 500g blue glaze.
每500g绿色釉料中添加25g白色调色釉料和20g无色调色釉料，Add 25g white tinting glaze and 20g colorless glaze to every 500g green glaze.
每500g紫色釉料中添加30g白色调色釉料和15g无色调色釉料，Add 30g white color glaze and 15g colorless glaze to every 500g purple glaze.
每500g橙色釉料中添加35g白色调色釉料和20g无色调色釉料，35g white tinting glaze and 20g colorless glaze are added to each 500g orange glaze.
每500g青色釉料中添加40g白色调色釉料和25g无色调色釉料；40g white color glaze and 25g colorless glaze are added to each 500g cyan glaze;
采用上述配比得到的各种高温颜色釉绘画颜料应用于瓷板画绘画时各种颜色釉料之间相融合，更使色相更纯、更饱和、更绚烂，在此也纳入本申请的保护范围。The various high-temperature color glaze paints obtained by the above ratios are used in the combination of various color glazes in porcelain painting, and the hue is more pure, more saturated and more splendid, and is also included in the protection of the present application. range.
实施例11：制作170cm×84cm高温颜色釉瓷板画Example 11: Making a 170 cm × 84 cm high temperature color glazed porcelain plate
高岭土(尤其是景德镇当地独有的高岭土)加水，配比为7：3参与搅拌成坯状，再用铁杖杆等压成平整如镜的大小不一的板块，厚度在2～3cm，然后不在阳光直晒下阴干，大约在一周左右即可；Kaolin (especially the unique kaolin in Jingdezhen) is added with water, and the ratio is 7:3. It is stirred into a billet, and then pressed into a flat plate of different sizes, such as a mirror, with a thickness of 2 to 3 cm. Do not dry in the sun, about a week or so;
各种颜色釉料由纯天然的耐高温矿物质加水配比而成：Various color glazes are made from pure natural high temperature minerals and water:
红色釉料矿物质和水配比为55％：45％，Red glaze mineral and water ratio is 55%: 45%,
黄色釉料矿物质和水配比为50％：50％，The yellow glaze mineral and water ratio is 50%: 50%,
蓝色釉料矿物质和水配比为60％：40％，Blue glaze mineral and water ratio is 60%: 40%,
绿色釉料矿物质和水配比为58％：42％，Green glaze mineral and water ratio is 58%: 42%,
紫色釉料矿物质和水配比为65％：35％，Purple glaze mineral and water ratio is 65%: 35%,
橙色釉料矿物质和水配比为63％：37％，Orange glaze mineral and water ratio is 63%: 37%,
青色釉料矿物质和水配比为66％：34％；Cyan glaze mineral and water ratio is 66%: 34%;
在得到上述各种颜色釉料后，在各种颜色釉料中加入白色调色釉料和无色调色釉料，其中所述白色调色釉料由70wt％的耐高温白色釉料矿物质和30wt％的水组成，所述无色调色釉料由30wt％的耐高温无色釉料矿物质和70wt％的水组成：After obtaining the above various color glazes, a white color glaze and a colorless glaze are added to the various color glazes, wherein the white color glaze is composed of 70% by weight of high temperature resistant white glaze minerals and 30wt% water composition, the clear color glaze consists of 30wt% high temperature resistant colorless glaze mineral and 70wt% water:
每500g红色釉料中添加10g白色调色釉料和5g无色调色釉料，Add 10g white color glaze and 5g colorless glaze to every 500g red glaze.
每500g黄色釉料中添加15g白色调色釉料和10g无色调色釉料，Add 15g white tinting glaze and 10g colorless glaze to every 500g yellow glaze.
每500g蓝色釉料中添加20g白色调色釉料和15g无色调色釉料，Add 20g white tinting glaze and 15g colorless glaze to every 500g blue glaze.
每500g绿色釉料中添加25g白色调色釉料和20g无色调色釉料，Add 25g white tinting glaze and 20g colorless glaze to every 500g green glaze.
每500g紫色釉料中添加30g白色调色釉料和15g无色调色釉料，Add 30g white color glaze and 15g colorless glaze to every 500g purple glaze.
每500g橙色釉料中添加35g白色调色釉料和20g无色调色釉料，35g white tinting glaze and 20g colorless glaze are added to each 500g orange glaze.
每500g青色釉料中添加40g白色调色釉料和25g无色调色釉料；40g white color glaze and 25g colorless glaze are added to each 500g cyan glaze;
采用上述配比得到的各种高温颜色釉绘画颜料应用于瓷板画绘画时各种颜色釉料 之间相融合，更使色相更纯、更饱和、更绚烂，在此也纳入本申请的保护范围。Various high-temperature color glaze paints obtained by the above ratios are used for various color glazes in porcelain painting The fusion between the two makes the hue more pure, more saturated, and more splendid, and is also included in the scope of protection of the present application.
惟以上所述仅为本发明的较佳实施例，非意欲局限本发明的专利保护范围，故举凡运用本发明说明书及图式内容所为的等效变化，均同理皆包含于本发明的权利保护范围内。以上所述仅为本发明的较佳实施例，非局限本发明的专利保护范围，故运用本发明说明书及图式内容所为的等效变化，均同理皆包含于本发明的权利保护范围内。 The above are only the preferred embodiments of the present invention, and are not intended to limit the scope of the present invention. Therefore, the equivalent changes of the present invention and the contents of the drawings are all included in the present invention. Within the scope of rights protection. The above are only the preferred embodiments of the present invention, and are not intended to limit the scope of the present invention. Therefore, the equivalent changes of the present invention and the contents of the drawings are all included in the scope of protection of the present invention. Inside.

Claims (5)

  1. 一种BZ釉绘画颜料材料组合物：由天然矿物质色粉、合成树脂、醋丙所制成的绘画材料组合物加入颜色釉料、白色调色釉料以及无色调色釉料，其中所述颜色釉料由60wt％至40wt％的耐高温颜色釉料矿物质和40wt％至60wt％的水组成，所述白色调色釉料由60wt％的耐高温白色釉料矿物质和40wt％的水组成，所述无色调色釉料由40wt％的耐高温无色釉料矿物质和60wt％的水组成。A BZ glaze paint material composition: a paint material composition made of natural mineral toner, synthetic resin, vinegar and cacetate, a color glaze, a white color glaze, and a colorless glaze, wherein The color glaze is composed of 60% by weight to 40% by weight of high temperature resistant color glaze mineral and 40% by weight to 60% by weight of water, the white color glaze consisting of 60% by weight of high temperature resistant white glaze mineral and 40% by weight of water Composition, the clear color glaze is composed of 40% by weight of high temperature resistant colorless glaze mineral and 60% by weight of water.
  2. 如权利要求1所述的BZ釉绘画颜料材料组合物，基于该组合物的总重量，所述天然矿物质色粉的含量为5wt％，所述合成树脂的含量为3wt％，所述醋丙的含量为2wt％。The BZ glaze paint material composition according to claim 1, wherein the content of the natural mineral toner is 5 wt%, the content of the synthetic resin is 3 wt%, and the vinegar is based on the total weight of the composition. The content is 2% by weight.
  3. 如权利要求1所述的BZ釉绘画颜料材料组合物，其中，该组合物还含有润滑剂，该润滑剂的重百分比含量不超过3％。The BZ glaze paint material composition according to claim 1, wherein the composition further contains a lubricant having a weight percentage of not more than 3%.
  4. 如权利要求1所述的BZ釉绘画颜料材料组合物，其中，该组合物还含有杀菌剂，该杀菌剂的重百分比含量不超过2％。The BZ glaze paint material composition according to claim 1, wherein the composition further contains a bactericide having a weight percentage of not more than 2%.
  5. 一种BZ釉绘画颜料材料组合物绘画方法，该方法包含：A method for painting a BZ glaze paint material composition, the method comprising:
    (1)制作画布，根据画面大小选择适合尺寸的天然亚麻布作为画布，对其进行防水、加固处理；(1) Making a canvas, selecting a natural linen of a suitable size as a canvas according to the size of the screen, and performing waterproofing and reinforcement treatment thereon;
    (2)制作底层，在所述画布上涂刷底料，对画布进行打底及调色，然后充分干燥；以及绘制画面，将完成底层的画布水平固定于背板，根据画布尺寸制作适量的所述BZ釉绘画颜料材料组合物，充分搅拌后加入耐高温矿物质与水按照以下重量比进行配比，分别形成红色釉料、黄色釉料、蓝色釉料、绿色釉料、紫色釉料、橙色釉料和青色釉料：(2) making the bottom layer, applying the primer on the canvas, bottoming and coloring the canvas, and then drying it fully; and drawing the picture, fixing the finished canvas horizontally to the backboard, and making an appropriate amount according to the size of the canvas. The BZ glaze paint material composition is fully stirred and then added with high temperature resistant minerals and water according to the following weight ratio to form red glaze, yellow glaze, blue glaze, green glaze, purple glaze , orange glaze and cyan glaze:
    红色釉料矿物质和水配比为60％：40％，Red glaze mineral and water ratio is 60%: 40%,
    黄色釉料矿物质和水配比为55％：45％，The yellow glaze mineral and water ratio is 55%: 45%.
    蓝色釉料矿物质和水配比为65％：35％，Blue glaze mineral and water ratio is 65%: 35%,
    绿色釉料矿物质和水配比为63％：37％，The green glaze mineral and water ratio is 63%: 37%,
    紫色釉料矿物质和水配比为70％：30％，Purple glaze mineral and water ratio is 70%: 30%,
    橙色釉料矿物质和水配比为68％：32％，Orange glaze mineral and water ratio is 68%: 32%,
    青色釉料矿物质和水配比为71％：29％。 The cyan glaze mineral and water ratio is 71%: 29%.
PCT/CN2016/070663 2016-01-12 2016-01-12 Bz glaze painting pigment composition and painting method using same WO2017120759A1 (en)