CN101671955A - Oily canvas coating and manufacture method thereof - Google Patents
Oily canvas coating and manufacture method thereof Download PDFInfo
- Publication number
- CN101671955A CN101671955A CN200910153478A CN200910153478A CN101671955A CN 101671955 A CN101671955 A CN 101671955A CN 200910153478 A CN200910153478 A CN 200910153478A CN 200910153478 A CN200910153478 A CN 200910153478A CN 101671955 A CN101671955 A CN 101671955A
- Authority
- CN
- China
- Prior art keywords
- oily
- coating
- canvas
- add
- carbonic acid
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention relates to an oily canvas coating which is manufactured by the following materials in percentage by weight: 30 to 33 de-ionized water, 20 to 25 polyacrylic emulsion, 4 to 6 alkyd resin,12 to 15 titanium pigment, 10 to 12 talcum powder, 8 to 13 light calcium carbonate, 8 to 13 heavy calcium carbonate, 0.3 to 0.4 dispersant, 0.2 to 0.3 anti-foaming agent, and 1 to 2 thickening agent;and the coating adopts a special emulsion coating which contains oil and polyacrylic emulsion, has the property which is similar to oil paint, has better binding force with the oil paint during the drawing, provides an oil painting with better oily gloss, and replaces the original flax oil with the alkyd resin, so as to ensure that the canvas is uneasy to turn yellow.
Description
Technical field
The present invention relates to a kind of oily canvas coating, the invention still further relates to the preparation method of this coating.
Background technology
When using traditional painting canvas to carry out the oil painting creation, often because the oil in the oil colour is absorbed fully by painting canvas and the oiliness gloss of works is affected, the relatively poor oil that makes again of pliability of painting canvas is not easy to roll collection simultaneously, and used raw material linseed oil makes the painting canvas yellowing easily in the canvas coating, thereby influences the preservation and the reserve value of oil painting.
Therefore for to make the oiliness gloss of oil not influenced by painting canvas, can make simultaneously oil be convenient to collect preservation need a kind ofly can make the oil in the oil colour do not absorbed fully, give works better oiliness gloss, and the pliability of painting canvas is better, be convenient to batch harvesting, make painting canvas be difficult for the painting canvas of yellowing.
Summary of the invention
The object of the present invention is to provide a kind of painting canvas pliability that makes better, be convenient to batch harvesting and make painting canvas be difficult for the oily canvas coating of yellowing and the preparation method of this coating.
For achieving the above object, the present invention adopts following technical scheme: a kind of oily canvas coating, it is made by the following weight proportion raw material: deionized water 30-33, acrylic emulsion 25-30, alkyd resins 4-6, titanium dioxide 12-15, talcum powder 10-12, carbonic acid fine particle calcium carbonate 8-13, carbonic acid coarse whiting 8-13, dispersant 0.3-0.4, defoamer 0.2-0.3, thickener 1-2.
The preparation method of described oily canvas coating: may further comprise the steps successively: (1) is at first opened mixer and is done low cruise, progressively add deionized water, dispersant, defoamer, carbonic acid fine particle calcium carbonate, carbonic acid coarse whiting, speed-raising fully mixes material gradually, and mixing speed reaches more than the dispersion impeller peripheral speed 20m/s; (2) add titanium dioxide and talcum powder, add the back and mix stirring 40 minutes; (3) add alkyd resins and acrylic emulsion, this moment, the dispersion impeller peripheral speed was controlled to be 8-10m/s, and mixing time is 10 minutes; (4) add thickener, this moment, the dispersion impeller peripheral speed was controlled to be 10-12m/s, and mixing time is 5 minutes.
Compared with prior art, the present invention has following beneficial effect: this coating is the coating of oil-containing and acrylic emulsion, during drawing and the adhesion of pigment fine, but the oil in the oil colour can not absorbed again fully, give works better oiliness gloss, and the pliability of painting canvas is better, is convenient to batch harvesting, with alkyd resins replacement linseed oil in the past, make painting canvas be difficult for yellowing simultaneously.
The specific embodiment
Below in conjunction with specific embodiment the present invention is further described.
A kind of oily canvas coating, it is made by the following weight proportion raw material: deionized water 30-33, acrylic emulsion 25-30, alkyd resins 4-6, titanium dioxide 12-15, talcum powder 10-12, carbonic acid fine particle calcium carbonate 8-13, carbonic acid coarse whiting 8-13, dispersant 0.3-0.4, defoamer 0.2-0.3, thickener 1-2.
The main component of described acrylic emulsion is: butyl acrylate 35%, methymethacrylate 13%, deionized water 52%.
Dispersant is joined polyalcohol and many aziridines block copolymer for many in oneself, and thickener is an organic cellulose, and defoamer is a polyvinyl isobutyl ether.
The fineness of described coating is 50um, and the pH value of described coating is 8.5-9.0, and the viscosity of described coating is 2-3Pa.S.
The preparation method of described oily canvas coating: may further comprise the steps successively: (1) is at first opened mixer and is done low cruise, progressively add deionized water, dispersant, defoamer, carbonic acid fine particle calcium carbonate, carbonic acid coarse whiting, speed-raising fully mixes material gradually, and mixing speed reaches more than the dispersion impeller peripheral speed 20m/s; (2) add titanium dioxide and talcum powder, add the back and mix stirring 40 minutes; (3) add alkyd resins and acrylic emulsion, this moment, the dispersion impeller peripheral speed was controlled to be 8-10m/s, and mixing time is 10 minutes; (4) add thickener, this moment, the dispersion impeller peripheral speed was controlled to be 10-12m/s, and mixing time is 5 minutes.
Embodiment 1
(1) open mixer and do low cruise, progressively add deionized water 16kg, dispersant 0.2kg, defoamer 0.125kg, carbonic acid fine particle calcium carbonate 5kg, carbonic acid coarse whiting 5kg, speed-raising fully mixes material gradually, and mixing speed reaches more than the dispersion impeller peripheral speed 20m/s; (2) add titanium dioxide 6kg and talcum powder 5kg, add the back and mix stirring 40 minutes; (3) add alkyd resins 2.5kg and acrylic emulsion 14kg, this moment, the dispersion impeller peripheral speed was controlled to be 8-10m/s, and mixing time is 10 minutes; (4) add thickener 0.5kg, this moment, the dispersion impeller peripheral speed was controlled to be 10-12m/s, and mixing time is 5 minutes.
Embodiment 2
(1) open mixer and do low cruise, progressively add deionized water 31kg, dispersant 0.4kg, defoamer 0.25kg, carbonic acid fine particle calcium carbonate 9kg, carbonic acid coarse whiting 9kg, speed-raising fully mixes material gradually, and mixing speed reaches more than the dispersion impeller peripheral speed 20m/s; (2) add titanium dioxide 12.5kg and talcum powder 10.5kg, add the back and mix stirring 40 minutes; (3) add alkyd resins 6kg and acrylic emulsion 26.25kg, this moment, the dispersion impeller peripheral speed was controlled to be 8-10m/s, and mixing time is 10 minutes; (4) add thickener 1.1kg, this moment, the dispersion impeller peripheral speed was controlled to be 10-12m/s, and mixing time is 5 minutes.
Claims (7)
1, a kind of oily canvas coating is characterized in that being made by the following weight proportion raw material: deionized water 30-33, acrylic emulsion 25-30, alkyd resins 4-6, titanium dioxide 12-15, talcum powder 10-12, carbonic acid fine particle calcium carbonate 8-13, carbonic acid coarse whiting 8-13, dispersant 0.3-0.4, defoamer 0.2-0.3, thickener 1-2.
2, oily canvas coating as claimed in claim 1 is characterized in that: the main component of described acrylic emulsion is: butyl acrylate 35%, methymethacrylate 13%, deionized water 52%.
3, oily canvas coating as claimed in claim 2 is characterized in that: dispersant is joined polyalcohol and many aziridines block copolymer for many in oneself, and thickener is an organic cellulose, and defoamer is a polyvinyl isobutyl ether.
4, oily canvas coating as claimed in claim 1 is characterized in that: the fineness of described coating is 50um.
5, oily canvas coating as claimed in claim 4 is characterized in that: the pH value of described coating is 8.5-9.0.
6, oily canvas coating as claimed in claim 5 is characterized in that: the viscosity of described coating is 2-3Pa.S.
7, the preparation method of oily canvas coating as claimed in claim 1: may further comprise the steps successively: (1) is at first opened mixer and is done low cruise, progressively add deionized water, dispersant, defoamer, carbonic acid fine particle calcium carbonate, carbonic acid coarse whiting, speed-raising fully mixes material gradually, and mixing speed reaches more than the dispersion impeller peripheral speed 20m/s; (2) add titanium dioxide and talcum powder, add the back and mix stirring 40 minutes; (3) add alkyd resins and acrylic emulsion, this moment, the dispersion impeller peripheral speed was controlled to be 8-10m/s, and mixing time is 10 minutes; (4) add thickener, this moment, the dispersion impeller peripheral speed was controlled to be 10-12m/s, and mixing time is 5 minutes.