CN107954737A - 一种具有甲醛净化功能的建筑装饰材料及其制备方法 - Google Patents
一种具有甲醛净化功能的建筑装饰材料及其制备方法 Download PDFInfo
- Publication number
- CN107954737A CN107954737A CN201610905792.6A CN201610905792A CN107954737A CN 107954737 A CN107954737 A CN 107954737A CN 201610905792 A CN201610905792 A CN 201610905792A CN 107954737 A CN107954737 A CN 107954737A
- Authority
- CN
- China
- Prior art keywords
- formaldehyde
- parts
- purifying
- building
- ornament materials
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明属于空气净化技术领域，涉及一种具有甲醛净化功能的建筑装饰材料及其制备方法。该材料由以重量份计的下列成分组成：1～20份甲醛净化剂、100份基材、0.5～1份改性淀粉、1～1.5份粘接剂、0.6～1份木质纤维素、0.01～0.1份发泡剂和65～75份水组成，其中甲醛净化剂由以重量份计的下列成分组成：2～10份聚乙烯吡咯烷酮、1～6份水溶性高分子化合物、4～42份手性氨基醇、1～7份二氧化钛、1～7份二氧化锡、1～7份二氧化硅、2～6份氧化镁、1～13份活性炭、1～9份氯化钙和1～13份可溶性弱酸盐。本发明的材料能够快速、稳定、高效地净化甲醛，适合于大规模推广应用。
Description
技术领域
本发明属于空气净化技术领域，涉及一种具有甲醛净化功能的建筑装饰材料及其制备方法。
背景技术
甲醛是原浆毒物质，能够与蛋白质中的氨基结合，进而生成甲酰化蛋白。甲醛对于人体健康的影响包括嗅觉异常、呼吸道刺激、肺功能异常、中枢神经系统影响、免疫功能异常以及损伤细胞内遗传物质，危害严重，不可不察。因此，我国标准规定室内空气中的甲醛浓度不能大于0.08mg/m3，而公共场所空气中的甲醛浓度不得超过0.12mg/m3。
目前，室内甲醛污染已成为我国最主要的室内空气污染问题，严重危害人们的生命健康。在日常生活中，建筑装饰材料广泛应用于装修过程中，现售的普通建筑装饰材料大多会释放甲醛等有害物质，无法保障室内环境的健康。
针对甲醛污染的治理方法已成为环境污染治理研究的热点之一，研究者提出了多种治理甲醛污染的方法，包括通气换气法、植物净化法、物理吸附法等。但是，现有方法都不能快速、高效、彻底地解决甲醛污染问题。作为人们日常生活中的隐形杀手，甲醛越来越严重地危害着人体的健康，普通的稀释、吸附等物理除甲醛方法已经不能满足人们对于室内空气质量的要求。因此，研究一种能够高效、快速净化甲醛的新型建筑装饰材料是目前亟待解决的难题。
中国发明专利CN 103351151 A中公开了一种能吸收甲醛的建筑材料，其中的功能材料为硅藻土和石墨粉等吸附材料。中国发明专利CN 103601459 A中公开了利用植物纤维制备治理室内甲醛的石膏基建筑材料及其应用方法，其中的功能材料为半碳化植物纤维。中国发明专利CN 104046087 A中公开了一种吸收甲醛的环保建筑材料，其中的功能材料为贝壳的外壳粉末、硅藻土、海泡石等吸附材料。上述除甲醛建筑材料大都只能实现对于甲醛的吸附，而无法达到消除的目的。
发明内容
为了解决上述技术问题，本发明旨在提供一种快速、高效、长效的具有甲醛净化功能的建筑装饰材料及其制备方法。
具体而言，本发明采用如下技术方案：
一种具有甲醛净化功能的建筑装饰材料，其由以重量份计的下列成分组成：1～20份甲醛净化剂、100份基材、0.5～1份改性淀粉、1～1.5份粘接剂、0.6～1份木质纤维素、0.01～0.1份发泡剂和65～75份水组成。
在上述具有甲醛净化功能的建筑装饰材料中，所述甲醛净化剂由以重量份计的下列成分组成：2～10份聚乙烯吡咯烷酮、1～6份水溶性高分子化合物、4～42份手性氨基醇、1～7份二氧化钛、1～7份二氧化锡、1～7份二氧化硅、2～6份氧化镁、1～13份活性炭、1～9份氯化钙和1～13份可溶性弱酸盐。
优选的，所述甲醛净化剂由以重量份计的下列成分组成：4～8份聚乙烯吡咯烷酮、2～5份水溶性高分子化合物、10～30份手性氨基醇、2～6份二氧化钛、2～6份二氧化锡、2～6份二氧化硅、3～5份氧化镁、3～10份活性炭、2～6份氯化钙和3～10份可溶性弱酸盐。
更优选的，所述甲醛净化剂由以重量份计的下列成分组成：6份聚乙烯吡咯烷酮、4份水溶性高分子化合物、20份手性氨基醇、3份二氧化钛、3份二氧化锡、3份二氧化硅、4份氧化镁、6份活性炭、4份氯化钙和6份可溶性弱酸盐。
在上述甲醛净化剂中，所述水溶性高分子化合物选自聚乙二醇(PEG)、聚丙烯酰胺(PAM)、聚丙烯酸(PAA)、羧甲基纤维素(CMC)、聚氧化乙烯(PEO)、聚乙烯醇(PVA)、聚甲基丙烯酸(PMAA)中的任意一种或多种以任意比例形成的混合物。
在上述甲醛净化剂中，所述手性氨基醇为两种对映异构体分子等摩尔混合后的外消旋体，选自1,2-二甲氨基乙醇、2,3-二甲氨基丙醇、1,2-二乙氨基乙醇、1,2-二苯氨基乙醇、1,2,2-三苯基-1,2-二氨基乙醇、2,2-二乙基-1,2-二氨基乙醇、N-甲基-N-乙基氨基三丁醇中的任意一种或多种以任意比例形成的混合物，结构式如下所示。
在上述甲醛净化剂中，所述可溶性弱酸盐在电离后显碱性，选自碳酸盐、碳酸氢盐、亚硫酸盐、硅酸盐、饱和一元羧酸盐中的任意一种或多种以任意比例形成的混合物。
在上述具有甲醛净化功能的建筑装饰材料中，所述基料为粉末状基材，包括石膏粉、腻子粉、水泥、陶土等。
在上述具有甲醛净化功能的建筑装饰材料中，所述粘接剂为水性粘接剂，包括聚乙烯醇类水性粘接剂、乙烯乙酸酯类水性粘接剂、丙烯酸类水性粘接剂、聚氨酯类水性粘接剂、环氧树脂类水性粘接剂、酚醛树脂类水性粘接剂、有机硅类水性粘接剂等。
在上述具有甲醛净化功能的建筑装饰材料中，所述发泡剂包括松香树脂型发泡剂(例如松香皂)、表面活性剂型发泡剂(例如十二烷基苯磺酸钠、聚乙二醇)、蛋白活性物型发泡剂(例如茶皂素发泡剂、动物毛发泡剂)和复合型发泡剂。
一种具有甲醛净化功能的建筑装饰材料的制备方法，其包括如下步骤：
1)将配方量的聚乙烯吡咯烷酮和水溶性高分子化合物球磨混合，得到混合物A；
2)将配方量的二氧化钛、二氧化锡、二氧化硅、氧化镁、活性炭、氯化钙、可溶性弱酸盐和手性氨基醇加入到步骤1)中得到的混合物A中球磨混合，得到混合物B，经过200～300目滤网过滤，得到甲醛净化剂；
3)将配方量的基材和改性淀粉混合，得到混合物C；
4)将配方量的粘接剂、木质纤维素、水和步骤2)中得到的甲醛净化剂搅拌均匀，得到混合物D；
5)将步骤4)中得到的混合物D加入到步骤3)中得到的混合物C中，再加入配方量的发泡剂混合，经过一体化成型，得到具有甲醛净化功能的建筑装饰材料。
在上述制备方法中，步骤1)中所述球磨混合通过球磨机完成，速度为300～800rpm，时间为30～60分钟。
在上述制备方法中，步骤2)中所述球磨混合通过球磨机完成，速度为300～800rpm，时间为30～120分钟。
在上述制备方法中，步骤3)中所述混合通过混合机完成。
在上述制备方法中，步骤4)中所述搅拌通过机械搅拌装置或磁力搅拌装置完成。
在上述制备方法中，步骤5)中所述混合通过混合机完成，速度为200～1000rpm，时间为30～90分钟。
在上述制备方法中，步骤5)中所述一体化成型通过挤出式成型机完成。
除了将甲醛净化剂应用于粉末状基材来制备建筑装饰材料以外，还可以按照甲醛净化剂:溶剂＝1:50～2000的重量比，将甲醛净化剂加入到溶剂(例如水、乙醇)中配制成甲醛净化液，通过将甲醛净化液喷涂或刷涂在成型基材的表面来制备具有甲醛净化功能的建筑装饰材料，其中所述甲醛净化液的用量为1～1000g/m2。
在上述具有甲醛净化功能的建筑装饰材料中，所述成型基材包括木板、石板、石膏板、钢筋混凝土板、瓷砖、壁纸等。
在本发明的具有甲醛净化功能的建筑装饰材料中，活性炭因其具有较高的化学稳定性、较大的比表面积而被用作甲醛净化剂中的吸附载体；手性氨基醇在碱性和/或催化条件下能够与甲醛发生羟醛缩合反应，从而达到净化甲醛的作用；氧化镁能够吸收空气中的水和二氧化碳，进而生成碱式碳酸镁，为羟醛缩合反应提供碱性环境，并且氧化镁吸潮后不会影响复合材料的固体状态；可溶性弱酸盐能够保证甲醛净化剂长期处于碱性条件下，有利于羟醛反应的持续进行；二氧化钛、二氧化锡、二氧化硅等因其自身具有催化性能而被用作催化剂，提高羟醛缩合反应的效率，增强复合材料去除甲醛的能力；作为粘结剂，聚乙烯吡咯烷酮和水溶性高分子能够以均一稳定的形式将上述组分结合在一起，促进甲醛净化剂与甲醛的高效反应。
与现有技术相比，本发明中的具有甲醛净化功能的建筑装饰材料不仅能够实现甲醛的快速吸附，而且能够通过化学反应将其消除，整个净化过程表现出快速、稳定、高效的特点。另外，用于制备建筑装饰材料的生产原料廉价易得，制备过程简便易行，适合于大规模推广应用，极具市场前景。
附图说明
图1为实施例1中的建筑装饰材料成品的SEM谱图。
图2为应用本发明的建筑装饰材料净化空气中的甲醛的效果示意图。
具体实施方式
下面将结合附图和具体的实施例对本发明中的技术方案做出进一步的描述。除非另有说明，下列实施例中所使用的仪器、材料、试剂等均可通过常规商业手段获得。
实施例1：具有甲醛净化功能的石膏材料的制备。
1)采用球磨机，将2g聚乙烯吡咯烷酮和1g聚乙二醇在300rpm的速度下球磨混合60分钟，得到混合物A；
2)将1g二氧化钛、1g二氧化锡、1g二氧化硅、2g氧化镁、1g活性炭、1g氯化钙、1g碳酸钠和4g 1,2-二甲氨基乙醇加入到步骤1)中得到的混合物A中，在300rpm的速度下球磨混合120分钟，得到混合物B，经过200目滤网过滤，得到甲醛净化剂；
3)采用混合机，将100g石膏粉、0.5g改性淀粉混合，得到混合物C；
4)采用机械搅拌，将1g聚乙烯醇、0.6g木质纤维素、65g水和1g步骤2)中得到的甲醛净化剂搅拌均匀，得到混合物D；
5)将步骤4)中得到的混合物D加入到步骤3)中得到的混合物C中，再加入0.01g松香皂，采用混合机在200rpm的速度下混合90分钟，然后采用挤出式成型机一体化成型，得到具有甲醛净化功能的石膏材料，其SEM谱图如图1所示。
实施例2：具有甲醛净化功能的腻子材料的制备。
1)采用球磨机，将10g聚乙烯吡咯烷酮和6g聚丙烯酰胺在800rpm的速度下球磨混合30分钟，得到混合物A；
2)将7g二氧化钛、7g二氧化锡、7g二氧化硅、6g氧化镁、13g活性炭、9g氯化钙、13g亚硫酸钠和42g 2,3-二甲氨基丙醇加入到步骤1)中得到的混合物A中，在800rpm的速度下球磨混合30分钟，得到混合物B，经过200目滤网过滤，得到甲醛净化剂；
3)采用混合机，将100g腻子粉、1g改性淀粉混合，得到混合物C；
4)采用机械搅拌，将1.5g乙烯乙酸酯、1g木质纤维素、75g水和20g步骤2)中得到的甲醛净化剂搅拌均匀，得到混合物D；
5)将步骤4)中得到的混合物D加入到步骤3)中得到的混合物C中，再加入0.1g十二烷基苯磺酸钠，采用混合机在1000rpm的速度下混合30分钟，然后采用挤出式成型机一体化成型，得到具有甲醛净化功能的腻子材料。
实施例3：具有甲醛净化功能的陶土材料的制备。
1)采用球磨机，将4g聚乙烯吡咯烷酮和2g羧甲基纤维素在500rpm的速度下球磨混合40分钟，得到混合物A；
2)将6g二氧化钛、6g二氧化锡、5g二氧化硅、3g氧化镁、3g活性炭、2g氯化钙、3g碳酸氢钠和10g 1,2-二苯氨基乙醇加入到步骤1)中得到的混合物A中，在500rpm的速度下球磨混合80分钟，得到混合物B，经过200目滤网过滤，得到甲醛净化剂；
3)采用混合机，将100g陶土、0.8g改性淀粉混合，得到混合物C；
4)采用机械搅拌，将1.2g聚氨酯、0.8g木质纤维素、70g水和5g步骤2)中得到的甲醛净化剂搅拌均匀，得到混合物D；
5)将步骤4)中得到的混合物D加入到步骤3)中得到的混合物C中，再加入0.05g聚乙二醇，采用混合机在500rpm的速度下混合60分钟，然后采用挤出式成型机一体化成型，得到具有甲醛净化功能的陶土材料。
实施例4：具有甲醛净化功能的水泥材料的制备。
1)采用球磨机，将6g聚乙烯吡咯烷酮和4g聚丙烯酰胺在800rpm的速度下球磨混合30分钟，得到混合物A；
2)将3g二氧化钛、3g二氧化锡、3g二氧化硅、4g氧化镁、6g活性炭、4g氯化钙、6g乙酸钠和20g N-甲基-N-乙基氨基三丁醇加入到步骤1)中得到的混合物A中，在800rpm的速度下球磨混合30分钟，得到混合物B，经过200目滤网过滤，得到甲醛净化剂；
3)采用混合机，将100g水泥、1g改性淀粉混合，得到混合物C；
4)采用机械搅拌，将1.5g乙烯乙酸酯、1g木质纤维素、75g水和20g步骤2)中得到的甲醛净化剂搅拌均匀，得到混合物D；
5)将步骤4)中得到的混合物D加入到步骤3)中得到的混合物C中，再加入0.1g茶皂素发泡剂，采用混合机在1000rpm的速度下混合30分钟，然后采用挤出式成型机一体化成型，得到具有甲醛净化功能的水泥材料。
实施例5：具有甲醛净化功能的石膏材料的制备。
1)采用球磨机，将2g聚乙烯吡咯烷酮和1g聚乙二醇在300rpm的速度下球磨混合60分钟，得到混合物A；
2)将2g二氧化钛、2g二氧化锡、5g二氧化硅、2g氧化镁、1g活性炭、1g氯化钙、1g碳酸钠和4g 1,2-二甲氨基乙醇加入到步骤1)中得到的混合物A中，在300rpm的速度下球磨混合120分钟，得到混合物B，经过200目滤网过滤，得到甲醛净化剂；
3)将5g步骤2)中得到的甲醛净化剂加入到500g水中，通过超声震动的方式分散均匀，得到甲醛净化液；
4)将步骤4)中得到的甲醛净化液反复刷涂在1m×1m的石膏板上，得到具有甲醛净化功能的石膏材料。
实施例6：本发明中的建筑装饰材料的甲醛净化效果实验。
分别称取50g实施例1～5中的建筑装饰材料作为待测样品，同时按照CN103351151中记载的方法制备相应的材料并称取50g作为平行对照品。
将上述除甲醛产品分别装入微孔盒中并置于封闭实验装置的中心位置，加入3.3μl的30％甲醛液体后立即关闭装置门，打开加热台，开启风扇搅拌，使得甲醛气体均匀分布于整个实验装置中，同时使用甲醛传感器实时记录实验装置中的甲醛气体浓度，并按照下式计算甲醛去除率(％)：甲醛去除率＝(C0-Ct)/C0×100％，其中：C0为初始含量，Ct为某时刻的实时含量，相应的实验结果如图2所示。
如图2可知，现有产品去除甲醛的曲线基本上呈线性，随着时间的推移呈现出匀速去除的态势，实验时间为50分钟时，甲醛去除率可达到44％左右。与之相比，本发明的建筑装饰材料在实验最初的4～6分钟内就能够达到80％以上的甲醛去除率。由此可见，本发明的建筑装饰材料确实具备快速、高效净化甲醛的功能。
Claims (9)
1.一种具有甲醛净化功能的建筑装饰材料，其由以重量份计的下列成分组成：1～20份甲醛净化剂、100份基材、0.5～1份改性淀粉、1～1.5份粘接剂、0.6～1份木质纤维素、0.01～0.1份发泡剂和65～75份水组成；其中：
所述甲醛净化剂由以重量份计的下列成分组成：2～10份聚乙烯吡咯烷酮、1～6份水溶性高分子化合物、4～42份手性氨基醇、1～7份二氧化钛、1～7份二氧化锡、1～7份二氧化硅、2～6份氧化镁、1～13份活性炭、1～9份氯化钙和1～13份可溶性弱酸盐。
2.根据权利要求1所述的具有甲醛净化功能的建筑装饰材料，其特征在于：
所述水溶性高分子化合物选自聚乙二醇、聚丙烯酰胺、聚丙烯酸、羧甲基纤维素、聚氧化乙烯、聚乙烯醇、聚甲基丙烯酸中的任意一种或多种以任意比例形成的混合物。
3.根据权利要求1所述的具有甲醛净化功能的建筑装饰材料，其特征在于：
所述手性氨基醇选自1,2-二甲氨基乙醇、2,3-二甲氨基丙醇、1,2-二乙氨基乙醇、1,2-二苯氨基乙醇、1,2,2-三苯基-1,2-二氨基乙醇、2,2-二乙基-1,2-二氨基乙醇、N-甲基-N-乙基氨基三丁醇中的任意一种或多种以任意比例形成的混合物。
4.根据权利要求1所述的具有甲醛净化功能的建筑装饰材料，其特征在于：
所述可溶性弱酸盐选自碳酸盐、碳酸氢盐、亚硫酸盐、硅酸盐、饱和一元羧酸盐中的任意一种或多种以任意比例形成的混合物。
5.根据权利要求1所述的具有甲醛净化功能的建筑装饰材料，其特征在于：
所述基材为粉末状基材，包括石膏粉、腻子粉、水泥和陶土。
6.根据权利要求1所述的具有甲醛净化功能的建筑装饰材料，其特征在于：
所述粘接剂为水性粘接剂，包括聚乙烯醇类水性粘接剂、乙烯乙酸酯类水性粘接剂、丙烯酸类水性粘接剂、聚氨酯类水性粘接剂、环氧树脂类水性粘接剂、酚醛树脂类水性粘接剂和有机硅类水性粘接剂。
7.根据权利要求1所述的具有甲醛净化功能的建筑装饰材料，其特征在于：
所述发泡剂包括松香树脂型发泡剂、表面活性剂型发泡剂、蛋白活性物型发泡剂和复合型发泡剂。
8.一种根据权利要求1至7中任一项所述的具有甲醛净化功能的建筑装饰材料的制备方法，其包括如下步骤：
1)将配方量的聚乙烯吡咯烷酮和水溶性高分子化合物球磨混合，得到混合物A；
2)将配方量的二氧化钛、二氧化锡、二氧化硅、氧化镁、活性炭、氯化钙、可溶性弱酸盐和手性氨基醇加入到步骤1)中得到的混合物A中球磨混合，得到混合物B，经过200～300目滤网过滤，得到甲醛净化剂；
3)将配方量的基材和改性淀粉混合，得到混合物C；
4)将配方量的粘接剂、木质纤维素、水和步骤2)中得到的甲醛净化剂搅拌均匀，得到混合物D；
5)将步骤4)中得到的混合物D加入到步骤3)中得到的混合物C中，再加入配方量的发泡剂混合，经过一体化成型，得到具有甲醛净化功能的建筑装饰材料。
9.根据权利要求8所述的制备方法，其特征在于：
步骤1)中所述球磨混合通过球磨机完成，速度为300～800rpm，时间为30～60分钟；
步骤2)中所述球磨混合通过球磨机完成，速度为300～800rpm，时间为30～120分钟；
步骤3)中所述混合通过混合机完成；
步骤4)中所述搅拌通过机械搅拌装置或磁力搅拌装置完成；
步骤5)中所述混合通过混合机完成，速度为200～1000rpm，时间为30～90分钟；
步骤5)中所述一体化成型通过挤出式成型机完成。