CN1226357C - 环保型石膏基建筑腻子粉 - Google Patents
环保型石膏基建筑腻子粉 Download PDFInfo
- Publication number
- CN1226357C CN1226357C CN 03117999 CN03117999A CN1226357C CN 1226357 C CN1226357 C CN 1226357C CN 03117999 CN03117999 CN 03117999 CN 03117999 A CN03117999 A CN 03117999A CN 1226357 C CN1226357 C CN 1226357C
- Authority
- CN
- China
- Prior art keywords
- powder
- plaster
- paris
- environment
- friendly type
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
环保型石膏基建筑腻子粉属于建筑材料,它主要解决传统建筑腻子粘结强度低、收缩大、易开裂、施工效率低、施工周期长、环境污染大的问题,本发明的技术方案是以建筑石膏为主要凝结硬化组分,通过复合缓凝剂解决建筑石膏凝结硬化快、单一缓凝剂强度损失大的问题,采用无机矿粉与纤维素醚复合,降低材料成本,改善腻子的保水性,采用水溶性胶粉提高建筑腻子的粘结强度,该环保型石膏基建筑腻子粉为单组分固体粉末状,不含有毒物质,施工性能好,施工周期短,粘结强度高,腻子表面细腻光滑,可用作建筑物内墙腻子。
Description
技术领域:
本发明属于建筑材料,它用作建筑物内墙腻子。
背景技术:
传统建筑腻子主要以无机惰性矿物为填料,以有机高分子物质为成膜物质,腻子固化完全依赖聚合物成膜。该类建筑腻子粘结强度较低,收缩较大,一般仅适于在较平整的墙面上施工,若厚度过大,则易开裂;施工效率低,干燥慢,施工周期长;在施工现场配制,使用不方便;有的腻子施工和使用期间释放甲醛等有毒物质,施工环境恶劣,环境污染大。并且传统建筑腻子通常采用单一的保水剂技术,即纤维素醚保水,其成本较高。考虑到建筑石膏具有水化活性、凝结硬化快、粘结强度高、体积稳定性好、质感细腻,满足建筑腻子对材性的基本要求,且对人体亲和无害,为绿色建材,发明人在国家自然科学基金委员会和重庆市科学技术委员会的资助(资助项目编号分别为50078055、2000-6375)下,以建筑石膏为主要原料,以腻子工作性、保水性、粘结性为研究重点进行了实验研究。采用建筑石膏作为建筑腻子粉的主要凝结硬化组分,突破了传统建筑腻子依赖在有机高分子成膜物质中添加无机惰性填料的技术模式,并在2002年的《新型建筑材料》第1期上发表了论文“磷石膏基建筑腻子的配方与性能研究”,该文着重介绍了此研究的部分成果。
本发明采用的生产工艺为常规工艺。
发明内容:
本发明的目的在于避免上述现有技术的不足之处而提供一种不含有毒物质、施工性能好、施工周期短、粘结强度高、保水性好、腻子表面细腻光滑的环保型石膏基建筑腻子粉。
为了实现上述发明目的,本发明的技术方案是:
配制了环保型石膏基建筑腻子粉,它包括以下组分和重量百分比:
建筑石膏 60-85
复合缓凝剂 0.15-0.5
复合保水剂 3.05-10.2
水溶性胶粉 0.1-3
填料 5-30
其中,建筑石膏为下列建筑石膏中的一种:天然石膏制备的建筑石膏、磷石膏制备的建筑石膏、脱硫石膏制备的建筑石膏;水溶性胶粉为下列水溶性胶粉中的一种:改性木薯淀粉、聚乙烯醇胶粉、乙烯-醋酸乙烯共聚乳胶粉、聚丙烯酸酯乳胶粉;填料为下列填料中的一种:双飞粉、滑石粉。建筑石膏具有水化活性、凝结硬化快、粘结强度高、体积稳定性好、质感细腻、对人体亲和无害,为绿色建材,可用于制备环保型建筑腻子,加入建筑石膏,以改善该环保型石膏基建筑腻子粉的粘结强度。加入上述水溶性固体粉末胶粉,以改善该建筑腻子粉的粘结强度。乙烯-醋酸乙烯共聚乳胶粉、聚乙烯醇、改性木薯淀粉、聚丙烯酸酯乳胶粉可有效提高建筑腻子的粘结强度。掺入0.1%~0.5%乙烯-醋酸乙烯共聚乳胶粉或0.6%~1.0%聚乙烯醇胶粉或2%~3%改性木薯淀粉胶,可满足该环保型石膏基建筑腻子粉对粘结强度的要求。加入上述填料,以改善该环保型石膏基建筑腻子粉的施工性。为了减少缓凝剂掺量,改善腻子施工性,可掺入一定比例的无机惰性填料,随填料掺量增加,腻子凝结时间延长,涂刮性、打磨性趋好,但强度、粘结性降低。滑石粉、双飞粉等可有效改善建筑腻子的施工性能。
采用复合缓凝剂,其组分及重量百分比:
柠檬酸 0.05-0.2
骨胶 0.1-0.3
加入上述复合缓凝剂,以调节建筑石膏凝结硬化时间。通常建筑石膏凝结硬化很快,初凝时间为6~30分钟,可操作时间只有4~10分钟,不能满足建筑腻子的施工要求,建筑腻子的工作时间一般在2小时以上才能满足施工要求,为此必须采用缓凝技术。缓凝剂种类、掺量不同,对初凝时间和终凝时间的延长不同。普通的单一缓凝技术存在缓凝剂用量较大、硬化体强度损失很大的缺陷。本腻子采用柠檬酸与骨胶复合缓凝技术,可有效改善单一缓凝技术存在的缺陷。当柠檬酸掺量为0.1%、骨胶掺量为0.2%时,建筑石膏的初凝时间可长达172分钟,终凝时间可达到213分钟,而其抗折强度可达到2.11MPa,抗压强度可达到8.53MPa。
采用复合保水剂,其组分及重量百分比:
甲基纤维素醚或羧甲基纤维素醚或羟丙基甲基纤维素醚0.05-0.2
膨润土 3-10
加入上述复合保水剂,以改善该环保型石膏基建筑腻子粉的保水性。保水性是建筑腻子的重要技术指标,良好的保水性可避免建筑腻子塑性开裂和表面粉化。建筑腻子通常采用单一的保水剂技术,纤维素醚是常用的商品保水剂,不同的保水剂种类和掺量,改善建筑腻子的保水性不同,其中甲基纤维素醚保水效果最好,但其掺量较大,成本较高。新加入的组分膨润土,又名斑脱岩或膨土岩,以蒙脱石为主要矿物成分的的细粒粘土,常含有长石、石英、拜来石、方解石及火山碎屑物。主要化学成分为:SiO2、Al2O3及少量Fe2O3、MgO、CaO、K2O、Na2O和TiO2等。一般呈白色,含杂质时呈淡绿、淡青、灰白、粉红等色。膨润土有强烈的吸水性,吸水后体积膨大10-30倍,在水溶液中呈悬浮和胶凝状态,具有阳离子交换的特性,还具有高的粘结性和耐火性。膨润土为层状结构,具有保水作用,与甲基纤维素醚复合使用可有效降低后者掺量,降低腻子配制的材料成本。当甲基纤维素醚掺量为0.2%、膨润土为3%~10%时,建筑腻子失水率为0.1042g/cm2,绝干抗折强度和抗压强度分别为2.60MPa和9.70MPa。
试验表明,当配比为:建筑石膏68.96、柠檬酸0.1、骨胶0.2、甲基纤维素醚0.1、膨润土4.0、乙烯-醋酸乙烯共聚乳胶粉0.25、双飞粉26.39,该环保型石膏基建筑腻子粉的性能为:标准稠度46%、表干时间2小时10分钟、打磨性48%、白度78、保水率96%、绝干抗折强度2.8MPa、绝干抗压强度6.2MPa、粘结强度0.72MPa。
本发明相比现有技术具有如下优点:
1.不含有毒物质。
2.粘结强度高,施工效率高,施工周期短。
3.采用膨润土与纤维素醚复合保水技术,不但降低了腻子的材料成本,而且改善了保水性能。
4.施工性能好,腻子表面细腻光滑。
5.本发明为单组分固体粉末状产品,无须现场配制,使用方便。
具体实施方式:
本发明的具体实施例如下,各实施例均用重量百分比表示。
实施例1:
建筑石膏 68.96
柠檬酸 0.1
骨胶 0.2
甲基纤维素醚 0.1
膨润土 4
乙烯-醋酸乙烯共聚乳胶粉 0.25
双飞粉 26.39。
实施例2:
建筑石膏 77.3
柠檬酸 0.15
骨胶 0.1
羟丙基甲基纤维素醚 0.2
膨润土 5.7
聚乙烯醇胶粉 0.85
滑石粉 15.7。
实施例3:
建筑石膏 85
柠檬酸 0.1
骨胶 0.2
羧甲基纤维素醚 0.1
膨润土 6.25
乙烯-醋酸乙烯共聚乳胶粉 0.25
双飞粉 8.1。
实施例4:
建筑石膏 60
柠檬酸 0.05
骨胶 0.25
甲基纤维素醚 0.05
膨润土 8
改性木薯淀粉 2.5
滑石粉 29.15。
实施例5:
建筑石膏 81.5
柠檬酸 0.2
骨胶 0.1
羟丙基甲基纤维素醚 0.2
膨润土 3
改性木薯淀粉 2.5
双飞粉 12.5。
实施例6:
建筑石膏 65
柠檬酸 0.1
骨胶 0.1
甲基纤维素醚 0.05
膨润土 10
聚乙烯醇胶粉 1
滑石粉 23.75。
实施例7:
建筑石膏 71.39
柠檬酸 0.05
骨胶 0.25
羧甲基纤维素醚 0.2
膨润土 7.45
乙烯-醋酸乙烯乳胶粉 0.1
滑石粉 20.56。
上述石膏基建筑腻子粉可将所需原材料按比例一次称足同时搅拌而成。
Claims (8)
1.环保型石膏基建筑腻子粉,其特征在于该环保型石膏基建筑腻子粉包括以下组分和重量百分比:
建筑石膏 60-85
复合缓凝剂 0.15-0.5
复合保水剂 3.05-10.2
水溶性胶粉 0.1-3
填料 5-30
其中,建筑石膏为下述建筑石膏中的一种:天然石膏制备的建筑石膏、磷石膏制备的建筑石膏、脱硫石膏制备的建筑石膏;复合缓凝剂的组分及重量百分比为:柠檬酸0.05-0.2、骨胶0.1-0.3;复合保水剂的组分及重量百分比为:甲基纤维素醚或羧甲基纤维素醚或羟丙基甲基纤维素醚0.05-0.2、膨润土3-10;水溶性胶粉为下述水溶性胶粉中的一种:改性木薯淀粉、乙烯—醋酸乙烯共聚乳胶粉、聚乙烯醇胶粉、聚丙烯酸酯乳胶粉;填料为下述填料中的一种:滑石粉、双飞粉。
2.如权利要求1所述的环保型石膏基建筑腻子粉,其特征在于该环保型石膏基建筑腻子粉的具体组分及重量百分比:
建筑石膏 68.96
柠檬酸 0.1
骨胶 0.2
甲基纤维素醚 0.1
膨润土 4
乙烯—醋酸乙烯共聚乳胶粉 0.25
双飞粉 26.39。
3.如权利要求1所述的环保型石膏基建筑腻子粉,其特征在于该环保型石膏基建筑腻子粉的具体组分及重量百分比:
建筑石膏 77.3
柠檬酸 0.15
骨胶 0.1
羟丙基甲基纤维素醚 0.2
膨润土 5.7
聚乙烯醇胶粉 0.85
滑石粉 15.7。
4.如权利要求1所述的环保型石膏基建筑腻子粉,其特征在于该环保型石膏基建筑腻子粉的具体组分及重量百分比:
建筑石膏 85
柠檬酸 0.1
骨胶 0.2
羧甲基纤维素醚 0.1
膨润土 6.25
乙烯—醋酸乙烯共聚乳胶粉 0.25
双飞粉 8.1。
5.如权利要求1所述的环保型石膏基建筑腻子粉,其特征在于该环保型石膏基建筑腻子粉的具体组分及重量百分比:
建筑石膏 60
柠檬酸 0.05
骨胶 0.25
膨润土 8
甲基纤维素醚 0.05
改性木薯淀粉 2.5
滑石粉 29.15。
6.如权利要求1所述的环保型石膏基建筑腻子粉,其特征在于该环保型石膏基建筑腻子粉的具体组分及重量百分比:
建筑石膏 81.5
柠檬酸 0.2
骨胶 0.1
羟丙基甲基纤维素醚 0.2
膨润土 3
改性木薯淀粉 2.5
双飞粉 12.5。
7.如权利要求1所述的环保型石膏基建筑腻子粉,其特征在于该环保型石膏基建筑腻子粉的具体组分及重量百分比:
建筑石膏 65
柠檬酸 0.1
骨胶 0.1
甲基纤维素醚 0.05
膨润土 10
聚乙烯醇胶粉 1
滑石粉 23.75。
8.如权利要求1所述的环保型石膏基建筑腻子粉,其特征在于该环保型石膏基建筑腻子粉的具体组分及重量百分比:
建筑石膏 71.39
柠檬酸 0.05
骨胶 0.25
羧甲基纤维素醚 0.2
膨润土 7.45
乙烯—醋酸乙烯乳胶粉 0.1
滑石粉 20.56。