CN107937977A - 一种阴极辊电解抛光液及抛光方法 - Google Patents

一种阴极辊电解抛光液及抛光方法 Download PDF

Info

Publication number
CN107937977A
CN107937977A CN201711379114.1A CN201711379114A CN107937977A CN 107937977 A CN107937977 A CN 107937977A CN 201711379114 A CN201711379114 A CN 201711379114A CN 107937977 A CN107937977 A CN 107937977A
Authority
CN
China
Prior art keywords
concentration
electrolytic polishing
polishing liquid
hno
nano
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201711379114.1A
Other languages
English (en)
Inventor
张玉萍
方媛
任鹏
徐尚元
张苓
唐飞飞
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Xian Taijin Industrial Electrochemical Technology Co Ltd
Original Assignee
Xian Taijin Industrial Electrochemical Technology Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Xian Taijin Industrial Electrochemical Technology Co Ltd filed Critical Xian Taijin Industrial Electrochemical Technology Co Ltd
Priority to CN201711379114.1A priority Critical patent/CN107937977A/zh
Publication of CN107937977A publication Critical patent/CN107937977A/zh
Pending legal-status Critical Current

Abstract

一种阴极辊电解抛光液及抛光方法，该电解抛光液由两种或两种以上的NH4HF2、NaNO3、HNO3、H2SO4、(CH2OH)2溶液混合而成，其中混合液中NH4HF2的浓度为20‑100g/L，NaNO3的浓度为10‑50g/L，HNO3的浓度为10‑20ml/L，H2SO4的浓度为10‑20ml/L，(CH2OH)2的浓度为5‑10ml/L。本发明的阴极辊电解抛光方法为：将钛阴极辊清洗去油后，放置于电解抛光液中，在20‑50℃，20‑50V电压下抛光3‑5min。本发明操作简单、便利，抛光的钛阴极辊表面光洁，具有镜面反光的效果，制造的电解铜箔，具有厚度薄、结晶细小致密、容易剥离的优点，实测铜箔厚度δ≤10微米，可以满足锂电池生产需要。锂电池使用性能优异的薄铜箔，可以降低成本，同时提供更高的能量密度。

Description

一种阴极辊电解抛光液及抛光方法
技术领域
本发明涉及一种钛阴极辊抛光方法，特别涉及一种阴极辊电解抛光液及抛光方法。
背景技术
钛阴极辊是电解制造铜箔的核心部件，钛阴极辊在电解生产铜箔的过程中，不断被腐蚀，阴极辊表面氧化膜逐渐增厚，粗糙度不断增大，导致铜离子在阴极辊表面结晶粗大，需要定期抛光。目前阴极辊运行一段时间后采用研磨的方法进行抛光，该方法费时费力，需要专门的研磨设备。
发明内容
本发明的目的在于提供一种简单方便，抛光效果优良，可以有效去除钛阴极辊表面的氧化皮，使得钛阴极辊表观光亮的阴极辊电解抛光液及抛光方法。
为达到上述目的，本发明的电解抛光液由两种或两种以上的NH4HF2、NaNO3、HNO3、H2SO4、(CH2OH)2溶液混合而成，其中混合液中NH4HF2的浓度为20-100g/L，NaNO3的浓度为10-50g/L，HNO3的浓度为10-20ml/L，H2SO4的浓度为10-20ml/L，(CH2OH)2的浓度为5-10ml/L。
本发明的阴极辊电解抛光方法为：将钛阴极辊清洗去油后，放置于电解抛光液中，在20-50℃，20-50V电压下抛光3-5min。
本发明与现有技术相比具有以下优点：不需要专有研磨设备，只需要一台简易电解抛光槽，就可以抛光各种规格钛阴极辊；现有技术研磨一台阴极辊需要花费数小时，本发明抛光一台阴极辊只需要3-5min,可以节约时间，并节省人力物力；相比研磨，电解抛光没有引入杂质，使钛表面的洁净度非常高，提高了铜的过沉积电位，有利于细小的铜离子析出，增大了铜箔的抗拉强度和延伸率，且铜箔厚度均匀性好，延长了锂电池的使用寿命。
具体实施方式
实施例1：
1)电解抛光液的制备：将NH4HF2、HNO3溶液混合，其中混合液中NH4HF2的浓度为80g/L，HNO3的浓度为20ml/L。
2)将钛阴极辊清洗去油后，放置于电解抛光液中，在20℃，50V电压下抛光5min。
实施例2：
1)电解抛光液的制备：将NH4HF2、H2SO4溶液混合，其中混合液中NH4HF2的浓度为50g/L，混合液中H2SO4的浓度为10ml/L；
2)将钛阴极辊清洗去油后，放置于电解抛光液中，在30℃，40V电压下抛光5min。
实施例3：
1)电解抛光液的制备：将NH4HF2、NaNO3、HNO3溶液混合，其中混合液中NH4HF2的浓度为50g/L，NaNO3的浓度为20g/L，HNO3的浓度为18ml/L；
2)将钛阴极辊清洗去油后，放置于电解抛光液中，在40℃，30V电压下抛光4min。
实施例4：
1)电解抛光液的制备：将NH4HF2、HNO3、H2SO4、(CH2OH)2溶液混合，其中混合液中的NH4HF2浓度为30g/L，HNO3的浓度为13ml/L，H2SO4的浓度为15ml/L，(CH2OH)2的浓度为8ml/L；
2)将钛阴极辊清洗去油后，放置于电解抛光液中，在50℃，20V电压下抛光3.5min。
实施例5：
1)电解抛光液的制备：将NH4HF2、NaNO3、HNO3、H2SO4、(CH2OH)2溶液混合而成，其中混合液中NH4HF2的浓度为100g/L，NaNO3的浓度为40g/L，HNO3的浓度为10ml/L，H2SO4的浓度为13ml/L，(CH2OH)2的浓度为5ml/L；
2)将钛阴极辊清洗去油后，放置于电解抛光液中，在35℃，35V电压下抛光3min。
实施例6：
1)电解抛光液的制备：将NH4HF2、HNO3、H2SO4、(CH2OH)2溶液混合而成，其中混合液中NH4HF2的浓度为80g/L，HNO3的浓度为20ml/L，H2SO4的浓度为18ml/L，(CH2OH)2的浓度为9ml/L；
2)将钛阴极辊清洗去油后，放置于电解抛光液中，在25℃，45V电压下抛光4min。
实施例7：
1)电解抛光液的制备：将NH4HF2、NaNO3、HNO3、H2SO4、(CH2OH)2溶液混合而成，其中混合液中NH4HF2的浓度为100g/L，NaNO3的浓度为20g/L，HNO3的浓度为10ml/L，H2SO4的浓度为20ml/L，(CH2OH)2的浓度为10ml/L；
2)将钛阴极辊清洗去油后，放置于电解抛光液中，在45℃，25V电压下抛光3min。
本发明操作简单、便利，抛光的钛阴极辊表面光洁，具有镜面反光的效果，制造的电解铜箔，具有厚度薄、结晶细小致密、容易剥离的优点，实测铜箔厚度δ≤10微米，铜箔强度大，延伸率高，用于锂电池负极集流体，与锂电池负极材料亲和性良好。

Claims (2)

1.一种阴极辊电解抛光液，其特征在于：由两种或两种以上的NH4HF2、NaNO3、HNO3、H2SO4、(CH2OH)2溶液混合而成，其中混合液中NH4HF2的浓度为20-100g/L，NaNO3的浓度为10-50g/L，HNO3的浓度为10-20ml/L，H2SO4的浓度为10-20ml/L，(CH2OH)2的浓度为5-10ml/L。
2.一种如权利要求1所述抛光液的阴极辊电解抛光方法，其特征在于：将钛阴极辊清洗去油后，放置于电解抛光液中，在20-50℃，20-50V电压下抛光3-5min。
CN201711379114.1A 2017-12-20 2017-12-20 一种阴极辊电解抛光液及抛光方法 Pending CN107937977A (zh)