CN107910427A - 一种二极管转色薄膜 - Google Patents
一种二极管转色薄膜 Download PDFInfo
- Publication number
- CN107910427A CN107910427A CN201711193073.7A CN201711193073A CN107910427A CN 107910427 A CN107910427 A CN 107910427A CN 201711193073 A CN201711193073 A CN 201711193073A CN 107910427 A CN107910427 A CN 107910427A
- Authority
- CN
- China
- Prior art keywords
- annesl
- diode
- film according
- film
- antioxidant
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
一种二极管转色薄膜，属于光学材料技术领域，包括如下重量百分比的组分：颜料5～12%，荧光粉3～8%，分散剂8～12%，成膜助剂6～12%，消泡剂5～8%，聚苯醚树脂粉2～6%，增塑剂1～3%，偶联剂1～3%，辅料2～4%，阻燃剂1～3%，抗氧剂2～4%，其余为基体材料。本发明组分科学，并且灯具组装简单，提高了生产效率，降低了生产成本。而且与传统LED灯具相比，转色薄膜可使荧光粉转换效率增高，而且能够直接获得均匀的高品质白光，提高了灯具的系统光效，消费者在使用过程中可以根据需要方便更换薄膜，该薄膜对光学基材控制较为理想，色温均匀、产品合格率高，增加了转换效率，减少了光衰，延长了产品的使用寿命。
Description
技术领域
本发明属于光学材料技术领域，涉及一种二极管薄膜，特别是涉及一种用于二极管转色的薄膜。
背景技术
发光二极管是利用半导体等固体材料所制作而成的光源系统。LED光源与传统光源相比较更具有诸多优点，如：耗电量低、体积小、反应速度快、高效率、环保及可平面封装等；而在节能方面，其可使用的寿命长达60 年，是传统电灯泡的100倍，消耗的能量却只有传统电灯泡的10%。LED已被公认为 21 世纪最具潜力的环保照明光源，也是继白炽灯、日光灯和节能灯之后的第四代照明电光源。
在能源日趋紧张的当今时代，只有高效、环保地利用现有能源才能更好地可持续发展。LED作为照明光源无论从亮度还是节能环保方面都要好于现有的白炽灯等照明光源，已经成为世界各国大力推行及重点研究的新型产业之一。如果利用发光二极管制作白光LED用作照明光源，则必须应用光色组合的技术，才能达成获得白光的目的。目前在各种可行的光色组合技术中，利用荧光材料来进行光色转变，是一种最为便捷、最节省成本的方法。传统白光LED结构的封装形式一般采用点胶法，此方法虽然简单，但对荧光粉混合的光学基材厚度控制不理想，且荧光粉混胶40分钟后沉降严重，容易造成荧光粉层厚度不均匀，影响产品一致性，导致出光时色温不均匀并产生内白外黄的黄圈光晕。而且在高功率光源上使用时，发光芯片与荧光粉层直接接触，容易导致发热量过大，而荧光粉层散热不良，致使发光效率降低并损耗率增加，产品合格率降低，造成生产成本过高且光衰现象严重。
发明内容
本发明针对传统发光二极管制作白光LED需要进行光色转变，现有技术中采用点胶法，该方法对光学基材控制不理想，容易引起色温不均、荧光粉层散热不良，产品合格率低，光衰现象严重等不足，提出一种二极管转色薄膜，可增加转换效率，减少光衰，延长产品的使用寿命。
本发明的技术方案：一种二极管转色薄膜，其特征在于，包括如下重量百分比的组分：颜料 5～12%，荧光粉 3～8%，分散剂 8～12%，成膜助剂 6～12%，消泡剂 5～8%，聚苯醚树脂粉 2～6%，增塑剂 1～3%，偶联剂 1～3%，辅料 2～4%，阻燃剂 1～3%，抗氧剂2～4%，其余为基体材料。
所述颜料为钛白粉、氧化铁红、氧化铬绿、联苯胺黄、酞青蓝中的一种。
所述基体材料为PC、PET、PMMA 中的一种。
所述增塑剂为磷酸三甲苯酯。
所述分散剂是硬脂酸、硬脂酸单甘油酯、硬脂酸丁酯、油酸酰胺、芥酸酰胺中的一种。
所述成膜助剂为乙二醇乙醚。
所述消泡剂为酰胺。
所述偶联剂为硅烷偶联剂。
所述抗氧剂为受阻酚类抗氧剂与亚磷酸酯类抗氧剂按照1:1.2比例构成。
本发明的有益效果为：本发明提出的一种二极管转色薄膜，组分科学，可通过注塑成型工艺将荧光粉均匀地分散在光学基材中，可以与蓝光芯片组合成各种不同的灯具，并且灯具组装简单，提高了生产效率，降低了生产成本。而且与传统LED 灯具相比，转色薄膜可使荧光粉转换效率增高，而且能够直接获得均匀的高品质白光，提高了灯具的系统光效，消费者在使用过程中可以根据需要方便更换薄膜，该薄膜对光学基材控制较为理想，色温均匀、产品合格率高，增加了转换效率，减少了光衰，延长了产品的使用寿命。
具体实施方式
下面结合实施例对本发明作进一步说明：
一种二极管转色薄膜，其特征在于，包括如下重量百分比的组分：颜料 5～12%，荧光粉3～8%，分散剂 8～12%，成膜助剂 6～12%，消泡剂 5～8%，聚苯醚树脂粉 2～6%，增塑剂 1～3%，偶联剂 1～3%，辅料 2～4%，阻燃剂 1～3%，抗氧剂2～4%，其余为基体材料。
一种二极管转色薄膜，颜料为钛白粉、氧化铁红、氧化铬绿、联苯胺黄、酞青蓝中的一种；基体材料为PC、PET、PMMA 中的一种；增塑剂为磷酸三甲苯酯；分散剂是硬脂酸、硬脂酸单甘油酯、硬脂酸丁酯、油酸酰胺、芥酸酰胺中的一种；成膜助剂为乙二醇乙醚；消泡剂为酰胺；偶联剂为硅烷偶联剂；抗氧剂为受阻酚类抗氧剂与亚磷酸酯类抗氧剂按照1:1.2比例构成。
本发明组分科学，与传统LED 灯具相比，转色薄膜可使荧光粉转换效率增高，而且能够直接获得均匀的高品质白光，提高了灯具的系统光效，消费者在使用过程中可以根据需要方便更换薄膜，该薄膜对光学基材控制较为理想，色温均匀、产品合格率高，增加了转换效率，减少了光衰，延长了产品的使用寿命。
Claims (9)
1.一种二极管转色薄膜，其特征在于，包括如下重量百分比的组分：颜料 5～12%，荧光粉 3～8%，分散剂 8～12%，成膜助剂 6～12%，消泡剂 5～8%，聚苯醚树脂粉 2～6%，增塑剂1～3%，偶联剂 1～3%，辅料 2～4%，阻燃剂 1～3%，抗氧剂2～4%，其余为基体材料。
2.根据权利要求1所述的一种二极管转色薄膜，其特征在于：所述颜料为钛白粉、氧化铁红、氧化铬绿、联苯胺黄、酞青蓝中的一种。
3.根据权利要求1所述的一种二极管转色薄膜，其特征在于：所述基体材料为PC、PET、PMMA 中的一种。
4.根据权利要求1所述的一种二极管转色薄膜，其特征在于：所述增塑剂为磷酸三甲苯酯。
5.根据权利要求1所述的一种二极管转色薄膜，其特征在于：所述分散剂是硬脂酸、硬脂酸单甘油酯、硬脂酸丁酯、油酸酰胺、芥酸酰胺中的一种。
6.根据权利要求1所述的一种二极管转色薄膜，其特征在于：所述成膜助剂为乙二醇乙醚。
7.根据权利要求1所述的一种二极管转色薄膜，其特征在于：所述消泡剂为酰胺。
8.根据权利要求1所述的一种二极管转色薄膜，其特征在于：所述偶联剂为硅烷偶联剂。
9.根据权利要求1所述的一种二极管转色薄膜，其特征在于：所述抗氧剂为受阻酚类抗氧剂与亚磷酸酯类抗氧剂按照1:1.2比例构成。