CN107892812A - 一种耐磨级pps - Google Patents
一种耐磨级pps Download PDFInfo
- Publication number
- CN107892812A CN107892812A CN201711186312.6A CN201711186312A CN107892812A CN 107892812 A CN107892812 A CN 107892812A CN 201711186312 A CN201711186312 A CN 201711186312A CN 107892812 A CN107892812 A CN 107892812A
- Authority
- CN
- China
- Prior art keywords
- pps
- wear
- conductive
- tetrafluoroethene
- potassium titanate
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种耐磨级PPS，其按重量份数表示包括：PPS树脂40—60，钛酸钾晶须10—30，玻璃纤维20—30，四氟乙烯10—20，环氧树脂1‑5，本发明具有的优良机械性能和电绝缘性能以及良好的热稳定性、优越的耐化学腐蚀性、优异的抗化学腐蚀性等特点。
Description
工艺领域
本发明涉及一种耐磨级PPS，属于塑料制备的技术领域。
技术背景
PPS薄膜产业作为一种新兴行业，其最大优点就是耐热性好，特别是在高应力、高温情况下耐热性能非常好，而且PPS薄膜高温劣化速度在高湿条件下和在干燥空气中没有差别，完全不会存在水解性，同时PPS薄膜在不添加任何添加剂的情况下就能具有很高的阻燃性，在低温状况下PPS薄膜仍可保持较高的机械特性以及充分的挠性，可用作超导绝缘材料，PPS薄膜有着显著的电气性能，在电绝缘材料中比PET膜受温度影响还小，作为电容器介电质其电容量受温度变化频率的影响小，可得到低损耗的电容器，PPS薄膜在常温下还没有可以将其溶解的有机溶剂，其拉伸强度可30浸泡10d于氢氧化钠、稀硝酸、浓盐酸、丁酮、正己烷、丙酮、甲苯、甲醇、苯和二氯甲烷中而不会有所下降，但PPS薄膜对于强氧化性酸，如浓硝酸、浓硫酸等是抵抗不了的，依上所述，PPS薄膜所具有高绝缘性、高耐热性、阻燃性、机械性和高介电性，现如今，PPS薄膜芯片已成功应用于电容器制造业当中，PPS薄膜的高耐热性、难燃性和湿度稳定性，可用来制作感热复印、音响振动板、耐热食品容器和包装袋以及磁记录材料和百叶窗、电线包覆材料等。
可通过注塑、挤出、模压和精密加工成型的聚苯硫醚PPS塑料，在未增强改性的情况下弯曲强度、拉伸强度属中等水平，冲击强度和伸长率由于其主涟上含有大量苯环而呈较低状态，而PPS塑料在各大特殊领域的应用多为增强型，聚苯硫醚PPS与玻璃纤维，芳纶纤维，碳纤维等亲和力较好，这都取决于PPS主涟上硫原子中含有的孤对电子所赋予;通过纤维增强所获得的PPS复合材料可以弥补PPS树脂性能上的缺陷，使其耐热性、力学性能和刚度在进一步得以提高的同时，还能保持良好的耐介质性和阻燃性;纤维可分短纤维和长纤维，长纤维增强PPS复合材料耐高温稳定性良好，能在高温条件下保持较好的刚性，在低温情况下耐磨性、尺寸稳定性和冲击强度以及抗蠕变性能保持良好，同时具有较高的冲击性能、弯曲性能和拉伸性能，耐化学品性和耐腐浊性也相当优异;在应用上，质轻、又能有效节约燃料和增加飞行距离的长纤维增强PPS复合材料已广泛的被应用于航空航天、军事、汽车和化工等领域。
发明内容
发明目的：本发明所要解决不耐磨的技术问题，本发明提供一种耐磨级PPS。
工艺方案：一种耐磨级PPS，其按重量份数表示包括：
PPS树脂40—60；
钛酸钾晶须：10—30；
玻璃纤维：20—30；
四氟乙烯：10—20；
环氧树脂：1-5。
优选于，一种耐磨级PPS制造工艺，括如下步骤，将钛酸钾晶须、四氟乙烯、环氧树脂及PPS树脂按比例配制后，在高速混合机内混合20分钟，然后通过失重称计量喂入双螺杆造粒挤出机，玻璃纤维从侧喂料口喂入，熔融共混后拉条冷却造粒。
优选于，所述四氟乙烯可加压液化，临界温度33.3℃，临界压力3.92MPa。
优选于，所述钛酸钾晶须直径为0.1~0.6μm，长度为3~ 20μm。
优选于，所述玻璃纤维直径为16微米。
本发明具有的优良机械性能和电绝缘性能以及良好的热稳定性、优越的耐化学腐蚀性、优异的抗化学腐蚀性等特点。
具体实施方式
以下通过具体实施例对本发明做进一步阐述，应当指出：对于本工艺领域的普通工艺人员来说，在不脱离本发明原理的前提下，对本发明的各种等价形式的修改均落于本申请所附权利要求所限定的范围。
实施例1：
一种耐磨级PPS，其按重量份数表示包括：
PPS树脂40—60；
钛酸钾晶须：10；
玻璃纤维：20；
四氟乙烯：10—20；
环氧树脂：1-5。
优选于，一种耐磨级PPS制造工艺，括如下步骤，将钛酸钾晶须、四氟乙烯、环氧树脂及PPS树脂按比例配制后，在高速混合机内混合20分钟，然后通过失重称计量喂入双螺杆造粒挤出机，玻璃纤维从侧喂料口喂入，熔融共混后拉条冷却造粒。
优选于，所述四氟乙烯可加压液化，临界温度33.3℃，临界压力3.92MPa。
优选于，所述钛酸钾晶须直径为0.1~0.6μm，长度为3~ 20μm。
优选于，所述玻璃纤维直径为16微米。
本发明具有的优良机械性能和电绝缘性能以及良好的热稳定性、优越的耐化学腐蚀性、优异的抗化学腐蚀性等特点。
实施例2：
一种耐磨级PPS，其按重量份数表示包括：
PPS树脂40—60；
钛酸钾晶须：30；
玻璃纤维：0；
四氟乙烯：10—20；
环氧树脂：1-5。
优选于，一种耐磨级PPS制造工艺，括如下步骤，将钛酸钾晶须、四氟乙烯、环氧树脂及PPS树脂按比例配制后，在高速混合机内混合20分钟，然后通过失重称计量喂入双螺杆造粒挤出机，玻璃纤维从侧喂料口喂入，熔融共混后拉条冷却造粒。
优选于，所述四氟乙烯可加压液化，临界温度33.3℃，临界压力3.92MPa。
优选于，所述钛酸钾晶须直径为0.1~0.6μm，长度为3~ 20μm。
优选于，所述玻璃纤维直径为16微米。
本发明具有的优良机械性能和电绝缘性能以及良好的热稳定性、优越的耐化学腐蚀性、优异的抗化学腐蚀性等特点。
实施例3：
一种耐磨级PPS，其按重量份数表示包括：
PPS树脂40—60；
钛酸钾晶须：20；
玻璃纤维：25；
四氟乙烯：10—20；
环氧树脂：1-5。
优选于，一种耐磨级PPS制造工艺，括如下步骤，将钛酸钾晶须、四氟乙烯、环氧树脂及PPS树脂按比例配制后，在高速混合机内混合20分钟，然后通过失重称计量喂入双螺杆造粒挤出机，玻璃纤维从侧喂料口喂入，熔融共混后拉条冷却造粒。
优选于，所述四氟乙烯可加压液化，临界温度33.3℃，临界压力3.92MPa。
优选于，所述钛酸钾晶须直径为0.1~0.6μm，长度为3~ 20μm。
优选于，所述玻璃纤维直径为16微米。
本发明具有的优良机械性能和电绝缘性能以及良好的热稳定性、优越的耐化学腐蚀性、优异的抗化学腐蚀性等特点。
根据对钛酸钾晶须和玻璃纤维重量不同做出结论，玻璃纤维重量越小，钛酸钾晶须越大，整个塑料制品的稳定性越好，越耐老化，使用寿命更长。
Claims (5)
1.一种耐磨级PPS，其特征在于，其按重量份数表示包括：
PPS树脂40—60；
钛酸钾晶须：10—30；
玻璃纤维：20—30；
四氟乙烯：10—20；
环氧树脂：1-5。
2.根据权利要求1所述一种耐磨级PPS制造工艺，其特征在于，包括如下步骤，将钛酸钾晶须、四氟乙烯、环氧树脂及PPS树脂按比例配制后，在高速混合机内混合20分钟，然后通过失重称计量喂入双螺杆造粒挤出机，玻璃纤维从侧喂料口喂入，熔融共混后拉条冷却造粒。
3.根据权利要求1所述一种导电导热PPS，其特征在于，所述四氟乙烯可加压液化，临界温度33.3℃，临界压力3.92MPa。
4.根据权利要求1所述一种导电导热PPS，其特征在于，所述钛酸钾晶须直径为0.1~0.6μm，长度为3~ 20μm。
5.根据权利要求1所述一种导电导热PPS，其特征在于，所述玻璃纤维直径为16微米。