CN107890777A - 一种干法催化还原脱硝方法 - Google Patents
一种干法催化还原脱硝方法 Download PDFInfo
- Publication number
- CN107890777A CN107890777A CN201711312107.XA CN201711312107A CN107890777A CN 107890777 A CN107890777 A CN 107890777A CN 201711312107 A CN201711312107 A CN 201711312107A CN 107890777 A CN107890777 A CN 107890777A
- Authority
- CN
- China
- Prior art keywords
- denitrfying agent
- catalytic
- dispersant
- reduction denitrified
- lanthanum nitrate
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种干法催化还原脱硝方法，其具体方法步骤是：第一步，制备脱硝剂，所述的脱硝剂由胺(氨)类化合物、硝酸镧、分散剂组成，所述的胺类化合物、硝酸镧、分散剂的质量比为(2.5～3)∶(0.2～0.3)∶(0.1～0.2)。第二步，将脱硝剂置于带喷枪的储罐中。第三步，在炉膛温度为450℃～1450℃时，将脱硝剂均匀喷于炉膛中，脱硝剂在反应区内将烟气中氮氧化物还原为氮气和水，脱硝后的净烟气由烟囱排出。本发明工艺简单，运行成本低，经济适用，适用于规模化推广应用的方法。
Description
一、技术领域
本发明涉及一种工业废气的干法脱硝方法，具体地说是一种干法催化还原脱硝方法。
二、背景技术
当前，各行各业应用的工业窑炉、分解炉、锅炉所产生的烟尘中含有大量的二氧化硫、氮氧化物(NOx)、粉尘等有害气体，有害气体排入大气中造成污染，破坏生态环境，对人体健康构成巨大的威胁。氮氧化物(NOx)是有害气体中主要的大气污染物之一，不仅会产生光化学烟雾和酸雨，还会导致严重的温室效应及破坏臭氧层。因此对工业废气的脱硝问题日益受到人们的重视，有效去除烟气排放中的氮氧化物(NOx)成为保护大气环境的有效途径。
烟气脱硝技术是一种对氮氧化物(NOx)进行控制的技术，主要是通过各种物理、化学过程使烟气中的氮氧化物还原成氮气，常用的方法有氧化还原法、吸收和吸附法。对于氧化还原法是利用氧化剂与烟气中的氮氧化物反应生成无害的氮气和水，从而去除烟气中的氮氧化物。当前，该种方法应用多数是在多级净化塔中进行的，是先将烟气引入净化塔中，再向烟气中喷入氧气，氧气与氮氧化物进行氧化还原反应实现净化的。中国专利(CN102357340 A)公开了一种氮氧化物净化塔，该塔由左右两级塔构成，左侧塔有进烟口、注氧口、氧化填料室；右侧塔体内从下至上依次固定有多层塔孔板、喷淋管、旋流板、挡水环和排烟口。进烟口进入的烟尘中的氮氧化物与氧气反应经填料室改变成分，经水面冲击、导流板自激、喷淋管喷淋多级净化，使烟尘中的氮氧化物得到净化。此法应用的脱硝设备投资和运行费用大，占地面积大，工艺复杂，操作与维修困难。
三、发明内容
为了解决现有技术的不足，本发明的目的是提供一种干法催化还原脱硝方法。该种方法是一种脱硝工艺简单，运行成本低，经济适用，适用于规模化推广应用的方法。
实现本发明的目的采用的技术方案是：一种干法催化还原脱硝方法，其具体方法步骤是：
第一步，制备脱硝剂，所述的脱硝剂由胺(氨)类化合物、硝酸镧、分散剂组成，所述的胺类化合物、硝酸镧、分散剂的质量比为(2.5～3)∶(0.2～0.3)∶(0.1～0.2)。
第二步，将脱硝剂置于带喷枪的储罐中。
第三步，在炉膛温度为450℃～1450℃时，将脱硝剂均匀喷于炉膛中，脱硝剂在反应区内将烟气中氮氧化物还原为氮气和水，脱硝后的净烟气由烟囱排出。
所述的胺(氨)类化合物为三聚氰胺、尿素、氯化铵、硫酸铵、碳酸氢铵中的一种。
所述的分散剂为石墨粉、交联耦合剂中的一种。
本发明的有益效果是：由于本发明应用了能够提高氮氧化物去除率高的脱硝剂，又将脱硝剂直接喷入产生氮氧化物的炉膛内，将烟气中氮氧化物还原为氮气和水，可有效去除烟气中氮氧化物。所以，本发明工艺简单，运行成本低，经济适用，适用于规模化推广应用的方法。
四、具体实施方式
本发明一种干法催化还原脱硝方法，其具体方法步骤是：
第一步，制备脱硝剂，所述的脱硝剂由胺(氨)类化合物、硝酸镧、分散剂组成，所述的胺类化合物、硝酸镧、分散剂的质量比为(2.5～3)∶(0.2～0.3)∶(0.1～0.2)。
第二步，将脱硝剂置于带喷枪的储罐中。
第三步，在炉膛温度为450℃～1450℃时，将脱硝剂均匀喷于炉膛中，脱硝剂在反应区内将烟气中氮氧化物还原为氮气和水，脱硝后的净烟气由烟囱排出。
所述的胺(氨)类化合物为三聚氰胺、尿素、氯化铵、硫酸铵、碳酸氢铵中的一种。
所述的分散剂为石墨粉、交联耦合剂中的一种。
所述的胺(氨)类化合物为一种还原剂，所述的硝酸镧为一种催化剂，其脱硝原理是：高温烟气中的氮氧化物(NOx)在催化剂作用下与还原剂反应，是NOx被还原成氨气和水。
其化学反应方程式为：
Claims (3)
1.一种干法催化还原脱硝方法，其具体方法步骤是：
第一步，制备脱硝剂，所述的脱硝剂由胺(氨)类化合物、硝酸镧、分散剂组成，所述的胺类化合物、硝酸镧、分散剂的质量比为(2.5～3)∶(0.2～0.3)∶(0.1～0.2)。
第二步，将脱硝剂置于带喷枪的储罐中。
第三步，在炉膛温度为450℃～1450℃时，将脱硝剂均匀喷于炉膛中，脱硝剂在反应区内将烟气中氮氧化物还原为氮气和水，脱硝后的净烟气由烟囱排出。
2.如权利要求1所述的一种干法催化还原脱硝方法，其特征在于：所述的胺(氨)类化合物为三聚氰胺、尿素、氯化铵、硫酸铵、碳酸氢铵中的一种。
3.如权利要求1所述的一种干法催化还原脱硝方法，其特征在于：所述的分散剂为石墨粉、交联耦合剂中的一种。